CN106498746A - A kind of use for synthetic leather washes bright carbon black treatment agent and preparation method thereof - Google Patents
A kind of use for synthetic leather washes bright carbon black treatment agent and preparation method thereof Download PDFInfo
- Publication number
- CN106498746A CN106498746A CN201610966124.4A CN201610966124A CN106498746A CN 106498746 A CN106498746 A CN 106498746A CN 201610966124 A CN201610966124 A CN 201610966124A CN 106498746 A CN106498746 A CN 106498746A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- carbon black
- treatment agent
- synthetic leather
- washes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of use for synthetic leather washes bright carbon black treatment agent and preparation method thereof.The use for synthetic leather washes bright carbon black treatment agent comprising following components：Modified polyurethane resin, acrylic resin, nitrocotton, dimethylformamide, butyl ester, butanone, DAA, silicon dioxide flatting silica, carbon powder, epoxy soybean oil, oleamide and organic silicone oil.Each component that use for synthetic leather of the present invention washes bright carbon black treatment agent is mutually coordinated, collective effect, and after white carbon black is washed, bright face, oily wax effect are good, and feel is smooth, and the leather gloss nature that is made with this kind of inorganic agent, blackness are good, and color clarification, resultant effect are good.
Description
Technical field
The present invention relates to a kind of use for synthetic leather washes bright carbon black treatment agent, the conjunction of synthetic leather rear section technique is more particularly to applied to
Finished leather with bright carbon black treatment agent is washed, while the invention also discloses the use for synthetic leather washes the preparation method of bright carbon black treatment agent.
Background technology
At present, existing use for synthetic leather is washed bright carbon black treatment agent white carbon black and washes brightness below, oily wax effect, and feel is not very
Preferable.The synthetic leather of bright carbon black treatment agent is washed as application, and its gloss and color and luster are poor, and blackness is also not fully up to expectations.Therefore,
Needs one kind is improved to wash bright carbon black treatment agent.
Content of the invention
It is an object of the invention to provide a kind of use for synthetic leather washes bright carbon black treatment agent.
The use for synthetic leather of the present invention is washed bright carbon black treatment agent and is achieved through the following technical solutions：
Use for synthetic leather disclosed in this invention washes bright carbon black treatment agent, comprising following components：Modified polyurethane resin, propylene
Acid resin, nitrocotton, dimethylformamide, butyl ester, butanone, DAA, silicon dioxide flatting silica, carbon powder, epoxy soybean
Oil, oleamide and organic silicone oil.
On the basis of the gross weight of resin, the use for synthetic leather that the present invention is provided washes the proportioning of each component of bright carbon black treatment agent
Can be：12～14 mass parts of modified polyurethane resin, 6～8 mass parts of acrylic resin, 2～3 mass parts of nitrocotton, diformazan
2～4 mass parts of base Methanamide, 23～25 mass parts of butyl ester, 8～10 mass parts of butanone, 13～15 mass parts of DAA, dioxy
2～3 mass parts of SiClx flatting silica, 18～20 mass parts of carbon powder, 2～3 mass parts of epoxy soybean oil, 1～2 mass of oleamide
Part, 1～2 mass parts of organic silicone oil.
In one embodiment of the invention, use for synthetic leather wash each component of bright carbon black treatment agent proportioning as follows：Modified
12 mass parts of polyurethane resin, 8 mass parts of acrylic resin, 3 mass parts of nitrocotton, 2 mass parts of dimethylformamide, butyl ester 23
Mass parts, 9 mass parts of butanone, 13 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, 20 mass parts of carbon powder, epoxy
3 mass parts of soybean oil, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.
In another embodiment of the invention, use for synthetic leather wash each component of bright carbon black treatment agent proportioning as follows：Modified
14 mass parts of polyurethane resin, 6 mass parts of acrylic resin, 3 mass parts of nitrocotton, 3 mass parts of dimethylformamide, butyl ester 24
Mass parts, 10 mass parts of butanone, 15 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, 18 mass parts of carbon powder, ring
2 mass parts of oxygen soybean oil, 1 mass parts of oleamide, 1 mass parts of organic silicone oil.
In another embodiment of the invention, use for synthetic leather wash each component of bright carbon black treatment agent proportioning as follows：Modified
13 mass parts of polyurethane, 7 mass parts of acrylic resin, 2 mass parts of nitrocotton, 3 mass parts of dimethylformamide, 24 mass of butyl ester
Part, 8 mass parts of butanone, 15 mass parts of DAA, 2 mass parts of silicon dioxide flatting silica, 19 mass parts of carbon powder, epoxy soybean
Oily 3 mass parts, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.
The present invention also provides the preparation method that a kind of use for synthetic leather washes bright carbon black treatment agent, comprises the steps of：
1) by the acrylic resin in formula, nitrocotton, dimethylformamide, butyl ester, butanone, DAA, titanium dioxide
Grinding after silicon flatting silica, carbon powder stirring is filtered；
2) in step 1) in the mixture that obtains plus modified polyurethane resin, epoxy soybean oil, oleamide and organosilicon
Oil, uniform stirring.
The proportioning of each component that the use for synthetic leather of the present invention is washed in the preparation method of bright carbon black treatment agent can be as follows：Modified
12～14 mass parts of polyurethane resin, 6～8 mass parts of acrylic resin, 2～3 mass parts of nitrocotton, dimethylformamide 2～4
Mass parts, 23～25 mass parts of butyl ester, 8～10 mass parts of butanone, 13～15 mass parts of DAA, silicon dioxide flatting silica 2
～3 mass parts, 18～20 mass parts of carbon powder, 2～3 mass parts of epoxy soybean oil, 1～2 mass parts of oleamide, organic silicone oil
1～2 mass parts.
Preferably, the proportioning of each component is as follows：12 mass parts of modified polyurethane resin, 8 mass parts of acrylic resin, nitrification
3 mass parts of cotton, 2 mass parts of dimethylformamide, 23 mass parts of butyl ester, 9 mass parts of butanone, 13 mass parts of DAA, dioxy
3 mass parts of SiClx flatting silica, 20 mass parts of carbon powder, 3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, organic silicone oil 2
Mass parts.
It is highly preferred that the proportioning of each component is as follows：14 mass parts of modified polyurethane resin, 6 mass parts of acrylic resin, nitre
Change 3 mass parts of cotton, 3 mass parts of dimethylformamide, 24 mass parts of butyl ester, 10 mass parts of butanone, 15 mass parts of DAA, two
3 mass parts of silicon oxide flatting silica, 18 mass parts of carbon powder, 2 mass parts of epoxy soybean oil, 1 mass parts of oleamide, organic silicone oil
1 mass parts.
It is highly preferred that the proportioning of each component is as follows：13 mass parts of modified polyurethane, 7 mass parts of acrylic resin, nitrocotton
2 mass parts, 3 mass parts of dimethylformamide, 24 mass parts of butyl ester, 8 mass parts of butanone, 15 mass parts of DAA, titanium dioxide
2 mass parts of silicon flatting silica, 19 mass parts of carbon powder, 3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, 2 matter of organic silicone oil
Amount part.
Due to adopting above technical scheme, the present invention to have the advantage that compared with prior art：
1. use for synthetic leather of the present invention wash bright carbon black treatment agent each component is mutually coordinated, collective effect, white carbon black is washed
Bright face, oily wax effect are good afterwards, and feel is smooth, and the leather gloss nature that is made with this kind of inorganic agent, blackness are good, color clarification, comprehensive
Effect is good；
2. use for synthetic leather of the present invention is washed bright carbon black treatment agent and is applied on existing synthetic leather production line, technique letter
Single, it is a kind of new material of back segment process, need not change production equipment increases cost；
3. use for synthetic leather of the present invention wash bright carbon black treatment agent preparation method simple, without the need for using complicated machinery
Process, saved production cost, be suitable to industrialized production.
Specific embodiment
Below by embodiment, technical solution of the present invention is described in detail, but protection scope of the present invention not office
It is limited to the embodiment.
Embodiment 1
Use for synthetic leather washes bright carbon black treatment agent comprising 12 mass parts modified polyurethane resins, 8 mass parts acrylic resins, and 3
Mass parts nitrocotton, 2 mass parts dimethylformamides, 23 mass parts butyl esters, 9 mass parts butanone, 13 mass parts DAAs, 3
Mass parts silicon dioxide flatting silica, 20 mass parts of carbon black powder, 3 mass parts epoxy soybean oils, 2 mass oleamide parts, 2 mass parts
Organic silicone oil.
Above-mentioned use for synthetic leather washes the preparation method of bright carbon black treatment agent：By 8 mass parts acrylic resins in formula, 3
Mass parts nitrocotton, 2 mass parts dimethylformamides, 23 mass parts butyl esters, 9 mass parts butanone, 13 mass parts DAAs, 3
Mass parts silicon dioxide flatting silica, grinding after the stirring of 20 mass parts of carbon black powder are filtered；Then 12 are added in the mixture of gained
Mass parts modified polyurethane resin, 3 mass parts epoxy soybean oils, 2 mass oleamide parts, 2 mass parts organic silicone oils are uniformly stirred
Described use for synthetic leather is obtained final product after mixing washes bright carbon black treatment agent.Obtained use for synthetic leather washes the performance indications of bright carbon black treatment agent
It is shown in Table 1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Embodiment 2
Use for synthetic leather washes bright carbon black treatment agent comprising 14 mass parts modified polyurethane resins, 6 mass parts acrylic resins, and 3
Mass parts nitrocotton, 3 mass parts dimethylformamides, 24 mass parts butyl esters, 10 mass parts butanone, 15 mass parts DAAs, 3
Mass parts silicon dioxide flatting silica, 18 mass parts of carbon black powder, 2 mass parts epoxy soybean oils, 1 mass parts oleamide, 1 mass parts
Organic silicone oil.
Above-mentioned use for synthetic leather washes the preparation method of bright carbon black treatment agent：By 6 mass parts acrylic resins in formula, 3
Mass parts nitrocotton, 3 mass parts dimethylformamides, 24 mass parts butyl esters, 10 mass parts butanone, 15 mass parts DAAs, 3
Mass parts silicon dioxide flatting silica, grinding after the stirring of 18 mass parts of carbon black powder are filtered；Then 14 are added in the mixture of gained
Mass parts modified polyurethane resin, 2 mass parts epoxy soybean oils, 1 mass parts oleamide, 1 mass parts organic silicone oil are uniformly stirred
Described use for synthetic leather is obtained final product after mixing washes bright carbon black treatment agent.Obtained use for synthetic leather washes the performance indications of bright carbon black treatment agent
It is shown in Table 1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Embodiment 3
Use for synthetic leather washes bright carbon black treatment agent comprising 13 mass parts modified polyurethanes, 7 mass parts acrylic resins, 2 mass
Part nitrocotton, 3 mass parts dimethylformamides, 24 mass parts butyl esters, 8 mass parts butanone, 15 mass parts DAAs, 2 mass
Part silicon dioxide flatting silica, 19 mass parts of carbon black powder, 3 mass parts epoxy soybean oils, 2 mass parts oleamides, 2 mass parts are organic
Silicone oil.
Above-mentioned use for synthetic leather washes the preparation method of bright carbon black treatment agent：By 7 mass parts acrylic resins in formula, 2
Mass parts nitrocotton, 3 mass parts dimethylformamides, 24 mass parts butyl esters, 8 mass parts butanone, 15 mass parts DAAs, 2
Mass parts silicon dioxide flatting silica, grinding after the stirring of 19 mass parts of carbon black powder are filtered；Then 13 are added in the mixture of gained
Mass parts modified polyurethane, 3 mass parts epoxy soybean oils, 2 mass parts oleamides, 2 mass parts organic silicone oils, after uniform stirring
Obtain final product described use for synthetic leather and wash bright carbon black treatment agent.Obtained use for synthetic leather is washed the performance indications of bright carbon black treatment agent and is shown in Table
1.
The methods such as stirring, grinding, filtration employed in above-mentioned preparation process are customary way in the art.
Table 1
Presently preferred embodiments of the present invention is the foregoing is only, is not used for the practical range for limiting the present invention；If do not taken off
From the spirit and scope of the present invention, the present invention is modified or equivalent, all should be covered in the claims in the present invention
In the middle of protection domain.
Claims (10)
1. a kind of use for synthetic leather washes bright carbon black treatment agent, it is characterised in that comprising following components：Modified polyurethane resin, propylene
Acid resin, nitrocotton, dimethylformamide, butyl ester, butanone, DAA, silicon dioxide flatting silica, carbon powder, epoxy soybean
Oil, oleamide and organic silicone oil.
2. use for synthetic leather according to claim 1 washes bright carbon black treatment agent, it is characterised in that each component with such as
Under：12～14 mass parts of modified polyurethane resin, 6～8 mass parts of acrylic resin, 2～3 mass parts of nitrocotton, dimethyl methyl
2～4 mass parts of amide, 23～25 mass parts of butyl ester, 8～10 mass parts of butanone, 13～15 mass parts of DAA, silicon dioxide
2～3 mass parts of flatting silica, 18～20 mass parts of carbon powder, 2～3 mass parts of epoxy soybean oil, 1～2 mass parts of oleamide,
1～2 mass parts of organic silicone oil.
3. use for synthetic leather according to claim 2 washes bright carbon black treatment agent, it is characterised in that each component with such as
Under：12 mass parts of modified polyurethane resin, 8 mass parts of acrylic resin, 3 mass parts of nitrocotton, 2 mass of dimethylformamide
Part, 23 mass parts of butyl ester, 9 mass parts of butanone, 13 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, 20 matter of carbon powder
Amount part, 3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.
4. use for synthetic leather according to claim 2 washes bright carbon black treatment agent, it is characterised in that each component with such as
Under：14 mass parts of modified polyurethane resin, 6 mass parts of acrylic resin, 3 mass parts of nitrocotton, 3 mass of dimethylformamide
Part, 24 mass parts of butyl ester, 10 mass parts of butanone, 15 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, carbon powder 18
Mass parts, 2 mass parts of epoxy soybean oil, 1 mass parts of oleamide, 1 mass parts of organic silicone oil.
5. use for synthetic leather according to claim 2 washes bright carbon black treatment agent, it is characterised in that each component with such as
Under：13 mass parts of modified polyurethane, 7 mass parts of acrylic resin, 2 mass parts of nitrocotton, 3 mass parts of dimethylformamide, fourth
24 mass parts of ester, 8 mass parts of butanone, 15 mass parts of DAA, 2 mass parts of silicon dioxide flatting silica, 19 mass parts of carbon powder,
3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.
6. the use for synthetic leather described in claim 1 washes the preparation method of bright carbon black treatment agent, it is characterised in that comprising following step
Suddenly：
1) by the acrylic resin in formula, nitrocotton, dimethylformamide, butyl ester, butanone, DAA, silicon dioxide disappear
Grinding after light powder, carbon powder stirring is filtered；
2) in step 1) in the mixture that obtains plus modified polyurethane resin, epoxy soybean oil, oleamide and organic silicone oil,
Even stirring.
7. use for synthetic leather according to claim 6 washes the preparation method of bright carbon black treatment agent, it is characterised in that each component
Proportioning is as follows：12～14 mass parts of modified polyurethane resin, 6～8 mass parts of acrylic resin, 2～3 mass parts of nitrocotton, two
2～4 mass parts of methylformamide, 23～25 mass parts of butyl ester, 8～10 mass parts of butanone, 13～15 mass parts of DAA, two
2～3 mass parts of silicon oxide flatting silica, 18～20 mass parts of carbon powder, 2～3 mass parts of epoxy soybean oil, 1～2 matter of oleamide
Amount part, 1～2 mass parts of organic silicone oil.
8. use for synthetic leather according to claim 7 washes the preparation method of bright carbon black treatment agent, it is characterised in that each component
Proportioning is as follows：12 mass parts of modified polyurethane resin, 8 mass parts of acrylic resin, 3 mass parts of nitrocotton, dimethylformamide 2
Mass parts, 23 mass parts of butyl ester, 9 mass parts of butanone, 13 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, carbon powder
20 mass parts, 3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.
9. use for synthetic leather according to claim 7 washes the preparation method of bright carbon black treatment agent, it is characterised in that each component
Proportioning is as follows：14 mass parts of modified polyurethane resin, 6 mass parts of acrylic resin, 3 mass parts of nitrocotton, dimethylformamide 3
Mass parts, 24 mass parts of butyl ester, 10 mass parts of butanone, 15 mass parts of DAA, 3 mass parts of silicon dioxide flatting silica, white carbon black
18 mass parts of powder, 2 mass parts of epoxy soybean oil, 1 mass parts of oleamide, 1 mass parts of organic silicone oil.
10. use for synthetic leather according to claim 7 washes the preparation method of bright carbon black treatment agent, it is characterised in that each component
Proportioning as follows：13 mass parts of modified polyurethane, 7 mass parts of acrylic resin, 2 mass parts of nitrocotton, 3 matter of dimethylformamide
Amount part, 24 mass parts of butyl ester, 8 mass parts of butanone, 15 mass parts of DAA, 2 mass parts of silicon dioxide flatting silica, carbon powder 19
Mass parts, 3 mass parts of epoxy soybean oil, 2 mass parts of oleamide, 2 mass parts of organic silicone oil.