CN106752487B - 一种jr-40聚合柔性耐低温防水防腐材料 - Google Patents
一种jr-40聚合柔性耐低温防水防腐材料 Download PDFInfo
- Publication number
- CN106752487B CN106752487B CN201610720730.8A CN201610720730A CN106752487B CN 106752487 B CN106752487 B CN 106752487B CN 201610720730 A CN201610720730 A CN 201610720730A CN 106752487 B CN106752487 B CN 106752487B
- Authority
- CN
- China
- Prior art keywords
- temperature
- water
- parts
- anticorrosive material
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种JR‑40聚合柔性耐低温防水防腐材料,由以下原料制成:丙烯酸乳液、微硅粉料、硅酸盐粉料、水、碳酸钙、增稠剂和增塑剂。相对于现有技术,该材料防腐、防水效果好。
Description
技术领域
本发明涉及一种JR-40聚合柔性耐低温防水防腐材料。
背景技术
目前,国内外的建筑防水工程,一致延用沥青为主其它多种材料为辅,综合各种性能均存在诸多不足。
发明内容
针对现有技术的上述缺陷和问题,本发明的目的是提供一种无污染环境物资施工简便、实用性强、防水防腐效果好的JR-40聚合柔性耐低温防水防腐材料。
基于上述目的,本发明提供如下技术方案:
根据本发明的一方面,提供了一种JR-40聚合柔性耐低温防水防腐材料,由以下原料制成:丙烯酸乳液、微硅粉料、硅酸盐粉料、水、碳酸钙、增稠剂和增塑剂。
进一步,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液40%-46%、微硅粉料10%-18%、硅酸盐粉料10%-18%、水10%-18%、碳酸钙5%-10%、增稠剂0.2%-0.8%和增塑剂0.3%-0.7%。
进一步,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液45%、微硅粉料16%、硅酸盐粉料15%、水15%、碳酸钙8%、增稠剂0.5%和增塑剂0.5%。
进一步,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液42%、微硅粉料17%、硅酸盐粉料14%、水16%、碳酸钙10%、增稠剂0.4%和增塑剂0.6%。
进一步,所述丙烯酸乳液由丙烯酸丁酯,乙酸乙烯酯,丙烯酸,N-羟甲基丙烯酰胺,水,过硫酸钾,亚硫酸氢钠,硫酸亚铁,乳化剂组成。
进一步,所述丙烯酸乳液由丙烯酸丁酯50份,乙酸乙烯酯10份,丙烯酸1份,N-羟甲基丙烯酰胺1份,水150份,过硫酸钾1份,亚硫酸氢钠2份,硫酸亚铁2份,乳化剂1份组成。
进一步,增塑剂为已二酸二辛酯、酞酸二辛酯、顺丁烯二酸二丁酯、二甲基丙烯酸丁二醇酯、富马酸二丁酯中的一种。
与现有技术相比,本发明具备以下有益效果,本发明的防腐材料可以在水泥、玻璃、金属、木材、塑料等的表面形成一层致密的薄膜,他可以阻止水分以及酸、碱等各种盐溶液透过而直接作用水泥、玻璃、金属、木材、塑料表面,对其产生腐蚀作用,从而发挥防腐效能,另外,本发明的防水防腐材料抗拉伸,耐低温,JR-40可理解为聚合、柔性、适应温度在零下40度左右,吸水率小于等于0.1%。
具体实施方式
下面将结合本发明的实施例,对本发明的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
一种JR-40聚合柔性耐低温防水防腐材料,由以下原料制成:丙烯酸乳液、微硅粉料、硅酸盐粉料、水、碳酸钙、增稠剂和增塑剂。
具体的,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液40%-46%、微硅粉料10%-18%、硅酸盐粉料10%-18%、水10%-18%、碳酸钙5%-10%、增稠剂0.2%-0.8%和增塑剂0.3%-0.7%。
具体的,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液45%、微硅粉料16%、硅酸盐粉料15%、水15%、碳酸钙8%、增稠剂0.5%和增塑剂0.5%。
具体的,根据本发明JR-40聚合柔性耐低温防水防腐材料,所述原料的百分比为:丙烯酸乳液42%、微硅粉料17%、硅酸盐粉料14%、水16%、碳酸钙10%、增稠剂0.4%和增塑剂0.6%。
具体的,所述丙烯酸乳液由丙烯酸丁酯,乙酸乙烯酯,丙烯酸,N-羟甲基丙烯酰胺,水,过硫酸钾,亚硫酸氢钠,硫酸亚铁,乳化剂组成。
具体的,所述丙烯酸乳液由丙烯酸丁酯50份,乙酸乙烯酯10份,丙烯酸1份,N-羟甲基丙烯酰胺1份,水150份,过硫酸钾1份,亚硫酸氢钠2份,硫酸亚铁2份,乳化剂1份组成。
具体的,增塑剂为已二酸二辛酯、酞酸二辛酯、顺丁烯二酸二丁酯、二甲基丙烯酸丁二醇酯、富马酸二丁酯中的一种。
通过上述内容不难发现,本发明防腐材料可以在水泥、玻璃、金属、木材、塑料等的表面形成一层致密的薄膜,他可以阻止水分以及酸、碱等各种盐溶液透过而直接作用水泥、玻璃、金属、木材、塑料表面,对其产生腐蚀作用,从而发挥防腐效能,另外,本发明的防水防腐材料抗拉伸,耐低温,JR-40可理解为聚合、柔性、适应温度在零下40度左右,吸水率小于等于0.1%。
本发明具有以下特性:
1、经过30分钟抗渗透性实验,在0.1MPa下,无渗透现象。
2、经过耐热性实验,在90℃下,无鼓包、无流淌。
3、经过低温柔性实验,在-40℃保持30分钟,无裂纹现象。
4、经过拉伸强度实验,拉伸强度为1.6MPa.
5、经过断裂延伸实验,延伸率在429%。
6、经过冻融循环,在-15℃至23℃循环20次,无裂纹现象。
另外需要说明的是,微硅粉料具有显著提高抗压、抗折、抗渗、防腐、抗冲击及耐磨性能;具有保水、防止离析、泌水、大幅降低砼泵送阻力的作用;显著延长砼的使用寿命。特别是在氯盐污染侵蚀、硫酸盐侵蚀、高湿度等恶劣环境下,可使砼的耐久性提高一倍甚至数倍。
通过上述内容可知,本发明通过丙烯酸乳液、微硅粉料、硅酸盐粉料、水、碳酸钙、增稠剂和增塑剂聚合后制得的材料,防水防腐性能提高,成本降低,抗冻、抗老化。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应所述以权利要求的保护范围为准。
Claims (1)
1.一种JR-40聚合柔性耐低温防水防腐材料,其特征在于,由以下原料制成:丙烯酸乳液、微硅粉料、硅酸盐粉料、水、碳酸钙、增稠剂和增塑剂,其中,所述增塑剂为己二酸二辛酯、酞酸二辛酯、顺丁烯二酸二丁酯、二甲基丙烯酸丁二醇酯、富马酸二丁酯中的一种,所述原料的百分比为:丙烯酸乳液10%-46%、微硅粉料10%-18%、硅酸盐粉料10%-18%、水10%-18%碳酸钙5%-10%、增稠剂0.2%-0.8%和增塑剂0.3%-0.7%,其中,所述JR-40聚合柔性耐低温防水防腐材料耐低温-40摄氏度,断裂延伸率429%;
所述丙烯酸乳液由丙烯酸丁酯50份,乙酸乙烯酯10份,丙烯酸1份,N-羟甲基丙烯酰胺1份,水150份,过硫酸钾1份,亚硫酸氢钠2份,硫酸亚铁2份,乳化剂1份组成。