CN106626681A - Novel combined protective film use technology of conducting film - Google Patents
Novel combined protective film use technology of conducting film Download PDFInfo
- Publication number
- CN106626681A CN106626681A CN201710001623.4A CN201710001623A CN106626681A CN 106626681 A CN106626681 A CN 106626681A CN 201710001623 A CN201710001623 A CN 201710001623A CN 106626681 A CN106626681 A CN 106626681A
- Authority
- CN
- China
- Prior art keywords
- pet
- high temperature
- protective film
- back side
- conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel combined protective film of a conducting film. The novel combined protective film of the conducting film structurally comprises a PET conducting film, a PE high-temperature-resistant protective film layer, a PET high-temperature protective film, a PET conducting film conducting surface, a PET conducting film back surface, a PE high-temperature-resistant protective film layer low-viscous-force surface, a PE high-temperature-resistant protective film layer back side, a PET high-temperature protective film viscous-force surface, a PET high-temperature protective film back side, an upper pressing stick, a lower pressing stick and a rolling body, wherein the PET conducting film is connected with the PE high-temperature-resistant protective film layer. The novel combined protective film of the conducting film has the beneficial effects the defects that after adhering to the conducting film, various high-temperature-resistant protective film materials with different characteristics have residual adhesive, are deformed and warped, soft and easy to bend and damage, difficult to strip from the protective film, bad in back side protection, high in cost of protective film due to unmatched heating high-temperature baking shrinkage rate, and the qualified product yield in the production process is high.
Description
Technical field
The present invention is a kind of combination diaphragm of novel conductive film, belongs to diaphragm field.
Background technology
Diaphragm can be divided into protective film for digital product according to purposes, and protection film for automobile, family expenses diaphragm, food fresh keeping is protected
Cuticula etc..As the digital products such as mobile phone are in the popularization of China, a kind of diaphragm system for becoming screen protecting film slowly
Claim.
A kind of PVC diaphragms of application number 201520444746.1 are prior art discloses, the PVC diaphragms are from top to bottom
Include with the addition of the pressure-sensitive adhesive layer of auxiliary agent of absorbable plasticizer, the separation layers of PVDC first successively, with the addition of the plasticizer
PVC base film layer, the separation layers of PVDC second and parting agent layer, the pressure-sensitive adhesive layer is directly coated at the separation layers of the PVDC first
Surface；The separation layers of PVDC first are located between pressure-sensitive adhesive layer and PVC base film layer, and the separation layers of PVDC first can prevent plasticizer
Pressure-sensitive adhesive layer is moved to from PVC base film layer；The separation layers of PVDC second are located between PVC base film layer and parting agent layer, PVDC second
Separation layer can prevent plasticizer from penetrating parting agent layer from PVC base film layer and move to the pressure-sensitive adhesive layer after rolling, parting agent layer
The rubberised layer that the diaphragm of rolling can be prevented instead glues non-rubberised layer, so as to product uncoiling.The PVC diaphragms of the present invention, it is convenient
Uncoiling, can effectively prevent and reduce pressure-sensitive adhesive layer to come off, and when directly the PVC diaphragms are covered in into sheet material, effectively reduce plate
Occurs the probability of the defects such as cull, ghost on material.Because various high temperature resistant Protective coatings there are different qualities, therefore exist and lead
Exist to heat high-temperature baking shrinkage factor and do not match after electrolemma laminating and cull occur, deformation is tilted, soft pliable injured, and hardly possible peels off guarantor
Cuticula, back-protective is not good, the shortcomings of diaphragm high cost, causes procedure for producing yields low.
The content of the invention
In view of the shortcomings of the prior art, it is an object of the present invention to provide a kind of combination diaphragm of novel conductive film, with
Solve because various high temperature resistant Protective coatings there are different qualities, therefore there is heating high-temperature baking after presence is fitted with conducting film
Shrinkage factor is not matched there is cull, and deformation is tilted, soft pliable injured, and hardly possible peels off diaphragm, and back-protective is not good, diaphragm
The shortcomings of high cost, the problem for causing procedure for producing yields low.
To achieve these goals, the present invention is by the following technical solutions realizing：A kind of group of novel conductive film
Close diaphragm, its structure include PET conducting films, PE high temperature resistant protection film layers, PET high temperature dwell cuticula, PET conducting film conducting surfaces,
The PET conducting films back side, the low power of the being stained with face of PE high temperature resistant protection film layers, the PE high temperature resistant protection film layers back side, PET high temperature dwell cuticula are stained with power
Face, the PET high temperature dwell cuticula back side, upper pressing rod, lower nip roll, winding body, the PET conducting films are connected with PE high temperature resistant diaphragms
Layer, the PET conducting films are connected with PET high temperature dwell cuticula, and the PE high temperature resistants protection film layer back side is by upper pressing rod and pushes
Rod is connected with the PET conducting films back side, and the PET high temperature dwells cuticula back side is connected with PET conducting films by upper pressing rod and lower nip roll
The back side.
Further, the PET conducting films are provided with PET conducting films conducting surface and the PET conducting films back side.
Further, the PE high temperature resistants protection film layer is provided with the low power of the being stained with face of PE high temperature resistant protection film layers and PE high temperature resistants are protected
The cuticular layer back side.
Further, the PET high temperature dwells cuticula is stained with power face and the PET high temperature dwell cuticula back side including PET high temperature dwell cuticula.
Further, the upper pressing rod and lower nip roll are connected with winding body.
Beneficial effect
A kind of combination diaphragm of novel conductive film of the present invention, PET conducting films are connected with PE high temperature resistant protection film layers,
PET conducting films are connected with PET high temperature dwell cuticula, and the PE high temperature resistant protection film layer back sides are connected with PET by upper pressing rod and lower nip roll
The conducting film back side, the PET high temperature dwell cuticula back sides are connected with the PET conducting films back side by upper pressing rod and lower nip roll, solve due to
Various high temperature resistant Protective coatings have different qualities, therefore there is heating high-temperature baking shrinkage factor after presence is fitted with conducting film not
Supporting cull occur, deformation is tilted, and soft pliable injured, hardly possible peels off diaphragm, and back-protective is not good, diaphragm cost height etc.
Shortcoming, makes procedure for producing yields high.
Description of the drawings
The detailed description by reading non-limiting example made with reference to the following drawings, the further feature of the present invention,
Objects and advantages will become more apparent upon：
Fig. 1 is the structural representation of conducting film of the present invention；
Fig. 2 is a kind of structural representation of the combination diaphragm of novel conductive film of the invention；
In figure：PET conducting films -1, PE high temperature resistants protection film layer -2, PET high temperature dwells cuticula -3, PET conducting film conducting surfaces -
4th, the PET conducting films back side -5, the low power of the being stained with face -6 of PE high temperature resistant protection film layers, the PE high temperature resistant protection film layers back side -7, PET high temperature dwells
Cuticula is stained with power face -8, the PET high temperature dwell cuticula back side -9, upper pressing rod -10, lower nip roll -11, winding body -12.
Specific embodiment
Technological means, creation characteristic, reached purpose and effect to make present invention realization is easy to understand, with reference to
Specific embodiment, is expanded on further the present invention.
Fig. 1 and Fig. 2 is referred to, the present invention provides a kind of technical scheme：Its structure includes that PET conducting films 1, PE high temperature resistants are protected
Cuticular layer 2, PET high temperature dwells cuticula 3, PET conducting films conducting surface 4, the PET conducting films back side 5, the low power of being stained with of PE high temperature resistant protection film layers
Face 6, the PE high temperature resistant protection film layers back side 7, PET high temperature dwell cuticula be stained with power face 8, the PET high temperature dwell cuticula back side 9, upper pressing rod 10, under
Nip roll 11, winding body 12, the PET conducting films 1 are connected with PE high temperature resistants protection film layer 2, and the PET conducting films 1 are connected with PET
High temperature dwell cuticula 3, the PE high temperature resistants protection film layer back side 7 is connected with the PET conducting films back of the body by upper pressing rod 10 and lower nip roll 11
Face 5, the PET high temperature dwells cuticula back side 9 is connected with the PET conducting films back side 5, the PET by upper pressing rod 10 and lower nip roll 11
Conducting film 1 is provided with PET conducting films conducting surface 4 and the PET conducting films back side 5, and the PE high temperature resistants protection film layer 2 is provided with PE high temperature resistants
The low power of the being stained with face 6 of protection film layer and the PE high temperature resistant protection film layers back side 7, the PET high temperature dwells cuticula 3 includes PET high temperature dwell cuticula
Power face 8 and the PET high temperature dwell cuticula back side 9 are stained with, the upper pressing rod 10 and lower nip roll 11 are connected with winding body 12.The present invention's is beneficial
Effect is solved because various high temperature resistant Protective coatings have different qualities, therefore there is heating after presence is fitted with conducting film
High-temperature baking shrinkage factor is not matched there is cull, and deformation is tilted, soft pliable injured, and hardly possible peels off diaphragm, and back-protective is bad
Well, the shortcomings of diaphragm high cost, make procedure for producing yields high.
When being used, PE high temperature resistants protection film layer and PET high temperature dwells cuticula are adjusted into suitable technique with coating machine
It is required that successively uniform ground is fitted in the back side of PET conducting films.The bad phenomenon such as bubble, striped, concavo-convex must not be produced during laminating.
The general principle and principal character and advantages of the present invention of the present invention are had been shown and described above, for this area skill
For art personnel, it is clear that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the spirit without departing substantially from the present invention or
In the case of essential characteristic, the present invention can be in other specific forms realized.Therefore, no matter from the point of view of which point, all should be by
Embodiment regards exemplary as, and be it is nonrestrictive, the scope of the present invention by claims rather than on state
Bright restriction, it is intended that all changes in the implication and scope of the equivalency of claim that will fall are included in the present invention
It is interior.Any reference in claim should not be considered as and limit involved claim.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity those skilled in the art should
Using specification as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (5)
1. a kind of combination diaphragm of novel conductive film, it is characterised in that：Its structure includes that PET conducting films (1), PE high temperature resistants are protected
Cuticular layer (2), PET high temperature dwell cuticula (3), PET conducting film conducting surfaces (4), the PET conducting films back side (5), PE high temperature resistant diaphragms
The low power of the being stained with face (6) of layer, the PE high temperature resistant protection film layers back side (7), PET high temperature dwell cuticula are stained with power face (8), the PET high temperature dwells cuticula back of the body
Face (9), the PET conducting films (1) are connected with PE high temperature resistant protection film layers (2), and it is high that the PET conducting films (1) are connected with PET
Warm diaphragm (3), the PE high temperature resistants protection film layer back side (7) is connected with PET and is led by upper pressing rod (10) and lower nip roll (11)
The electrolemma back side (5), the PET high temperature dwells cuticula back side (9) is connected with PET conducting films by upper pressing rod (10) and lower nip roll (11)
The back side (5).
2. the combination diaphragm of a kind of novel conductive film according to claim 1, it is characterised in that：The PET conducting films
(1) PET conducting film conducting surfaces (4) and the PET conducting films back side (5) are provided with.
3. the combination diaphragm of a kind of novel conductive film according to claim 1, it is characterised in that：The PE high temperature resistants are protected
Cuticular layer (2) is provided with the low power of the being stained with face (6) of PE high temperature resistant protection film layers and the PE high temperature resistant protection film layers back side (7).
4. the combination diaphragm of a kind of novel conductive film according to claim 1, it is characterised in that：The PET high temperature dwells
Cuticula (3) is stained with power face (8) and the PET high temperature dwell cuticula back side (9) including PET high temperature dwell cuticula.
5. the combination diaphragm of a kind of novel conductive film according to claim 1, it is characterised in that：The upper pressing rod (10)
Winding body (12) is connected with lower nip roll (11).