CN106117911A - A kind of plastic material and preparation method thereof - Google Patents
A kind of plastic material and preparation method thereof Download PDFInfo
- Publication number
- CN106117911A CN106117911A CN201610651785.8A CN201610651785A CN106117911A CN 106117911 A CN106117911 A CN 106117911A CN 201610651785 A CN201610651785 A CN 201610651785A CN 106117911 A CN106117911 A CN 106117911A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic material
- glass
- toughener
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plastic material, it includes the raw material of following weight portion: Corvic 50 85 parts, glycidyl methacrylate 48 parts, glass fibre 25 parts, wood fibre 36 parts, acrylamide 12 24 parts, glass microballoon 15 25 parts, white carbon black 49 parts, silane coupler 2.5 6 parts, nano titanium oxide 49 parts, potassium titanate crystal whisker 26 parts, zinc stearate 13 parts, dispersant 13 parts, toughener 2.5 5 parts, lubricant 13 parts, antioxidant 1.5 3 parts, sepiolite powder 10 20 parts, sodium lactate 13 parts, calcium bicarbonate 14 parts, 36 parts of polyester fiber.Plastic material in the present invention is ageing-resistant, water resistance good, and bending resistance is strong, thus can bear bigger extraneous load.
Description
Technical field
The present invention relates to plastics arts, particularly relate to a kind of plastic material and preparation method thereof.
Background technology
Plastic be use plastics be primary raw material process the articles for daily use, the general designation of industrial goods, including with
Plastics are the goods of all techniques such as the injection of raw material, plastic uptake.Plastic cement is that a class has plastic synthesis macromolecular material, it
The big synthetic material of current daily life indispensable three is defined with synthetic rubber, synthetic fibers.Specifically, plastics be with
Naturally occurring or synthetic resin is main component, adds various additive, can mould and make one under the conditions of uniform temperature and pressure etc.
Shaped, keeps the material of shape invariance at normal temperatures.Relative to metal, stone material, timber, plastic have low cost, can
The advantages such as plasticity is strong, are widely used in national economy, and plastics industry occupies particularly important status in today's world, for many years
Carry out the production of plastic in development at high speed all over the world.But, the resistance to water of current plastic material, mechanical property, resistance to always
Change poor-performing, it is impossible to meet people's life and industrial use requirement.
Summary of the invention
It is an object of the invention to provide a kind of plastic material and preparation method thereof, it is ageing-resistant, water resistance good, and resists
Crooking ability is strong, thus can bear bigger extraneous load.
For achieving the above object, the present invention provides following technical scheme:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 50-85 part, methacrylic acid contracts
Water glyceride 4-8 part, glass fibre 2-5 part, wood fibre 3-6 part, acrylamide 12-24 part, glass microballoon 15-25 part, charcoal
Black 4-9 part, silane coupler 2.5-6 part, nano titanium oxide 4-9 part, potassium titanate crystal whisker 2-6 part, zinc stearate 1-3 part, point
Powder 1-3 part, toughener 2.5-5 part, lubricant 1-3 part, antioxidant 1.5-3 part, sepiolite powder 10-20 part, sodium lactate 1-3
Part, calcium bicarbonate 1-4 part, polyester fiber 3-6 part.
Preferably, described plastic material includes the raw material of following weight portion: Corvic 70 parts, methacrylic acid contracts
Water glyceride 5 parts, glass fibre 3.5 parts, wood fibre 4 parts, acrylamide 18 parts, glass microballoon 16 parts, white carbon black 5 parts, silane
Coupling agent 4.5 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 5 parts, zinc stearate 2 parts, dispersant 2.5 parts, toughener 3 parts,
Lubricant 2.5 parts, antioxidant 1.5 parts, sepiolite powder 16 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 5 parts of polyester fiber.
Preferably, described plastic material includes the raw material of following weight portion: Corvic 80 parts, methacrylic acid contracts
Water glyceride 7 parts, glass fibre 3 parts, wood fibre 4.5 parts, acrylamide 18 parts, glass microballoon 20 parts, white carbon black 6 parts, silane
Coupling agent 4.8 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 4 parts, zinc stearate 3 parts, dispersant 1 part, toughener 5 parts, profit
Lubrication prescription 1 part, antioxidant 2.6 parts, sepiolite powder 15 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 5 parts of polyester fiber.
Preferably, described plastic material includes the raw material of following weight portion: Corvic 68 parts, methacrylic acid contracts
Water glyceride 5 parts, glass fibre 3.6 parts, wood fibre 6 parts, acrylamide 22 parts, glass microballoon 19 parts, white carbon black 5 parts, silane
Coupling agent 3.5 parts, nano titanium oxide 8 parts, potassium titanate crystal whisker 3.6 parts, zinc stearate 2 parts, dispersant 2 parts, toughener 4 parts,
Lubricant 3 parts, antioxidant 3 parts, sepiolite powder 14 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 6 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Compared with prior art, the invention has the beneficial effects as follows:
Plastic material in the present invention has been especially added with glass fibre, wood fibre, glass microballoon, white carbon black, nano-silica
Change titanium, potassium titanate crystal whisker, and with other raw materials with the use of, thus be greatly improved its shock resistance, non-oxidizability and corrosion resistant
Erosion property, is also equipped with hot strength and the fracture elongation of excellence simultaneously, and using effect is more preferable, it is damaged to be difficult to.
Detailed description of the invention
Describe technical scheme in detail below in conjunction with embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 65 parts, Glycidyl methacrylate is sweet
Grease 6.5 parts, glass fibre 3 parts, wood fibre 3 parts, acrylamide 20 parts, glass microballoon 15 parts, white carbon black 8 parts, silane coupled
Agent 4 parts, nano titanium oxide 8 parts, potassium titanate crystal whisker 6 parts, zinc stearate 2.5 parts, dispersant 2 parts, toughener 3.6 parts, lubrication
Agent 3 parts, antioxidant 2 parts, sepiolite powder 14 parts, sodium lactate 1.5 parts, calcium bicarbonate 2.5 parts, 4.5 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment two:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 70 parts, Glycidyl methacrylate is sweet
Grease 5 parts, glass fibre 3.5 parts, wood fibre 4 parts, acrylamide 18 parts, glass microballoon 16 parts, white carbon black 5 parts, silane coupled
Agent 4.5 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 5 parts, zinc stearate 2 parts, dispersant 2.5 parts, toughener 3 parts, lubrication
Agent 2.5 parts, antioxidant 1.5 parts, sepiolite powder 16 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 5 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment three:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 80 parts, Glycidyl methacrylate is sweet
Grease 7 parts, glass fibre 3 parts, wood fibre 4.5 parts, acrylamide 18 parts, glass microballoon 20 parts, white carbon black 6 parts, silane coupled
Agent 4.8 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 4 parts, zinc stearate 3 parts, dispersant 1 part, toughener 5 parts, lubricant 1
Part, antioxidant 2.6 parts, sepiolite powder 15 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 5 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment four:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 68 parts, Glycidyl methacrylate is sweet
Grease 5 parts, glass fibre 3.6 parts, wood fibre 6 parts, acrylamide 22 parts, glass microballoon 19 parts, white carbon black 5 parts, silane coupled
Agent 3.5 parts, nano titanium oxide 8 parts, potassium titanate crystal whisker 3.6 parts, zinc stearate 2 parts, dispersant 2 parts, toughener 4 parts, lubrication
Agent 3 parts, antioxidant 3 parts, sepiolite powder 14 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, 6 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment five:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 85 parts, Glycidyl methacrylate is sweet
Grease 6 parts, glass fibre 5 parts, wood fibre 5 parts, acrylamide 18 parts, glass microballoon 22 parts, white carbon black 7 parts, silane coupler
4.2 parts, nano titanium oxide 8 parts, potassium titanate crystal whisker 5 parts, zinc stearate 1.6 parts, dispersant 2.3 parts, toughener 4 parts, lubrication
Agent 2 parts, antioxidant 2.6 parts, sepiolite powder 17 parts, sodium lactate 1.8 parts, calcium bicarbonate 3.5 parts, 5 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment six:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 60 parts, Glycidyl methacrylate is sweet
Grease 4 parts, glass fibre 3.5 parts, wood fibre 3 parts, acrylamide 15 parts, glass microballoon 15 parts, white carbon black 5 parts, silane coupled
Agent 3 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 4.5 parts, zinc stearate 2.2 parts, dispersant 3 parts, toughener 3 parts, lubrication
Agent 1.2 parts, antioxidant 1.7 parts, sepiolite powder 15 parts, sodium lactate 1.6 parts, calcium bicarbonate 2.3 parts, 6 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Embodiment seven:
A kind of plastic material, it includes the raw material of following weight portion: Corvic 80 parts, Glycidyl methacrylate is sweet
Grease 7 parts, glass fibre 5 parts, wood fibre 6 parts, acrylamide 20 parts, glass microballoon 28 parts, white carbon black 5 parts, silane coupler 5
Part, nano titanium oxide 6 parts, potassium titanate crystal whisker 5.5 parts, zinc stearate 2.7 parts, dispersant 2 parts, toughener 4 parts, lubricant
2.5 parts, antioxidant 3 parts, sepiolite powder 17 parts, sodium lactate 1.4 parts, calcium bicarbonate 4 parts, 3 parts of polyester fiber.
The preparation method of described plastic material, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate
Whisker puts into reactor, and stirs 6-8min with the mixing speed of 35-40rpm, is subsequently adding zinc stearate with 25-28rpm's
Mixing speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, third
After acrylamide, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with
The second mixed material is obtained after the mixing speed stirring 45-60min of 30-35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, forming temperature
For 150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to relatively
The present invention has been described in detail by good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent, and without deviating from objective and the scope of the technical program, it all should be contained in the present invention
Right in the middle of.
Claims (5)
1. a plastic material, it is characterised in that include the raw material of following weight portion: Corvic 50-85 part, methyl-prop
Olefin(e) acid ethylene oxidic ester 4-8 part, glass fibre 2-5 part, wood fibre 3-6 part, acrylamide 12-24 part, glass microballoon 15-25
Part, white carbon black 4-9 part, silane coupler 2.5-6 part, nano titanium oxide 4-9 part, potassium titanate crystal whisker 2-6 part, zinc stearate 1-3
Part, dispersant 1-3 part, toughener 2.5-5 part, lubricant 1-3 part, antioxidant 1.5-3 part, sepiolite powder 10-20 part, lactic acid
Sodium 1-3 part, calcium bicarbonate 1-4 part, polyester fiber 3-6 part.
Plastic material the most according to claim 1, it is characterised in that include the raw material of following weight portion: polrvinyl chloride tree
70 parts of fat, glycidyl methacrylate 5 parts, glass fibre 3.5 parts, wood fibre 4 parts, acrylamide 18 parts, glass is micro-
16 parts of pearl, white carbon black 5 parts, silane coupler 4.5 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 5 parts, zinc stearate 2 parts, dispersion
Agent 2.5 parts, toughener 3 parts, lubricant 2.5 parts, antioxidant 1.5 parts, sepiolite powder 16 parts, sodium lactate 2 parts, calcium bicarbonate 3
Part, 5 parts of polyester fiber.
Plastic material the most according to claim 1, it is characterised in that include the raw material of following weight portion: polrvinyl chloride tree
80 parts of fat, glycidyl methacrylate 7 parts, glass fibre 3 parts, wood fibre 4.5 parts, acrylamide 18 parts, glass is micro-
20 parts of pearl, white carbon black 6 parts, silane coupler 4.8 parts, nano titanium oxide 6 parts, potassium titanate crystal whisker 4 parts, zinc stearate 3 parts, dispersion
Agent 1 part, toughener 5 parts, lubricant 1 part, antioxidant 2.6 parts, sepiolite powder 15 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, poly-
Ester fiber 5 parts.
Plastic material the most according to claim 1, it is characterised in that include the raw material of following weight portion: polrvinyl chloride tree
68 parts of fat, glycidyl methacrylate 5 parts, glass fibre 3.6 parts, wood fibre 6 parts, acrylamide 22 parts, glass is micro-
19 parts of pearl, white carbon black 5 parts, silane coupler 3.5 parts, nano titanium oxide 8 parts, potassium titanate crystal whisker 3.6 parts, zinc stearate 2 parts, point
Powder 2 parts, toughener 4 parts, lubricant 3 parts, antioxidant 3 parts, sepiolite powder 14 parts, sodium lactate 2 parts, calcium bicarbonate 3 parts, poly-
Ester fiber 6 parts.
5. according to the preparation method of the plastic material according to any one of claim 1-4, it is characterised in that include following step
Rapid:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by silane coupler, glass fibre, wood fibre, glass microballoon, white carbon black, nano titanium oxide and potassium titanate crystal whisker
Put into reactor, and stir 6-8min with the mixing speed of 35-40rpm, be subsequently adding the zinc stearate stirring with 25-28rpm
Speed stirring 5-8min, obtains the first ready-mixed thing；
(3) temperature of reaction kettle is risen to 135-140 DEG C, add Corvic, glycidyl methacrylate, acryloyl
After amine, dispersant, toughener, lubricant, antioxidant, sepiolite powder, sodium lactate, calcium bicarbonate and polyester fiber, with 30-
The second mixed material is obtained after the mixing speed stirring 45-60min of 35rpm；
(4) the second mixed material being placed in hot pressing on vulcanizing press, flat-plate molded pressure is 15-16MPa, and forming temperature is
150-155 DEG C, take out after 10-12min and be cooled to room temperature, obtain plastic material.