CN106543872A - A kind of water-proof climate resisting powdery paints and preparation method thereof - Google Patents
A kind of water-proof climate resisting powdery paints and preparation method thereof Download PDFInfo
- Publication number
- CN106543872A CN106543872A CN201611120816.3A CN201611120816A CN106543872A CN 106543872 A CN106543872 A CN 106543872A CN 201611120816 A CN201611120816 A CN 201611120816A CN 106543872 A CN106543872 A CN 106543872A
- Authority
- CN
- China
- Prior art keywords
- powdery paints
- water
- proof climate
- climate resisting
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-proof climate resisting powdery paints, is prepared from the following raw materials in parts by weight：Drying oil alkyd resin 42 55, Polyamide-Polyamsne-Epichlorohydrin resin 16 23, distearyl dimethylammonium Strese Hofmann's hectorite. 2.5 3.8, sericite in powder 79, azodiisobutyronitrile 12, sodium lignin sulfonate 23, trimethylhexamethylenediamine 13, coumarone indene resin 12, organic silicone quaternary ammonium salt 0.1 1, compounded mix 58；Invention also provides the preparation method of the water-proof climate resisting powdery paints; the water-proof climate resisting powdery paints that the present invention is provided; transparency is high; good dispersion; the powdery paints of the present invention is with its excellent waterproof, weatherability and high-decoration; can be used for the durable protective decoration industries such as shop equipment facility, aluminium alloy curtain wall, television transmitting tower coating, it is also possible to be widely used in the building material fields such as bridge, door and window, enclosure wall, domestic mark color material.
Description
Technical field
The present invention relates to a kind of paint field, more particularly to a kind of water-proof climate resisting powdery paints and preparation method thereof.
Background technology
Powdery paints by polymer, pigment and additive constitute it is a kind of new, without solvent, pure solid powdery
Coating；With without solvent, pollution-free, save energy and resource, reduce labor intensity high with coating machinery intensity the features such as.Powder
Last coating due to not discharging VOC thus utilization rate is higher, in past 10 years, powdery paints in the world
Development speed quickly, annual average rate of increase is 8%-15%.But, also there is coating with metal-like in current powdery paints
Clear with reference to the effect not as paint, the thermal diffusivity of powdery paints is not good enough, the defect such as water-proof climate resisting poor performance.
The content of the invention
It is an object of the invention to the above-mentioned deficiency in the presence of overcoming prior art, there is provided a kind of water-proof climate resisting powder is applied
Material and preparation method thereof.The water-proof climate resisting powdery paints transparency is high, good dispersion, with excellent waterproof, weatherability and height
It is ornamental.
In order to realize foregoing invention purpose, the invention provides technical scheme below：
A kind of water-proof climate resisting powdery paints, is prepared from the following raw materials in parts by weight：
Drying oil alkyd resin 42-55, Polyamide-Polyamsne-Epichlorohydrin resin 16-23, distearyl dimethylammonium lithium cover de-
Stone 2.5-3.8, sericite in powder 7-9, azodiisobutyronitrile 1-2, sodium lignin sulfonate 2-3, trimethylhexamethylenediamine 1-3,
Coumarone indene resin 1-2, organic silicone quaternary ammonium salt 0.1-1, compounded mix 5-8；
Described compounded mix is made up of the raw material of following weight parts：
Stalactitum 15-21, active hargil 12-16, precipitated calcium carbonate 4-9, Zinc Oxide 2-4, carboxymethyl cellulose 1-2；
By above-mentioned Stalactitum, active hargil, precipitated calcium carbonate mixing, 1-3 hours are calcined at 700-800 DEG C, is discharged cold
But ball milling mixing is carried out in sending into ball mill afterwards, add Zinc Oxide and carboxymethyl cellulose, continue ball milling 1-2 hours, cross 80-
100 mesh sieves, obtain final product the compounded mix.
Another object of the present invention is to provide the preparation method of above-mentioned water-proof climate resisting powdery paints, comprise the following steps：
By above-mentioned each raw material mixing in addition to sericite in powder, high-speed mixer, 1200-1600 rev/min of stirring are sent into
Dispersion 2-6 minutes, extruder is sent into, melting extrusion is subsequently placed in grinder, adds sericite in powder, at 1500-2000 rev/min
Lower speed lapping, after 80-100 mesh sieves, obtains final product the water-proof climate resisting powdery paints.
Compared with prior art, beneficial effects of the present invention：
The water-proof climate resisting powdery paints that the present invention is provided, transparency are high, good dispersion, and the powdery paints of the present invention is excellent with which
Different waterproof, weatherability and high-decoration, can be used for shop equipment facility, aluminium alloy curtain wall, television transmitting tower coating etc. durable
Protective and decorative industry, it is also possible to be widely used in the building material fields such as bridge, door and window, enclosure wall, domestic mark color material.
Specific embodiment
With reference to test example and specific embodiment, the present invention is described in further detail.But this should not be understood
Scope for above-mentioned theme of the invention is only limitted to below example, and all technologies realized based on present invention belong to this
The scope of invention.
Embodiment 1
A kind of water-proof climate resisting powdery paints, is prepared from the following raw materials in parts by weight：
Drying oil alkyd resin 49, Polyamide-Polyamsne-Epichlorohydrin resin 18, distearyl dimethylammonium Strese Hofmann's hectorite. 3.5,
Sericite in powder 8, azodiisobutyronitrile 1, sodium lignin sulfonate 2, trimethylhexamethylenediamine 2, coumarone indene resin 1, organosilicon
Ketone quaternary ammonium salt 0.6, compounded mix 7；
Described compounded mix is made up of the raw material of following weight parts：
Stalactitum 18, active hargil 14, precipitated calcium carbonate 7, Zinc Oxide 3, carboxymethyl cellulose 1；
By above-mentioned Stalactitum, active hargil, precipitated calcium carbonate mixing, calcine 2 hours at 800 DEG C, send after discharging cooling
Ball milling mixing is carried out in entering ball mill, Zinc Oxide and carboxymethyl cellulose is added, continues ball milling 1 hour, cross 100 mesh sieves, i.e.,
Obtain the compounded mix.
The preparation method of above-mentioned water-proof climate resisting powdery paints, comprises the following steps：
By above-mentioned each raw material mixing in addition to sericite in powder, high-speed mixer, 1400 revs/min of dispersed with stirring 5 are sent into
Minute, extruder is sent into, melting extrusion is subsequently placed in grinder, adds sericite in powder, in 1700 revs/min of lower speed lappings, then
90 mesh sieves are crossed, the water-proof climate resisting powdery paints is obtained final product.
Water-proof climate resisting powdery paints prepared by above-described embodiment 1 is sprayed at through pretreatment using the method for electrostatic spraying
Substrate of steel plate on, test film performance, test result is as follows, film adhesive (IS02409)：1 grade, film impact strength
(GB/T1732-93)：》60kg/cm, film resist bending：《2mm.
Claims (2)
1. a kind of water-proof climate resisting powdery paints, it is characterised in that be prepared from the following raw materials in parts by weight：
Drying oil alkyd resin 42-55, Polyamide-Polyamsne-Epichlorohydrin resin 16-23, distearyl dimethylammonium Strese Hofmann's hectorite.
2.5-3.8, sericite in powder 7-9, azodiisobutyronitrile 1-2, sodium lignin sulfonate 2-3, trimethylhexamethylenediamine 1-3, Gu
The grand resin 1-2 of horse, organic silicone quaternary ammonium salt 0.1-1, compounded mix 5-8；
Described compounded mix is made up of the raw material of following weight parts：
Stalactitum 15-21, active hargil 12-16, precipitated calcium carbonate 4-9, Zinc Oxide 2-4, carboxymethyl cellulose 1-2；
By above-mentioned Stalactitum, active hargil, precipitated calcium carbonate mixing, 1-3 hours are calcined at 700-800 DEG C, after discharging cooling
Ball milling mixing is carried out in sending into ball mill, Zinc Oxide and carboxymethyl cellulose is added, continues ball milling 1-2 hours, cross 80-100
Mesh sieve, obtains final product the compounded mix.
2. the preparation method of water-proof climate resisting powdery paints according to claim 1, it is characterised in that comprise the following steps：
By each raw material mixing in addition to sericite in powder, high-speed mixer, 1200-1600 rev/min of dispersed with stirring 2-6 point are sent into
Clock, sends into extruder, and melting extrusion is subsequently placed in grinder, adds sericite in powder, ground under 1500-2000 rev/min at a high speed
Mill, after 80-100 mesh sieves, obtains final product the water-proof climate resisting powdery paints.