CN106645167A - Fast detection method of aluminum anode dark line - Google Patents
Fast detection method of aluminum anode dark line Download PDFInfo
- Publication number
- CN106645167A CN106645167A CN201611168454.5A CN201611168454A CN106645167A CN 106645167 A CN106645167 A CN 106645167A CN 201611168454 A CN201611168454 A CN 201611168454A CN 106645167 A CN106645167 A CN 106645167A
- Authority
- CN
- China
- Prior art keywords
- concealed wire
- quickly detecting
- aluminium
- aluminium anode
- dark line
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fast detection method of an aluminum anode dark line. The method comprises that after the anodic alumina plate is washed by alkali and pickled, the anodic alumina plate is put into a triple acid mixture solution to be etched, then the anodic alumina plate is put into a camera obscura and tested by bright light. The fast detection method of aluminum anode dark line is easy to operate, after treatment for 10-20 minutes, the aluminum anode dark line can be quickly detected by naked eyes, and the detection result is accurate.
Description
Technical field
The present invention relates to a kind of method for quickly detecting of aluminium anode concealed wire.
Background technology
Concealed wire be aluminium section bar in extrusion process because the slag inclusion or impression of material internal cause, it is carried out in aluminium section bar
Directly detection is difficult to before oxidation, needs the operation such as Jing alkali cleanings, pickling, neutralization, powered anode after oxidation that defect could be allowed to manifest
Out.Therefore, time-consuming for the characterization processes of current aluminium anode dark line, high cost, affects very big to production efficiency.
The content of the invention
For the problems referred to above, the invention provides a kind of method for quickly detecting of aluminium anode concealed wire, at its Jing short time
The quick naked eyes that aluminium anode concealed wire is capable of achieving after reason are detected.
For achieving the above object, the present invention is adopted the following technical scheme that:
A kind of method for quickly detecting of aluminium anode concealed wire, it is comprised the following steps:
1)Alkali cleaning:Anodic oxidation aluminium plate is put in the NaOH solution that mass fraction is 8% ~ 12% and is soaked after 2 ~ 3min, taken out,
Rinsed well with water;
2)Pickling:Sheet material is put into into 0.5 ~ 2min of immersion in the hydrochloric acid solution that mass fraction is 5%, is taken out, rinsed well with water;
3)Three acid etch:By hydrofluoric acid, hydrochloric acid, nitric acid and water by volume 2:6:6:86 are mixed into three sour mixed solutions, then
By the sheet material after surface treated in three sour mixed solutions 2 ~ 3min of etch;
4)Inspection:Sheet material after etch is taken out, is rinsed well with water, then dried, in placing into camera bellows, using high light(Work(
The LED lamp source of rate > 5W)Irradiation is tested.
The present invention enables aluminium anode concealed wire in strong illumination by alkali cleaning, pickling, three acid-etched fast version processing steps
Under present canescence fine strip shape, so as to can by naked eyes be detected, its whole process only needs more than ten minutes, compares traditional
Testing process(Nearly 45 minutes)Save time about 30min;Meanwhile, the inventive method is simple due to treatment process, and at normal temperatures
Processed, monthly 20,000 yuan nearly compared with traditional detection method escapable cost.Therefore, the present invention can the current aluminium sun of effectively solving
Time-consuming for very dark line characterization processes, high cost the problems such as, the value with good popularization and application.
Description of the drawings
Fig. 1 is using the concealed wire on the aluminium observed after the inventive method process.
Specific embodiment
In order that content of the present invention easily facilitates understanding, with reference to specific embodiment to of the present invention
Technical scheme is described further, but the present invention is not limited only to this.
Embodiment 1
A kind of method for quickly detecting of aluminium anode concealed wire, its concrete operations are as follows:
1)Sampling:Detection model, a width of 450 ± 30mm of plate are taken in production aluminium volume parent roll;
2)Alkali cleaning:Model is put in the NaOH solution that mass fraction is 8% and is soaked after 3min, taken out, rinsed well with water, with
Eliminate the alkali lye of remained on surface;
3)Pickling:Model is put into into immersion 0.5min in the hydrochloric acid solution that mass fraction is 5% to be neutralized, is then taken out, use water
Rinse well;
4)Three acid etch:By hydrofluoric acid, hydrochloric acid, nitric acid and water by volume 2:6:6:86 are mixed into three sour mixed solutions, then
By the model after surface treated in three sour mixed solutions etch 2min, model immersion depth is wide 2/3 of plate;
5)Inspection:Model after etch is taken out, is rinsed well with water, then dried up with electric fan, placed into closed unglazed
In camera bellows, using high light(The LED lamp source of power > 5W)Irradiation is tested, and the canescence slice presented in surface of aluminum plate is i.e.
For concealed wire.
Embodiment 2
A kind of method for quickly detecting of aluminium anode concealed wire, its concrete operations are as follows:
1)Sampling:Detection model, a width of 450 ± 30mm of plate are taken in production aluminium volume parent roll;
2)Alkali cleaning:Model is put in the NaOH solution that mass fraction is 10% and is soaked after 2min, taken out, rinsed well with water, with
Eliminate the alkali lye of remained on surface;
3)Pickling:Model is put into into immersion 1min in the hydrochloric acid solution that mass fraction is 5% to be neutralized, is then taken out, rushed with water
Wash clean;
4)Three acid etch:By hydrofluoric acid, hydrochloric acid, nitric acid and water by volume 2:6:6:86 are mixed into three sour mixed solutions, then
By the model after surface treated in three sour mixed solutions etch 3min, model immersion depth is wide 2/3 of plate;
5)Inspection:Model after etch is taken out, is rinsed well with water, then dried up with electric fan, placed into closed unglazed
In camera bellows, using high light(The LED lamp source of power > 5W)Irradiation is tested, and the canescence slice presented in surface of aluminum plate is i.e.
For concealed wire.
Embodiment 3
A kind of method for quickly detecting of aluminium anode concealed wire, its concrete operations are as follows:
1)Sampling:Detection model, a width of 450 ± 30mm of plate are taken in production aluminium volume parent roll;
2)Alkali cleaning:Model is put in the NaOH solution that mass fraction is 12% and is soaked after 2min, taken out, rinsed well with water, with
Eliminate the alkali lye of remained on surface;
3)Pickling:Model is put into into immersion 2min in the hydrochloric acid solution that mass fraction is 5% to be neutralized, is then taken out, rushed with water
Wash clean;
4)Three acid etch:By hydrofluoric acid, hydrochloric acid, nitric acid and water by volume 2:6:6:86 are mixed into three sour mixed solutions, then
By the model after surface treated in three sour mixed solutions 2 ~ 3min of etch, model immersion depth is wide 2/3 of plate;
5)Inspection:Model after etch is taken out, is rinsed well with water, then dried up with electric fan, placed into closed unglazed
In camera bellows, using high light(The LED lamp source of power > 5W)Irradiation is tested, and the canescence slice presented in surface of aluminum plate is i.e.
For concealed wire.
More than ten minutes are only needed to process the detection of i.e. achievable aluminium anode concealed wire using the inventive method.Fig. 1 is to observe
Aluminium on concealed wire.
Claims (5)
1. a kind of method for quickly detecting of aluminium anode concealed wire, it is characterised in that:By anodic oxidation aluminium plate Jing alkali cleanings, pickling
Afterwards, being put in three sour mixed solutions carries out etch, places in camera bellows and is tested using strong illumination.
2. the method for quickly detecting of aluminium anode concealed wire according to claim 1, it is characterised in that:The alkali cleaning is by sheet material
It is put into is soaked in the NaOH solution that mass fraction is 8% ~ 12% and take out after 2 ~ 3min.
3. the method for quickly detecting of aluminium anode concealed wire according to claim 1, it is characterised in that:The pickling is by Jing alkali
Sheet material after washing places into 0.5 ~ 2min of immersion in the hydrochloric acid solution that mass fraction is 5%.
4. the method for quickly detecting of aluminium anode concealed wire according to claim 1, it is characterised in that:Described three sour mixed solutions
It is to mix in hydrofluoric acid, hydrochloric acid, nitric acid and water, its volume ratio is 2:6:6:86.
5. the method for quickly detecting of aluminium anode concealed wire according to claim 1, it is characterised in that:The leaching of three sour mixed solutions
The erosion time is 2 ~ 3min.