CN106894294A - A kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper and its manufacturing process - Google Patents

A kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper and its manufacturing process Download PDF

Info

Publication number
CN106894294A
CN106894294A CN201710224683.2A CN201710224683A CN106894294A CN 106894294 A CN106894294 A CN 106894294A CN 201710224683 A CN201710224683 A CN 201710224683A CN 106894294 A CN106894294 A CN 106894294A
Authority
CN
China
Prior art keywords
layer
moisturizing
fragrant
paper
original paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710224683.2A
Other languages
Chinese (zh)
Inventor
陈毕峰
陈慷磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Huadu Lianhua Packing Material Co Ltd
Original Assignee
Guangzhou Huadu Lianhua Packing Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Huadu Lianhua Packing Material Co Ltd filed Critical Guangzhou Huadu Lianhua Packing Material Co Ltd
Priority to CN201710224683.2A priority Critical patent/CN106894294A/en
Publication of CN106894294A publication Critical patent/CN106894294A/en
Priority to PCT/CN2017/093825 priority patent/WO2018184323A1/en
Pending legal-status Critical Current

Abstract

Perfume is guaranteed the quality without aluminium tobacco lining paper, including original paper layer the invention discloses a kind of constant humidity, wherein：The upper surface of the original paper layer is also disposed with hot-melting sealed layer, aqueous sealant, water-based printing layer and aqueous overcoat from the inside to the outside, the lower surface of the original paper layer is provided with moisture also wet layer, and the tobacco lining paper also includes that being arranged at the original paper layer upper surface or the moisturizing of lower surface protects fragrant layer；Wherein, the moisturizing is protected fragrant layer and is arranged between the original paper layer and hot-melting sealed layer, or, the moisturizing is protected fragrant layer and is arranged between the original paper layer and moisture also wet layer.Additionally, being guaranteed the quality the fragrant manufacturing process without aluminium tobacco lining paper the invention also discloses the constant humidity.It is of the invention that the setting of fragrant layer is protected by moisturizing without aluminium tobacco lining paper, cigarette product moisture can be effectively balanced, keep the quality of cigarette product.

Description

A kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper and its manufacturing process
Technical field
The present invention relates to a kind of internal lining paper and its manufacturing process, and in particular to it is a kind of for cigarette pack, with constant humidity The tobacco lining paper and its corresponding manufacturing process of Xiang Gong of guaranteeing the quality energy, belong to pulp technology for making paper.
Background technology
Tobacco lining paper as cigarette package supplementary material, its effect is the iris action that plays cigarette.Existing market On the tobacco lining paper that uses, mainly by aluminium foil compound lining paper, transfer internal lining paper, the vacuum aluminum-coated internal lining paper and without aluminium of aluminizing Internal lining paper clock.Due to the difference of internal lining paper penetrability index, and its demarcate moisture (5% ± 1%), when cigarette bag Install after finishing and entering market, with resting period and envionmental humidity, the difference of temperature, the moisture of cigarette itself can be due to Resting period is more long and high temperature, the storage environment of high humidity and go mouldy, and the storage environment of low temperature, low humidity can then influence volume The quality of cigarette.Therefore, how to solve cigarette due to caused by relative humidity, the change of temperature the change of cigarette quality ask Topic, is always Field of Tobacco problem demanding prompt solution.
The content of the invention
It is an object of the invention to overcome the deficiencies in the prior art, there is provided it is a kind of with constant humidity guarantee the quality Xiang Gong can without aluminium Tobacco lining paper.Additionally, guaranteeing the quality perfume without aluminium tobacco lining paper another object of the present invention is to provide a kind of constant humidity Manufacturing process.
To achieve the above object, the present invention uses following technical scheme：
A kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper, including original paper layer, wherein：The upper surface of the original paper layer is from interior To be also disposed with outward hot-melting sealed layer, aqueous sealant, water-based printing layer and aqueous overcoat, under the original paper layer Surface is provided with moisture also wet layer, and the tobacco lining paper also includes that being arranged at the original paper layer upper surface or the moisturizing of lower surface protects Fragrant layer.
Preferably：The moisturizing is protected fragrant layer and is arranged between the original paper layer and hot-melting sealed layer.
Preferably：The moisturizing is protected fragrant layer and is arranged between the original paper layer and moisture also wet layer.
Preferably：It is inorganic powder or organic powder material layer that fragrant layer is protected in the moisturizing, and fragrant layer is protected in the moisturizing Dry-coated amount is 1g/m2-5g/m2。
Preferably：The particle diameter of the inorganic powder or organic dust is 0.3-100 μm, and specific surface area is 30-2000g/ m2。
Preferably：The hot-melting sealed layer is polymer material layer, and the hot melting temperature of the macromolecular material is 100 ℃-180℃。
Preferably：The aqueous sealant is polymer waterborne emulsion layer or polymer waterborne resin bed, and the water Property sealant dry-coated amount be 1g/m2-5g/m2, smoothness is 400s-1000s.
Preferably：The solidification temperature of the water-based printing layer is 80 DEG C -120 DEG C.
Another object of the present invention, a kind of manufacturing process of tobacco lining paper as described above, it includes following manufacture step Suddenly：
1) form moisturizing in the upper surface of the original paper layer by way of roller coat or spraying and protect fragrant layer, wherein, the guarantor The wet dry-coated amount for protecting fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
2) upper surface for protecting fragrant layer in the moisturizing by way of slot coated forms hot-melting sealed layer, and the slit The temperature of coating is 100 DEG C -180 DEG C, and its coating weight is 8g/m2-18g/m2；
3) aqueous sealant is formed on the surface of hot-melting sealed layer by way of intaglio printing, wherein, the water Property sealant solidification temperature control at 80-120 DEG C, its surface smoothness control in 400s-1000s, Paper Moisture content ＜ 5%；
4) surface printing in the aqueous sealant by way of intaglio printing forms water-based printing layer；
5) aqueous overcoat is formed on the surface of water-based printing layer by way of intaglio printing, wherein, the water Property overcoat dry-coated amount be 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
6) lower surface to the original paper layer carries out also wet process with also wet in the lower surface of original paper layer formation moisture Layer, the moisture of finished paper is controlled 5% ± 1%.
Or, the manufacturing process of described tobacco lining paper, it may include following manufacturing step：
1) by way of slot coated original paper layer upper surface formed hot-melting sealed layer, and the slot coated temperature It is 100 DEG C -180 DEG C to spend, and its coating weight is 8g/m2-18g/m2；
2) aqueous sealant is formed on the surface of hot-melting sealed layer by way of intaglio printing, wherein, the water Property sealant solidification temperature control at 80-120 DEG C, its surface smoothness control in 400s-1000s, Paper Moisture content ＜ 5%；
3) surface printing in the aqueous sealant by way of intaglio printing forms water-based printing layer；
4) aqueous overcoat is formed on the surface of water-based printing layer by way of intaglio printing, wherein, the water Property overcoat dry-coated amount be 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
5) lower surface in the original paper layer by way of roller coat or spraying forms the fragrant layer of moisturizing guarantor, wherein, the guarantor The wet dry-coated amount for protecting fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
6) lower surface to the original paper layer carries out also wet process to protect the lower surface formation moisture of fragrant layer in the moisturizing Also wet layer, the moisture of finished paper is controlled 5% ± 1%.
The beneficial effects of the present invention are, it is of the invention that the setting of fragrant layer is protected by moisturizing without aluminium tobacco lining paper, can be real Existing cigarette product can absorb moisture when being stored under high temperature, high humidity environment, and can be discharged when under depositing in low temperature, low moisture environments Moisture, will not reduce the quality of cigarette because of the length of resting period and envionmental humidity, the difference of temperature.Can be effectively Balance cigarette product moisture, keeps the quality of cigarette product.
Brief description of the drawings
Fig. 1 shows that constant humidity of the present invention is guaranteed the quality the fragrant structural representation without aluminium tobacco lining paper；
Fig. 2 shows that the constant humidity in another implementation method of the invention is guaranteed the quality the fragrant structural representation without aluminium tobacco lining paper Figure.
Specific embodiment
Specific embodiment of the invention is described further below in conjunction with the accompanying drawings.
As shown in figure 1, constant humidity of the present invention is guaranteed the quality, perfume includes original paper layer 1, the body paper without aluminium tobacco lining paper The upper surface of layer 1 is also cascading from the inside to the outside hot-melting sealed layer 3, aqueous sealant 4, water-based printing layer 5 and water Property overcoat 6, the lower surface of the original paper layer 1 is additionally provided with moisture also wet layer 7.Additionally, internal lining paper of the present invention also includes Fragrant layer 2 is protected in moisturizing, and the upper surface that fragrant layer 2 can be set the original paper layer 1 is protected in the moisturizing, close with hot melt positioned at the original paper layer 1 Between sealing 3.Or, as shown in Fig. 2 fragrant layer 2 is protected in the moisturizing may be disposed between the original paper layer 1 and moisture also wet layer 7.
Specifically, in the present invention, the original paper layer 1 can be using aluminium foil composite base paper layer；The hot-melting sealed layer 3 is heat Melting temperatur is 100 DEG C -180 DEG C of heat molten type polymer material layer, and it is by way of slot coated by the heat molten type high score Sub- material is coated on corresponding original paper layer 1 or moisturizing and protects the upper surface of fragrant layer 2 and formed, and the coating temperature for 100 DEG C- 180 DEG C, its coating weight is 8g/m2-18g/m2。
The preferred polymer waterborne emulsion layer of aqueous sealant 4 or polymer waterborne resin bed, it passes through intaglio printing Mode, by the polymer waterborne emulsion or polymer waterborne be coated on hot-melting sealed layer 3 surface and formed, with seal hot melting Issuable gap in sealant 3, also, the aqueous sealant 4 dry-coated amount control in 1g/m2-5g/m2, solidification temperature At 80-120 DEG C, its surface smoothness is controlled in 400s-1000s, Paper Moisture content ＜ 5% for control.
Then, by the way of intaglio printing, water-based printing layer is formed in the surface intaglio printing of the aqueous sealant 4 5, wherein, the solidification temperature of the water-based printing layer is 80 DEG C -120 DEG C；
The surface that the aqueous overcoat 6 is formed at the water-based printing layer 5 by way of intaglio printing is anti-to play Only scratch water-based printing layer 5 and ensure the smooth effect of the internal lining paper, wherein, the aqueous overcoat 6 it is dry-coated Amount 1g/m2-5g/m2, at 80-120 DEG C, the pit depth of the intaglio plate for being used is 30 μm -50 μm for solidification temperature control.
Adding water to the lower surface of the original paper layer 1 add water also wet process/humidification process with the original paper layer 1 Surface forms moisture also wet layer 7, to cause that the moisture of finished paper is controlled 5% ± 1%.
Additionally, the internal lining paper may also include positioned at the upper surface of the original paper layer 1 and the hot-melting sealed layer 3 between or Fragrant layer 2 is protected in moisturizing between lower surface and the moisture also wet layer 7 of the original paper layer 1, and it is nothing that fragrant layer 2 is protected in the moisturizing Machine powder or organic powder material layer, wherein, the inorganic powder is ceramic powder, and the organic dust is macromolecule material Feed powder end, and the particle diameter of the inorganic powder or organic dust is 0.3-100 μm, specific surface area is 30-2000g/m2, it passes through Roller coat or the mode of spraying are formed at upper surface or the lower surface of original paper layer 1, also, the dry-coated amount of the fragrant layer 2 of moisturizing guarantor is 1g/m2-5g/m2, and roller coat uses anilox roll, its pit depth is 30 μm -80 μm, and anilox roll line number is 10 lines -150 Line, its solidification temperature is 80 DEG C -120 DEG C.
Embodiment 1
A kind of constant humidity guarantee the quality perfume without aluminium tobacco lining paper, its structure as shown in figure 1, including original paper layer 1 and from it is interior to Fragrant layer 2, hot-melting sealed layer 3, aqueous sealant 4, aqueous is protected in the moisturizing for being cascadingly set on the upper surface of the original paper layer 1 outward Printing layer 5 and aqueous overcoat 6, the lower surface of the original paper layer 1 are also formed with moisture also wet layer 7.The manufacture of the internal lining paper Step includes：
1) by way of roller coat by particle diameter be 50 μm, specific surface area is 50g/m2Ceramic powders coat original paper layer 1 Upper surface form moisturizing and protect fragrant layer 2, wherein, the dry-coated amount that fragrant layer 2 is protected in the moisturizing is 3g/m2, employed in roller coating process Anilox roll pit depth be 60 μm, anilox roll line number be 100 lines, its solidification temperature be 100 DEG C；
2) the heat molten type macromolecular material that hot melting temperature is 150 DEG C is coated on moisturizing by way of slot coated and protects fragrant The upper surface of layer 2 forms hot-melting sealed layer 3, and the temperature of the slot coated is 150 DEG C, and coating weight is 10g/m2；
3) it is by way of intaglio printing, polymer waterborne emulsion coating is aqueous in the 3 surfaces formation one of hot-melting sealed layer Sealant 4, is existed with the dry-coated amount control in issuable gap in seal hot melting sealant 3, also, the aqueous sealant 4 3g/m2, at 100 DEG C, its surface smoothness is controlled in 800s, Paper Moisture content ＜ 5% for solidification temperature control；
5) by the way of intaglio printing, water-based printing layer 5 is formed in the surface intaglio printing of the aqueous sealant 4, Wherein, the solidification temperature of the water-based printing layer is 100 DEG C；
6) an aqueous overcoat 6 is formed on the surface of water-based printing layer 5 by way of intaglio printing, it is anti-to play Only scratch water-based printing layer 5 and ensure the smooth effect of the internal lining paper, wherein, the aqueous overcoat 6 it is dry-coated Amount 3g/m2, at 100 DEG C, the intaglio plate pit depth for being used is 40 μm for solidification temperature control；
7) adding water carries out also wet/humidification process to the lower surface of the original paper layer 1 with the lower surface shape of the original paper layer 1 Into moisture also wet layer 7, to cause that the moisture of finished paper is controlled 5% ± 1%.
Embodiment 2
A kind of constant humidity guarantee the quality perfume without aluminium tobacco lining paper, its structure as shown in Fig. 2 including original paper layer 1 and from it is interior to Hot-melting sealed layer 3, aqueous sealant 4, the water-based printing layer 5 and water of the upper surface of the original paper layer 1 are cascadingly set on outward Property overcoat 6, the lower surface of the original paper layer 1 is sequentially formed with moisturizing and protects fragrant layer 2 and moisture also wet layer 7 from the inside to the outside.Institute The manufacturing step for stating internal lining paper includes：
1) the heat molten type macromolecular material that hot melting temperature is 120 DEG C is coated on original paper layer 1 by way of slot coated Upper surface formed hot-melting sealed layer 3, and the slot coated temperature be 120 DEG C, coating weight is 15g/m2；
2) it is by way of intaglio printing, polymer waterborne is resin-coated aqueous in the 3 surfaces formation one of hot-melting sealed layer Sealant 4, is existed with the dry-coated amount control in issuable gap in seal hot melting sealant 3, also, the aqueous sealant 4 5g/m2, at 120 DEG C, its surface smoothness is controlled in 400s, Paper Moisture content ＜ 5% for solidification temperature control；
3) by the way of intaglio printing, water-based printing layer 5 is formed in the surface intaglio printing of the aqueous sealant 4, Wherein, the solidification temperature of the water-based printing layer is 80 DEG C；
4) an aqueous overcoat 6 is formed on the surface of water-based printing layer 5 by way of intaglio printing, it is anti-to play Only scratch water-based printing layer 5 and ensure the smooth effect of the internal lining paper, wherein, the aqueous overcoat 6 it is dry-coated Amount 5g/m2, at 80 DEG C, the intaglio plate pit depth for being used is 50 μm for solidification temperature control；
5) spraying by way of by particle diameter be 1 μm, specific surface area is 2000g/m2Macromolecule material powder be sprayed at The lower surface of original paper layer 1 forms moisturizing and protects fragrant layer 2, wherein, the dry-coated amount that fragrant layer 2 is protected in the moisturizing is 1g/m2, and its solidification temperature Spend is 100 DEG C；
7) adding water carries out also wet/humidification process to the lower surface of the original paper layer 1 and is guaranteed the quality under fragrant 2 with the constant humidity Surface forms moisture also wet layer 7, to cause that the moisture of finished paper is controlled 5% ± 1%.
The present invention has passed through preferred embodiment to have carried out detailed explanation.However, by studying carefully above, to each The change and increase of implementation method are also apparent to those of ordinary skill in the art.It is intended that it is all this A little changes and increase fall in the protection domain of the claims in the present invention.Term used herein is only to specific implementation Example is illustrated, and it is not intended to limit the invention.Unless otherwise defined, all terms used herein (including Technical term and scientific terminology) understanding with those skilled in the art of the art is identical.It is any that this product is entered Capable modification and improvement, the replacement of similar in the scope of the claims or category or close material with use, belong to patent of the present invention Protection domain.

Claims (10)

1. a kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper, including original paper layer, it is characterised in that：The upper surface of the original paper layer Hot-melting sealed layer, aqueous sealant, water-based printing layer and aqueous overcoat, the original paper layer are also disposed with from the inside to the outside Lower surface be provided with moisture also wet layer, the tobacco lining paper also includes being arranged at the guarantor of the original paper layer upper surface or lower surface It is wet to protect fragrant layer.
2. tobacco lining paper according to claim 1, it is characterised in that：The moisturizing protects fragrant layer and is arranged at the original paper layer Between hot-melting sealed layer.
3. tobacco lining paper according to claim 1, it is characterised in that：The moisturizing protects fragrant layer and is arranged at the original paper layer Between moisture also wet layer.
4. the tobacco lining paper according to any one in claim 1-3, it is characterised in that：It is nothing that fragrant layer is protected in the moisturizing Machine powder or organic powder material layer, and the dry-coated amount of the fragrant layer of moisturizing guarantor is 1g/m2-5g/m2。
5. tobacco lining paper according to claim 4, it is characterised in that：The particle diameter of the inorganic powder or organic dust is 0.3-100 μm, specific surface area is 30-2000g/m2。
6. the tobacco lining paper according to any one in claim 1-3, it is characterised in that：The hot-melting sealed layer is height Molecular material layer, and the hot melting temperature of the macromolecular material is 100 DEG C -180 DEG C.
7. the tobacco lining paper according to any one in claim 1-3, it is characterised in that：The aqueous sealant is height The aqueous emulsion layer of molecule or polymer waterborne resin bed, and the dry-coated amount of the aqueous sealant is 1g/m2-5g/m2, smoothness It is 400s-1000s.
8. the tobacco lining paper according to any one in claim 1-3, it is characterised in that：Water-based printing layer is consolidated It is 80 DEG C -120 DEG C to change temperature.
9. the manufacturing process of tobacco lining paper as claimed in claim 1, it is characterised in that：Including following manufacturing step：
1) form moisturizing in the upper surface of the original paper layer by way of roller coat or spraying and protect fragrant layer, wherein, the moisturizing is protected The dry-coated amount of fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
2) upper surface for protecting fragrant layer in the moisturizing by way of slot coated forms hot-melting sealed layer, and the slot coated Temperature be 100 DEG C -180 DEG C, its coating weight be 8g/m2-18g/m2；
3) aqueous sealant is formed on the surface of hot-melting sealed layer by way of intaglio printing, wherein, it is described aqueous close The solidification temperature of sealing is controlled at 80-120 DEG C, and its surface smoothness is controlled in 400s-1000s, Paper Moisture content ＜ 5%；
4) surface printing in the aqueous sealant by way of intaglio printing forms water-based printing layer；
5) aqueous overcoat is formed on the surface of water-based printing layer by way of intaglio printing, wherein, it is described aqueous anti- The dry-coated amount of sheath is 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
6) adding water carries out also wet process to the lower surface of the original paper layer with also wet in the lower surface of original paper layer formation moisture Layer, the moisture of finished paper is controlled 5% ± 1%.
10. the manufacturing process of tobacco lining paper as claimed in claim 1, it is characterised in that：Including following manufacturing step：
1) hot-melting sealed layer is formed in the upper surface of original paper layer by way of slot coated, and the temperature of the slot coated is 100 DEG C -180 DEG C, its coating weight is 8g/m2-18g/m2；
2) aqueous sealant is formed on the surface of hot-melting sealed layer by way of intaglio printing, wherein, it is described aqueous close The solidification temperature of sealing is controlled at 80-120 DEG C, and its surface smoothness is controlled in 400s-1000s, Paper Moisture content ＜ 5%；
3) surface printing in the aqueous sealant by way of intaglio printing forms water-based printing layer；
4) aqueous overcoat is formed on the surface of water-based printing layer by way of intaglio printing, wherein, it is described aqueous anti- The dry-coated amount of sheath is 1g/m2-5g/m2, solidification temperature is 80-120 DEG C；
5) lower surface in the original paper layer by way of roller coat or spraying forms the fragrant layer of moisturizing guarantor, wherein, the moisturizing is protected The dry-coated amount of fragrant layer is 1g/m2-5g/m2, and its solidification temperature is 80 DEG C -120 DEG C；
6) add water the lower surface formation moisture that also wet process is carried out to the lower surface of the original paper layer to protect fragrant layer in the moisturizing Also wet layer, the moisture of finished paper is controlled 5% ± 1%.
CN201710224683.2A 2017-04-07 2017-04-07 A kind of constant humidity guarantees the quality perfume without aluminium tobacco lining paper and its manufacturing process Pending CN106894294A (en)