CN106521612A - 一种新型环保电解挂具剥离粉 - Google Patents

一种新型环保电解挂具剥离粉 Download PDF

Info

Publication number
CN106521612A
CN106521612A CN201610854305.8A CN201610854305A CN106521612A CN 106521612 A CN106521612 A CN 106521612A CN 201610854305 A CN201610854305 A CN 201610854305A CN 106521612 A CN106521612 A CN 106521612A
Authority
CN
China
Prior art keywords
hanger
powder
sodium
alum
protective agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610854305.8A
Other languages
English (en)
Inventor
蔡艳辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610854305.8A priority Critical patent/CN106521612A/zh
Publication of CN106521612A publication Critical patent/CN106521612A/zh
Pending legal-status Critical Current

Abstract

本发明涉及挂具电解领域，更具体的说是一种新型环保电解挂具剥离粉，包括硫酸钠、硝酸钠、硼酸钠、不锈保护剂、促进剂和明矾，能一次性退除电镀挂具不锈钢钩头的铜镍铬镀层，不伤钩头；不锈钢挂具退镀后再电镀，钩头镀层结合力好，不易掉碴起毛刺；不含污水难处理的络合剂。所述的配方中各成分按重量比例分别为：硫酸钠15‑20克/升、硝酸钠30‑40克/升、硼酸钠15‑20克/升、不锈保护剂20‑30克/升、促进剂A2‑3克/升、明矾2‑3克/升。

Description

一种新型环保电解挂具剥离粉
技术领域
本发明涉及挂具电解领域，更具体的说是一种新型环保电解挂具剥离粉。
背景技术
电镀生产过程中，需要反复用到不锈钢挂具，传统的方法是用硝酸退镀，会产生大量黄烟，目前用的电解挂具剥离粉，虽取代了硝酸，但因含大量络合剂，污水很难处理。
发明内容
本发明主要解决的技术问题是提供一种新型环保电解挂具剥离粉，能一次性退除电镀挂具不锈钢钩头的铜镍铬镀层，不伤钩头；不锈钢挂具退镀后再电镀，钩头镀层结合力好，不易掉碴起毛刺；不含污水难处理的络合剂。
为解决上述技术问题，本发明涉及挂具电解领域，更具体的说是一种新型环保电解挂具剥离粉，包括硫酸钠、硝酸钠、硼酸钠、不锈保护剂、促进剂和明矾，能一次性退除电镀挂具不锈钢钩头的铜镍铬镀层，不伤钩头；不锈钢挂具退镀后再电镀，钩头镀层结合力好，不易掉碴起毛刺；不含污水难处理的络合剂。
所述的配方中各成分按重量比例分别为：硫酸钠15-20克/升、硝酸钠30-40克/升、硼酸钠15-20克/升、不锈保护剂20-30克/升、促进剂A2-3克/升、明矾2-3克/升。
作为本技术方案的进一步优化，本发明一种新型环保电解挂具剥离粉所述的配方中各成分按重量比例具体为：硫酸钠15克/升、硝酸钠30克/升、硼酸钠15克/升、不锈保护剂20克/升、促进剂A2克/升、明矾2克/升。
作为本技术方案的进一步优化，本发明一种新型环保电解挂具剥离粉所述的配方中各成分按重量比例具体为：硫酸钠20克/升、硝酸钠40克/升、硼酸钠20克/升、不锈保护剂30克/升、促进剂A3克/升、明矾3克/升。
作为本技术方案的进一步优化，本发明一种新型环保电解挂具剥离粉所述的配方中各成分按重量比例具体为：硫酸钠17.5克/升、硝酸钠35克/升、硼酸钠17.5克/升、不锈保护剂25克/升、促进剂A2.5克/升、明矾2.5克/升。
本发明一种新型环保电解挂具剥离粉的有益效果为：
本发明一种新型环保电解挂具剥离粉，能一次性退除电镀挂具不锈钢钩头的铜镍铬镀层，不伤钩头；不锈钢挂具退镀后再电镀，钩头镀层结合力好，不易掉碴起毛刺；不含污水难处理的络合剂。
具体实施方式
具体实施方式一：
本发明涉及挂具电解领域，更具体的说是一种新型环保电解挂具剥离粉，包括硫酸钠、硝酸钠、硼酸钠、不锈保护剂、促进剂和明矾，能一次性退除电镀挂具不锈钢钩头的铜镍铬镀层，不伤钩头；不锈钢挂具退镀后再电镀，钩头镀层结合力好，不易掉碴起毛刺；不含污水难处理的络合剂。
所述的配方中各成分按重量比例分别为：硫酸钠15-20克/升、硝酸钠30-40克/升、硼酸钠15-20克/升、不锈保护剂20-30克/升、促进剂A2-3克/升、明矾2-3克/升。
具体实施方式二：
本实施方式对实施方式一作进一步说明，所述的配方中各成分按重量比例具体为：硫酸钠15克/升、硝酸钠30克/升、硼酸钠15克/升、不锈保护剂20克/升、促进剂A2克/升、明矾2克/升。
具体实施方式三：
本实施方式对实施方式一作进一步说明，所述的配方中各成分按重量比例具体为：硫酸钠20克/升、硝酸钠40克/升、硼酸钠20克/升、不锈保护剂30克/升、促进剂A3克/升、明矾3克/升。
具体实施方式四：
本实施方式对实施方式一作进一步说明，所述的配方中各成分按重量比例具体为：硫酸钠17.5克/升、硝酸钠35克/升、硼酸钠17.5克/升、不锈保护剂25克/升、促进剂A2.5克/升、明矾2.5克/升。
配制工艺：上述六种原材料混合均匀后，分袋包装即可。
通过各成分不同重量百分比进行配比，使得得到的产品的性能高低不一。
当然，上述说明并非对本发明的限制，本发明也不仅限于上述举例，本技术领域的普通技术人员在本发明的实质范围内所做出的变化、改型、添加或替换，也属于本发明的保护范围。

Claims (4)

1.一种新型环保电解挂具剥离粉，其特征在于：所述的配方包括硫酸钠、硝酸钠、硼酸钠、不锈保护剂、促进剂和明矾，所述的配方中各成分按重量比例分别为：硫酸钠15-20克/升、硝酸钠30-40克/升、硼酸钠15-20克/升、不锈保护剂20-30克/升、促进剂A2-3克/升、明矾2-3克/升。
2.根据权利要求1所述的一种新型环保电解挂具剥离粉，其特征在于，所述的配方中各成分按重量比例具体为：硫酸钠15克/升、硝酸钠30克/升、硼酸钠15克/升、不锈保护剂20克/升、促进剂A2克/升、明矾2克/升。
3.根据权利要求1所述的一种新型环保电解挂具剥离粉，其特征在于，所述的配方中各成分按重量比例具体为：硫酸钠20克/升、硝酸钠40克/升、硼酸钠20克/升、不锈保护剂30克/升、促进剂A3克/升、明矾3克/升。
4.根据权利要求1所述的一种新型环保电解挂具剥离粉，其特征在于，所述的配方中各成分按重量比例具体为：硫酸钠17.5克/升、硝酸钠35克/升、硼酸钠17.5克/升、不锈保护剂25克/升、促进剂A2.5克/升、明矾2.5克/升。
CN201610854305.8A 2016-09-28 2016-09-28 一种新型环保电解挂具剥离粉 Pending CN106521612A (zh)