CN106700426A - 无卤无锑环保型覆铜板的添加剂材料配方 - Google Patents

无卤无锑环保型覆铜板的添加剂材料配方 Download PDF

Info

Publication number
CN106700426A
CN106700426A CN201611268682.XA CN201611268682A CN106700426A CN 106700426 A CN106700426 A CN 106700426A CN 201611268682 A CN201611268682 A CN 201611268682A CN 106700426 A CN106700426 A CN 106700426A
Authority
CN
China
Prior art keywords
parts
additive
hydroxide powder
free
halogen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611268682.XA
Other languages
English (en)
Inventor
孙茂云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Huake Electronic Materials Co Ltd
Original Assignee
Tongling Huake Electronic Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Huake Electronic Materials Co Ltd filed Critical Tongling Huake Electronic Materials Co Ltd
Priority to CN201611268682.XA priority Critical patent/CN106700426A/zh
Publication of CN106700426A publication Critical patent/CN106700426A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种无卤无锑环保型覆铜板的添加剂材料配方，通过将添加剂由二甲基甲酰胺、氢氧化铝粉末、过氧化二异丙苯、氢氧化镁粉末、二乙烯三胺、十二烷基苯磺酸钠、聚酰胺、氢氧化钠粉末、己二酸二甲酯和二甲基咪唑组成，并将这些种类的添加剂按照适当的比例配制好在高温下熔融搅拌混合而成，将得到的添加剂运用到覆铜板的生产工艺当中，这种类型的添加剂在使用时固化性能优异，且制作方法简单、方便，能够提高其稳定性能、粘接效果，能够防止铜箔脱落。

Description

无卤无锑环保型覆铜板的添加剂材料配方
技术领域
本发明涉及覆铜板生产技术领域，尤其涉及一种无卤无锑环保型覆铜板的添加剂材料配方。
背景技术
覆铜板又称基材，它是由木浆纸或玻纤布等作增强材料，浸以树脂，单面或双面覆以铜箔，经热压而成的一种板状材料，称为覆铜箔层压板。 它是做PCB的基本材料，常叫基材，当它用于多层板生产时，也叫芯板。覆铜板按照机械刚性分为：刚性板、挠性板；按照不同绝缘材料结构分为：有机树脂类覆铜板、金属基覆铜板、陶瓷基覆铜板；按照厚度分为：常规板和薄板，其中厚度小于0.5mm的为薄板；按照增强材料分为：玻璃布基覆铜板、纸基覆铜板、复合基覆铜板；按照某些特殊性能分为：高TG板、高介电性能办、防UV板。
由于普通型覆铜板的阻燃体系为含溴树脂体系（溴为卤素元素），溴化物燃烧产生对人类和环境有害的二恶英物质，寻找理想的阻燃体系代替卤素化物，生产制造环境友好型无卤覆铜板是推动电子产业发展，保护人类生存环境的前提。无卤覆铜板在必须保持普通覆铜板的基本性能的前提下，还需具有良好的介电性能，优异的耐离子迁移性和高CTI性，应用更加广泛。
目前覆铜板在生产过程中，需要先进行制胶，需要先将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态。在制作胶黏剂过程中，需要加入添加剂，目前的添加剂的组分为较为单一，其粘结效果较差，有待进一步的完善，且固化效果有待进一步的提高。
发明内容
本发明为了克服现有技术中的不足，提供了一种无卤无锑环保型覆铜板的添加剂材料配方。
本发明是通过以下技术方案实现：
一种无卤无锑环保型覆铜板的添加剂材料配方，所述的覆铜板包括胶黏剂层、玻璃纤维布、铜箔层，将所述胶黏剂层涂布于玻璃纤维布上，用环氧树脂在50℃以上将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态，在树脂制作完成后，将树脂温度保持在 60℃，用玻璃纤维布浸渍树脂，并在一定的温度下进行烘烤制作成半固化片，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺3-7份、氢氧化铝粉末13-27份、过氧化二异丙苯1-5份、氢氧化镁粉末2-5份、二乙烯三胺3-7份、十二烷基苯磺酸钠6-13份、聚酰胺13-23份、氢氧化钠粉末5-7份、己二酸二甲酯8-12份和二甲基咪唑5-8份。
进一步地，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺3份、氢氧化铝粉末13份、过氧化二异丙苯1份、氢氧化镁粉末2份、二乙烯三胺3份、十二烷基苯磺酸钠6份、聚酰胺13份、氢氧化钠粉末5份、己二酸二甲酯8份和二甲基咪唑5份。
进一步地，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺7份、氢氧化铝粉末27份、过氧化二异丙苯5份、氢氧化镁粉末5份、二乙烯三胺7份、十二烷基苯磺酸钠13份、聚酰胺23份、氢氧化钠粉末7份、己二酸二甲酯12份和二甲基咪唑8份。
进一步地，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺5份、氢氧化铝粉末20份、过氧化二异丙苯3份、氢氧化镁粉末4份、二乙烯三胺5份、十二烷基苯磺酸钠10份、聚酰胺18份、氢氧化钠粉末6份、己二酸二甲酯10份和二甲基咪唑7份。
二甲基甲酰胺（DMF）是一种透明液体，能和水及大部分有机溶剂互溶。它是化学反应的常用溶剂。纯二甲基甲酰胺是没有气味的，但工业级或变质的二甲基甲酰胺则有鱼腥味，因其含有二甲基胺的不纯物。名称来源是由于它是甲酰胺（甲酸的酰胺）的二甲基取代物，而二个甲基都位于N（氮）原子上。二甲基甲酰胺是高沸点的极性（亲水性）非质子性溶剂，能促进SN2反应机理的进行。 二甲基甲酰胺是利用甲酸甲酯和二甲基胺制造的。二甲基甲酰胺在强碱如氢氧化钠或强酸如盐酸或硫酸的存在下是不稳定的（尤其在高温下），并水解为甲酸与二甲基胺。
氢氧化铝的化学式Al(OH)3，是铝的氢氧化物。氢氧化铝既能与酸反应生成盐和水又能与强碱反应生成盐和水，因此也是一种两性氢氧化物。化学式Al(OH)3，是铝的氢氧化物。由于又显一定的酸性，所以又可称之为铝酸（H3AlO3），但实际与碱反应时生成的是四羟基合铝酸盐（[Al(OH)4]-）。
过氧化二异丙苯，又称硫化剂DCP、过氧化二枯茗。 白色结晶。室温下稳定，见光逐渐变成微黄色。不溶于水，溶于乙醇、***、乙酸、苯和石油醚。是一种强氧化剂。可作为单体聚合的引发剂，高分子材料的硫化剂、交联剂、固化剂、阻燃添加剂等。
氢氧化镁别名苛性镁石，轻烧镁砂等，氢氧化镁在水中的悬浊液称为氢氧化镁乳剂，简称镁乳，氢氧化镁是无色六方柱晶体或白色粉末，难溶于水和醇，溶于稀酸和铵盐溶液，水溶液呈弱碱性。在水中的溶解度很小，但溶于水的部分完全电离。氢氧化镁的天然矿物水镁石。可用于制糖和氧化镁等。因氢氧化镁在大自然含量比较丰富，而其化学性质和铝较相近，因此使用者开始用氢氧化镁来取代氯化铝用于香体产品。化学式Mg(OH)2，式量58.32。白色无定形粉末。难溶于水，易溶于稀酸和铵盐溶液。饱和水溶液的浓度为1.9毫克/升(18℃)，呈碱性。加热到350℃失去水生成氧化镁。
二乙烯三胺是黄色具有吸湿性的透明粘稠液体，有刺激性氨臭，可燃，呈强碱性。溶于水、丙酮、苯、乙醇、甲醇等，难溶于正庚烷，对铜及其合金有腐蚀性。熔点-35℃，沸点207℃，相对密度0.9586（20、20℃），折射率1.4810。闪点94℃。本品具有仲胺的反应性，易与多种化合物起反应，其衍生物有广泛的用途。易吸收空气中的水分和二氧化碳。
十二烷基苯磺酸钠简称SDBS，白色或淡黄色粉状或片状固体。难挥发，易溶于水，溶于水而成半透明溶液。对碱，稀酸，硬水化学性质稳定。
聚酰胺它是大分子主链重复单元中含有酰胺基团的高聚物的总称。聚酰胺可由内酸胺开环聚合制得，也可由二元胺与二元酸缩聚等得到的。是美国DuPont公司最先开发用于纤维的树脂，于1939年实现工业化。20世纪50年代开始开发和生产注塑制品，以取代金属满足下游工业制品轻量化、降低成本的要求。PA具有良好的综合性能，包括力学性能、耐热性、耐磨损性、耐化学药品性和自润滑性，且摩擦系数低，有一定的阻燃性，易于加工，适于用玻璃纤维和其它填料填充增强改性，提高性能和扩大应用范围。
氢氧化钠，化学式为NaOH，俗称烧碱、火碱、苛性钠，为一种具有强腐蚀性的强碱，一般为片状或块状形态，易溶于水（溶于水时放热）并形成碱性溶液，另有潮解性，易吸取空气中的水蒸气（潮解）和二氧化碳（变质），可加入盐酸检验是否变质。NaOH是化学实验室其中一种必备的化学品，亦为常见的化工品之一。纯品是无色透明的晶体。密度2.130g/cm³。熔点318.4℃。沸点1390℃。工业品含有少量的氯化钠和碳酸钠，是白色不透明的晶体。有块状，片状，粒状和棒状等。式量39.997。氢氧化钠在水处理中可作为碱性清洗剂，溶于乙醇和甘油；不溶于丙醇、***。与氯、溴、碘等卤素发生歧化反应。与酸类起中和作用而生成盐和水。
己二酸二甲酯的化学式为：C8H14O4，又称己二酸双甲酯、肥酸二甲酯，为一种无色透明液体，其熔点为8℃，沸点为109-110℃ (14 mmHg)、228.7℃(760mmHg)，不溶于水，能溶于醇、醚，属于低毒类物质，工业上主要用于合成中间体、医药、香料的原料，用作增塑剂和高沸点溶剂等。
二甲基咪唑是白色结晶粉末，有吸潮性，溶于水、醇中，溶于丙酮，DMF。难溶于苯；有毒，对皮肤、粘膜有刺激性和腐蚀性。本品用于甲硝唑，迪美唑的合成。
与现有的技术相比，本发明的有益效果是：本发明通过将添加剂由二甲基甲酰胺、氢氧化铝粉末、过氧化二异丙苯、氢氧化镁粉末、二乙烯三胺、十二烷基苯磺酸钠、聚酰胺、氢氧化钠粉末、己二酸二甲酯和二甲基咪唑组成，并将这些种类的添加剂按照适当的比例配制好在高温下熔融搅拌混合而成，将得到的添加剂运用到覆铜板的生产工艺当中，这种类型的添加剂在使用时固化性能优异，且制作方法简单、方便，能够提高其稳定性能、粘接效果，能够防止铜箔脱落。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例一：
一种无卤无锑环保型覆铜板的添加剂材料配方，所述的覆铜板包括胶黏剂层、玻璃纤维布、铜箔层，将所述胶黏剂层涂布于玻璃纤维布上，用环氧树脂在50℃以上将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态，在树脂制作完成后，将树脂温度保持在 60℃，用玻璃纤维布浸渍树脂，并在一定的温度下进行烘烤制作成半固化片，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺3份、氢氧化铝粉末13份、过氧化二异丙苯1份、氢氧化镁粉末2份、二乙烯三胺3份、十二烷基苯磺酸钠6份、聚酰胺13份、氢氧化钠粉末5份、己二酸二甲酯8份和二甲基咪唑5份。
实施例二：
一种无卤无锑环保型覆铜板的添加剂材料配方，所述的覆铜板包括胶黏剂层、玻璃纤维布、铜箔层，将所述胶黏剂层涂布于玻璃纤维布上，用环氧树脂在50℃以上将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态，在树脂制作完成后，将树脂温度保持在 60℃，用玻璃纤维布浸渍树脂，并在一定的温度下进行烘烤制作成半固化片，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺7份、氢氧化铝粉末27份、过氧化二异丙苯5份、氢氧化镁粉末5份、二乙烯三胺7份、十二烷基苯磺酸钠13份、聚酰胺23份、氢氧化钠粉末7份、己二酸二甲酯12份和二甲基咪唑8份。
实施例三：
一种无卤无锑环保型覆铜板的添加剂材料配方，所述的覆铜板包括胶黏剂层、玻璃纤维布、铜箔层，将所述胶黏剂层涂布于玻璃纤维布上，用环氧树脂在50℃以上将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态，在树脂制作完成后，将树脂温度保持在 60℃，用玻璃纤维布浸渍树脂，并在一定的温度下进行烘烤制作成半固化片，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺5份、氢氧化铝粉末20份、过氧化二异丙苯3份、氢氧化镁粉末4份、二乙烯三胺5份、十二烷基苯磺酸钠10份、聚酰胺18份、氢氧化钠粉末6份、己二酸二甲酯10份和二甲基咪唑7份。
本发明通过将添加剂由二甲基甲酰胺、氢氧化铝粉末、过氧化二异丙苯、氢氧化镁粉末、二乙烯三胺、十二烷基苯磺酸钠、聚酰胺、氢氧化钠粉末、己二酸二甲酯和二甲基咪唑组成，并将这些种类的添加剂按照适当的比例配制好在高温下熔融搅拌混合而成，将得到的添加剂运用到覆铜板的生产工艺当中，这种类型的添加剂在使用时固化性能优异，且制作方法简单、方便，能够提高其稳定性能、粘接效果，能够防止铜箔脱落。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的仅为本发明的优选例，并不用来限制本发明，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.无卤无锑环保型覆铜板的添加剂材料配方，所述的覆铜板包括胶黏剂层、玻璃纤维布、铜箔层，将所述胶黏剂层涂布于玻璃纤维布上，用环氧树脂在50℃以上将固化剂溶解，然后加入添加剂经过充分溶解和充分搅拌混合均匀后，让胶液熟化若干小时，让各组分有足够相互接触、相互渗透，经一段时间使胶体达到一个稳定平衡状态，在树脂制作完成后，将树脂温度保持在 60℃，用玻璃纤维布浸渍树脂，并在一定的温度下进行烘烤制作成半固化片，其特征在于，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺3-7份、氢氧化铝粉末13-27份、过氧化二异丙苯1-5份、氢氧化镁粉末2-5份、二乙烯三胺3-7份、十二烷基苯磺酸钠6-13份、聚酰胺13-23份、氢氧化钠粉末5-7份、己二酸二甲酯8-12份和二甲基咪唑5-8份。
2.根据权利要求1所述的无卤无锑环保型覆铜板的添加剂材料配方，其特征在于，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺3份、氢氧化铝粉末13份、过氧化二异丙苯1份、氢氧化镁粉末2份、二乙烯三胺3份、十二烷基苯磺酸钠6份、聚酰胺13份、氢氧化钠粉末5份、己二酸二甲酯8份和二甲基咪唑5份。
3.根据权利要求1所述的无卤无锑环保型覆铜板的添加剂材料配方，其特征在于，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺7份、氢氧化铝粉末27份、过氧化二异丙苯5份、氢氧化镁粉末5份、二乙烯三胺7份、十二烷基苯磺酸钠13份、聚酰胺23份、氢氧化钠粉末7份、己二酸二甲酯12份和二甲基咪唑8份。
4.根据权利要求1所述的无卤无锑环保型覆铜板的添加剂材料配方，其特征在于，所述的添加剂由如下重量份的组分制成：二甲基甲酰胺5份、氢氧化铝粉末20份、过氧化二异丙苯3份、氢氧化镁粉末4份、二乙烯三胺5份、十二烷基苯磺酸钠10份、聚酰胺18份、氢氧化钠粉末6份、己二酸二甲酯10份和二甲基咪唑7份。
CN201611268682.XA 2016-12-31 2016-12-31 无卤无锑环保型覆铜板的添加剂材料配方 Pending CN106700426A (zh)