CN106589669A - Thermal insulation, heat isolation and self-cleaning plastic sheet and preparation method thereof - Google Patents
Thermal insulation, heat isolation and self-cleaning plastic sheet and preparation method thereof Download PDFInfo
- Publication number
- CN106589669A CN106589669A CN201611010204.9A CN201611010204A CN106589669A CN 106589669 A CN106589669 A CN 106589669A CN 201611010204 A CN201611010204 A CN 201611010204A CN 106589669 A CN106589669 A CN 106589669A
- Authority
- CN
- China
- Prior art keywords
- weight
- mentioned
- added
- parts
- stirred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a thermal insulation, heat isolation and self-cleaning plastic sheet. The plastic sheet is prepared from 0.7 to 1 part by weight of sodium akylbenzene sulfonate, 0.2 to 0. 5 parts by weight of monobutyltin oxide, 0.4 to 1 part by weight of 2, 4-imidazolinedione, 10 to 14 parts by weight of titanium tetrachloride, 3.7 to 4 parts by weight of ferric chloride, 6 to 8 parts by weight of hydrogen peroxide with a concentration of 25 to 30%, 7 to 9 parts by weight of methyl methacrylate, 0.1 to 0.2 parts by weight of azobisisobutyronitrile, 100 to 130 parts by weight of polyvinyl chloride, 0.7 to 1 part by weight of a silane coupling agent kh560, 3 to 4 parts by weight of hollow glass beads, 7 to 9 parts by weight of calcium zeolite, 0.3 to 1 part by weight of trimethylethoxylethylenediamine, 2 to 3 parts by weight of polystyrene, and 3 to 4 parts by weight of butyl epoxidized cottonseed oleate. The iron-doped titania has good photocatalytic ability, can degrade and remove pollutants attached to the surface of the sheet and can realize the self-cleaning performances.
Description
Technical field
The present invention relates to board technology field, more particularly to a kind of insulation self-clean type plastic plate and its preparation side
Method.
Background technology
Titanium dioxide is a kind of transition metal oxide while being also a kind of semi-conducting material, as which has preferable life
The thing compatibility, can resist chemical attack, the advantages of harmless, meanwhile, the material abundance of titanium source content makes titanium dioxide thing
Produce abundant and cheap, therefore obtained people and widely pay close attention to, the application of titanium dioxide is embodied in each of people's life
Aspect, current titanium dioxide have reached world lead level without mechanical goods usage amount.Due to the characteristic of titanium dioxide, Ke Yizuo
For very important inorganic chemical industry material, therefore which has huge in various fields such as national defence aviation industry, commercial production, hard-core technologies
Big power of influence and application.Titanium dioxide can possess color using titanium white production coating out as Chinese white again
Bright-coloured, colorability is strong, and the advantages of covering power is high, and its service life is longer compared with other pigment, therefore its usage amount accounts for institute
Have the 80% of Chinese white.Rather than the other titanium dioxide of pigment-level still possesses the field of being widely applied, be concentrated mainly on metallurgy,
The fields such as ceramics, glass, sheet material;As titanium dioxide has the ability and higher photocatalytic activity that absorb ultraviolet, therefore can
Catalyst, adsorbent, antibacterial etc. are prepared with using this characteristic, in the 70's of eighties of last century, people are found that to water
Middle addition titanium dioxide, under the irradiation of visible ray, water can resolve into oxygen and hydrogen.Subsequently, it is and special because of titanium dioxide
Some physicochemical properties and every excellent properties, so be widely used in numerous fields, including environment, the energy, information,
Material, health, building, medical treatment etc., especially in fields such as photocatalysis, solaode, gas sensor, sterilizations, embody very
Big researching value;
Nano titanium oxide has excellent photocatalytic activity, has quite varied application prospect, however, there is also some
Weak point, nano titanium oxide just must can play a part of catalyst under the promotion of ultraviolet light, and solar energy is produced
Great waste, which greatly limits the use of nano titanium oxide.So we are needed by modified this
Method improves utilization of the nano titanium oxide to solar energy, allows it to make full use of the light of visible region.Research shows, when subtracting
During the size of little titanium dioxide nanoparticle, its surface area, surface tension can be strengthened therewith with surface energy.Little chi is provided with accordingly
The characteristics such as very little effect, quantum size effect, skin effect, it is widely used various that these speciality also cause titanium dioxide to become
Inorganic material product;
Catalysis material improves the living environment of people, and we are can be not only used for using the photoelectric characteristic of catalysis material
Solaode is prepared, can be with degradation of contaminant, maintaining ecological balance.But the problem that needs are solved is, catalysis material
Solar energy can't be efficiently utilized more, and this causes energy transition rate low or the shortcomings of poor photocatalytic degradation efficiency;On the one hand
Shortage of resources, is on the one hand unable to effectively utilizes effective energy(Visible light part), will all cause the extreme loss of resource.Cause
This, for how to improve titanium dioxide as the problem of photocatalysis efficiency, still needs to further study and improve;
Polyacrylate has pollution-free, low cost and other advantages, has obtained more wide in fields such as building, automobile, packaging, printings
General application, but there is also thermostability, hardness etc. it is poor the problems such as, limit to a certain extent its application, using inorganic nano
Titania modified polyacrylate, can significantly improve the performances such as the hardness of polyacrylate, thermostability, impact strength, from
And further expand its use range;
However, as the specific surface area of nano titanium oxide is big, surface energy is high, in non-thermodynamics stable state, prepared answers
The shortcomings of easily there is nanoparticle reunion, composite poor storage stability, complicated process of preparation in condensation material.
The content of the invention
The object of the invention is exactly for the defect for making up prior art, there is provided a kind of insulation self-clean type plastic plate and
Its preparation method.
The present invention is achieved by the following technical solutions:
A kind of insulation self-clean type plastic plate, it is made up of the raw material of following weight parts:
Sodium alkyl benzene sulfonate 0.7-1, Mono-n-butyltin 0.2-0.5,2,4- imidazolinedione 0.4-1, titanium tetrachloride 10-14,
The hydrogen peroxide 6-8 of iron chloride 3.7-4,25-30%, methyl methacrylate 7-9, azodiisobutyronitrile 0.1-0.2, polychlorostyrene second
Alkene 100-130, silane coupler kh5600.7-1, hollow glass micropearl 3-4, scolecite 7-9, trimethyl hydroxyethylammonium ethylenediamine
0.3-1, polystyrene 2-3, epoxy cotton seed oil acid butyl ester 3-4.
A kind of preparation method of described insulation self-clean type plastic plate, comprises the following steps:
(1)Above-mentioned scolecite is calcined into 1-2 hours at 700-800 DEG C, fine powder is worn into after cooling, its weight 20-27 is added to
In deionized water again, it is 53-60 DEG C to rise high-temperature, adds sodium alkyl benzene sulfonate, insulated and stirred 6-10 minute, obtains zeolite dispersion
Liquid;
(2)Above-mentioned titanium tetrachloride is added in the deionized water of its weight 60-70 times, is stirred, add above-mentioned iron chloride,
Ammonia spirit of the Deca concentration for 5.4-6%, regulation pH is 8-9, stirs, obtains chlorinated solution;
(3)Above-mentioned Zeolite dispersion, chlorinated solution are mixed, it is 57-60 DEG C to rise high-temperature, insulated and stirred 10-20 minute, is added
Above-mentioned Mono-n-butyltin, stirs to room temperature, sucking filtration, precipitation is added in the deionized water of its weight 40-50 times, ultrasonic 6-
10 minutes, the hydrogen peroxide of above-mentioned 25-30% is added, magnetic agitation 20-30 minute, insulated and stirred 4-5 is little at 100-105 DEG C
When, to send in 57-60 DEG C of baking oven, drying, discharging obtains Fe2O3 doping titanium dioxide;
(4)Above-mentioned 2,4- imidazolinediones are added in the dehydrated alcohol of its weight 5-7 times, it is 50-60 DEG C to rise high-temperature, is protected
Temperature stirring 7-10 minutes, above-mentioned Fe2O3 doping titanium dioxide is added, is stirred to room temperature, is obtained titania-doped alcohol liquid;
(5)Above-mentioned silane coupler kh560 is taken, is added in the acetone of its weight 50-60 times, Deca acetic acid, regulation pH are 5-
6, stir, add titania-doped alcohol liquid, ultrasonic 20-30 minutes, sucking filtration obtains Silane Grafted titania-doped;
(6)Take above-mentioned Silane Grafted titania-doped, be added in the dimethyl sulfoxide of its weight 37-40 times, ultrasonic 5-7 point
Clock, the above-mentioned methyl methacrylate of addition, azodiisobutyronitrile, the insulated and stirred 4-6 hour at 57-60 DEG C, centrifugation will
Precipitation absolute ethanol washing 3-4 time, at 50-60 DEG C, vacuum drying 1-2 hours, obtain titania-doped graft polymers;
(7)Above-mentioned titania-doped graft polymers are mixed with remaining each raw material, at 70-80 DEG C, insulated and stirred 1-2 is little
When, double screw extruder is sent into, extrusion, mould molding, is cut off, overlay film, obtain final product the plastic plate.
It is an advantage of the invention that:
The present invention silane coupler is anchored in into less aggregate surface, reduce titania-doped particle surface energy and
Surface activity, prevents doping particle itself that soft-agglomerated phenomenon occurs, due to particle diameter very little of adulterating, enhances and be covered in doping
Active force and the sterically hindered repulsive force produced as coupling agent adsorbs between the coupling agent molecule of particle surface, its
Secondary, after polymethyl methacrylate is grafted on silane treatment by emulsion graft polymerization in situ particle surface, realizes particle table
Face organises completely, cause the carbochain of inorganic nano doping particle surface to be extended, especially polymethyl methacrylate
After linear long-chain molecule is by emulsion graft polymerization introducing, hence it is evident that improve inorganic/organic biphase interfacial structure, increased the compatibility,
Improve the stability of composite;The titania-doped graft polymers that the present invention is added can increase matrix resin strand
Intersegmental crosslink density, causes organic matrix macromolecular chain certain distance from shortening, and intermolecular active force is strengthened, secondly, anchoring
Grafting and the realization of emulsion graft polymerization so that the two-phase interface compatibility is enhanced, bonding interface effect are further reinforced, these works
Final result results in organic molecule chain movement ability in system and reduces, and improves the heat resistance of composite, in addition,
The Fe2O3 doping titanium dioxide that the present invention is added has good photo-catalysis capability, the contaminant degradation that can adhere to plate surface
Remove, so as to realize self-cleaning performance.Present invention adds hollow glass micropearl, scolecite, polystyrene, effectively can carry
The thermal and insulating performance of high finished product sheet material.
Specific embodiment
A kind of insulation self-clean type plastic plate, it is made up of the raw material of following weight parts:
Sodium alkyl benzene sulfonate 0.7,0.2,2,4 imidazolinedione 0.4 of Mono-n-butyltin, titanium tetrachloride 10, iron chloride 3.7,25%
Hydrogen peroxide 6, methyl methacrylate 7, azodiisobutyronitrile 0.1, polrvinyl chloride 100, silane coupler kh5600.7, sky
Heart glass microballoon 3, scolecite 7, trimethyl hydroxyethylammonium ethylenediamine 0.3, polystyrene 2, epoxy cotton seed oil acid butyl ester 3.
A kind of preparation method of described insulation self-clean type plastic plate, comprises the following steps:
(1)Above-mentioned scolecite is calcined 1 hour at 700 DEG C, fine powder after cooling, is worn into, the deionization of 20 times of its weight is added to
In water, it is 53 DEG C to rise high-temperature, adds sodium alkyl benzene sulfonate, insulated and stirred 6 minutes to obtain Zeolite dispersion;
(2)Above-mentioned titanium tetrachloride is added in the deionized water of 60 times of its weight, is stirred, add above-mentioned iron chloride, drop
Plus the ammonia spirit that concentration is 5.4%, it is 8 to adjust pH, stirs, obtains chlorinated solution;
(3)Above-mentioned Zeolite dispersion, chlorinated solution are mixed, it is 57 DEG C to rise high-temperature, and insulated and stirred 10 minutes adds above-mentioned list
Butyl stannum oxide, stirs to room temperature, sucking filtration, precipitation is added in the deionized water of 40 times of its weight, and ultrasound 6 minutes is added
Above-mentioned 25% hydrogen peroxide, magnetic agitation 20 minutes, insulated and stirred 4 hours at 100 DEG C are sent in 57 DEG C of baking oven, are dried
Dry, discharging obtains Fe2O3 doping titanium dioxide;
(4)Above-mentioned 2,4 imidazolinediones are added in the dehydrated alcohol of 5 times of its weight, it is 50 DEG C to rise high-temperature, insulated and stirred
7 minutes, above-mentioned Fe2O3 doping titanium dioxide is added, is stirred to room temperature, is obtained titania-doped alcohol liquid;
(5)Above-mentioned silane coupler kh560 is taken, is added in the acetone of 50 times of its weight, Deca acetic acid, it is 5 to adjust pH, stirring
Uniformly, titania-doped alcohol liquid is added, ultrasonic 20 minutes, sucking filtration obtains Silane Grafted titania-doped;
(6)Take that above-mentioned Silane Grafted is titania-doped, be added in the dimethyl sulfoxide of 37 times of its weight, ultrasound 5 minutes, plus
Enter above-mentioned methyl methacrylate, azodiisobutyronitrile, insulated and stirred 4 hours at 57 DEG C, centrifugation, will precipitation with anhydrous
Washing with alcohol 3 times, is vacuum dried 1 hour at 50 DEG C, obtains titania-doped graft polymers;
(7)Above-mentioned titania-doped graft polymers are mixed with remaining each raw material, at 70 DEG C, insulated and stirred 1 hour, send
Enter double screw extruder, extrusion, mould molding, cut off, overlay film, obtain final product the plastic plate.
Performance test:
Tensile strength: 44.3MPa;
Bending strength: 71MPa;
Anti-flammability:Put out from fire, no black smoke.
Claims (2)
1. a kind of insulation self-clean type plastic plate, it is characterised in that it is made up of the raw material of following weight parts:
Sodium alkyl benzene sulfonate 0.7-1, Mono-n-butyltin 0.2-0.5,2,4- imidazolinedione 0.4-1, titanium tetrachloride 10-14,
The hydrogen peroxide 6-8 of iron chloride 3.7-4,25-30%, methyl methacrylate 7-9, azodiisobutyronitrile 0.1-0.2, polychlorostyrene second
Alkene 100-130, silane coupler kh5600.7-1, hollow glass micropearl 3-4, scolecite 7-9, trimethyl hydroxyethylammonium ethylenediamine
0.3-1, polystyrene 2-3, epoxy cotton seed oil acid butyl ester 3-4.
2. a kind of preparation method of insulation self-clean type plastic plate as claimed in claim 1, it is characterised in that include with
Lower step:
(1)Above-mentioned scolecite is calcined into 1-2 hours at 700-800 DEG C, fine powder is worn into after cooling, its weight 20-27 is added to
In deionized water again, it is 53-60 DEG C to rise high-temperature, adds sodium alkyl benzene sulfonate, insulated and stirred 6-10 minute, obtains zeolite dispersion
Liquid;
(2)Above-mentioned titanium tetrachloride is added in the deionized water of its weight 60-70 times, is stirred, add above-mentioned iron chloride,
Ammonia spirit of the Deca concentration for 5.4-6%, regulation pH is 8-9, stirs, obtains chlorinated solution;
(3)Above-mentioned Zeolite dispersion, chlorinated solution are mixed, it is 57-60 DEG C to rise high-temperature, insulated and stirred 10-20 minute, is added
Above-mentioned Mono-n-butyltin, stirs to room temperature, sucking filtration, precipitation is added in the deionized water of its weight 40-50 times, ultrasonic 6-
10 minutes, the hydrogen peroxide of above-mentioned 25-30% is added, magnetic agitation 20-30 minute, insulated and stirred 4-5 is little at 100-105 DEG C
When, to send in 57-60 DEG C of baking oven, drying, discharging obtains Fe2O3 doping titanium dioxide;
(4)Above-mentioned 2,4- imidazolinediones are added in the dehydrated alcohol of its weight 5-7 times, it is 50-60 DEG C to rise high-temperature, is protected
Temperature stirring 7-10 minutes, above-mentioned Fe2O3 doping titanium dioxide is added, is stirred to room temperature, is obtained titania-doped alcohol liquid;
(5)Above-mentioned silane coupler kh560 is taken, is added in the acetone of its weight 50-60 times, Deca acetic acid, regulation pH are 5-
6, stir, add titania-doped alcohol liquid, ultrasonic 20-30 minutes, sucking filtration obtains Silane Grafted titania-doped;
(6)Take above-mentioned Silane Grafted titania-doped, be added in the dimethyl sulfoxide of its weight 37-40 times, ultrasonic 5-7 point
Clock, the above-mentioned methyl methacrylate of addition, azodiisobutyronitrile, the insulated and stirred 4-6 hour at 57-60 DEG C, centrifugation will
Precipitation absolute ethanol washing 3-4 time, at 50-60 DEG C, vacuum drying 1-2 hours, obtain titania-doped graft polymers;
(7)Above-mentioned titania-doped graft polymers are mixed with remaining each raw material, at 70-80 DEG C, insulated and stirred 1-2 is little
When, double screw extruder is sent into, extrusion, mould molding, is cut off, overlay film, obtain final product the plastic plate.