CN106756963A - A kind of addition CNT has water base brass antioxidant of heat sinking function and preparation method thereof - Google Patents
A kind of addition CNT has water base brass antioxidant of heat sinking function and preparation method thereof Download PDFInfo
- Publication number
- CN106756963A CN106756963A CN201611157450.7A CN201611157450A CN106756963A CN 106756963 A CN106756963 A CN 106756963A CN 201611157450 A CN201611157450 A CN 201611157450A CN 106756963 A CN106756963 A CN 106756963A
- Authority
- CN
- China
- Prior art keywords
- cnt
- antioxidant
- water
- phytic acid
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
There is the water base brass antioxidant of heat sinking function the invention discloses a kind of CNT that adds, every liter of antioxidant is made from the following raw materials in parts by weight:50wt.% phytic acid 13 16, 30wt.% hydrogen peroxide 23 25, polyethylene glycol 13 15, Sodium Benzoate 0.7 0.9, boric acid 68, Strong flour 13, gelatin 35, pure-acrylic emulsion 57, monoethanolamine 23, CNT 0.9 1.2, methyl triacetoxysilane 2.7 2.9, appropriate deionized water, the present invention is with phytic acid, hydrogen peroxide is main component, by phytic acid carry out it is silane coupler modified after, compatibility is through CNT again, the modified Strong flour of pure-acrylic emulsion and other compositions, obtained antioxidant can be directly dissolved in water, it is easy to operate, it is not necessary to special installation, product is coated in brass heat sink surface radiating good, preservation antioxidation is good, the anti-corrosion time is long.
Description
Technical field
There is the water of heat sinking function the present invention relates to metal oxidation resistance technical field, more particularly to a kind of CNT that adds
Base brass antioxidant and preparation method thereof.
Background technology
The alloy that brass is made up of copper and zinc, both with excellent conductive, thermal conductivity and easily processed into type excellent
Point, and with enough mechanical strengths, hardness and chemical resistance, be commonly used for manufacture valve, water pipe, air-conditioning internal-external machine and connect
Adapter and radiator etc..But run into acid, alkaline corrosion medium or in higher temperatures and high humidity environment be still susceptible to oxygen
Change corrosion and change colour, have a strong impact on outward appearance and use value while also bringing bad influence to secondary operation.It is domestic at present
The outer handling process to copper and its anti-oxidant discoloration of alloy surface mainly has:It is inorganic passivation technique for filming, organic inhibition technology, dilute
Native addition method, self-assembling technique and resinous coat technology etc., wherein most economical, easy method is passivated in brass surfaces
Treatment.Most ripe method is to use bichromate Passivation Treatment, but the sexavalence that the method is remained in process of production and in waste liquid
Chromium is noxious material, and many countries have prohibitted the use of bichromate Passivation Treatment, therefore, document《Brass surfaces richness phytic acid is blunt
Change technical study》With phytic acid, hydrogen peroxide, polyethylene glycol etc. for passivating solution prepared by primary raw material has for brass surfaces antirust
Important realistic meaning.
Treatment is passivated to cold rolling HAl72-2.5-1 brass strips using passivating solution in document, is as a result shown, rich phytic acid
The optimum process condition of passivating film is:Passivation temperature scope is 35~40 DEG C, and pH value is 2.5, and passivation time is 60s;SEM is microcosmic
Pattern shows that film surface is smooth, compact structure;Zero-G test result shows can be to alloy material using rich phytic acid Passivation Treatment
Play a very good protection;Bichromate is used using the sample ratio that rich phytic acid is processed by the saline fog method experiment display of 12h
The sample for the treatment of is free of chromium in having more preferable anti-tarnishing ability and rich phytic acid passivating solution, and pollution of chromium will not be produced in waste liquid.
But the phytic acid film in document, under the heavier environment of humidity, because damp moisture resistance is not good, storage time is short, coating
When brass surfaces carry out secondary operation, resistance to elevated temperatures is limited, in welding process, it is impossible to keep for a long time and multiple
High temperature impact;Secondly in document also there is short anti oxidation time, environmentally friendly bad adaptability, unitary function, heat surely in obtained passivator
The problems such as qualitative difference, weatherability difference and sun-proof ultraviolet radiation preventing difference, thus limit the lifting of overall performance and apply model
Enclose, it is necessary to improve existing production technology and formula, prepare the brass table with the function such as anti-corrosion, anti-oxidant, wear-resisting, sun-proof
Face treatment antioxidant.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided one kind addition CNT has heat sinking function
Water base brass antioxidant and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of CNT that adds has the water base brass antioxidant of heat sinking function, and every liter of antioxidant is by following weight portion
Raw material is made:50wt.% phytic acid 13-16,30wt.% hydrogen peroxide 23-25, polyethylene glycol 13-15, Sodium Benzoate 0.7-0.9, boric acid
6-8, Strong flour 1-3, gelatin 3-5, pure-acrylic emulsion 5-7, monoethanolamine 2-3, CNT 0.9-1.2, methyl triacetoxyl group
Silane 2.7-2.9, appropriate deionized water.
The preparation method that a kind of described addition CNT has the water base brass antioxidant of heat sinking function, including with
Lower step:
(1)Strong flour is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add CNT ultrasonic disperse to grind 6-12 hours, add pure-acrylic emulsion ultrasound wave irradiation to react 2-8 hours,
Be cooled to room temperature, filtration washing to neutrality, the dry Strong flour that must be modified;
(2)Methyl triacetoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add monoethanolamine ultrasonic disperse to grind 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified Strong flour grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Warm to 70-80 DEG C adds gelatin stirring reaction 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds boric acid and other residual components to stir and evenly mix, and adds water to 1L, in
40-50 DEG C is stirred 20-60 minutes, discharging.
It is an advantage of the invention that:The present invention with phytic acid, hydrogen peroxide as main component, due to there is 24 oxygen originals in phytate molecule
Son, 12 hydroxyls and 6 are phosphate-based, and these atoms or group can form complex compound with metallic atom and metal ion, will plant
Acid carry out it is silane coupler modified after, on the one hand can be anti-by hydrogen bond or dehydration between unreacted phosphorus hydroxyl in passivating process
Should, connection forms spatial networks phytic acid (salt) passivating film of high crosslink density, on the other hand can with silane hydrolyzate after generate-
Si-OH- reaction generation-P-O-Si- keys, can be attached to one layer of metal surface formation colourless with the chelate of metal generation stabilization
Homogeneous, the non-microcracked protective film of transparent, surfacing, thickness densification effectively prevents corrosive medium from penetrating into metal surface,
So as to slow down corrosion of metal, by Strong flour through CNT, pure-acrylic emulsion is modified is added in raw material, improves it
Viscosity in water, then compatibility other antioxidants obtained in effective auxiliary agent can be directly dissolved in water, and easy to operate, it is special to be not necessary to
Equipment, product is coated in brass heat sink surface radiating is good, preservation antioxidation is good, the anti-corrosion time is long.
Specific embodiment
A kind of CNT that adds has the water base brass antioxidant of heat sinking function, and every liter of antioxidant is by following weight
The raw material of part is made:50wt.% phytic acid 13,30wt.% hydrogen peroxide 23, polyethylene glycol 13, Sodium Benzoate 0.7, boric acid 6, muscle face high
Powder 1, gelatin 3, pure-acrylic emulsion 5, monoethanolamine 2, CNT 0.9, methyl triacetoxysilane 2.7, appropriate deionized water.
The preparation method that a kind of described addition CNT has the water base brass antioxidant of heat sinking function, including with
Lower step:
(1)Strong flour is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add CNT ultrasonic disperse to grind 6-12 hours, add pure-acrylic emulsion ultrasound wave irradiation to react 2-8 hours,
Be cooled to room temperature, filtration washing to neutrality, the dry Strong flour that must be modified;
(2)Methyl triacetoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add monoethanolamine ultrasonic disperse to grind 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified Strong flour grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Warm to 70-80 DEG C adds gelatin stirring reaction 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds boric acid and other residual components to stir and evenly mix, and adds water to 1L, in
40-50 DEG C is stirred 20-60 minutes, discharging.
There is following technical parameter using copper antioxidant obtained in the present invention:
(1)Resistance to neutral salt spray corrosion test:By the brass of antioxidant of the present invention treatment, its anti-tarnishing ability is significantly improved, and 8
After h sample remain to keep alloy primary colors there is no Staining, after 12 h, specimen surface remain to keep alloy primary colors, it is only few
The Staining of amount;
(2)The corrosion resistant time of the sample drop of resistance to nitric acid reaches most when sample is put into Passivation Treatment in product of the present invention 60 seconds
Big value 13 seconds.
Claims (2)
1. a kind of CNT that adds has the water base brass antioxidant of heat sinking function, it is characterised in that every liter of antioxidant
It is made from the following raw materials in parts by weight:50wt.% phytic acid 13-16,30wt.% hydrogen peroxide 23-25, polyethylene glycol 13-15, benzoic acid
Sodium 0.7-0.9, boric acid 6-8, Strong flour 1-3, gelatin 3-5, pure-acrylic emulsion 5-7, monoethanolamine 2-3, CNT 0.9-1.2,
Methyl triacetoxysilane 2.7-2.9, appropriate deionized water.
2. a kind of addition CNT according to claim 1 has the making of the water base brass antioxidant of heat sinking function
Method, it is characterised in that comprise the following steps:
(1)Strong flour is mixed the suspension for being configured to that mass percent concentration is 5-10% in deionized water, 40- is put into
In 60 DEG C of water-baths, add CNT ultrasonic disperse to grind 6-12 hours, add pure-acrylic emulsion ultrasound wave irradiation to react 2-8 hours,
Be cooled to room temperature, filtration washing to neutrality, the dry Strong flour that must be modified;
(2)Methyl triacetoxysilane and deionized water are pressed 1:3 mass ratio is warming up to 80- after mixing is stirred at room temperature
100 DEG C, add monoethanolamine ultrasonic disperse to grind 5-7 hours, be cooled to 45-55 DEG C and add reaction of phytic acid 1-2 hours, obtain modified plant
Acid;
(3)By step(1)Obtained modified Strong flour grinding distribution is in step(2)In the obtained modified phytic acid aqueous solution, rise
Warm to 70-80 DEG C adds gelatin stirring reaction 4-6 hours, cooling;
(4)By step(3)Material is put into reactor, adds boric acid and other residual components to stir and evenly mix, and adds water to 1L, in
40-50 DEG C is stirred 20-60 minutes, discharging.