CN106592256A - Ultraviolet-proof fabric for umbrella and manufacturing method of ultraviolet-proof fabric - Google Patents
Ultraviolet-proof fabric for umbrella and manufacturing method of ultraviolet-proof fabric Download PDFInfo
- Publication number
- CN106592256A CN106592256A CN201611131737.2A CN201611131737A CN106592256A CN 106592256 A CN106592256 A CN 106592256A CN 201611131737 A CN201611131737 A CN 201611131737A CN 106592256 A CN106592256 A CN 106592256A
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- fabric
- umbrella
- layer
- cloth layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an ultraviolet-proof fabric for an umbrella and a manufacturing method of the ultraviolet-proof fabric. The ultraviolet-proof fabric for the umbrella comprises a waterproof layer, a gray cloth layer and an anti-ultraviolet layer which are arranged in sequence from top to bottom, wherein the waterproof layer adopts a waterproofing agent C6; the gray cloth layer is a low-stretch silk fabric made of polyester 20D. According to the ultraviolet-proof fabric, the gray cloth layer adopts the lighter low-stretch silk fabric made of polyester 20D, with the fabric density of 400 T, and if the density of the fabric is larger, the ultraviolet resisting effect is better; therefore, compared with the conventional ultraviolet-proof fabric, the ultraviolet-proof fabric for the umbrella has a good ultraviolet-proofing function, is lighter and thinner, and is convenient to use and carry.
Description
Technical field
The present invention relates to fabric for umbrella technical field, and in particular to a kind of fabric for umbrella of anti-ultraviolet and its manufacturer
Method.
Background technology
Ultraviolet can excite the melanocyte of basal to enliven rapidly, cause skin darkening, and when ultraviolet is strong
It is strong when acting on skin, solar dermatitis can occur, it is serious also to cause skin carcinoma, therefore, people are when ultraviolet is stronger
Trip would generally select parasols to weaken injury of the ultraviolet to skin.
, typically using the yarn weaving that 50D or 75D is even more thick, fabric is thicker for the UV resistance fabric of existing parasols
Weight, UV resistance coating are also in the majority with black glue and elargol, and the feed particles of coating are painted with than larger
Accept also relatively thicker, it has not been convenient to put.
The content of the invention
For defect of the prior art, the present invention provides a kind of fabric for umbrella and its manufacture method of anti-ultraviolet,
Ensure while its anti-ultraviolet function, to reduce the thickness of fabric, in order to using and carrying.
In a first aspect, a kind of fabric for umbrella of anti-ultraviolet of present invention offer, anti-including what is set gradually from top to bottom
Water layer, embryo cloth layer and ultraviolet resistant layer；The waterproof layer adopts C6 waterproofing agents, and the embryo cloth layer is 20D polyester low stretch silk face fabrics.
In the present invention, embryo cloth layer adopts more frivolous 20D polyester low stretch silk face fabrics, its fabric density to reach 400T, and face
The effect of bigger its anti-ultraviolet of material density is better, it can be seen that, compared with existing ultraviolet-resistant fabric, the present invention is provided
Anti-ultraviolet fabric for umbrella while with good UV resistance function quality it is more frivolous, be easy to use and carry.
Preferably, the 20D polyester low stretch silk face fabric adopts check weave.As embryo cloth layer is using the frivolous 20D of quality
Polyester low stretch silk face fabric, is easier to situation about being damaged, and adopts check weave, can increase the anti tear power of fabric, extend which
Service life.
Preferably, the ultraviolet resistant layer includes glue-line and nano anti-ultraviolet coating.Using glue-line and nanometer UV resistance
The double-decker of line coating can strengthen the ultraviolet resistance of fabric for umbrella, using the fabric thickness of nano anti-ultraviolet coating
Substantially reduce, compared with the ultraviolet-proof using black glue or elargol, the present invention provide fabric for umbrella weight only with
The 1/2-1/3 of umbrella cover material as previous, and half of general umbrella cover material or so before fabric thickness also only has.
Preferably, the nano anti-ultraviolet coating includes Zinc Oxide and titanium dioxide superfine chemical powder.Zinc Oxide and
Titanium dioxide superfine chemical powder has good ultraviolet-shielding type and superior antibacterial, bacteriostasis property, is added in fabric,
Fabric can be given with functions such as sun-proof, antibacterial, deodorization, therefore, the present invention can be carried as nano anti-ultraviolet coating using which
The ultraviolet resistance of high fabric for umbrella, and while fabric can be caused more frivolous.
Preferably, the nano anti-ultraviolet coating also includes anti-adhesion agent.In order to prevent what fabric from sticking together when folding
Situation, adds anti-adhesion agent in nano anti-ultraviolet coating, to improve the performance of fabric.
Preferably, the glue-line is PA white glue.PA white glue can stablize the surface color of fabric, so as to not affect fabric to print
Colored visual effect.
A kind of second aspect, the manufacture method of the fabric for umbrella of anti-ultraviolet that the present invention is provided, comprises the steps：Will
20D polyester low stretch silk face fabric makes embryo cloth layer, and the surface thereon when the fabric finished product of embryo cloth layer is shaped using check weave
C6 waterproofing agents are added, to form waterproof layer；And PA white glue is coated in the lower surface of embryo cloth layer, then made by the bonding of PA white glue
With the nano anti-ultraviolet layer containing Zinc Oxide, titanium dioxide superfine chemical powder and anti-adhesion agent and PA white glue are merged.
Description of the drawings
In order to be illustrated more clearly that the specific embodiment of the invention or technical scheme of the prior art, below will be to concrete
Needed for embodiment or description of the prior art, accompanying drawing to be used is briefly described.In all of the figs, similar element
Or part is typically identified by similar reference.In accompanying drawing, each element or part might not be drawn according to actual ratio.
Fig. 1 is a kind of structural representation of the fabric for umbrella of anti-ultraviolet of the present invention.
Reference：
1- waterproof layers；2- embryo cloth layers；3-PA white adhesive layers；4- nano anti-ultraviolet layers.
Specific embodiment
The embodiment of technical solution of the present invention is described in detail below in conjunction with accompanying drawing.Following examples are only used for
Technical scheme is clearly illustrated, therefore is only used as example, and the protection model of the present invention can not be limited with this
Enclose.
In a first aspect, as shown in figure 1, a kind of fabric for umbrella of anti-ultraviolet that provides of one embodiment of the invention, including anti-
Water layer 1 and embryo cloth layer 2, wherein, waterproof layer 1 adopts C6 waterproofing agents, embryo cloth layer 2 to adopt the double check polyester low stretch silk face fabrics of 20D, its
Fabric density reaches 400T, and preventing ultraviolet effect is good, and compared with existing ultraviolet-resistant fabric, has the advantages that quality is frivolous,
It is easy to use and carries, while the fabric adopts check weave, substantially increases the anti tear power of fabric.
The bottom surface of embryo cloth layer 2 is provided with PA white adhesive layers 3 and nano anti-ultraviolet layer 4, to strengthen the anti-ultraviolet of fabric
Performance.Wherein, PA white glue can stablize the surface color of fabric, not affect the visual effect of fabric stamp；And nanometer UV resistance
Line layer 4 includes Zinc Oxide, titanium dioxide superfine chemical powder and anti-adhesion agent, with traditional employing black glue or elargol as UV resistance
The fabric of line coating is compared, the 1/2-1/3 of the weight of the fabric for umbrella that the present embodiment is provided general umbrella cover material before only having, and face
Material thickness half of general umbrella cover material or so before also only having.
Second aspect, present invention also offers a kind of embodiment of the manufacture method of the fabric for umbrella of anti-ultraviolet, including
Following steps：20D polyester low stretch silk face fabric is made into embryo cloth layer using check weave, and when the fabric finished product of embryo cloth layer is shaped
Surface adds C6 waterproofing agents thereon, to form waterproof layer；And PA white glue is coated in the lower surface of embryo cloth layer using high temperature, then
By the adhesive effect of PA white glue by the nano anti-ultraviolet layer containing Zinc Oxide, titanium dioxide superfine chemical powder and anti-adhesion agent
Merged with PA white glue.
Finally it should be noted that：Various embodiments above only to illustrate technical scheme, rather than a limitation；To the greatest extent
Pipe has been described in detail to the present invention with reference to foregoing embodiments, it will be understood by those within the art that：Its according to
So the technical scheme described in foregoing embodiments can be modified, or which part or all technical characteristic are entered
Row equivalent；And these modifications or replacement, do not make the essence of appropriate technical solution depart from various embodiments of the present invention technology
The scope of scheme, which all should be covered in the middle of the scope of the claim and description of the present invention.
Claims (7)
1. a kind of fabric for umbrella of anti-ultraviolet, it is characterised in that：
Including the waterproof layer, embryo cloth layer and ultraviolet resistant layer that set gradually from top to bottom；
The waterproof layer adopts C6 waterproofing agents, and the embryo cloth layer is 20D polyester low stretch silk face fabrics.
2. the fabric for umbrella of anti-ultraviolet according to claim 1, it is characterised in that：
The 20D polyester low stretch silk face fabric adopts check weave.
3. the fabric for umbrella of anti-ultraviolet according to claim 2, it is characterised in that：
The ultraviolet resistant layer includes glue-line and nano anti-ultraviolet coating.
4. the fabric for umbrella of anti-ultraviolet according to claim 3, it is characterised in that：
The nano anti-ultraviolet coating includes Zinc Oxide and titanium dioxide superfine chemical powder.
5. the fabric for umbrella of anti-ultraviolet according to claim 4, it is characterised in that：
The nano anti-ultraviolet coating also includes anti-adhesion agent.
6. the fabric for umbrella of the anti-ultraviolet according to claim 3 or 5, it is characterised in that：
The glue-line is PA white glue.
7. a kind of manufacture method of the fabric for umbrella of anti-ultraviolet, it is characterised in that comprise the steps：
20D polyester low stretch silk face fabric is made into embryo cloth layer using check weave, and when the fabric finished product of embryo cloth layer is shaped at which
Upper surface adds C6 waterproofing agents, to form waterproof layer；And PA white glue is coated in the lower surface of embryo cloth layer, then by PA white glue
Nano anti-ultraviolet layer containing Zinc Oxide, titanium dioxide superfine chemical powder and anti-adhesion agent and PA white glue are carried out by adhesive effect
Fusion.