CN106671388A - Wood-plastic decorative board high in moisture resistance - Google Patents

Wood-plastic decorative board high in moisture resistance Download PDF

Info

Publication number
CN106671388A
CN106671388A CN201611004021.6A CN201611004021A CN106671388A CN 106671388 A CN106671388 A CN 106671388A CN 201611004021 A CN201611004021 A CN 201611004021A CN 106671388 A CN106671388 A CN 106671388A
Authority
CN
China
Prior art keywords
parts
moisture resistance
wood
decorative board
plastic decorative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611004021.6A
Other languages
Chinese (zh)
Inventor
史兆武
屈山峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Golden Crown Green Wood Industry Co Ltd
Original Assignee
Anhui Golden Crown Green Wood Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Golden Crown Green Wood Industry Co Ltd filed Critical Anhui Golden Crown Green Wood Industry Co Ltd
Priority to CN201611004021.6A priority Critical patent/CN106671388A/en
Publication of CN106671388A publication Critical patent/CN106671388A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the technical field of wood-plastic composite boards and particularly relates to a wood-plastic decorative board high in moisture resistance. The wood-plastic decorative board high in moisture resistance comprises a core layer and a decorative layer. The core layer is made of prepreg. The prepreg is made of the following raw materials comprising sulfonated amino-formaldehyde resin, pinus elliottii rosin, carbonized softwood pulp, waxy corn starch, ash calcium powder, ardealite, dihydrocumic acid, acrylic fiber pulp, coal ash floating beads, diphenylamine, Fischer-tropsch wax, calcium stearate, terephthaloyl chloride and an accelerant. Compared with the prior art, the wood-plastic decorative board high in moisture resistance has the advantages that materials having multiple properties cooperate, so that the structure stability is high after forming, the wood-plastic decorative board high in moisture resistance is good in aging resistance, corrosion resistance, sound insulation effect, heat preservation effect, flame retardant effect and mechanical property, the moisture resistance is greatly improved under the corresponding strength, and the wood-plastic decorative board high in moisture resistance is suitable for suspended ceiling engineering and buildings in southern cities wherein the plum rain season exists, capable of guaranteeing the construction quality and the service life period of the buildings and remarkable in economic benefit.

Description

A kind of strong wood-plastic decorative board of moisture resistance
Technical field
The invention belongs to wood-plastic clad plate technical field, and in particular to a kind of strong wood-plastic decorative board of moisture resistance.
Background technology
Wood-plastic composite panel is one kind mainly by timber（Lignose, plant cellulose）Based on material and thermoplasticity it is high Molecular material（Plastics）With processing aid etc., after being well mixed again the heating extrusion molding of Jing die apparatus and made by high-tech it is green Colour circle protects new decorative material, has the performance and feature of timber and plastics concurrently, is the NEW TYPE OF COMPOSITE material that can substitute timber and plastics Material, with expanding economy, the improvement of people's living standards, people have higher wanting to the speed and quality of Decoration Industry Ask, wood-plastic composite panel compare common wood loss it is low, be not required to paint or water paint coating process, easy construction, price be adapted to, Long service life, maintenance cost is low, therefore is increasingly liked by masses, and existing wood-plastic composite panel has had stronger anti- It is aqueous, but many areas in south can be moister for a long time in rainy season, and at this moment, part wood-plastic clad plate is it is possible that inhale Situations such as wet, softening, deformation, therefore have larger requirement to moisture resistance.
The content of the invention
The purpose of the present invention is for existing problem, there is provided a kind of strong wood-plastic decorative board of moisture resistance.
The present invention is achieved by the following technical solutions：A kind of strong wood-plastic decorative board of moisture resistance, including sandwich layer and dress Decorations layer, its center core layer is made up of prepreg, and the prepreg is made up of the raw material of following weight portion：Sulfonated amino resin 15-20 parts, Slash pine rosin 13-15 parts, carbonization softwood pulp 5-8 parts, waxy corn starch 2-6 parts, sierozem power 3-6 parts, ardealite 6-10 Part, dihydrocumic acid 4-6 parts, acrylic fibers pulp 2-4 parts, fly ash float 3-5 parts, diphenylamines 0.2-0.4 parts, Fischer-Tropsch wax 2-3 parts, Calcium stearate 0.7-1.5 parts, paraphthaloyl chloride 0.1-0.3 parts, accelerator 0.2-0.5 parts；
Waxy corn starch using it is front its water content is adjusted to 42% after, sealing and balancing 5-8 minute, be subsequently placed in Microwave Frequency Rate is cooled to room temperature to process 20 seconds in the microwave device of 350-400MHz, and drying and crushing to particle diameter is 200-400nm.
Used as further improvement of these options, the sulfonation degree of the sulfonated amino resin is 16.5-18%.
As further improvement of these options, the model FUJICURE FXR1020/1081 of the accelerator.
Used as further improvement of these options, the decorative layer is made by the mixing of kaolin, wollastonite in powder and sepiolite Into mixed weight ratio is 5:4:2.
Used as further improvement of these options, the preparation method of the sandwich layer is comprised the following steps：
（1）By the mixing of sulfonated amino resin, slash pine rosin, sierozem power and ardealite, mix under conditions of 95-100 DEG C, dry The mixed powder that particle diameter is 60-80 μm is ground to form after dry；
（2）By acrylic fibers pulp, carbonization softwood pulp, diphenylamines and dihydrocumic acid, insulated and stirred 3- under conditions of 35-40 DEG C 4 hours, obtain mixed serum；
（3）Mixed serum and mixed powder are mixed, is stirred 15-20 minutes under conditions of 600-800 rev/min, be cooled to often Temperature, adds surplus stock, is sufficiently mixed, and by double screw extruder melt blending, extrusion molding, obtains final product.
The present invention has compared to existing technology advantages below：The material of multiple performance mutually acts synergistically in the present invention, into Structural stability is high after type, maintains preferable Ageing-resistant corrosion-resistant effect property, and sound insulation, insulation, flame retardant effect, mechanical property compared with It is good, while also substantially increasing the moisture resistance under respective strengths, it is adaptable to which furred ceiling engineering has the city of plum rain season in south In city's building, it is ensured that Construction Quality and service life, remarkable in economical benefits.
Specific embodiment
Embodiment 1
A kind of strong wood-plastic decorative board of moisture resistance, including sandwich layer and decorative layer, its center core layer is made up of prepreg, the prepreg by The raw material of following weight portion is made：15 parts of sulfonated amino resin, 15 parts of slash pine rosin, 5 parts of softwood pulp of carbonization, waxy corn 6 parts of starch, 3 parts of sierozem power, 10 parts of ardealite, 4 parts of dihydrocumic acid, 4 parts of acrylic fibers pulp, 3 parts of fly ash float, diphenylamines 0.2 part, 2 parts of Fischer-Tropsch wax, 1.5 parts of calcium stearate, 0.1 part of paraphthaloyl chloride, 0.5 part of accelerator；
Waxy corn starch using it is front its water content is adjusted to 42% after, sealing and balancing 6 minutes is subsequently placed in microwave frequency To process 20 seconds in the microwave device of 350MHz, room temperature is cooled to, drying and crushing to particle diameter is 300nm.
Wherein, the sulfonation degree of the sulfonated amino resin is 18%；Model FUJICURE of the accelerator FXR1020/1081；The decorative layer is mixed by kaolin, wollastonite in powder and sepiolite, and mixed weight ratio is 5:4:2.
Wherein, the preparation method of the sandwich layer is comprised the following steps：
（1）By the mixing of sulfonated amino resin, slash pine rosin, sierozem power and ardealite, mix under conditions of 95-100 DEG C, dry The mixed powder that particle diameter is 60-80 μm is ground to form after dry；
（2）By acrylic fibers pulp, carbonization softwood pulp, diphenylamines and dihydrocumic acid, insulated and stirred 3- under conditions of 35-40 DEG C 4 hours, obtain mixed serum；
（3）Mixed serum and mixed powder are mixed, is stirred 15-20 minutes under conditions of 600-800 rev/min, be cooled to often Temperature, adds surplus stock, is sufficiently mixed, and by double screw extruder melt blending, extrusion molding, obtains final product.
Embodiment 2
A kind of strong wood-plastic decorative board of moisture resistance, including sandwich layer and decorative layer, its center core layer is made up of prepreg, the prepreg by The raw material of following weight portion is made：20 parts of sulfonated amino resin, 13 parts of slash pine rosin, 5 parts of softwood pulp of carbonization, waxy corn 2 parts of starch, 6 parts of sierozem power, 6 parts of ardealite, 6 parts of dihydrocumic acid, 2 parts of acrylic fibers pulp, 5 parts of fly ash float, diphenylamines 0.4 Part, 3 parts of Fischer-Tropsch wax, 1.5 parts of calcium stearate, 0.1 part of paraphthaloyl chloride, 0.4 part of accelerator；
Waxy corn starch using it is front its water content is adjusted to 42% after, sealing and balancing 6 minutes is subsequently placed in microwave frequency To process 20 seconds in the microwave device of 380MHz, room temperature is cooled to, drying and crushing to particle diameter is 400nm.
Remainder is in the same manner as in Example 1.
Embodiment 3
A kind of strong wood-plastic decorative board of moisture resistance, including sandwich layer and decorative layer, its center core layer is made up of prepreg, the prepreg by The raw material of following weight portion is made：18 parts of sulfonated amino resin, 14 parts of slash pine rosin, 6 parts of softwood pulp of carbonization, waxy corn 4 parts of starch, 5 parts of sierozem power, 8 parts of ardealite, 5 parts of dihydrocumic acid, 4 parts of acrylic fibers pulp, 4 parts of fly ash float, diphenylamines 0.3 Part, 3 parts of Fischer-Tropsch wax, 1.2 parts of calcium stearate, 0.2 part of paraphthaloyl chloride, 0.3 part of accelerator；
Waxy corn starch using it is front its water content is adjusted to 42% after, sealing and balancing 8 minutes is subsequently placed in microwave frequency To process 20 seconds in the microwave device of 350MHz, room temperature is cooled to, drying and crushing to particle diameter is 200nm.
Remainder is in the same manner as in Example 1.
The impact strength of decorative panel is 1.5KJ/ ㎡ or so in the present invention, in order to prove the present invention in the strong wood of moisture resistance The performance design contrast test of plastic decorative board, test method is wood of the impact strength for 1.5KJ/ ㎡ or so for taking conventional method Plastic decorative board cuts into the bar shaped plank that length and width specification is 300mm × 50mm, and as a control group, putting it into relative humidity is 98%th, temperature is in 40 DEG C of chamber, to ride upon on case inner support, and 15mm is taken per side, middle hanging, is kept in casing Stationary temperature and humidity, then at 2,4,6 hours measured its sagging size respectively, and testing result is as follows：
Table 1
Sagging size（mm） 2 hours 4 hours 6 hours
Embodiment 1 0 1.2 2.3
Embodiment 2 0 1.5 2.6
Embodiment 3 0 1.3 2.4
Control group 1.4 3.8 8.7
The moisture-resisting decoration board humidity resistance prepared in the present invention is can be seen that by data in table 1 higher, and with stronger power Intensity is learned, decorative panel prepared in the present invention is used for into furred ceiling engineering or in there is the urban architecture of plum rain season in south, can To ensure Construction Quality and service life.

Claims (5)

1. the strong wood-plastic decorative board of a kind of moisture resistance, it is characterised in that including sandwich layer and decorative layer, its center core layer is by prepreg system Into the prepreg is made up of the raw material of following weight portion：Sulfonated amino resin 15-20 parts, slash pine rosin 13-15 parts, carbonization Softwood pulp 5-8 parts, waxy corn starch 2-6 parts, sierozem power 3-6 parts, ardealite 6-10 parts, dihydrocumic acid 4-6 parts, acrylic fibers Pulp 2-4 parts, fly ash float 3-5 parts, diphenylamines 0.2-0.4 parts, Fischer-Tropsch wax 2-3 parts, calcium stearate 0.7-1.5 parts, to benzene Dimethyl chloride 0.1-0.3 parts, accelerator 0.2-0.5 parts；
Waxy corn starch using it is front its water content is adjusted to 42% after, sealing and balancing 5-8 minute, be subsequently placed in Microwave Frequency Rate is cooled to room temperature to process 20 seconds in the microwave device of 350-400MHz, and drying and crushing to particle diameter is 200-400nm.
2. a kind of as claimed in claim 1 strong wood-plastic decorative board of moisture resistance, it is characterised in that the sulphur of the sulfonated amino resin Change degree is 16.5-18%.
3. a kind of as claimed in claim 1 strong wood-plastic decorative board of moisture resistance, it is characterised in that the model of the accelerator FUJICURE FXR1020/1081。
4. the as claimed in claim 1 strong wood-plastic decorative board of a kind of moisture resistance, it is characterised in that the decorative layer by kaolin, Wollastonite in powder and sepiolite are mixed, and mixed weight ratio is 5:4:2.
5. a kind of as claimed in claim 1 strong wood-plastic decorative board of moisture resistance, it is characterised in that the preparation method bag of the sandwich layer Include following steps：
（1）By the mixing of sulfonated amino resin, slash pine rosin, sierozem power and ardealite, mix under conditions of 95-100 DEG C, dry The mixed powder that particle diameter is 60-80 μm is ground to form after dry；
（2）By acrylic fibers pulp, carbonization softwood pulp, diphenylamines and dihydrocumic acid, insulated and stirred 3- under conditions of 35-40 DEG C 4 hours, obtain mixed serum；
（3）Mixed serum and mixed powder are mixed, is stirred 15-20 minutes under conditions of 600-800 rev/min, be cooled to often Temperature, adds surplus stock, is sufficiently mixed, and by double screw extruder melt blending, extrusion molding, obtains final product.
CN201611004021.6A 2016-11-15 2016-11-15 Wood-plastic decorative board high in moisture resistance Pending CN106671388A (en)