CN106592228A - Temperature-control humidity-control silk quilt for children and manufacturing method of silk quilt - Google Patents

Temperature-control humidity-control silk quilt for children and manufacturing method of silk quilt Download PDF

Info

Publication number
CN106592228A
CN106592228A CN201610932209.0A CN201610932209A CN106592228A CN 106592228 A CN106592228 A CN 106592228A CN 201610932209 A CN201610932209 A CN 201610932209A CN 106592228 A CN106592228 A CN 106592228A
Authority
CN
China
Prior art keywords
silkworm silk
quilt
silk
temperature
child
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610932209.0A
Other languages
Chinese (zh)
Other versions
CN106592228B (en
Inventor
李风浪
李舒歆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Haimen Dixiu Household Textile Co ltd
Original Assignee
Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd filed Critical Dongguan Lianzhou Intellectual Property Operation and Management Co Ltd
Priority to CN201610932209.0A priority Critical patent/CN106592228B/en
Publication of CN106592228A publication Critical patent/CN106592228A/en
Application granted granted Critical
Publication of CN106592228B publication Critical patent/CN106592228B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a manufacturing method of a temperature-control humidity-control silk quilt for children. The method includes the following steps that silk cotton is bleached and refined to form a silk cotton pocket, the silk cotton pocket is subjected to finishing by means of a regenerated silk protein solution containing nano silicon dioxide silica sol and by means of ethyl alcohol steam respectively, then taken out, combed to be fluffy and dried, and pre-treated silk pieces are obtained; the pre-treated silk pieces are stacked to obtain a silk quilt batt which is 2-3 mm thick; bamboo charcoal staple fiber and Outlast viscose staple fiber serve as raw materials and are woven through a non-woven cloth technology to form non-woven cloth spacers; the silk quilt batt and the non-woven cloth spaces are laid in a cross mode and combed into a quilt batt, the quilt batt is quilted by means of quilting threads, and the batt is sleeved with a quilt cover to form the temperature-control humidity-control silk quilt for children. The silk quilt manufactured through the method is light, fluffy, constant in temperature and humidity, environmentally friendly, safe and comfortable.

Description

A kind of child silkworm silk quilt of temperature and humidity control and preparation method thereof
Technical field
The invention belongs to textile material technical field, and in particular to a kind of child's silkworm silk quilt of temperature and humidity control and its preparation side Method.
Background technology
Silkworm silk is good with the affinity of human body skin as a kind of natural animal protein fibre, is raw material preparation by silkworm silk Product is all substantially better than product prepared by other fibrous raw materials in terms of comfortableness, flexibility, safety and adsorptivity.By silkworm silk Silkworm silk quilt prepared by liner also has a performance such as next to the skin, warming, fluffy, soft, lightweight, ventilative, health care, but traditional silkworm silk By Jing after 1-2 uses, performance can be remarkably decreased, occur feel be hardened, the phenomenon such as not next to the skin, not warming, airtight, or even go out Existing hardened phenomenon.In order that silkworm silk is resumed original high-quality performance and being accomplished by recovery and carrying out scarifying maintenance, not only technique is answered It is miscellaneous, and performance is difficult to ensure that.
A kind of health velvet quilt of silk and taple and production method disclosed in Chinese patent CN 1398566A, the health quilt Intersect the silk fiber base net for aligning including multilamellar, chopped fiber floss, then combing are processed to after the silkworm silk of degumming is impregnated Into the silk fiber base net for aligning, then base net cross arrangement is formed the silkworm silk quilt with certain thickness and width.The party Silkworm silk quilt prepared by method is made up of short silk fiber floss, prepares silkworm silk quilt ventilating health-care warm, health care, but is also difficult to avoid that plate The phenomenon of knot.In addition, in order to increase the feature of silkworm silk quilt, a little functional materials are attached to into the surface of silk fiber.In A kind of production method of negative ion silk quilt disclosed in state patent CN 101569479B, by callouses it is refined after shake up stacking, In being placed in rotary type pressurized tank, the effect of the reagent such as Jing amido silicon oils, polyester-type quaternary ammonium salt, high-negative ion powder carries out anion and soft Along arrangement, then silkworm silk comforter batt is formed Jing after dehydration, drying and combing.One kind disclosed in Chinese patent CN 101507563B is used for The production method of the silkworm silk quilt of body immunity is improved, bulking agent, softening agent will be added in silk flosssilk wadding and containing Herba Ephedrae (processed), Semen Armeniacae Amarum, life The Chinese herbal medicine fluid of Gypsum Fibrosum, Radix Glycyrrhizae, Radix Bupleuri, Radix Scutellariae, Flos Lonicerae, Folium Perillae, the Rhizoma Atractylodis Macrocephalae, Radix Saposhnikoviae and Radix Ginseng, drying solidify to form pastille The silk cotton of agent, covers the silk flosssilk wadding containing medicament up and down the silk cotton without medicament and obtains that the silkworm silk of body immunity can be improved Quilt.Can give silkworm silk quilt excellent health properties with the short time by adding functional material, but the plate of silkworm silk quilt can be increased Knot phenomenon, reduces the use time of silkworm silk quilt.
From above-mentioned prior art, by the form of change silk fiber and to silk fiber surface attachment functional material Can give silkworm silk quilt excellent additional properties.Applicant of the present invention is based on and prior art is taken into full account, by intellectual material In combination with silkworm silk quilt, child's silkworm silk quilt of temperature and humidity control is prepared, fundamentally improves the moisture-penetrable ventilated performance of moisture absorption of silkworm silk, The hydraulic performance decline for preventing silkworm silk quilt long-time from using, or even hardened phenomenon.
The content of the invention
The technical problem to be solved in the present invention is to provide child's silkworm silk quilt of a kind of temperature and humidity control and preparation method thereof, by silkworm Silk fiber, nano silicon, fibroin, bamboo carbon fiber and Outlast viscose rayons are constituted silk fiber as raw material Silk flosssilk wadding pocket form silkworm silk comforter batt Jing after fibroin and nano silicon are processed, bamboo carbon fiber and Outlast viscose glues is fine Dimension makes non-woven fabrics partition, and silkworm silk comforter batt and non-woven fabrics partition are intersected into child's silkworm silk quilt that laying obtains temperature and humidity control.The party Method prepare silkworm silk quilt constant temperature and humidity, with fresh air, light soft, can long-time performance it is constant, be suitable for child and into People uses.
To solve above-mentioned technical problem, the technical scheme is that：
A kind of child's silkworm silk quilt of temperature and humidity control, child's silkworm silk quilt of the temperature and humidity control includes comforter batt, quilt line and quilt Cover, the comforter batt includes silk fiber, nano silicon, fibroin, bamboo carbon fiber and Outlast viscose rayons, the quilt Tire includes silkworm silk comforter batt and non-woven fabrics partition, and the silkworm silk comforter batt is made up of the silkworm silk piece of pretreatment, the silkworm of the pretreatment Silk piece includes silk cotton, fibroin and nano silicon, and the non-woven fabrics partition is by bamboo charcoal staple fiber and Outlast viscose glues Chopped fiber is constituted.
Used as the preferred of above-mentioned technical proposal, the comforter batt intersects laying and is formed by silkworm silk comforter batt and non-woven fabrics partition.
The present invention also provides a kind of preparation method of child's silkworm silk quilt of temperature and humidity control, comprises the following steps：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, Jing contains nano-silica under subnormal ambient by silk flosssilk wadding pocket The regenerated fibroin solution vapor of SiClx colloidal sol is arranged, and is taken out, then Jing alcohol steams are arranged, and are taken out, the fluffy baking of Jing combings It is dry, the silkworm silk piece of pretreatment is obtained, the silkworm silk piece of pretreatment is overlapped the silkworm silk comforter batt for obtaining that thickness is 2-3mm；
(2) using bamboo charcoal staple fiber and Outlast viscose staple fibres as raw material, Jing non-woven fabrics crafts are weaved and to form thickness and be The non-woven fabrics partition of 0.5-1mm；
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with child's silkworm silk quilt that quilt cover forms temperature and humidity control.
As the preferred of above-mentioned technical proposal, in the step (1), the regenerated fibroin of nano-silica-containing colloidal sol The mass fraction of nano silicon is 0.3-0.5% in solution, and the mass fraction of regenerated fibroin is 2-5%, and remaining is Deionized water.
Used as the preferred of above-mentioned technical proposal, in the step (1), the particle diameter of the nano silicon dioxide sol is 15- 30nm。
Used as the preferred of above-mentioned technical proposal, in the step (1), the volume ratio of alcohol steam is 1：1.
Used as the preferred of above-mentioned technical proposal, in the step (1), the temperature that steam is arranged is 60-70 DEG C, and the time is 5- 8min。
Used as the preferred of above-mentioned technical proposal, in the step (1), the thickness of the silkworm silk piece of pretreatment is less than 0.5mm.
As the preferred of above-mentioned technical proposal, in the step (2), bamboo charcoal staple fiber and Outlast in non-woven fabrics partition The mass ratio of viscose staple fibre is 1:0.8-1.2.
Used as the preferred of above-mentioned technical proposal, in the step (3), the thickness of child's silkworm silk quilt of temperature and humidity control is 2- 10cm。
Compared with prior art, the invention has the advantages that：
(1) child's silkworm silk quilt of temperature and humidity control prepared by the present invention is except comprising traditional silkworm silk tyre shoe, further comprises and receive Rice silicon dioxide, regenerated fibroin and bamboo charcoal staple fiber and Outlast viscose staple fibres constitute non-woven fabrics partition, silk fibroin Dimension, nanometer silicon dioxide particle, bamboo carbon fiber, Outlast viscose staple fibres all contain excellent moisture permeability, wherein Outlast viscose staple fibres have bidirectional temp regulation function, and it is automatic by phase transition process that can be changed with external ambient temperature Regulate and control the temperature of itself, nanometer silicon dioxide particle has very strong moisture absorption and water lock ability, can be preferential by unnecessary moisture It is stored in inside granule, prevents silk fiber moist, the present invention is also to silk fiber surface attachment fibroin, and Jing ethanol waters Steam cure process, make silk fiber surface formed one layer of fibroin film, improve silk fiber performance, in addition this Also containing the bamboo carbon fiber of superelevation absorbability in bright, the temperature and humidity inside silkworm silk quilt can be balanced, and keep silkworm silk quilt Abnormal smells from the patient is pure and fresh.
(2) comforter batt of child's silkworm silk quilt of temperature and humidity control prepared by the present invention intersects paving by silkworm silk comforter batt and non-woven fabrics partition It is folded to be formed, the non-woven fabrics partition cross action that silkworm silk comforter batt is constituted with bamboo charcoal staple fiber and Outlast viscose staple fibres, from each layer Face subtly adjusts the temperature and humidity of silkworm silk quilt, it is ensured that after silkworm silk quilt long-time use, pliability, thermal ressistance, health etc. Performance does not decline.
(3) child's silkworm silk quilt preparation method of temperature and humidity control prepared by the present invention is simple, and raw material environmental protection is suitable for Virgin and adult uses.
Specific embodiment
Describe the present invention, the illustrative examples of the here present invention and explanation in detail below in conjunction with specific embodiment It is for explaining the present invention but not as a limitation of the invention.
Embodiment 1：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 15nm is added In entering the regenerated fibroin solution that mass fraction is 2%, it is sufficiently stirred for obtaining the nano silicon that mass fraction is 0.3% The regenerated fibroin solution of colloidal sol, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk egg of Jing nano-silica-containing colloidal sols White solution vapor, arranges 5min at 60 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 60 DEG C 5min is arranged, and is taken Go out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped and is obtained Thickness is the silkworm silk comforter batt of 2mm.
(2) it is 1 by mass ratio:0.8 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics works Skill weaves the non-woven fabrics partition to form that thickness is 0.5mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 2cm.
Embodiment 2：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 30nm is added In entering the regenerated fibroin solution that mass fraction is 5%, it is sufficiently stirred for obtaining the nano silicon that mass fraction is 0.5% The regenerated fibroin solution of colloidal sol, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk egg of Jing nano-silica-containing colloidal sols White solution vapor, arranges 8min at 70 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 70 DEG C 8min is arranged, and is taken Go out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped and is obtained Thickness is the silkworm silk comforter batt of 3mm.
(2) it is 1 by mass ratio:1.2 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics works Skill weaves the non-woven fabrics partition to form that thickness is 1mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 10cm.
Embodiment 3：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 20nm is added In entering the regenerated fibroin solution that mass fraction is 3%, it is sufficiently stirred for obtaining the nano silicon that mass fraction is 0.4% The regenerated fibroin solution of colloidal sol, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk egg of Jing nano-silica-containing colloidal sols White solution vapor, arranges 6min at 65 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 65 DEG C 6min is arranged, and is taken Go out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped and is obtained Thickness is the silkworm silk comforter batt of 2.5mm.
(2) it is 1 by mass ratio:1 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics crafts Weaving forms the non-woven fabrics partition that thickness is 0.6mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 5cm.
Embodiment 4：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 25nm is added In entering the regenerated fibroin solution that mass fraction is 2-5%, it is sufficiently stirred for obtaining the nanometer titanium dioxide that mass fraction is 0.3% The regenerated fibroin solution of Ludox, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk of Jing nano-silica-containing colloidal sols Protein solution steam, arranges 5min at 70 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 70 DEG C 5min is arranged, Take out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped To the silkworm silk comforter batt that thickness is 2.7mm.
(2) it is 1 by mass ratio:0.9 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics works Skill weaves the non-woven fabrics partition to form that thickness is 0.8mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 8cm.
Embodiment 5：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 18nm is added In entering the regenerated fibroin solution that mass fraction is 3%, it is sufficiently stirred for obtaining the nano silicon that mass fraction is 0.3% The regenerated fibroin solution of colloidal sol, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk egg of Jing nano-silica-containing colloidal sols White solution vapor, arranges 8min at 65 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 60 DEG C 8min is arranged, and is taken Go out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped and is obtained Thickness is the silkworm silk comforter batt of 2.8mm.
(2) it is 1 by mass ratio:1.1 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics works Skill weaves the non-woven fabrics partition to form that thickness is 0.7mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 10cm.
Embodiment 6：
(1) silk cotton Jing bleaching refining treatments are formed into silk flosssilk wadding pocket, nano silicon dioxide sol of the particle diameter for 30nm is added In entering the regenerated fibroin solution that mass fraction is 4%, it is sufficiently stirred for obtaining the nano silicon that mass fraction is 0.4% The regenerated fibroin solution of colloidal sol, by silk flosssilk wadding pocket under subnormal ambient, the regenerated silk egg of Jing nano-silica-containing colloidal sols White solution vapor, arranges 7min at 70 DEG C, take out, then Jing volume ratios are 1：1 alcohol steam, at 60 DEG C 8min is arranged, and is taken Go out, the fluffy drying of Jing combings, obtain the silkworm silk piece of pretreatment of the thickness less than 0.5mm, the silkworm silk piece of pretreatment is overlapped and is obtained Thickness is the silkworm silk comforter batt of 2.4mm.
(2) it is 1 by mass ratio:1.2 bamboo charcoal staple fiber and Outlast viscose staple fibres are used as raw material, Jing non-woven fabrics works Skill weaves the non-woven fabrics partition to form that thickness is 0.7mm.
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, combing is made Comforter batt, then Jing quilt line quilts, are set with quilt cover and form child silkworm silk quilt of the thickness for the temperature and humidity control of 6cm.
After testing, embodiment 1-6 prepare temperature and humidity control child's silkworm silk quilt and prior art silkworm silk quilt grammes per square metre, Warming, air-moisture-permeable result is as follows：
Humidity be 65%, temperature be 40 DEG C of environment under, place 6 months after, after testing, embodiment 1-6 prepare temperature control The grammes per square metre of the silkworm silk quilt of the wet child's silkworm silk quilt of control and prior art, warming, air-moisture-permeable result are as follows：
As seen from the above table, child's silkworm silk quilt constant temperature and humidity effect of temperature and humidity control prepared by the present invention is good, and long-time makes With rear, performance difference is little.
The principle and its effect of above-described embodiment only illustrative present invention, it is of the invention not for limiting.It is any ripe Know the personage of this technology all can carry out modifications and changes under the spirit and the scope without prejudice to the present invention to above-described embodiment.Cause This, such as those of ordinary skill in the art is complete with institute under technological thought without departing from disclosed spirit Into all equivalent modifications or change, should by the present invention claim be covered.

Claims (10)

1. child's silkworm silk quilt of a kind of temperature and humidity control, it is characterised in that：Child's silkworm silk quilt of the temperature and humidity control includes comforter batt, spreads out Suture and quilt cover, the comforter batt includes that silk fiber, nano silicon, fibroin, bamboo carbon fiber and Outlast viscose glues are fine Dimension, the comforter batt includes silkworm silk comforter batt and non-woven fabrics partition, and the silkworm silk comforter batt is made up of the silkworm silk piece of pretreatment, described pre- The silkworm silk piece of process includes silk cotton, fibroin and nano silicon, the non-woven fabrics partition by bamboo charcoal staple fiber and Outlast viscose staple fibres are constituted.
2. child's silkworm silk quilt of a kind of temperature and humidity control according to claim 1, it is characterised in that：The comforter batt is by silkworm silk quilt Tire and non-woven fabrics partition intersect laying and are formed.
3. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control, it is characterised in that comprise the following steps：
(1) by silk cotton Jing bleaching refining treatment formed silk flosssilk wadding pocket, by silk flosssilk wadding pocket under subnormal ambient Jing nano-silica-containings The regenerated fibroin solution vapor of colloidal sol is arranged, and is taken out, then Jing alcohol steams are arranged, and are taken out, and the fluffy drying of Jing combings is obtained To the silkworm silk piece of pretreatment, the silkworm silk piece of pretreatment is overlapped the silkworm silk comforter batt for obtaining that thickness is 2-3mm；
(2) using bamboo charcoal staple fiber and Outlast viscose staple fibres as raw material, Jing non-woven fabrics crafts are weaved to form thickness for 0.5- The non-woven fabrics partition of 1mm；
(3) the non-woven fabrics partition that silkworm silk comforter batt prepared by step (1) is prepared with step (2) is intersected into laying, comforter batt is made in combing, Again Jing quilts line quilt, is set with child's silkworm silk quilt that quilt cover forms temperature and humidity control.
4. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (1), the mass fraction of nano silicon is 0.3- in the regenerated fibroin solution of nano-silica-containing colloidal sol 0.5%, the mass fraction of regenerated fibroin is 2-5%, and remaining is deionized water.
5. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (1), the particle diameter of the nano silicon dioxide sol is 15-30nm.
6. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (1), the volume ratio of alcohol steam is 1：1.
7. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (1), the temperature that steam is arranged is 60-70 DEG C, and the time is 5-8min.
8. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (1), the thickness of the silkworm silk piece of pretreatment is less than 0.5mm.
9. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：The step Suddenly in (2), the mass ratio of bamboo charcoal staple fiber and Outlast viscose staple fibres is 1 in non-woven fabrics partition:0.8-1.2.
10. the preparation method of child's silkworm silk quilt of a kind of temperature and humidity control according to claim 3, it is characterised in that：It is described In step (3), the thickness of child's silkworm silk quilt of temperature and humidity control is 2-10cm.
CN201610932209.0A 2016-10-25 2016-10-25 A kind of children's silk quilt of temperature and humidity control and preparation method thereof Active CN106592228B (en)