CN106634448A - Waterborne epoxy flash-rust preventing paint - Google Patents
Waterborne epoxy flash-rust preventing paint Download PDFInfo
- Publication number
- CN106634448A CN106634448A CN201611271370.4A CN201611271370A CN106634448A CN 106634448 A CN106634448 A CN 106634448A CN 201611271370 A CN201611271370 A CN 201611271370A CN 106634448 A CN106634448 A CN 106634448A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- paint
- flash
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to waterborne epoxy flash-rust preventing paint which is prepared from 30% to 33% of waterborne epoxy emulsion, 10% to 11% of waterborne epoxy curing agent, 40% to 46% of anti-corrosive filler, 1% to 2% of flash-rust preventing agent, 1% to 2% of dispersing agent, 1% to 2% of wetting agent, 1% to 2% of defoaming agent and the balance of water in percentage by mass. According to the waterborne epoxy flash-rust preventing paint disclosed by the invention, the waterborne epoxy emulsion and the waterborne epoxy curing agent which are modified by pure plant cardanol are utilized, so that a prepared paint film is high in film hardness, good in adhesive force, excellent in anti-corrosive performance and mechanical performance, safe and environment-friendly and has no pollution. According to the waterborne epoxy flash-rust preventing paint disclosed by the invention, the paint film is better in flash-rust prevention ability and wider in construction environment, and can resist to low-temperature curing.
Description
Technical field
The present invention relates to chemical, more particularly to coating, a kind of specifically anti-flash rusting paint of water-base epoxy.
Background technology
Jiangsu University of Science and Technology applies《A kind of water corrosion-resistant epoxy paint containing anti-flash rusting agent and preparation method thereof》's
Patent, is with aqueous epoxy resins, waterborne curing agent, anti-flash rusting and other color stuffings as primary raw material, with certain percentage
After proportioning is mixed, the anti-flash rusting coating required for being formed, wherein waterborne curing agent are its specific alkyl phenol structure.Pass through
Coating prepared by the formula has stronger anti-flash rusting and high temperature resistant, acidproof, alkaline-resisting, organic solvent-resistant ability, while construction
It is convenient, prepare simple, pollution-free, be a kind of water-based anticorrosive paint of environment-friendly type.
Northwest Yongxin Paint & Coatings Co., Ltd. applies《Aqueous antirust paint and preparation method thereof》Patent, be mainly with aqueous
Acrylic modified epoxy resin, nertralizer, aqueous anti-flash rusting agent and anticorrosive pigment/filler are primary raw material, are matched somebody with somebody with certain percentage
Anti- flash rusting coating after mixing, required for being formed.The aqueous antirust paint hardness of film is high, and adhesive force is good, anticorrosive property
Energy and mechanical performance are excellent, and the addition of aqueous anti-flash rusting agent improves the flash rusting inhibition of paint film.The aqueous antirust paint is with water
Diluent, greatly reduces the discharge of VOC in production and work progress, safe and environment-friendly, can be widely used in steel construction, pipe
The application of the aspects such as road, auto parts and components.
The content of the invention
It is an object of the invention to provide a kind of anti-flash rusting paint of water-base epoxy, the anti-flash rusting paint of described this water-base epoxy will
Solve anti-flash rusting in prior art and paint the not good technical problem of this high and low temperature performance.
The invention provides a kind of anti-flash rusting paint of water-base epoxy, is made up of the component of following mass percent:
Further, the structural formula of described aqueous epoxy curing agent is as follows:
Or Or, wherein
R is polyethylene polyamine base, m-phenylene diamine (MPD) base or m-xylene diamine base.
Further, described aqueous epoxy emulsion is by bisphenol A type epoxy resin, emulsifying agent, water, surfactant group
Into bisphenol A type epoxy resin, emulsifying agent, water, the mass ratio of surfactant are 10: 1: 10: 1.
Further, described anticorrosive packing is one or more in zinc powder, titanium dioxide, barium sulfate, iron oxide red.
Further, described anti-flash rusting agent is Lodge L8AF, L8NF difficult to understand.
Further, described dispersant is Nuo Pu sections 5040.
Further, described wetting agent is the peaceful 2103-3 of German section.
Further, described defoamer is Nuo Pu sections 154.
The present invention adopts the anacardol refined from cashew nut shell for initial feed, by the modified water required for modified synthesis
Property epoxy resin and waterborne curing agent, in this, as the main constituents of aqueous paint film, the Long carbon chain of anacardol has preferable
Pliability can be used to modified bisphenol A type epoxy resin, make the toughness of epoxy resin more preferably, heat resistance increases, resin
Viscosity decreases, more resistant to low-temperature setting.Improve the flash rusting inhibition of paint film by adding anti-flash rusting agent.
The present invention adopt curing agent structure in, phenolic hydroxyl group give curing agent rapid curing, low-temperature setting, it is corrosion-resistant,
The characteristics such as excellent adhesive force, long unsaturated aliphatic carbochain imparts the characteristics such as the more excellent toughness of curing agent, wellability.
The present invention is compared with prior art, and its technological progress is positive and obvious.The present invention utilizes a kind of pure plant waist
Aqueous epoxy resins and waterborne curing agent that fruit phenol is modified to, the hardness of film of the paint film being prepared into for making is high, and adhesive force is good, anti-
Corrosive nature and mechanical performance are excellent, safety and environmental protection is pollution-free.The present invention makes the anti-flash rusting ability of paint film more preferably, ring of constructing
Border is wider, is resistant to low-temperature setting.
Specific embodiment
Embodiment 1:
The invention provides a kind of anti-flash rusting paint of water-base epoxy, according to weight following component is weighed:
Aqueous epoxy emulsion 99g,
Waterborne curing agent 33g,
Anticorrosive pigment/filler 45g,
Anti- flash rusting agent 2g,
Defoamer 0.1g,
Dispersant 0.1g,
Wetting agent 0.1g,
Wax powder 1g, stirs after above-mentioned component is mixed and obtains final product the anti-flash rusting paint of water-base epoxy.
Further, the structural formula of described aqueous epoxy curing agent is as follows:
Or Or, wherein R is
Polyethylene polyamine base, m-phenylene diamine (MPD) base or m-xylene diamine base.
Further, described aqueous epoxy emulsion is by bisphenol A type epoxy resin, emulsifying agent, water, surfactant group
Into bisphenol A type epoxy resin, emulsifying agent, water, the mass ratio of surfactant are 10: 1: 10: 1.
Further, described anticorrosive packing is one or more in zinc powder, titanium dioxide, barium sulfate, iron oxide red.
Further, described anti-flash rusting agent is Lodge L8AF difficult to understand.
Further, described dispersant is Nuo Pu sections 5040.
Further, described wetting agent is the peaceful 2103-3 of German section.
Further, described defoamer is Nuo Pu sections 154.
Paint film measured performance such as following table:
Claims (4)
1. the anti-flash rusting paint of a kind of water-base epoxy, it is characterised in that:It is made up of the component of following mass percent:
2. the anti-flash rusting paint of a kind of water-base epoxy according to claim 1, it is characterised in that:Described aqueous epoxy curing agent
Structural formula it is as follows:
,
Wherein R is polyethylene polyamine base, m-phenylene diamine (MPD) base or m-xylene diamine base.
3. the anti-flash rusting paint of a kind of water-base epoxy according to claim 1, it is characterised in that:Described aqueous epoxy emulsion by
Bisphenol A type epoxy resin, emulsifying agent, water, surfactant composition, bisphenol A type epoxy resin, emulsifying agent, water, surfactant
Mass ratio be 10: 1: 10: 1.
4. the anti-flash rusting paint of a kind of water-base epoxy according to claim 1, it is characterised in that:Described anticorrosive packing is zinc
One or more in powder, titanium dioxide, barium sulfate, iron oxide red, described anti-flash rusting agent is Lodge L8AF or L8NF difficult to understand, institute
The dispersant stated is Nuo Pu sections 5040, and described wetting agent is the peaceful 2103-3 of German section, and described defoamer is Nuo Pu sections 154.