CN106868933B - A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil and its manufacturing process - Google Patents

A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil and its manufacturing process Download PDF

Info

Publication number
CN106868933B
CN106868933B CN201710224310.5A CN201710224310A CN106868933B CN 106868933 B CN106868933 B CN 106868933B CN 201710224310 A CN201710224310 A CN 201710224310A CN 106868933 B CN106868933 B CN 106868933B
Authority
CN
China
Prior art keywords
layer
fragrant
aluminium foil
moisturizing
original paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710224310.5A
Other languages
Chinese (zh)
Other versions
CN106868933A (en
Inventor
陈毕峰
陈慷磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Huadu Lianhua Packing Material Co Ltd
Original Assignee
Guangzhou Huadu Lianhua Packing Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Huadu Lianhua Packing Material Co Ltd filed Critical Guangzhou Huadu Lianhua Packing Material Co Ltd
Priority to CN201710224310.5A priority Critical patent/CN106868933B/en
Publication of CN106868933A publication Critical patent/CN106868933A/en
Priority to PCT/CN2017/093812 priority patent/WO2018184322A1/en
Application granted granted Critical
Publication of CN106868933B publication Critical patent/CN106868933B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

It guarantees the quality the fragrant compound tobacco lining paper of aluminium foil, including original paper layer the invention discloses a kind of constant humidity, wherein：The upper surface of the original paper layer is also disposed with composite layer, aluminium foil layer and aqueous protective layer from the inside to the outside, the lower surface of the original paper layer is equipped with moisture also wet layer, and the tobacco lining paper further includes the fragrant layer of moisturizing guarantor for being set to the original paper layer upper surface or lower surface；Wherein, the moisturizing is protected fragrant layer and is set between the original paper layer and composite layer, is set between the original paper layer and moisture also wet layer alternatively, fragrant layer is protected in the moisturizing.In addition, the manufacturing process for the compound tobacco lining paper of fragrant aluminium foil of guaranteeing the quality the invention also discloses the constant humidity.The compound tobacco lining paper of aluminium foil of the present invention is protected the setting of fragrant layer by moisturizing, can effectively balance cigarette product moisture, keep the quality of cigarette product.

Description

A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil and its manufacturing process
Technical field
The present invention relates to a kind of internal lining paper and its manufacturing process, and in particular to it is a kind of for cigarette pack, have constant humidity The compound tobacco lining paper of aluminium foil of Xiang Gong of guaranteeing the quality energy and its corresponding manufacturing process, belong to pulp technology for making paper.
Background technology
Supplementary material of the tobacco lining paper as cigarette package, effect is the iris action for playing cigarette.Existing market On the tobacco lining paper that uses, mainly by aluminium foil compound lining paper, transfer internal lining paper, the vacuum aluminum-coated internal lining paper and without aluminium of aluminizing Internal lining paper clock.Due to the difference of internal lining paper penetrability index and the moisture (5% ± 1%) of its calibration, when cigarette packet It installs after finishing and entering market, with resting period and the difference of envionmental humidity, temperature, the moisture of cigarette itself can be due to Resting period is longer and high temperature, high humidity storage environment and go mouldy, and the storage environment of low temperature, low humidity can then influence to roll up The quality of cigarette.Therefore, how to solve cigarette due to relative humidity, temperature variation caused by the variation of cigarette quality ask Topic, is always Field of Tobacco urgent problem to be solved.
Invention content
It is an object of the invention to overcome the deficiencies of the prior art and provide it is a kind of with constant humidity guarantee the quality Xiang Gong energy aluminium foil Compound tobacco lining paper.In addition, another object of the present invention is to provide a kind of constant humidity fragrant aluminium foil composite smokes of guaranteeing the quality to use The manufacturing process of internal lining paper.
To achieve the above object, the present invention uses following technical scheme：
A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil, including original paper layer, wherein：The upper surface of the original paper layer It is also disposed with composite layer, aluminium foil layer and aqueous protective layer from the inside to the outside, the lower surface of the original paper layer is equipped with moisture Also wet layer, the tobacco lining paper further include the fragrant layer of moisturizing guarantor for being set to the original paper layer upper surface or lower surface.
Preferably：The moisturizing is protected fragrant layer and is set between the original paper layer and composite layer.
Preferably：The moisturizing is protected fragrant layer and is set between the original paper layer and moisture also wet layer.
Preferably：It is inorganic powder or organic powder material layer that fragrant layer is protected in the moisturizing, and fragrant layer is protected in the moisturizing Dry-coated amount is 1g/m2-5g/m2。
Preferably：The grain size of the inorganic powder or organic dust is 0.3-100 μm, specific surface area 30-2000g/ m2。
Preferably：The composite layer is aqueous composite layer, and dry-coated amount is 1g/m2-5g/m2, solidification temperature 80 ℃-120℃。
Preferably：The thickness of the aluminium foil layer is 0.006mm.
Preferably：The dry-coated amount of the aqueous protective layer is 1g/m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C.
Another object of the present invention, a kind of manufacturing process of tobacco lining paper as described above comprising following manufacturing step：
1) moisturizing is formed in the upper surface of the original paper layer by way of roller coating or spraying and protect fragrant layer, wherein the guarantor The wet dry-coated amount for protecting fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
2) upper surface for protecting fragrant layer in the moisturizing by gravure technique forms composite layer, wherein the composite layer Dry-coated amount be 1g/m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C；
3) by wet type combination process, it is compound to form aluminium foil layer through composite layer that aluminium foil and moisturizing are protected into fragrant layer；
4) aqueous protective layer is formed on the surface of the aluminium foil layer, wherein described aqueous anti-by way of intaglio printing The dry-coated amount of sheath is 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
5) plus water carries out also wet process to form moisture in the lower surface of the original paper layer to the lower surface of the original paper layer Also wet layer controls the moisture of finished paper 5% ± 1%.
Alternatively, the manufacturing process of the tobacco lining paper, may include following manufacturing step：
1) composite layer is formed in the upper surface of original paper layer by gravure technique, wherein the dry-coated amount of the composite layer For 1g/m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C；
2) by wet type combination process, aluminium foil and original paper layer is compound to form aluminium foil layer through composite layer；
3) aqueous protective layer is formed on the surface of the aluminium foil layer, wherein described aqueous anti-by way of intaglio printing The dry-coated amount of sheath is 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
4) moisturizing is formed in the lower surface of the original paper layer by way of roller coating or spraying and protect fragrant layer, wherein the guarantor The wet dry-coated amount for protecting fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
5) plus water is carried out also wet process to the lower surface of the original paper layer and is formed with the lower surface for protecting fragrant layer in the moisturizing Moisture also wet layer controls the moisture of finished paper 5% ± 1%.
The beneficial effects of the present invention are, the compound tobacco lining paper of aluminium foil of the invention protects the setting of fragrant layer by moisturizing, Achievable cigarette product can absorb moisture when being stored under high temperature, high humidity environment, and the energy when depositing under low temperature, low moisture environments Discharge moisture, will not because the length of resting period and envionmental humidity, temperature difference due to reduce the quality of cigarette.Can have Effect ground balance cigarette product moisture, keeps the quality of cigarette product.
Description of the drawings
Fig. 1 shows that constant humidity of the present invention is guaranteed the quality the structural schematic diagram of the fragrant compound tobacco lining paper of aluminium foil；
Fig. 2 shows the guarantee the quality structures of the fragrant compound tobacco lining paper of aluminium foil of the constant humidity in another embodiment of the invention to show It is intended to.
Specific implementation mode
The following further describes the specific embodiments of the present invention with reference to the drawings.
As shown in Figure 1, constant humidity of the present invention is guaranteed the quality, the fragrant compound tobacco lining paper of aluminium foil includes original paper layer 1, described The upper surface of original paper layer 1 is also cascading from the inside to the outside composite layer 3, aluminium foil layer 4 and aqueous protective layer 5, described The lower surface of original paper layer 1 is additionally provided with moisture also wet layer 6.In addition, internal lining paper of the present invention, which further includes moisturizing, protects fragrant layer 2, institute The upper surface of the original paper layer 1 can be arranged by stating moisturizing guarantor's perfume layer 2, between the original paper layer 1 and composite layer 3.Alternatively, such as Shown in Fig. 2, the moisturizing is protected fragrant layer 2 and be may be disposed between the original paper layer 1 and moisture also wet layer 6.
Specifically, in the present invention, aluminium foil composite base paper layer can be used in the original paper layer 1；The composite layer 3 will be aqueous Compound adhesive is formed in the original paper layer 1 by gravure technique or the upper surface of fragrant layer 2 is protected in moisturizing, wherein the gravure technique Intaglio plate pit depth is 30 μm -70 μm, and dry-coated amount is 1g/m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C.
It is preferably that the aluminium foil of 0.006mm and moisturizing protect fragrant layer 2 or original paper layer 1 through multiple by thickness by wet type combination process It is compound to form aluminium foil layer 4 to close glue-line 3.
Then, by the way of intaglio printing, aqueous protective layer 5 is formed on the surface of the aluminium foil layer 4, is prevented with playing It scratches the aluminium foil layer 4 and ensures the smooth effect of the internal lining paper, wherein the dry-coated amount 1g/ of the aqueous protective layer 5 m2-5g/m2, at 80-120 DEG C, used intaglio plate pit depth is 30 μm -50 μm for solidification temperature control.
Water is added to carry out also wet process/humidification process to the lower surface of the original paper layer 1 in the lower surface of the original paper layer 1 Moisture also wet layer 7 is formed, so that the moisture of finished paper is controlled 5% ± 1%.
In addition, the internal lining paper may also include between 1 upper surface of the original paper layer and the composite layer 3 or position Fragrant layer 2 is protected in moisturizing between the lower surface of the original paper layer 1 and the moisture also wet layer 6, and it is inorganic that fragrant layer 2 is protected in the moisturizing Powder or organic powder material layer, wherein the inorganic powder is ceramic powders, and the organic dust is high molecular material powder End；And the grain size of the inorganic powder or organic dust is 0.3-100 μm, specific surface area 30-2000g/m2, pass through roller coating Or the mode of spraying is formed in the upper surface or lower surface of original paper layer 1, also, it is 1g/ that the dry-coated amount of fragrant layer 2 is protected in the moisturizing m2-5g/m2, and be anilox roll used by roller coating, pit depth is 30 μm -80 μm, and anilox roll line number is -150 line of 10 line, Its solidification temperature is 80 DEG C -120 DEG C.
Embodiment 1
A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil, structure as shown in Figure 1, including original paper layer 1 and from Fragrant layer 2, composite layer 3, aluminium foil layer 4 and aqueous are protected in the interior moisturizing to the upper surface for being cascadingly set on the original paper layer 1 outside The lower surface of protective layer 5, the original paper layer 1 is also formed with moisture also wet layer 6.The manufacturing step of the internal lining paper includes：
1) it is 50 μm by grain size by way of roller coating, specific surface area 60g/m2Ceramic powders be coated on original paper layer 1 Upper surface form moisturizing and protect fragrant layer 2, wherein the dry-coated amount that fragrant layer 2 is protected in the moisturizing is 3g/m2, employed in roller coating process Anilox roll pit depth be 60 μm, anilox roll line number be 100 lines, solidification temperature be 100 DEG C；
2) upper surface that aqueous compound adhesive is protected by gravure technique in the moisturizing to fragrant layer 2 forms composite layer 3, wherein The intaglio plate pit depth of the gravure technique is 35 μm, and dry-coated amount is 5g/m2, solidification temperature is 100 DEG C；
It is 3) by wet type combination process, thickness is compound through composite layer 3 for the aluminium foil of 0.006mm and the fragrant layer 2 of moisturizing guarantor, To form aluminium foil layer 4；
4) an aqueous protective layer 5 is formed on the surface of the aluminium foil layer 4 by way of intaglio printing, prevents from drawing to play Hinder the aluminium foil layer 4 and ensure the smooth effect of the internal lining paper, wherein the dry-coated amount 3g/m of the aqueous protective layer 52, Solidification temperature is controlled at 100 DEG C, and used intaglio plate depth is 40 μm；
5) plus water carries out also wet process in the lower surface shape of the original paper layer 1 to the original paper layer 1 without aluminium lower surface At moisture also wet layer 6, so that the moisture of finished paper is controlled 5% ± 1%.
Embodiment 2
A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil, structure as shown in Fig. 2, including original paper layer 1 and from Interior composite layer 3, aluminium foil layer 4 and aqueous protective layer 5 to the upper surface for being cascadingly set on the original paper layer 1 outside, it is described The lower surface of original paper layer 1 is sequentially formed with moisturizing and protects fragrant layer 2 and moisture also wet layer 6 from the inside to the outside.The manufacture of the internal lining paper Step includes：
1) aqueous compound adhesive is formed into composite layer 3 by gravure technique in the upper surface of the original paper layer 1, wherein described The intaglio plate pit depth of gravure technique is 70 μm, and dry-coated amount is 2g/m2, solidification temperature is 12 DEG C；
2) by wet type combination process, thickness is compound with shape through composite layer 3 for the aluminium foil and original paper layer 1 of 0.006mm At aluminium foil layer 4；
3) an aqueous protective layer 5 is formed on the surface of the aluminium foil layer 4 by way of intaglio printing, prevents from drawing to play Hinder the aluminium foil layer 4 and ensure the smooth effect of the internal lining paper, wherein the dry-coated amount 5g/m of the aqueous protective layer 52, Solidification temperature is controlled at 120 DEG C, and used intaglio plate pit depth is 50 μm；
4) it is 1 μm by grain size by way of spraying, specific surface area 2000g/m2Macromolecule material powder be sprayed at The lower surface of original paper layer 1 forms moisturizing and protects fragrant layer 2, wherein the dry-coated amount that fragrant layer 2 is protected in the moisturizing is 1g/m2, and its solidification temperature Degree is 100 DEG C；
5) also wet process is carried out to be formed in guarantee the quality fragrant 2 lower surface of the constant humidity to the lower surface of the original paper layer 1 Moisture also wet layer 6, so that the moisture of finished paper is controlled 5% ± 1%.
The present invention has carried out detailed explanation by preferred embodiment.However, by studying carefully above, to each The variation and increase of embodiment are also apparent to those of ordinary skill in the art.It is intended that it is all this A little variations and increase are fallen in the protection domain of the claims in the present invention.Term used herein is only to specifically implementing Example is illustrated, and is not intended to and is limited the invention.Unless otherwise defined, all terms used herein (including Technical terms and scientific terms) it is identical as the understanding of those skilled in the art of the art.It is any to this product into Capable modification and improvement, similar in the scope of the claims or scope or close substance replacement and use, belong to patent of the present invention Protection domain.

Claims (8)

  1. The manufacturing method of the compound tobacco lining paper of fragrant aluminium foil 1. a kind of constant humidity is guaranteed the quality, the internal lining paper includes original paper layer, described The upper surface of original paper layer is also disposed with composite layer, aluminium foil layer and aqueous protective layer from the inside to the outside, the original paper layer Lower surface is equipped with moisture also wet layer, and the tobacco lining paper further includes the fragrant layer of moisturizing guarantor for being set to the original paper layer upper surface, It is characterized in that the manufacturing method includes the following steps：
    1) moisturizing is formed in the upper surface of the original paper layer by way of roller coating or spraying and protect fragrant layer, wherein the moisturizing is protected The dry-coated amount of fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
    2) upper surface for protecting fragrant layer in the moisturizing by gravure technique forms composite layer, wherein the composite layer is done Painting amount is 1g/m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C；
    3) by wet type combination process, it is compound to form aluminium foil layer through composite layer that aluminium foil and moisturizing are protected into fragrant layer；
    4) aqueous protective layer is formed on the surface of the aluminium foil layer, wherein the aqueous protective layer by way of intaglio printing Dry-coated amount be 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
    5) plus water carries out also wet process with also wet in the lower surface of original paper layer formation moisture to the lower surface of the original paper layer Layer controls the moisture of finished paper 5% ± 1%.
  2. 2. the manufacturing method of tobacco lining paper according to claim 1, it is characterised in that：It is inorganic that fragrant layer is protected in the moisturizing Powder or organic powder material layer.
  3. 3. the manufacturing method of tobacco lining paper according to claim 2, it is characterised in that：The inorganic powder or organic powder The grain size at end is 0.3-100 μm, specific surface area 30-2000g/m2。
  4. 4. the manufacturing method of the tobacco lining paper according to any one of claim 1-3, it is characterised in that：It is described compound Glue-line is aqueous composite layer.
  5. 5. the manufacturing method of the tobacco lining paper according to any one of claim 1-3, it is characterised in that：The aluminium foil The thickness of layer is 0.006mm.
  6. The manufacturing method of the compound tobacco lining paper of fragrant aluminium foil 6. a kind of constant humidity is guaranteed the quality, wherein the internal lining paper includes original paper layer, The upper surface of the original paper layer is also disposed with composite layer, aluminium foil layer and aqueous protective layer, the body paper from the inside to the outside The lower surface of layer is equipped with moisture also wet layer, and the tobacco lining paper further includes the moisturizing guarantor's perfume for being set to the original paper layer lower surface Layer, it is characterised in that the manufacturing method includes the following steps：
    1) composite layer is formed in the upper surface of original paper layer by gravure technique, wherein the dry-coated amount of the composite layer is 1g/ m2-5g/m2, solidification temperature is 80 DEG C -120 DEG C；
    2) by wet type combination process, aluminium foil and original paper layer is compound to form aluminium foil layer through composite layer；
    3) aqueous protective layer is formed on the surface of the aluminium foil layer, wherein the aqueous protective layer by way of intaglio printing Dry-coated amount be 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
    4) moisturizing is formed in the lower surface of the original paper layer by way of roller coating or spraying and protect fragrant layer, wherein the moisturizing is protected The dry-coated amount of fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
    5) plus water carries out also wet process to the lower surface of the original paper layer and forms moisture with the lower surface for protecting fragrant layer in the moisturizing Also wet layer controls the moisture of finished paper 5% ± 1%.
  7. The compound tobacco lining paper of fragrant aluminium foil 7. the constant humidity manufactured by any one method in claim 1-5 is guaranteed the quality.
  8. The compound tobacco lining paper of fragrant aluminium foil 8. the constant humidity of the method manufacture of claim 6 is guaranteed the quality.
CN201710224310.5A 2017-04-07 2017-04-07 A kind of constant humidity is guaranteed the quality the compound tobacco lining paper of fragrant aluminium foil and its manufacturing process Active CN106868933B (en)