CN106784340A - 一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法 - Google Patents

一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法 Download PDF

Info

Publication number
CN106784340A
CN106784340A CN201611154648.XA CN201611154648A CN106784340A CN 106784340 A CN106784340 A CN 106784340A CN 201611154648 A CN201611154648 A CN 201611154648A CN 106784340 A CN106784340 A CN 106784340A
Authority
CN
China
Prior art keywords
ticl
solar cell
perovskite solar
spin coating
aqueous solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611154648.XA
Other languages
English (en)
Other versions
CN106784340B (zh
Inventor
王金淑
赵冰心
郑广伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Technology
Original Assignee
Beijing University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Technology filed Critical Beijing University of Technology
Priority to CN201611154648.XA priority Critical patent/CN106784340B/zh
Publication of CN106784340A publication Critical patent/CN106784340A/zh
Application granted granted Critical
Publication of CN106784340B publication Critical patent/CN106784340B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，属于薄膜太阳能电池领域。包含以下步骤：以硝酸铝水溶液与TiCl4水解产物(非晶TiO2)作为铝源与钛源，硝酸铝水溶液悬涂于TiCl4处理后的TiO2致密层上，400‑600℃退火；钛酸铝水溶液的浓度为：1‑4mM；硝酸铝水溶液的旋涂次数为1‑4次；旋涂速度为3000‑6000转；旋涂时长为5‑30s。本发明采用离子溶液和旋涂工艺相结合。简化工艺、节约能源。

Description

一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法
技术领域
一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，属于薄膜太阳能电池领域。
背景技术
钙钛矿太阳能电池(PSC)钙全称钛矿型甲胺铅碘薄膜太阳能电池，研究重点在于选择更适合传输电荷的材料，让电子传输层(ETL)和空穴传输层(HTL)能收集更多的电荷。研究学者们通常采用阻挡层印刷，其厚度通常超过100nm，或是采用原子层沉积(ALD)，工艺繁琐。而工艺简易而不增加其PSC厚度的还未见报道。
发明内容
本发明方法避免了常规阻挡层繁琐的工艺或是厚度的增加，而提供的一种离子型简易的制备方法。
本发明提供的一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，其特征在于，包含以下步骤：
将基底上的TiO2致密层浸置于TiCl4溶液中，加热一段时间后取出，乙醇、去离子水冲洗，烘干，冷却至室温；取硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂，然后400-600℃退火，然后经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
TiCl4溶液的浓度优选为40mM，在TiCl4溶液中加热70℃，加热30min。
硝酸铝水溶液的浓度为：1-4mM；硝酸铝水溶液的旋涂次数为1-4次；旋涂速度为3000-6000转/秒；旋涂时长为5-30s。
与现有技术相比，本发明的有益效果是：以硝酸铝水溶液与TiCl4水解产物(非晶TiO2)作为铝源与钛源。与现有常见Al2O3阻挡层(厚度超过100nm)相比，本发明采用离子溶液和旋涂工艺相结合。简化工艺、节约能源。
附图说明
图1：Al-PSC扫描电镜截面图。
图2：Al-PSC EDS能量射散谱图。
图3：DIXRD小角度掠射XRD
图4：TEM
图5：实施例2的Al-PSC IV曲线。
具体实施方式
下面通过实施例结合附图进一步描述本发明，其目的在于更好地理解本发明的内容，而不是对本发明的限制。
实施例1
基底为FTO的TiO2致密层浸置于40mM TiCl4溶液中，70℃30min后取出，乙醇、去离子水冲洗，烘干，冷却至室温；取2mM的硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂1次(4000转/秒10s 5000转/秒10s)，500℃退火。经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
实施例2
基底为FTO的TiO2致密层浸置于40mM TiCl4溶液中，70℃30min后取出，去乙醇、离子水冲洗，烘干，冷却至室温；取2mM的硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂2次(4000转/秒10s 5000转/秒10s)，500℃退火。经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
实施例3
基底为FTO的TiO2致密层浸置于40mM TiCl4溶液中，70℃30min后取出，去乙醇、离子水冲洗，烘干，冷却至室温；取2mM的硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂3次(4000转/秒10s 5000转/秒10s)，500℃退火。经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
实施例4
基底为FTO的TiO2致密层浸置于40mM TiCl4溶液中，70℃30min后取出，去乙醇、离子水冲洗，烘干，冷却至室温；取1mM的硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂3次(4000转/秒25s)，500℃退火。经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
实施例5
基底为FTO的TiO2致密层浸置于40mM TiCl4溶液中，70℃30min后取出，去乙醇、离子水冲洗，烘干，冷却至室温；取4mM的硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂1次(6000转/秒5s)，400℃退火。经钙钛矿层、空穴传输层等制备，组装成钙钛矿太阳能电池。
附表
表1实验参数列表

Claims (3)

1.一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，其特征在于，包含以下步骤：将基底上的TiO2致密层浸置于TiCl4溶液中，加热一段时间后取出，乙醇、去离子水冲洗，烘干，冷却至室温；取硝酸铝水溶液，铺展于TiCl4溶液处理后的TiO2致密层上，旋涂，然后400-600℃退火，然后经钙钛矿层、空穴传输层制备，组装成钙钛矿太阳能电池。
2.按照权利要求1所述的一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，其特征在于，TiCl4溶液的浓度优选为40mM，在TiCl4溶液中加热70℃，加热30min。
3.按照权利要求1所述的一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法，其特征在于，硝酸铝水溶液的浓度为：1-4mM；硝酸铝水溶液的旋涂次数为1-4次；旋涂速度为3000-6000转/秒；旋涂时长为5-30s。
CN201611154648.XA 2016-12-14 2016-12-14 一种用钛酸铝降低钙钛矿太阳能电池界面复合的方法 Active CN106784340B (zh)