CN104877504A - Graphene added anticorrosion latex paint for outer wall and preparation method thereof - Google Patents
Graphene added anticorrosion latex paint for outer wall and preparation method thereof Download PDFInfo
- Publication number
- CN104877504A CN104877504A CN201510327952.9A CN201510327952A CN104877504A CN 104877504 A CN104877504 A CN 104877504A CN 201510327952 A CN201510327952 A CN 201510327952A CN 104877504 A CN104877504 A CN 104877504A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- graphene
- minutes
- anticorrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a graphene added anticorrosion latex paint for an outer wall. The graphene added anticorrosion latex paint is characterized by being prepared from the following raw materials in parts by weight: 38 to 35 parts of pure acrylic emulsion, 7 to 9 parts of water-based fluorine carbon emulsion, 2 to 3 parts of silicone oil, 20 to 23 parts of rutile titanium dioxide, 5 to 6 parts of graphene, 7 to 9 parts of zeolite, 7 to 9 parts of pearl wool leftovers, 105 to 107 parts of water, 1.5 to 2 parts of asolo-OT, 3 to 4 parts of carrageenan, 2 to 3 parts of ammonium bicarbonate, 0.8 to 1 part of lignocelluloses, and 0.5 to 0.7 part of 1, 2-benzisothiazolin-3-ketone. According to the graphene added anticorrosion latex paint, pure acrylic emulsion and water-based fluorine carbon emulsion are prepared into a filming base material which is outstanding in weather resistance and water resistance; surface activated fillers are added to improve the corrosion resistance and insulation performance of the coating; the prepared coating paint film is high in attaching force, high in strength, difficult to crack and high in corrosion resistance.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, particularly a kind of anticorrosion latex coating of exterior wall adding Graphene and preparation method thereof.
Background technology
In the last few years, along with developing rapidly of China's economy, a large amount of iron and steel is used to the fields such as traffic, building, machinery, the energy, chemical industry, Infrastructure, railway and ocean exploitation, the steel corrosion brought thus is also more and more serious, therefore the performance requriements of people to protective system is also more and more higher, and traditional anti-corrosive organic coatings cannot satisfy the demands.
At present, the exterior coating that China adopts is mainly base-material with ACRYLIC EMULSION.Water-borne acrylic coatings has the advantages such as moderate cost, weathering resistance is excellent, adjustable good, organic solvent-free release, is a development in recent years class coating products very rapidly.Fluorine carbon emulsion, is polymerized by the advanced seed technique such as organic fluorine, (methyl) acrylate, extraordinary wet adhesion monomer, reactive emulsifier, Core-shell technology, thus the obtained comprehensive fluorine carbon emulsion of new generation of Performance comparision.There is splendid water tolerance; Overlength weathering resistance, anti-contamination, non yellowing; Alkali resistant, Acid Rain, salt fog resistance.In order to the development of construction industry, need the performance improving exterior coating further, especially antiseptic property.
Summary of the invention
The object of this invention is to provide a kind of anticorrosion latex coating of exterior wall adding Graphene and preparation method thereof.Pure-acrylic emulsion combines with water-base fluorocarbon emulsion by the present invention, makes the film with weather-proof, the splendid water tolerance of overlength, extends work-ing life; The filler such as Graphene, Rutile type Titanium Dioxide, zeolite of the surface active coordinating special process to make, is uniformly dispersed, can improves preservative property and the heat retaining property of coating in latex, the coating paint film adhesion made is good, intensity is high, not easy to crack, and antiseptic property is good.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of anticorrosion latex coating of exterior wall adding Graphene, be made up of the raw material of following weight part: pure-acrylic emulsion 38-35, water-base fluorocarbon emulsion 7-9, silicone oil 2-3, Rutile type Titanium Dioxide 20-23, Graphene 5-6, zeolite 7-9, PE Foam scrap stock 7-9, water 105-107, A Luosuo-OT 1.5-2, carrageenin 3-4, bicarbonate of ammonia 2-3, lignocellulose 0.8-1, BIT 0.5-0.7;
A kind of anticorrosion latex coating of exterior wall adding Graphene of the present invention, be made up of following concrete steps:
(1) zeolite powder is broken into 200 order powder, then with Graphene, Rutile type Titanium Dioxide mixing and ball milling 20 minutes, water and the A Luosuo-OT of 3 times amount is added in the mixed powder after ball milling, dispersed paste is formed after stirring 40 minutes with the speed of 600 revs/min, again by dispersed paste spraying dry, control spray-dired inlet temperature 150-180 DEG C, temperature out 60-75 DEG C, obtain surface active filler;
(2) carrageenin is added in the water of 3 times amount, be heated to 80 DEG C while stirring, then granulation in tablets press is jointly joined with surface active filler, bicarbonate of ammonia in step (1), the particle obtained first is sintered 60 minutes at the temperature of 220-250 DEG C, then 500-550 DEG C of sintering 2-2.5 hour is warming up to, be ground into 250 orders after being cooled to room temperature, obtain mixed powder A;
(3) PE Foam scrap stock are ground into 200 orders for subsequent use, the water of residual content is joined in dispersion cylinder, slowly pure-acrylic emulsion, water-base fluorocarbon emulsion, silicone oil, lignocellulose is added under the rotating speed of 450-500 rev/min, disperse after 40 minutes, improve rotating speed to 800 rev/min, add the PE Foam scrap stock after the mixed powder A of step (2), pulverizing and all the other remaining components successively, disperse after 20 minutes, raise speed to 1500 revs/min again, continue dispersion until fineness is less than 60 μm and get final product.
The invention has the beneficial effects as follows: Graphene, Rutile type Titanium Dioxide, zeolite etc. are carried out surface active by the present invention, then add appropriate bicarbonate of ammonia and carry out granulation, pulverize after final high temperature sintering, filler after the activation of making has good surface tension, can be good at coating compatible, there is loose porous feature simultaneously, improve the effect of sound-absorbing, insulation; The present invention adopts pure-acrylic emulsion to coordinate with water-base fluorocarbon emulsion and makes film forming binder, has weather-proof, the splendid water tolerance of overlength, the filler after matching surface activation, can improve preservative property and the heat retaining property of coating, the coating paint film adhesion made is good, and intensity is high, not easy to crack, antiseptic property is good.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of anticorrosion latex coating of exterior wall adding Graphene, be made up of the raw material of following weight part (kilogram): pure-acrylic emulsion 38, water-base fluorocarbon emulsion 7, silicone oil 2, Rutile type Titanium Dioxide 20, Graphene 5, zeolite 7, PE Foam scrap stock 7, water 105, A Luosuo-OT 1.5, carrageenin 3, bicarbonate of ammonia 2, lignocellulose 0.8, BIT 0.5;
A kind of anticorrosion latex coating of exterior wall adding Graphene of the present invention, be made up of following concrete steps:
(1) zeolite powder is broken into 200 order powder, then with Graphene, Rutile type Titanium Dioxide mixing and ball milling 20 minutes, water and the A Luosuo-OT of 3 times amount is added in the mixed powder after ball milling, dispersed paste is formed after stirring 40 minutes with the speed of 600 revs/min, again by dispersed paste spraying dry, control spray-dired inlet temperature 150-180 DEG C, temperature out 60-75 DEG C, obtain surface active filler;
(2) carrageenin is added in the water of 3 times amount, be heated to 80 DEG C while stirring, then granulation in tablets press is jointly joined with surface active filler, bicarbonate of ammonia in step (1), the particle obtained first is sintered 60 minutes at the temperature of 220-250 DEG C, then 500-550 DEG C of sintering 2-2.5 hour is warming up to, be ground into 250 orders after being cooled to room temperature, obtain mixed powder A;
(3) PE Foam scrap stock are ground into 200 orders for subsequent use, the water of residual content is joined in dispersion cylinder, slowly pure-acrylic emulsion, water-base fluorocarbon emulsion, silicone oil, lignocellulose is added under the rotating speed of 450 revs/min, disperse after 40 minutes, improve rotating speed to 800 rev/min, add the PE Foam scrap stock after the mixed powder A of step (2), pulverizing and all the other remaining components successively, disperse after 20 minutes, raise speed to 1500 revs/min again, continue dispersion until fineness is less than 60 μm and get final product.
Water-based exterior wall paint of the present invention adopts the form of construction work of roller coat, brushing, spraying, and coating appearance of film of the present invention is full, smooth, good without lump, glossiness; Water-fast 96 hours, alkaline-resisting 48 hours without exception; Abrasion resistance is tested 2000 times and is passed through, and film is without breakage; Artificial ageing resistance test 600 hours non-foaming, do not peel off, flawless.
Claims (2)
1. one kind is added the anticorrosion latex coating of exterior wall of Graphene, it is characterized in that, be made up of the raw material of following weight part: pure-acrylic emulsion 38-35, water-base fluorocarbon emulsion 7-9, silicone oil 2-3, Rutile type Titanium Dioxide 20-23, Graphene 5-6, zeolite 7-9, PE Foam scrap stock 7-9, water 105-107, A Luosuo-OT 1.5-2, carrageenin 3-4, bicarbonate of ammonia 2-3, lignocellulose 0.8-1, BIT 0.5-0.7.
2. a kind of anticorrosion latex coating of exterior wall adding Graphene according to claim 1, is characterized in that, be made up of following concrete steps:
(1) zeolite powder is broken into 200 order powder, then with Graphene, Rutile type Titanium Dioxide mixing and ball milling 20 minutes, water and the A Luosuo-OT of 3 times amount is added in the mixed powder after ball milling, dispersed paste is formed after stirring 40 minutes with the speed of 600 revs/min, again by dispersed paste spraying dry, control spray-dired inlet temperature 150-180 DEG C, temperature out 60-75 DEG C, obtain surface active filler;
(2) carrageenin is added in the water of 3 times amount, be heated to 80 DEG C while stirring, then granulation in tablets press is jointly joined with surface active filler, bicarbonate of ammonia in step (1), the particle obtained first is sintered 60 minutes at the temperature of 220-250 DEG C, then 500-550 DEG C of sintering 2-2.5 hour is warming up to, be ground into 250 orders after being cooled to room temperature, obtain mixed powder A;
(3) PE Foam scrap stock are ground into 200 orders for subsequent use, the water of residual content is joined in dispersion cylinder, slowly pure-acrylic emulsion, water-base fluorocarbon emulsion, silicone oil, lignocellulose is added under the rotating speed of 450-500 rev/min, disperse after 40 minutes, improve rotating speed to 800 rev/min, add the PE Foam scrap stock after the mixed powder A of step (2), pulverizing and all the other remaining components successively, disperse after 20 minutes, raise speed to 1500 revs/min again, continue dispersion until fineness is less than 60 μm and get final product.