CN106552758A - 建材的制造方法 - Google Patents

建材的制造方法 Download PDF

Info

Publication number
CN106552758A
CN106552758A CN201610657327.5A CN201610657327A CN106552758A CN 106552758 A CN106552758 A CN 106552758A CN 201610657327 A CN201610657327 A CN 201610657327A CN 106552758 A CN106552758 A CN 106552758A
Authority
CN
China
Prior art keywords
coating
enamel
building materials
manufacture method
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610657327.5A
Other languages
English (en)
Other versions
CN106552758B (zh
Inventor
田口博之
村濑美穗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nichiha Corp
Original Assignee
Nichiha Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nichiha Corp filed Critical Nichiha Corp
Publication of CN106552758A publication Critical patent/CN106552758A/zh
Application granted granted Critical
Publication of CN106552758B publication Critical patent/CN106552758B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种不用研磨最外表面的涂膜、并且隐蔽了无机质基材的镜面加工建材。本发明提供一种建材的制造方法，其具备：第一步骤，在无机质基材上(表面)涂布基底涂料，进行固化、研磨；和第二步骤，涂布釉质涂料，并使之固化，所述基底涂料含有基底形成材料和填充剂，所述釉质涂料含有釉质形成材料和颜料，将所述釉质形成材料设为溶剂系树脂，以固体成分比计将所述基底涂料的填充剂含量设为40～70％，以固体成分比计将所述釉质涂料的颜料含量设为1～50％。

Description

建材的制造方法
技术领域
本发明涉及外墙板等建材。
背景技术
作为构成建筑物的外壁、内壁的建材，使用了陶瓷系外墙板、ALC板等无机质材料。
近来，在建材中进一步提高外观的设计性的要求高涨，实行的方法是，以无机质材料作为基材，在其表面涂布涂料而形成涂膜，提高设计性。
作为其对策之一，在专利文献1中公开有如下的做法，即，在基材的表面涂布聚酯补土(フェ一サ一)而形成基底层，然后，涂布聚酯黑釉质涂料而形成中涂层，然后，涂布聚酯清漆涂料，固化干燥后，进行研磨而形成镜面加工。
根据专利文献1的方法，可以将表面设为镜面加工，然而需要研磨形成于最外表面的涂膜。研磨必须在涂膜固化后进行，因而花费时间和工夫。另外，要大范围地研磨涂膜，为了形成镜面加工需要设备和技术，有可能产生研磨不均(班驳花纹)。
此外，陶瓷系外墙板、ALC板等无机质材料由于在表面存在微细的凹凸，因此需要研磨。但是，在研磨无机质材料的情况下，会产生研磨不均(班驳花纹)，美观性差，因而还有需要隐蔽的实际情况。
现有技术文献
专利文献
专利文献1：日本特开2006-181492号公报
发明内容
发明所要解决的问题
本发明是鉴于所述的问题而完成的，提供一种不用研磨最外表面的涂膜、并且隐蔽了无机质基材的表面的缺点的镜面加工建材的制造方法。
用于解决问题的方法
为了达成所述目的，本发明的建材的制造方法的特征在于，具备：第一步骤，在无机质基材上(表面)涂布基底涂料，进行固化、研磨；和第二步骤，涂布釉质(エナメル)涂料，并使之固化，所述基底涂料含有基底形成材料和填充剂，所述釉质涂料含有釉质形成材料和颜料，将所述釉质形成材料设为溶剂系树脂，以固体成分比计将所述基底涂料的填充剂含量设为40～70％，以固体成分比计将所述釉质涂料的颜料含量设为1～50％。
发明效果
根据本发明，在表面存在有微细的凹凸的无机质材料中，可以提供不用研磨最外表面的涂膜、并且隐蔽了无机质基材的表面的缺点的镜面加工建材。
附图说明
图1是将利用本发明的实施方式1制造的建材的一部分放大了的纵剖面图。
图2是将利用本发明的实施方式2制造的建材的一部分放大了的纵剖面图。
图3是将利用本发明的实施方式3制造的建材的一部分放大了的纵剖面图。
具体实施方式
基于本发明的方式的制造方法具备：第一步骤，在无机质基材上(表面)涂布基底涂料，进行固化、研磨；和第二步骤，涂布釉质涂料，并使之固化。
作为无机质基材，例如可以举出：纤维增强水泥板、木质水泥板、木丝水泥板、矿渣石膏板、混入纸浆纤维的水泥板、纤维增强水泥·硅酸钙板、混入木片的水泥硅酸钙板、混入木质系纤维的水泥硅酸钙板、混入木纤维的水泥硅酸钙板、混入纤维的水泥硅酸钙板、ALC板等。
而且，也可以在无机质基材的表面形成包含环氧树脂、丙烯酸类树脂、氨基甲酸酯树脂等的保护层涂膜。
无机质基材由于即使研磨其表面也存在有微小的凹凸，因此为了将无机质基材的表面制成镜面而形成涂膜。本方式的建材的制造方法中，在无机质基材的表面形成基底涂料的涂膜，在基底涂料的涂膜的表面形成釉质涂料的涂膜。
基底涂料含有基底形成材料和填充剂。
作为基底形成材料，可以使用紫外线固化型树脂、溶剂系氨基甲酸酯树脂、溶剂系丙烯酸类树脂等。若作为基底形成材料使用紫外线固化型树脂、溶剂系氨基甲酸酯树脂，则可以形成膜厚大、表面接***滑的涂膜，并且容易进行研磨，因此优选。
作为基底涂料的填充剂，可以使用滑石、碳酸钙、二氧化硅(结晶性二氧化硅、熔融二氧化硅、无定型二氧化硅)、玻璃(玻璃片、玻璃纤维粉末)、石英(粉末)、铝(粉末)、云母(粉末)等。作为填充剂，若含有滑石、碳酸钙、二氧化硅的至少任意一种，则所形成的涂膜容易进行研磨，无机质基材的隐蔽优异，因此优选。
在基底涂料中，将填充剂的含量以固体成分比计调整为40质量％以上到70质量％以下的范围。通过确定填充剂的含量，可以形成容易进行研磨、隐蔽了无机质基材的表面的涂膜。需要说明的是，基底涂料根据需要可以含有光聚合引发剂、增稠剂、消泡剂、pH调整剂、溶剂、防腐剂等。
第一步骤中，在无机质基材上(表面)涂布基底涂料，进行固化、研磨，使得无机质基材的表面平滑。对于研磨没有特别限定，可以使用砂纸、抛光研磨、砂带研磨等一般的研磨方法。
釉质涂料是将建材的表面制成镜面加工、并且进一步隐蔽无机质基材的材料。釉质涂料含有釉质形成材料和颜料。釉质形成材料为溶剂系树脂，可以使用溶剂系氟树脂、溶剂系丙烯酸类树脂、溶剂系氨基甲酸酯树脂等。作为颜料，可以使用氧化钛、碳、红铁粉(弁柄)、铬黄、氧化铁、群青、酞菁蓝、钴、氧化铬等。作为颜料，若含有氧化钛、碳、氧化铁、有机颜料的至少任意一种，则所形成的涂膜的着色力优异，无机质基材得到进一步隐蔽，因此优选。通过涂布含有溶剂系树脂、并且将颜料的含量以固体成分比计调整为1质量％以上且50质量％以下的范围的釉质涂料、并使之固化，就可以形成即使不研磨表面也很平滑、且隐蔽了无机质基材的涂膜。而且，釉质涂料根据需要可以含有增稠剂、消泡剂、pH调整剂、防腐剂、填充剂、紫外线吸收剂、溶剂、光稳定剂等。
根据本方式的建材的制造方法，可以提供不用研磨最外表面的涂膜、并且隐蔽了无机质基材的镜面加工建材。
以下，参照附图对本发明的建材的实施方式进行说明。
(关于本发明的实施方式1)
图1是将利用本发明的实施方式1制造的建材的一部分放大了的纵剖面图。
图示的建材10在无机质基材1的表面形成基底涂膜2、在基底涂膜2的表面形成釉质涂膜3而构成其整体。
在此，作为无机质基材1，可以使用纤维增强水泥板、木质水泥板、木丝水泥板、矿渣石膏板、混入纸浆纤维的水泥板、纤维增强水泥·硅酸钙板、混入木片的水泥硅酸钙板、混入木质系纤维的水泥硅酸钙板、混入木纤维的水泥硅酸钙板、混入纤维的水泥硅酸钙板、ALC板等。
建材10的制造方法中，研磨无机质基材1的表面，使之平滑。对于研磨没有特别限定，可以使用砂纸、抛光研磨、砂带研磨等一般的研磨方法。作为一例，可以举出在用砂纸研磨无机质基材1的表面时、使砂纸的粗糙度从#80依次过渡到#100的方法。
然后，在无机质基材1的表面，涂布基底涂料，进行固化、研磨，形成基底涂膜2(第一步骤)。作为基底涂料，可以使用含有基底形成材料和填充剂的涂料。
作为基底形成材料，可以使用紫外线固化型树脂、溶剂系氨基甲酸酯树脂、溶剂系丙烯酸类树脂等。作为紫外线固化型树脂，可以使用作为主成分含有丙烯酸类树脂、环氧树脂、氨基甲酸酯树脂等的树脂。若作为基底形成材料使用紫外线固化型树脂、溶剂系氨基甲酸酯树脂，则可以容易地形成膜厚大、表面接***滑的涂膜，容易进行研磨，因此优选。在基底形成材料为紫外线固化型树脂的情况下，在基底涂料中，也可以还含有光聚合引发剂。另外，基底涂料根据需要可以含有增稠剂、消泡剂、pH调整剂、溶剂、防腐剂等。
作为填充剂，可以使用滑石、碳酸钙、二氧化硅(结晶性二氧化硅、熔融二氧化硅、无定型二氧化硅)、玻璃(玻璃片、玻璃纤维粉末)、石英(粉末)、铝(粉末)、云母(粉末)等。作为填充剂，若含有滑石、碳酸钙、二氧化硅的至少任意一种，则所形成的涂膜容易进行研磨，无机质基材的隐蔽优异，因此优选。在基底涂料中，通过将填充剂的含量以固体成分比计调整为40质量％以上且70质量％以下的范围，就可以形成容易进行研磨、且隐蔽了无机质基材的涂膜。
基底涂料的涂布可以使用喷雾器、流涂机、自然涂布机、辊涂机等一般的涂装工具。作为例子，可以举出使用喷雾器涂布基底形成材料为溶剂系氨基甲酸酯树脂的基底涂料的方法、使用辊涂机涂布基底形成材料为紫外线固化型树脂的涂料的方法。
对于基底涂料的固化，在基底涂料为紫外线固化型涂料的情况下，可以借助照射紫外线的方法来进行，在溶剂系涂料的情况下，可以借助50～120℃的干燥器中的干燥、常温干燥等一般的方法来进行。
研磨可以使用砂纸、抛光研磨、砂带研磨等一般的研磨方法。作为一例，可以举出在用砂纸研磨固化了的基底涂膜2的表面时使砂纸的粗糙度从#320依次过渡到#400的方法。
然后，在基底涂膜2的表面，涂布釉质涂料、并使之固化，形成釉质涂膜3(第二步骤)。作为釉质涂料，可以使用含有釉质形成材料和颜料的涂料。
釉质形成材料为溶剂系树脂，可以使用溶剂系氟树脂、溶剂系丙烯酸类树脂、溶剂系氨基甲酸酯树脂等。
作为颜料，可以使用氧化钛、碳、红铁粉、铬黄、氧化铁、群青、酞菁蓝、钴、氧化铬等。作为颜料，若含有氧化钛、碳、氧化铁、有机颜料的至少任意一种，则所形成的涂膜的着色力优异，无机质基材的表面得到进一步隐蔽，因此优选。在釉质涂料中，通过将颜料的含量以固体成分比计调整为1质量％以上且50质量％以下的范围，就可以形成隐蔽了无机质基材的涂膜。需要说明的是，对于釉质涂料而言，根据需要可以含有增稠剂、消泡剂、pH调整剂、防腐剂、填充剂、紫外线吸收剂、溶剂、光稳定剂等。
釉质涂料的涂布可以使用喷雾器、流涂机、自然涂布机、辊涂机等一般的涂装工具。
釉质涂料的固化可以利用50～120℃的干燥器中的干燥来进行。
下面，对本例的作用效果进行说明。
建材10中，在无机质基材1的表面，涂布以固体成分比计含有40～70％的填充剂的基底涂料，进行固化，因此所形成的涂膜容易进行研磨，并且将无机质基材的表面隐蔽。此后，通过研磨利用基底涂料形成的涂膜的表面，可以形成隐蔽无机质基材的表面、并且表面平滑的基底涂膜2。在平滑的基底涂膜2的表面，涂布含有溶剂系树脂的釉质涂料，进行固化，因此即使不研磨也可以形成表面平滑的釉质涂膜3。由于釉质涂膜3以固体成分比计含有1～50％的颜料，因此利用其着色，无机质基材的隐蔽优异，并且建材10的表面为镜面加工。
(关于本发明的实施方式2)
图2是将利用本发明的实施方式2制造的建材的一部分放大了的纵剖面图。
图示的建材10A在无机质基材1A的表面形成基底涂膜2、在基底涂膜2的表面形成釉质涂膜3而构成其整体。
在此，无机质基材1A是在无机质基材1的表面涂布有保护层的材料。作为保护层没有特别限定，可以使用包含环氧树脂、丙烯酸类树脂、氨基甲酸酯树脂等的保护层。另外，作为保护层的涂布工具可以使用喷雾器、流涂机、自然涂布机、辊涂机等一般的涂装工具。涂布量也没有特别限定，作为一例可以举出涂布3g/平方尺。
基底涂膜2、釉质涂膜3与建材10相同。
根据建材10A，由于在无机质基材1A上涂布有保护层，因此无机质基材1A成为耐水性更加优异、并且无机质基材1A与基底涂膜2的密合性优异的建材。
下面，若对建材10A的制造方法进行概述，则除了在无机质基材1A上涂布有保护层以外，与建材10相同。
建材10A的制造方法仅在无机质基材1A的表面(保护层涂布面)涂布基底涂料这一点不同，其他与建材10的制作方法相同。
(关于本发明的实施方式3)
图3是将利用本发明的实施方式3制造的建材的一部分放大了的纵剖面图。
图示的建材10B在无机质基材1的表面形成基底涂膜2、在基底涂膜2的表面形成釉质涂膜3、在釉质涂膜3的表面形成保护涂膜4而构成其整体。
在此，保护涂膜4由保护形成材料形成。作为保护形成材料，可以使用溶剂系氟树脂、溶剂系丙烯酸类树脂、溶剂系氨基甲酸酯树脂、溶剂系丙烯酸硅树脂等。
根据建材10B，因在最外表面具备保护涂膜4，而成为耐候性优异的建材。
下面，若对建材10B的制造方法进行概述，则直至釉质涂膜3的制作方法与建材10相同。
在釉质涂膜3的表面，涂布保护涂料，在50～120℃的干燥器中使之干燥。作为保护涂料，可以使用含有保护形成材料的涂料。作为涂布可以使用喷雾器、流涂机、自然涂布机、辊涂机等一般的涂装工具。
(关于验证实验及其结果)
本发明人等进行了验证本发明的建材的各种性能的实验。在该实验时，制作试样1～20的试验体，进行了各试验体的表面观察，并且评价了60度镜面光泽度、密合性确认、和无机质基材的隐蔽性。基底涂料、釉质涂料、保护涂料的构成如表1、2所示。另外，在将各试验体用砂纸(使砂纸的粗糙度从#80依次过渡到#100)研磨无机质基材的表面后，对试样1～6、10～16、18～20使用辊涂机涂布基底涂料，照射紫外线而使基底涂料固化，对试样7～9、17使用喷雾器涂布基底涂料，在50～120℃的干燥器中使之干燥。其后，将固化了的基底涂料的表面用砂纸(使砂纸的粗糙度从#320依次过渡到#400)研磨后，使用流涂机，在研磨了的基底涂膜的表面涂布釉质涂料，在50～120℃的干燥器中使之干燥。对于试样7～13、16～19，使用流涂机，在釉质涂膜的表面涂布保护涂料，在50～120℃的干燥器中使之干燥。使用了的无机质基材的表面都是平面花纹(平坦)。将各试样的评价结果也表示于表1、2中。
[表1]
[表2]
“表面观察”是将试验体置于荧光灯的2米下方，利用目视观察荧光灯向试验体的最外表面的映入，“○”是映入的荧光灯看起来为一条直线的(良好)，“×”是映入的荧光灯看起来摇摆的、或者映入的荧光灯看起来模糊的(不佳)。
“60度镜面光泽度”是依照JIS K 5600-4-7使用便携式光泽度仪(IG-320株式会社堀场制作所制)测定试验体的最外表面的60度镜面光泽度而得的结果，80以上的为良好。
“密合性确认”是在试验体的最外表面压接粘合带，观察剥离所述粘合带后的涂膜的状态，“○”是涂膜剥离小于10％(良好)，“×”是涂膜剥离为10％以上(不佳)。
“无机质基材的隐蔽性确认”是从上侧利用目视观察试验体，“○”是看不到无机质基材(良好)，“×”是可以看到无机质基材(不佳)。
根据表1、2，试样1～13是如下的证实，即，在基底形成材料中使用了紫外线固化型丙烯酸类树脂、溶剂系氨基甲酸酯树脂的任意一种，涂布以固体成分比计含有40～70％的填充剂的基底涂料，进行固化、研磨，并且在釉质涂膜形成材料中使用了溶剂系氟树脂、溶剂系氨基甲酸酯树脂、溶剂系丙烯酸类树脂的任意一种，涂布以固体成分比计含有1～50％的颜料的釉质涂料，进行固化。试样1～13被证实，表面观察为“○”，60度镜面光泽度都高达80以上，为镜面加工，并且密合性、无机质基材的隐蔽性也都是“○”的良好的结果。
另一方面，使用了填充剂的含量并非40～70％的基底涂料、和颜料的含量并非1～50％的釉质涂料的试样14、17被证实为如下的结果，即，60度镜面光泽度低，表面观察也为“×”，并非镜面加工。
对于使用了颜料的含量为60％的釉质涂料的试样15、16也证实为如下的结果，即，60度镜面光泽度低，表面观察也为“×”，并非镜面加工。
使用了颜料的含量低至0.4％的釉质涂料的试样18被证实为如下的结果，即，表面观察为“×”，并非镜面加工，无机质基材的隐蔽性也为“×”。
在釉质形成材料中使用了丙烯酸类乳液的试样19、20被证实为如下的结果，即，60度镜面光泽度低，表面观察也为“×”，并非镜面加工，密合性也差。
以上，使用附图对本发明的实施方式进行了详述，然而具体的构成并不限定于该实施方式，即使有不脱离本发明的主旨的范围中的设计变更等，它们也包含于本发明中。
产业上的可利用性
如上说明所示，根据本发明，可以提供不用研磨最外表面的涂膜、并且隐蔽了无机质基材的镜面加工建材。
符号的说明
1、1A 无机质基材，
2 基底涂膜，
3 釉质涂膜，
4 保护涂膜，
10、10A、10B 建材

Claims (5)

1.一种建材的制造方法，其特征在于，
具备：
第一步骤，在无机质基材上涂布基底涂料，进行固化、研磨；和
第二步骤，涂布釉质涂料，并使之固化，
所述基底涂料含有基底形成材料和填充剂，
所述釉质涂料含有釉质形成材料和颜料，
将所述釉质形成材料设为溶剂系树脂，
以固体成分比计将所述基底涂料的填充剂含量设为40～70％，
以固体成分比计将所述釉质涂料的颜料含量设为1～50％。
2.根据权利要求1所述的建材的制造方法，其特征在于，
作为所述釉质形成材料的所述溶剂系树脂，含有溶剂系氟树脂、溶剂系丙烯酸类树脂、溶剂系氨基甲酸酯树脂中的至少任意一种。
3.根据权利要求1所述的建材的制造方法，其特征在于，
作为所述基底形成材料含有紫外线固化型树脂、溶剂系氨基甲酸酯树脂中的至少任意一种。
4.根据权利要求1所述的建材的制造方法，其特征在于，
作为所述颜料，含有氧化钛、碳、氧化铁、有机颜料中的至少任意一种。
5.根据权利要求1所述的建材的制造方法，其特征在于，
作为所述填充剂，含有滑石、碳酸钙、二氧化硅中的至少任意一种。
CN201610657327.5A 2015-09-30 2016-08-11 建材的制造方法 Active CN106552758B (zh)