CN106830046A - 一种氯化钙溶液的制备方法 - Google Patents
一种氯化钙溶液的制备方法 Download PDFInfo
- Publication number
- CN106830046A CN106830046A CN201710132505.7A CN201710132505A CN106830046A CN 106830046 A CN106830046 A CN 106830046A CN 201710132505 A CN201710132505 A CN 201710132505A CN 106830046 A CN106830046 A CN 106830046A
- Authority
- CN
- China
- Prior art keywords
- calcium chloride
- chloride solution
- preparation
- calcium
- hydrochloric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种氯化钙溶液的制备方法,属于化工领域,其特征是采用连续法进行;包括将碳酸钙和盐酸连续加入三级串联反应釜中,生成氯化钙溶液;连续将氢氧化钙加入反应液中进行调节反应液pH值;采用三级连续过滤,除去不溶物、金属沉淀物及胶体后,得到38%‑42%浓度的氯化钙溶液。本发明工艺简单,产品具有纯度高、杂质含量低的特点,生产效率比现有间歇法提高了40‑60%。
Description
技术领域
本发明涉及的是一种浓度是38%-42%氯化钙溶液的方法,即利用盐酸和碳酸钙生产氯化钙溶液的方法。
背景技术
氯化钙是一种重要的无机化合物,其生产方法主要有氨碱法和酸钙法。一般来说,高品质氯化钙多采用酸钙法,即以盐酸和碳酸钙为原料进行生产。目前,采用盐酸和碳酸钙法进行生产氯化钙时,主要采用间歇法进行生产。该方法存在着生产效率不高、产品质量不稳定和自动化程度低等缺点,因此,开发更高效、更稳定的氯化钙生产工艺十分重要。
发明内容
本发明的目的是针对间歇法生产氯化钙时具有生产效率不高、产品质量不稳定和自动化程度不高的缺点,提供一种连续法制备高纯度氯化钙溶液的方法。
一种氯化钙溶液的制备方法,其特征是采用连续法制备氯化钙溶液。
所述连续法制备氯化钙溶液的方法包括如下内容:
(1)三级反应:即连续将碳酸钙和盐酸加入反应釜中,分三级反应;三级反应后,采用pH计对溶液的pH值进行控制,pH值控制在4.4-5.8范围内;所述盐酸浓度为32%-36%,所用碳酸钙纯度≥97.5%;
(2)反应液中和:连续将氢氧化钙加入上述反应液中调节pH值,以除去其中的铁、镁及其它金属盐;中和后的溶液pH值为8.5-10.5;
(3)采用三级连续过滤,得到38%-42%浓度的氯化钙溶液。
所述三级过滤依次为离心过滤、板框过滤和超滤,所用离心过滤的滤布的滤孔孔径是:700-1000微米,板框过滤的滤布孔的孔径是:30-60微米,超滤滤膜的孔径是:10-40纳米。
本发明工艺简单,产品具有纯度高、杂质含量低的特点,生产效率比现有间歇法提高了40-60%。
附图说明
图1是本发明的工艺流程图。
具体实施方式
氯化钙溶液的制备方法,包括下述步骤:
1、 将纯度的98.5%的碳酸钙加入到盛有浓度 是32%-36%盐酸的三级串联反应釜中,分三级进行反应,控制第三级溶液的pH值在4.4-5.8,最佳pH值是4.5-5.5;
2、连续将氢氧化钙加入到上述反应液中,调节反应液的pH值至8.5-10.5,以除去其中的铁、镁及其它金属盐;
3、采用三级连续过滤,除去不溶物、金属沉淀物及胶体后,得到38%-42%浓度是的氯化钙溶液。
一~三级过滤的滤布及滤膜孔的直径分别为:800-900微米、35-50微米和10-30纳米,以除去不溶物、金属沉淀物及胶体后,得到的滤液即为38%-42%浓度的氯化钙溶液产品,固体废弃物可直接填埋。
说明:本发明所述浓度均是质量浓度。
Claims (5)
1.一种氯化钙溶液的制备方法,其特征是采用连续法进行:包括将碳酸钙和盐酸连续加入三级串联反应釜中,生成氯化钙溶液;连续将氢氧化钙加入反应液中进行调节反应液pH值;采用三级连续过滤,除去不溶物、金属沉淀物及胶体后,得到38%-42%浓度的氯化钙溶液。
2.根据权利要求1所述一种氯化钙溶液的制备方法,其特征在于:所述盐酸质量浓度为32%-36%,所用碳酸钙纯度≥97.5%。
3.根据权利要求1所述一种氯化钙溶液的制备方法,其特征在于:所述盐酸与碳酸钙三级反应后,溶液的pH值控制在4.4-5.8。
4.根据权利要求1所述一种氯化钙溶液的制备方法,其特征在于:所述氢氧化钙中和后的溶液pH值为8.5-10.5。
5.根据权利要求1所述一种氯化钙溶液的制备方法,其特征在于:所述三级连续过滤所用滤布及滤膜孔的直径分别为:700-1000微米、30-60微米和10-40纳米。