CN106745836A - 一种耐高温缓蚀阻垢剂 - Google Patents
一种耐高温缓蚀阻垢剂 Download PDFInfo
- Publication number
- CN106745836A CN106745836A CN201510809581.8A CN201510809581A CN106745836A CN 106745836 A CN106745836 A CN 106745836A CN 201510809581 A CN201510809581 A CN 201510809581A CN 106745836 A CN106745836 A CN 106745836A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- temperature resistant
- water
- scale inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及水处理药剂领域,具体是一种耐高温缓蚀阻垢剂。是由以下重量份数的物质组成:淀粉基体6-12份、丙烯酸12-15份、2-丙烯酰胺基-2-甲基丙磺酸6-10份、聚天冬氨酸20-25份、含氮杂环化合物组合5-10份、水溶性氧化性无机金属盐10-15份、水溶性无机锌盐5-10份、均聚聚羧酸5-10份、木质素磺酸盐5-10份、多羟基羧酸钠10-15份、纤维素衍生物5-10份、复合引发剂5-8份、分散活化剂3-6份、辅助缓蚀剂5-10份。本发明提供的耐高温缓释阻垢剂,成本低廉,来源广泛,对环境友好,无毒、无二次污染,且本发明的阻垢剂耐高温,能够有效抑制油田管道和锅炉中碳酸钙垢、硫酸钙垢、硫酸钡垢和磷酸钙垢的形成,对于管道和锅炉具有很好的缓释作用,能够延长使用寿命。
Description
技术领域
本发明涉及水处理药剂领域,具体是一种耐高温缓蚀阻垢剂。
背景技术
中国水资源的匮乏和污染已引起了人们的严重关注,随着工业生产的日益发展,工业用水迅速增长,其中工业循环冷却水占工业用水的60%以上。,在冷却水循环过程中冷却水不断蒸发,水中的盐类被浓缩沉积,这些生物在循环冷却水***的适宜环境下,迅速的繁殖和生长,产生大量的生物粘泥、污垢附着或沉积在水***管道和设备的表面,严重地影响了循环水冷凝、冷却效果,增加了***阻力和端差,提高了能耗,严重时甚至堵塞管道,腐蚀设备降低了设备使用寿命,增加了检修频率,威胁正常生产运行,因此,在循环冷却水中必须要加杀生灭藻剂、阻垢剂和缓蚀剂等药剂以防止循环水***的结垢、腐蚀和菌、藻及水生物的迅速繁殖和生长。
在油田的开发中,保证油田的稳定、增产,合理有效地清除结垢,成为油田开发中迫切需要解决的问题,国内外最常用的阻垢方法为使用化学阻垢剂来抑制水垢的生成。常用的化学阻垢剂主要包括无机聚磷酸盐、有机多元磷酸盐、均聚物阻垢剂、共聚物阻垢剂等。但是,由于油田水质具有高温、高硬度、高盐度等特点,这些现有的化学阻垢剂在解决油田***的结垢问题时,往往由于稳定性不足,而不能有效地清除结垢,最终影响油水井正常工作。
在锅炉生产中,一般的锅炉用水采用离子交换软化器使水与交换剂接触,降低水的硬度即钙镁离子含量,使水软化,并对树脂进行再生,循环使用。但其存在的问题在于,树脂经过长期反复再生使用后,其交换能力也随之下降。因此,进入炉中的锅炉水的硬度也逐渐增大,并且在高温下多次循环后大量的纯净水被蒸发,使水中的钙、镁离子浓度大大增加,结垢型物质如Ca2+、Mg2+等因溶解度下降产生析出,析出的物质会沉积在锅炉钢管的换热表面上,形成水垢。
发明内容
为了解决上述问题,本发明提供了一种耐高温、环保的缓蚀型阻垢剂。
本发明的技术方案如下:
一种耐高温缓释阻垢剂,是由以下重量份数的物质组成:淀粉基体6-12份、丙烯酸12-15份、2-丙烯酰胺基-2-甲基丙磺酸6-10份、聚天冬氨酸20-25份、含氮杂环化合物组合5-10份、水溶性氧化性无机金属盐10-15份、水溶性无机锌盐5-10份、均聚聚羧酸5-10份、木质素磺酸盐5-10份、多羟基羧酸钠10-15份、纤维素衍生物5-10份、复合引发剂5-8份、分散活化剂3-6份、辅助缓蚀剂5-10份。
优选的,一种耐高温缓释阻垢剂,是由以下重量份数的物质组成:淀粉基体10份、丙烯酸14份、2-丙烯酰胺基-2-甲基丙磺酸8份、聚天冬氨酸22份、含氮杂环化合物组合8份、水溶性氧化性无机金属盐12份、水溶性无机锌盐8份、均聚聚羧酸8份、木质素磺酸盐8份、多羟基羧酸钠12份、纤维素衍生物8份、复合引发剂7份、分散活化剂5份、辅助缓蚀剂8份。
进一步的,一种耐高温缓释阻垢剂,含氮杂环化合物组合为烷基咪唑啉衍生物,水溶性氧化性无机金属盐为高锰酸钾,水溶性无机锌盐为氯化锌,纤维素衍生物为羧甲基纤维素、复合引发剂为硫酸铵复合引发剂,分散活化剂为硅酸钠,辅助缓蚀剂为碳酸钠。
本发明的有益效果:
与现有技术相比,本发明提供的耐高温缓释阻垢剂,采用淀粉为基体,成本低廉,来源广泛,对环境友好,无毒、无二次污染,且本发明的阻垢剂耐高温,能够有效抑制油田管道和锅炉中碳酸钙垢、硫酸钙垢、硫酸钡垢和磷酸钙垢的形成,对于管道和锅炉具有很好的缓释作用,能够延长使用寿命,本发明的阻垢剂配方环保,适用范围广。
具体实施方式
实施例1
一种耐高温缓释阻垢剂,是由以下重量份数的物质组成:淀粉基体6份、丙烯酸12份、2-丙烯酰胺基-2-甲基丙磺酸6份、聚天冬氨酸20份、含氮杂环化合物组合5份、水溶性氧化性无机金属盐10份、水溶性无机锌盐5份、均聚聚羧酸5份、木质素磺酸盐5-份、多羟基羧酸钠10份、纤维素衍生物5份、复合引发剂5份、分散活化剂3份、辅助缓蚀剂5份。
进一步的,一种耐高温缓释阻垢剂,含氮杂环化合物组合为烷基咪唑啉衍生物,水溶性氧化性无机金属盐为高锰酸钾,水溶性无机锌盐为氯化锌,纤维素衍生物为羧甲基纤维素、复合引发剂为硫酸铵复合引发剂,分散活化剂为硅酸钠,辅助缓蚀剂为碳酸钠。
实施例2
一种耐高温缓释阻垢剂,是由以下重量份数的物质组成:淀粉基体12份、丙烯酸15份、2-丙烯酰胺基-2-甲基丙磺酸10份、聚天冬氨酸25份、含氮杂环化合物组合10份、水溶性氧化性无机金属盐15份、水溶性无机锌盐10份、均聚聚羧酸10份、木质素磺酸盐10份、多羟基羧酸钠15份、纤维素衍生物10份、复合引发剂8份、分散活化剂6份、辅助缓蚀剂10份。
进一步的,一种耐高温缓释阻垢剂,含氮杂环化合物组合为烷基咪唑啉衍生物,水溶性氧化性无机金属盐为高锰酸钾,水溶性无机锌盐为氯化锌,纤维素衍生物为羧甲基纤维素、复合引发剂为硫酸铵复合引发剂,分散活化剂为硅酸钠,辅助缓蚀剂为碳酸钠。
实施例3
一种耐高温缓释阻垢剂,是由以下重量份数的物质组成:淀粉基体10份、丙烯酸14份、2-丙烯酰胺基-2-甲基丙磺酸8份、聚天冬氨酸22份、含氮杂环化合物组合8份、水溶性氧化性无机金属盐12份、水溶性无机锌盐8份、均聚聚羧酸8份、木质素磺酸盐8份、多羟基羧酸钠12份、纤维素衍生物8份、复合引发剂7份、分散活化剂5份、辅助缓蚀剂8份。
进一步的,一种耐高温缓释阻垢剂,含氮杂环化合物组合为烷基咪唑啉衍生物,水溶性氧化性无机金属盐为高锰酸钾,水溶性无机锌盐为氯化锌,纤维素衍生物为羧甲基纤维素、复合引发剂为硫酸铵复合引发剂,分散活化剂为硅酸钠,辅助缓蚀剂为碳酸钠。
Claims (9)
1.一种耐高温缓释阻垢剂,其特征在于,是由以下重量份数的物质组成:淀粉基体6-12份、丙烯酸12-15份、2-丙烯酰胺基-2-甲基丙磺酸6-10份、聚天冬氨酸20-25份、含氮杂环化合物组合5-10份、水溶性氧化性无机金属盐10-15份、水溶性无机锌盐5-10份、均聚聚羧酸5-10份、木质素磺酸盐5-10份、多羟基羧酸钠10-15份、纤维素衍生物5-10份、复合引发剂5-8份、分散活化剂3-6份、辅助缓蚀剂5-10份。
2.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,是由以下重量份数的物质组成:淀粉基体10份、丙烯酸14份、2-丙烯酰胺基-2-甲基丙磺酸8份、聚天冬氨酸22份、含氮杂环化合物组合8份、水溶性氧化性无机金属盐12份、水溶性无机锌盐8份、均聚聚羧酸8份、木质素磺酸盐8份、多羟基羧酸钠12份、纤维素衍生物8份、复合引发剂7份、分散活化剂5份、辅助缓蚀剂8份。
3.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述含氮杂环化合物组合为烷基咪唑啉衍生物。
4.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述水溶性氧化性无机金属盐为高锰酸钾。
5.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述水溶性无机锌盐为氯化锌。
6.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述纤维素衍生物为羧甲基纤维素。
7.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述复合引发剂为硫酸铵复合引发剂。
8.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述分散活化剂为硅酸钠。
9.如权利要求1所述,一种耐高温缓释阻垢剂,其特征在于,所述辅助缓蚀剂为碳酸钠。