CN106519860A - Environment-friendly industrial paint - Google Patents
Environment-friendly industrial paint Download PDFInfo
- Publication number
- CN106519860A CN106519860A CN201611005025.6A CN201611005025A CN106519860A CN 106519860 A CN106519860 A CN 106519860A CN 201611005025 A CN201611005025 A CN 201611005025A CN 106519860 A CN106519860 A CN 106519860A
- Authority
- CN
- China
- Prior art keywords
- environment
- minutes
- polymer emulsion
- added
- industrial paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to the technical field of building materials, and particularly relates to environment-friendly industrial paint. The preparation method of the environment-friendly industrial paint includes the following steps that a formula amount of softened water, wetting agent, dispersing agent, defoamer, preservative, mildew preventive and PH value modifier are added into a pulping container to be stirred for 8 minutes; a formula amount (more than half) of water is added to disperse nano polymer emulsion, and stirring is performed for 8 minutes; a formula amount of pigment filler is added to be stirred for 8 minutes, and the pigment filler is ground until the fineness is smaller than 20 microns; a formula amount of color paste is added into a paint container, the remaining nano polymer emulsion is stirred for 8 minutes, and a dryer is added under the condition of uniform stirring; stirring is continuously performed for 8 minutes after adding is completed, a thickening agent is added under the condition of uniform stirring, and stirring is performed for 8 minutes after adding is completed till dispersing is made uniform; and filtering is conducted with a 100-mesh screen cloth. The environment-friendly industrial paint is safe, nontoxic, free of environmental pollution, high in paint film drying speed, low in baking temperature, high in mechanical strength, excellent in anti-rust performance and good in weather resistance.
Description
Technical field
The invention belongs to building material technical field, specifically, is a kind of environment-protecting industrial paint.
Background technology
Traditional industrial paint mostly is solvent-based paints, and common kind has alkyd, acrylate, polyurethane, epoxy, chlorination
The paint for base material such as rubber, highly-chlorinated polyethylene.Wherein containing about 50% organic volatile (VOC), these are organic to wave
Stimulating food can be evaporate in air during paint production and paint use, pollute environment, and workmen's body is caused
Injury.Therefore, each state has all worked out corresponding regulation to limit volatile organic matter (VOC) discharge, and endeavours to study " green "
Coating and resin, to be inherently eliminated or reduce the problem of environmental pollution.
Industrial water paint has high demands, and development difficulty is big.Western developed country through the sixties start to walk, across the seventies,
The eighties, until the beginning of the nineties, just there is the patent report of the preferable water-based industrial paint of performance.As Wei Ruohua companies of Austria develop
Water-based acrylic acid modified alcoholic acid finish paint, Patent No. AT9400711 and nippon chemical company develop aqueous acrylamide
Sour acid modified alcoholic anti-corrosive primer, Patent No. JP92359970.Although this kind of water-based industrial paint reduces the discharge of some VOC,
Atmospheric pollution is alleviated, but as polymer emulsion particle diameter is big (230nm～1500nm), compact in paint film is poor, and resistance to water is not
Good, decorative and protective is far apart with traditional paint.At present, the aqueous industrial for also not having performance suitable with traditional paint on market
Paint occurs.
The content of the invention
The present invention seeks to aim to provide a kind of environment-protecting industrial paint, there is provided a kind of safety non-toxic, environmentally safe, and
Paint film do solid work soon, the environment-protecting industrial paint of low baking temperature, high mechanical strength, high rust resistance, good weatherability.
To realize above-mentioned technical purpose, the technical solution used in the present invention is as follows：
A kind of environment-protecting industrial paint, the environment-protecting industrial paint, comprises the steps：The soft of formula ratio is added in mash vessel
Change water, wetting agent, dispersant, defoamer, preservative, antifungus agent, pH value regulator, stir 8 minutes, rotating speed is 450 revs/min；
The water dispersion nano polymer emulsion of the more than half amounts of formula ratio is added, is stirred 8 minutes, rotating speed is 650 revs/min；Add formula ratio
Color stuffing, stirs 8 minutes, and rotating speed is 950 revs/min；Fineness is ground to less than 20 μm；The mill base of formula ratio is added in paint container,
Remaining nanometer polymer emulsion, stirs 8 minutes, and rotating speed is 750 revs/min；Drier is uniformly added under stirring, continuation stirring is added
8 minutes, rotating speed was 750 revs/min；Thickening agent being uniformly added under stirring, stirring being added 8 minutes to being uniformly dispersed, rotating speed is 950
Rev/min；With 100 mesh sieve net filtrations, which includes following weight percent composition：80～90% latex particle size is less than 110nm's
Moisture dissipate environmentally friendly nanometer polymer emulsion, 3～20% pigment, 6～24% inertia rust resisting pigment, 2～11%
Active rust resisting pigment, 7～28% filler, 3～10% drier, the auxiliary agent of 0.8-7% and surplus softened water, wherein, water
Decentralized environment friendly nanometer polymer emulsion presses 1 with hydrophilic (methyl) acrylic acid esters co-polymer by hydrophobic type polymer
: remove organic solvent at vacuum and 90～150 DEG C after 2～3 part by weight mix homogeneously, to mixture solid content more than etc.
Make with the softened water stirring containing pH value regulator and 2～6% tall and erect elder generation's liquid after 60%.
Using the invention of above-mentioned technical proposal, the present invention is for big particle diameter polymer emulsion base material poor water resistance, protection dress
The not good shortcoming of decorations performance, selects a kind of particle diameter in the nanometer polymer emulsion of below 90nm as base material, to solve aqueouss work
The problem that industry paint is present.As this kind of nanometer polymer emulsion emulsion particle diameter is very little, the paint film of formation is very fine and close, so
Resistance to water and decorative and protective can meet or exceed traditional paint.Due to this kind of nanometer polymer emulsion emulsion particle diameter pole
Little, surface tension is very low, therefore they have fabulous permeability, wettability, levelability and rheological characteristic.With coating made by it,
High-quality, high glaze, high performance application can be carried out to metal parts, corresponding traditional paint product can be substituted.And,
Nontoxic, environmentally safe of the invention, it is healthy to workmen harmless, it is safe and convenient to use.The nanostructured of the present invention
Water-based industrial paint can be widely used for the steel constructions such as the vehicles such as automobile, train, ship, bridge, steel tower, railing, petrochemical industry basin,
The protection of ferrous materials in the facilities such as pipeline.
Further limit, the moisture therein dissipate environmentally friendly nanometer polymer emulsion be divided into 20 selected from solid～
35% moisture dissipates the water that environmentally friendly (methyl) acrylated polyester nanometer polymer emulsion, solid are divided into 46～60%
Drying oil-modified (methyl) the acrylic polyester nanometer polymer emulsion of decentralized environment friendly, solid are divided into 46～60% moisture
Scattered environmentally friendly (methyl) acrylic acid epoxy polyester nano polymer emulsion and solid are divided into 46～60% water decentralized environment
Drying oil-modified (methyl) the acrylic acid epoxy polyester nano polymer emulsion of friendly.
Further limit, the softened water therein is deionized water or distilled water, and in water, soluble ion total amount is less than
90ppm, electrical conductivity are less than 15 μm/cm.
Further limit, the pigment is selected from Rutile type titanium dioxide, carbon black and phthalocyanine blue.
Further limit, the inertia rust resisting pigment selected from iron oxide red, iron oxide brown, iron oxide black, iron oxide yellow and
Micaceous iron oxide.
Further limit, the active rust resisting pigment is selected from zinc phosphate, zinc molybdate, aluminium triphosphate, alkali formula aluminosilicate aluminum
And sodium metaborate.
Further limit, described filler is selected from Pulvis Talci, mica powder, Calcium Carbonate, blanc fixe and Kaolin.
Further limit, the drier is cobalt, manganese, zirconium, the aqueous emulsion that calcium salt is active ingredient.
Further limit, the auxiliary agent includes dispersant, wetting agent, defoamer, thickening agent, preservative, antifungus agent and PH
Value regulator.
Description of the drawings
Nothing
Specific embodiment
In order that those skilled in the art may be better understood the present invention, with reference to embodiment to the technology of the present invention
Scheme is further illustrated.
A kind of environment-protecting industrial paint, the environment-protecting industrial paint, comprises the steps：The soft of formula ratio is added in mash vessel
Change water, wetting agent, dispersant, defoamer, preservative, antifungus agent, pH value regulator, stir 8 minutes, rotating speed is 450 revs/min；
The water dispersion nano polymer emulsion of the more than half amounts of formula ratio is added, is stirred 8 minutes, rotating speed is 650 revs/min；Add formula ratio
Color stuffing, stirs 8 minutes, and rotating speed is 950 revs/min；Fineness is ground to less than 20 μm；The mill base of formula ratio is added in paint container,
Remaining nanometer polymer emulsion, stirs 8 minutes, and rotating speed is 750 revs/min；Drier is uniformly added under stirring, continuation stirring is added
8 minutes, rotating speed was 750 revs/min；Thickening agent being uniformly added under stirring, stirring being added 8 minutes to being uniformly dispersed, rotating speed is 950
Rev/min；With 100 mesh sieve net filtrations, which includes following weight percent composition：80～90% latex particle size is less than 110nm's
Moisture dissipate environmentally friendly nanometer polymer emulsion, 3～20% pigment, 6～24% inertia rust resisting pigment, 2～11%
Active rust resisting pigment, 7～28% filler, 3～10% drier, the auxiliary agent of 0.8-7% and surplus softened water, wherein, water
Decentralized environment friendly nanometer polymer emulsion presses 1 with hydrophilic (methyl) acrylic acid esters co-polymer by hydrophobic type polymer
: remove organic solvent at vacuum and 90～150 DEG C after 2～3 part by weight mix homogeneously, to mixture solid content more than etc.
Make with the softened water stirring containing pH value regulator and 2～6% tall and erect elder generation's liquid after 60%.
It is preferred that moisture dissipates the water decentralized environment friend that environmentally friendly nanometer polymer emulsion is divided into 20～35% selected from solid
Good type (methyl) acrylated polyester nanometer polymer emulsion, solid are divided into 46～60% moisture and dissipate environmentally friendly dryness
Modified (methyl) the acrylic polyester nanometer polymer emulsion of oil, solid are divided into 46～60% moisture and dissipate environmentally friendly (methyl)
Acrylic acid epoxy polyester nano polymer emulsion and solid are divided into 46～60% moisture and dissipate environmentally friendly drying oil-modified (first
Base) acrylic acid epoxy polyester nano polymer emulsion.
It is preferred that softened water is deionized water or distilled water, in water, soluble ion total amount is less than 90ppm, and electrical conductivity is less than 15
μm/cm。
Preferred pigments are selected from Rutile type titanium dioxide, carbon black and phthalocyanine blue.
It is preferred that inertia rust resisting pigment is selected from iron oxide red, iron oxide brown, iron oxide black, iron oxide yellow and micaceous iron oxide.
It is preferred that active rust resisting pigment is selected from zinc phosphate, zinc molybdate, aluminium triphosphate, alkali formula aluminosilicate aluminum and sodium metaborate.
Preferred filler is selected from Pulvis Talci, mica powder, Calcium Carbonate, blanc fixe and Kaolin.
It is preferred that drier is cobalt, manganese, zirconium, the aqueous emulsion that calcium salt is active ingredient.
Preferred promoter includes dispersant, wetting agent, defoamer, thickening agent, preservative, antifungus agent and pH value regulator.
Embodiment 1
A kind of environment-protecting industrial paint, which includes following weight percent composition：Moisture of 80% latex particle size less than 110nm
Dissipate environmentally friendly nanometer polymer emulsion, 3% pigment, 6% inertia rust resisting pigment, 2% active rust resisting pigment, 7%
Filler, 3% drier, 0.8% auxiliary agent and surplus softened water, wherein, moisture dissipates environmentally friendly nanometer polymer breast
Liquid mixed homogeneously by 1: 2 part by weight with hydrophilic (methyl) acrylic acid esters co-polymer by hydrophobic type polymer after in vacuum
With 90 DEG C at remove organic solvent, to mixture solid content more than or equal to after 60% with contain pH value regulator and 2～6% tall and erect
The softened water stirring of first liquid is made, and the environment-protecting industrial paint comprises the steps：The softening of formula ratio is added in mash vessel
Water, wetting agent, dispersant, defoamer, preservative, antifungus agent, pH value regulator, stir 8 minutes, and rotating speed is 450 revs/min；Plus
Enter the water dispersion nano polymer emulsion of the more than half amounts of formula ratio, stir 8 minutes, rotating speed is 650 revs/min；Add the face of formula ratio
Filler, stirs 8 minutes, and rotating speed is 950 revs/min；Fineness is ground to less than 20 μm；The mill base of formula ratio is added in paint container, is remained
Remaining nanometer polymer emulsion, stirs 8 minutes, and rotating speed is 750 revs/min；Drier is uniformly added under stirring, continuation stirring 8 is added
Minute, rotating speed is 750 revs/min；Thickening agent is uniformly added under stirring, stirring is added 8 minutes to being uniformly dispersed, rotating speed is 950 turns/
Point；With 100 mesh sieve net filtrations.
Embodiment 2
A kind of environment-protecting industrial paint, which includes following weight percent composition：Moisture of 90% latex particle size less than 110nm
Dissipate environmentally friendly nanometer polymer emulsion, 20% pigment, 24% inertia rust resisting pigment, 11% active rust resisting pigment,
28% filler, 10% drier, 7% auxiliary agent and surplus softened water, wherein, moisture dissipates environmentally friendly nanometer polymer
Emulsion mixed homogeneously by 1: 3 part by weight with hydrophilic (methyl) acrylic acid esters co-polymer by hydrophobic type polymer after true
It is empty and 150 DEG C at remove organic solvent, to mixture solid content more than or equal to 60% after with contain pH value regulator and 2～
The softened water stirring of 6% tall and erect elder generation's liquid is made, and the environment-protecting industrial paint comprises the steps：Formula ratio is added in mash vessel
Softened water, wetting agent, dispersant, defoamer, preservative, antifungus agent, pH value regulator, stir 8 minutes, rotating speed be 450 turns/
Point；The water dispersion nano polymer emulsion of the more than half amounts of formula ratio is added, is stirred 8 minutes, rotating speed is 650 revs/min；Add formula ratio
Color stuffing, stir 8 minutes, rotating speed be 950 revs/min；Fineness is ground to less than 20 μm；The color of formula ratio is added in paint container
Slurry, remaining nanometer polymer emulsion are stirred 8 minutes, and rotating speed is 750 revs/min；Drier is uniformly added under stirring, continuation is added
Stirring 8 minutes, rotating speed are 750 revs/min；Thickening agent being uniformly added under stirring, stirring being added 8 minutes to being uniformly dispersed, rotating speed is
950 revs/min；With 100 mesh sieve net filtrations.
The present invention selects one for the not good shortcoming of big particle diameter polymer emulsion base material poor water resistance, protected decoration performance
Kind of particle diameter below 90nm nanometer polymer emulsion as base material, to solve the problems, such as water-based industrial paint.Due to this kind of
Nanometer polymer emulsion emulsion particle diameter is very little, and the paint film of formation is very fine and close, so resistance to water and decorative and protective can be with
Meet or exceed traditional paint.As this kind of nanometer polymer emulsion emulsion particle diameter is minimum, surface tension is very low, therefore they
There are fabulous permeability, wettability, levelability and rheological characteristic.With coating made by it, metal parts can be carried out it is high-quality,
High glaze, high performance application, can substitute corresponding traditional paint product.And, nontoxic, environmentally safe of the invention,
It is healthy to workmen harmless, it is safe and convenient to use.The present invention nanostructured water-based industrial paint can be widely used for automobile,
In the facilities such as the steel constructions such as the vehicles such as train, ship, bridge, steel tower, railing, petrochemical industry basin, pipeline, ferrous materials is anti-
Shield.
Above a kind of environment-protecting industrial paint that the present invention is provided is described in detail.The explanation of specific embodiment is simply used
The method of the present invention and its core concept are understood in help.It should be pointed out that for those skilled in the art,
Under the premise without departing from the principles of the invention, some improvement and modification can also be carried out to the present invention, these improve and modify
Fall in the protection domain of the claims in the present invention.
Claims (9)
1. a kind of environment-protecting industrial paint, the environment-protecting industrial paint, comprise the steps：The softening of formula ratio is added in mash vessel
Water, wetting agent, dispersant, defoamer, preservative, antifungus agent, pH value regulator, stir 8 minutes, and rotating speed is 450 revs/min；Plus
Enter the water dispersion nano polymer emulsion of the more than half amounts of formula ratio, stir 8 minutes, rotating speed is 650 revs/min；Add the face of formula ratio
Filler, stirs 8 minutes, and rotating speed is 950 revs/min；Fineness is ground to less than 20 μm；The mill base of formula ratio is added in paint container, is remained
Remaining nanometer polymer emulsion, stirs 8 minutes, and rotating speed is 750 revs/min；Drier is uniformly added under stirring, continuation stirring 8 is added
Minute, rotating speed is 750 revs/min；Thickening agent is uniformly added under stirring, stirring is added 8 minutes to being uniformly dispersed, rotating speed is 950 turns/
Point；With 100 mesh sieve net filtrations, which includes following weight percent composition：Moisture of 80～90% latex particle size less than 110nm
Dissipate environmentally friendly nanometer polymer emulsion, 3～20% pigment, 6～24% inertia rust resisting pigment, 2～11% activity
Rust resisting pigment, 7～28% filler, 3～10% drier, the auxiliary agent of 0.8-7% and surplus softened water, wherein, moisture dissipates
Environmentally friendly nanometer polymer emulsion by hydrophobic type polymer and hydrophilic (methyl) acrylic acid esters co-polymer by 1: 2～
Organic solvent is removed at vacuum and 90～150 DEG C after 3 part by weight mix homogeneously, is more than or equal to mixture solid content
Make with the softened water stirring containing pH value regulator and 2～6% tall and erect elder generation's liquid after 60%.
2. environment-protecting industrial paint according to claim 1, moisture therein dissipate environmentally friendly nanometer polymer emulsion and are selected from
Solid is divided into 20～35% moisture and dissipates environmentally friendly (methyl) acrylated polyester nanometer polymer emulsion, solid and is divided into
46～60% moisture dissipates environmentally friendly drying oil-modified (methyl) acrylic polyester nanometer polymer emulsion, solid and is divided into 46
～60% moisture dissipates environmentally friendly (methyl) acrylic acid epoxy polyester nano polymer emulsion and solid is divided into 46～60%
Moisture dissipate environmentally friendly drying oil-modified (methyl) acrylic acid epoxy polyester nano polymer emulsion.
3. environment-protecting industrial paint according to claim 2, softened water therein is deionized water or distilled water, solubility in water
Total ion concentration is less than 90ppm, and electrical conductivity is less than 15 μm/cm.
4. environment-protecting industrial paint according to claim 3, pigment therein are selected from Rutile type titanium dioxide, carbon black and phthalocyanine
It is blue.
5. environment-protecting industrial paint according to claim 4, inertia rust resisting pigment therein selected from iron oxide red, iron oxide brown,
Iron oxide black, iron oxide yellow and micaceous iron oxide.
6. environment-protecting industrial paint according to claim 5, active rust resisting pigment therein are selected from zinc phosphate, zinc molybdate, trimerization
Aluminum phosphate, alkali formula aluminosilicate aluminum and sodium metaborate.
7. environment-protecting industrial paint according to claim 6, filler therein are selected from Pulvis Talci, mica powder, Calcium Carbonate, precipitated sulfur
Sour barium and Kaolin.
8. environment-protecting industrial paint according to claim 7, drier therein be cobalt, manganese, zirconium, calcium salt for active ingredient water
Emulsion.
9. environment-protecting industrial paint according to claim 8, auxiliary agent therein include dispersant, wetting agent, defoamer, thickening
Agent, preservative, antifungus agent and pH value regulator.