CN106893214A - A kind of attapulgite material for plastic flower and preparation method thereof - Google Patents
A kind of attapulgite material for plastic flower and preparation method thereof Download PDFInfo
- Publication number
- CN106893214A CN106893214A CN201710231015.2A CN201710231015A CN106893214A CN 106893214 A CN106893214 A CN 106893214A CN 201710231015 A CN201710231015 A CN 201710231015A CN 106893214 A CN106893214 A CN 106893214A
- Authority
- CN
- China
- Prior art keywords
- parts
- attapulgite
- starch
- plastic flower
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of attapulgite material for plastic flower and preparation method thereof, including following weight portion raw material：40~50 parts of raw materials for plastics production, 10~18 parts of attapulgite powder, 15~25 parts of polyethylene, 2~3 parts of folium artemisiae argyi, 3~5 parts of ultraviolet screener, 7~15 parts of colouring agent, 3~7 parts of aromatic, 1~2 part of starch, 1~5 part of activated carbon；The raw material sequentially passes through and dries, grinding, fusing, moulding can obtain the attapulgite material for plastic flower；The attapulgite material fragrance release is slow, and guarantor's fragrant time is long, and low cost, softness is not easily broken, handsome in appearance true to nature, easily promotes.
Description
Technical field
The invention belongs to plastics arts, and in particular to a kind of for the attapulgite material of plastic flower and its preparation side
Method.
Background technology
, using plastic flower as ornament, plastics are, with monomer as raw material, to pass through for many megastore and meeting scene
The macromolecular compound (macromolecules) of addition polymerization or polycondensation polymerized, is commonly called as plastics (plastics) or resin
(resin) composition and body styles, can freely be changed, by synthetic resin and filler, plasticizer, stabilizer, lubricant, colorant
Deng additive composition.
The main component of plastics is resin.Resin this noun is initially the lipid that is secreted out of by animals and plants and gains the name, such as
Rosin, shellac etc., resin refer to the macromolecular compound for not yet mixing with various additives.Resin accounts for plastics gross weight
40%~100%.The key property of plastics depends mainly on the person's character of resin, but additive also plays an important role.Some plastics
Substantially be made up of synthetic resin, without or contain additive, such as lucite, polystyrene less.
But existing plastics fragrance not persistently, high cost, it is easily rupturable, can even discharge toxic gas.
The content of the invention
The invention provides a kind of attapulgite material for plastic flower and preparation method thereof, the attapulgite material fragrance
Release is slow, and guarantor's fragrant time is long, and low cost, softness is not easily broken, handsome in appearance true to nature.
In order to solve the problems, such as prior art, adopt the following technical scheme that：
A kind of attapulgite material for plastic flower of the invention, including following weight portion raw material：Raw materials for plastics production 40~50
Part, 10~18 parts of attapulgite powder, 15~25 parts of polyethylene, 2~3 parts of folium artemisiae argyi, 3~5 parts of ultraviolet screener, colouring agent 7~15
Part, 3~7 parts of aromatic, 1~2 part of starch, 1~5 part of activated carbon.
Preferably, the attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 42~
45 parts, 13~15 parts of attapulgite powder, 20~22 parts of polyethylene, 2.5~2.7 parts of folium artemisiae argyi, 4~4.8 parts of ultraviolet screener, coloring
9~11 parts of agent, 5~6 parts of aromatic, 1.3~1.5 parts of starch, 2~3 parts of activated carbon.
Preferably, the attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 44
Part, 14.7 parts of attapulgite powder, 21 parts of polyethylene, 2.6 parts of folium artemisiae argyi, 4.7 parts of ultraviolet screener, 10 parts of colouring agent, aromatic 5.8
Part, 1.4 parts of starch, 2.7 parts of activated carbon.
Preferably, the plastic raw materials are the mixture of one or more in AS, ABS, HIPS, GPPS, PC, PA, PMMA.
Preferably, the starch is cornstarch.
Preferably, the aromatic is plant extracts.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Melt in furnace is into being positioned in 80~100 DEG C of environment after plastics magma；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Preferably, the temperature of the smelting furnace is 200~500 DEG C.
Compared with prior art, it has the advantages that the present invention：
（1）, using attapulgite powder as raw material, fragrance release is slow, protects fragrant for attapulgite material for plastic flower of the present invention
Time is long, and low cost, softness is not easily broken, handsome in appearance true to nature；
（2）The present invention states attapulgite material for plastic flower using attapulgite powder and polyethylene as raw material, attapulgite
Powder and polyethylene form composite, there is good anti-flammability and corrosion resistance；
（3）The present invention states attapulgite material for plastic flower using attapulgite powder and activated carbon, starch as raw material, concavo-convex
Rod stone flour and activated carbon, starch constitute composite, stable performance, low cost together；
（4）Attapulgite material reasonable mixture ratio for plastic flower of the present invention, inexpensive, manufacture craft is simple, is adapted to push away
Extensively.
Specific embodiment
With reference to specific embodiment, the present invention is expanded on further.These embodiments be merely to illustrate the present invention and without
In limitation the scope of the present invention.
Embodiment 1
The present embodiment is related to a kind of attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 40
Part, 10 parts of attapulgite powder, 15 parts of polyethylene, 2 parts of folium artemisiae argyi, 3 parts of ultraviolet screener, 7 parts of colouring agent, 3 parts of aromatic, starch 2
Part, 5 parts of activated carbon.
In the present embodiment, the plastic raw materials are the mixture of AS, ABS, HIPS, GPPS, PC, PA, PMMA.
In the present embodiment, the starch is cornstarch, increases the cohesive force between each raw material.
In the present embodiment, the aromatic is plant extracts, the lasting fragrance for being distributed, and pollution-free.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Melt in furnace is positioned in 80~100 DEG C of environment into plastics magma, and the temperature of smelting furnace is 200 DEG C；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Embodiment 2
The present embodiment is related to a kind of attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 50
Part, 18 parts of attapulgite powder, 25 parts of polyethylene, 3 parts of folium artemisiae argyi, 5 parts of ultraviolet screener, 15 parts of colouring agent, 7 parts of aromatic, starch 2
Part, 5 parts of activated carbon.
In the present embodiment, the plastic raw materials are the mixture of AS, ABS, HIPS, GPPS, PC, PA.
In the present embodiment, the starch is cornstarch, increases the cohesive force between each raw material.
In the present embodiment, the aromatic is plant extracts, the lasting fragrance for being distributed, and pollution-free.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Into being positioned in 100 DEG C of environment after plastics magma, the temperature of smelting furnace is 500 DEG C to melt in furnace；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Embodiment 3
The present embodiment is related to a kind of attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 42
Part, 13 parts of attapulgite powder, 20 parts of polyethylene, 2.5 parts of folium artemisiae argyi, 4 parts of ultraviolet screener, 9 parts of colouring agent, 5 parts of aromatic, starch
1.3 parts, 2 parts of activated carbon.
In the present embodiment, the plastic raw materials are the mixture of AS.
In the present embodiment, the starch is cornstarch, increases the cohesive force between each raw material.
In the present embodiment, the aromatic is plant extracts, the lasting fragrance for being distributed, and pollution-free.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Into being positioned in 85 DEG C of environment after plastics magma, the temperature of smelting furnace is 300 DEG C to melt in furnace；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Embodiment 4
The present embodiment is related to a kind of attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 45
Part, 15 parts of attapulgite powder, 22 parts of polyethylene, 2.7 parts of folium artemisiae argyi, 4.8 parts of ultraviolet screener, 11 parts of colouring agent, 6 parts of aromatic,
1.5 parts of starch, 3 parts of activated carbon.
In the present embodiment, the plastic raw materials are the mixture of ABS, HIPS, GPPS, PC, PA, PMMA.
In the present embodiment, the starch is cornstarch, increases the cohesive force between each raw material.
In the present embodiment, the aromatic is plant extracts, the lasting fragrance for being distributed, and pollution-free.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Into being positioned in 90 DEG C of environment after plastics magma, the temperature of smelting furnace is 280 DEG C to melt in furnace；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Embodiment 5
The present embodiment is related to a kind of attapulgite material for plastic flower, including following weight portion raw material：Raw materials for plastics production 44
Part, 14.7 parts of attapulgite powder, 21 parts of polyethylene, 2.6 parts of folium artemisiae argyi, 4.7 parts of ultraviolet screener, 10 parts of colouring agent, aromatic 5.8
Part, 1.4 parts of starch, 2.7 parts of activated carbon.
In the present embodiment, the plastic raw materials are one or more mixed in AS, ABS, HIPS, GPPS, PC, PA, PMMA
Compound.
In the present embodiment, the starch is cornstarch, increases the cohesive force between each raw material.
In the present embodiment, the aromatic is plant extracts, the lasting fragrance for being distributed, and pollution-free.
A kind of method for preparing the attapulgite material for plastic flower, comprises the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Into being positioned in 100 DEG C of environment after plastics magma, the temperature of smelting furnace is 480 DEG C to melt in furnace；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
Be can be seen that from above-described embodiment, the attapulgite material fragrance release is slow, guarantor's fragrant time is long, low cost, and softness is not
It is easily rupturable, it is handsome in appearance true to nature.
Specific embodiment of the invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can within the scope of the claims make various deformations or amendments, this not shadow
Sound substance of the invention.
Claims (8)
1. a kind of attapulgite material for plastic flower, it is characterised in that the raw material including following weight portion：Raw materials for plastics production 40
~50 parts, 10~18 parts of attapulgite powder, 15~25 parts of polyethylene, 2~3 parts of folium artemisiae argyi, 3~5 parts of ultraviolet screener, colouring agent 7
~15 parts, 3~7 parts of aromatic, 1~2 part of starch, 1~5 part of activated carbon.
2. the attapulgite material for plastic flower according to claim 1, it is characterised in that the original including following weight portion
Material：42~45 parts of raw materials for plastics production, 13~15 parts of attapulgite powder, 20~22 parts of polyethylene, 2.5~2.7 parts of folium artemisiae argyi, UV resistance
4~4.8 parts of line agent, 9~11 parts of colouring agent, 5~6 parts of aromatic, 1.3~1.5 parts of starch, 2~3 parts of activated carbon.
3. the attapulgite material for plastic flower according to claim 1, it is characterised in that the original including following weight portion
Material：44 parts of raw materials for plastics production, 14.7 parts of attapulgite powder, 21 parts of polyethylene, 2.6 parts of folium artemisiae argyi, 4.7 parts of ultraviolet screener, coloring
10 parts of agent, 5.8 parts of aromatic, 1.4 parts of starch, 2.7 parts of activated carbon.
4. the attapulgite material for plastic flower according to claim 1, it is characterised in that the plastic raw materials be AS,
The mixture of one or more in ABS, HIPS, GPPS, PC, PA, PMMA.
5. the attapulgite material for plastic flower according to claim 1, it is characterised in that the starch is that corn forms sediment
Powder.
6. the attapulgite material for plastic flower according to claim 1, it is characterised in that the aromatic is carried for plant
Take thing.
7. it is a kind of prepare described in any one of claim 1~6 be used for plastic flower attapulgite material method, it is characterised in that
Comprise the following steps：
（1）The attapulgite powder, folium artemisiae argyi, starch, activated carbon are put into drying machine and are dried, until its water content is less than
3%, keep standby；
（2）By step（1）The dry attapulgite powder for completing, folium artemisiae argyi, starch, activated carbon are well mixed, and are put into grinder, grind
Cheng Fen, crosses 1000 mesh sieves；
（3）The raw materials for plastics production, polyethylene powder are broken into the particle of a diameter of 0.1~0.3mm, are well mixed, be then placed in
Melt in furnace is into being positioned in 80~100 DEG C of environment after plastics magma；
（4）Sequentially added in plastics magma and dry the attapulgite powder of completion, folium artemisiae argyi, starch, activated carbon, ultraviolet screener,
Toner, aromatic are put into moulding in plastics machine after stirring, be subsequently cooled to room temperature, you can obtain described for plastic flower
Attapulgite material.
8. preparation method according to claim 7, it is characterised in that the temperature of the smelting furnace is 200~500 DEG C.