CN106496918A - 一种复合型导电塑料的制备方法 - Google Patents

一种复合型导电塑料的制备方法 Download PDF

Info

Publication number
CN106496918A
CN106496918A CN201610990319.2A CN201610990319A CN106496918A CN 106496918 A CN106496918 A CN 106496918A CN 201610990319 A CN201610990319 A CN 201610990319A CN 106496918 A CN106496918 A CN 106496918A
Authority
CN
China
Prior art keywords
stainless steel
preparation
reach
conductive plastic
butadiene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610990319.2A
Other languages
English (en)
Inventor
过冬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610990319.2A priority Critical patent/CN106496918A/zh
Publication of CN106496918A publication Critical patent/CN106496918A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种复合型导电塑料的制备方法，包括：所述导电塑料由30～60％丙烯腈‑丁二烯‑苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维组成，其制备工艺工艺包括：将30～60％丙烯腈‑丁二烯‑苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维在开炼机上熔融共混，熔融温度为320～350℃，混合均匀后，挤出，冷却制粒。本发明打破了国外对我国的技术垄断，成功制备了不锈钢纤维/聚碳酸酯/丙烯晴‑丁二烯‑苯乙烯(SSF/PC/ABS)复合型导电塑料，其体积电阻率最低可达到10‑2Ω·cm，拉伸强度最高可达247MPa，弯曲强度可到299MPa，屏蔽效能可达到70～90dB，能够满足航空航天和军用要求。

Description

一种复合型导电塑料的制备方法
技术领域
本发明涉及塑料技术领域，尤其涉及一种复合型导电塑料的制备方法。
背景技术
塑料一般都具有良好的绝缘性能，并因此在很多领域得到了广泛应用，例如电线电缆、电子电气等。但是随着社会的发展和科技的进步，在某些领域塑料的绝缘性能反而变成了不利因素，于是人们开始研究如何改善塑料的导电性能。目前主要有两种方法，一种是改进分子结构，即制备结构型导电塑料，另一种是与可导电的填料复合，即制备复合型导电塑料。
随着社会不断的进步，电子、电器制造技术的不断发展，导电塑料的应用越来越多，需求量越来越大，而且对导电塑料的要求也越来越高，复合型导电塑料的目前主要是向高性能化、多功能化、良好的加工性和低成本方面发展，其中关键的技术包括：(1)如何能够在保持优异的导电性能和屏蔽性能的前提下，尽可能地降低导电填料的用量，以达到提高加工性能、降低生产成本的目的；(2)如何能尽可能的提高复合导电塑料的导电性能，而又保持良好的加工性能和力学性能；(3)如何使导电塑料在具备导电塑料的同时，也具有优秀的阻燃、耐热、耐磨、耐腐蚀、高导热等其他性能；(4)新的高效导电填料和新的导电塑料制备工艺的开发。
目前生产纤维复合型导电塑料的工艺主要为双螺杆反应挤出工艺，纤维在该工艺过程中受到很强的剪切作用，导致纤维长度过短，添加量高，而且纤维对设备磨损严重。国外已经有企业采用电缆包覆工艺生产导电塑料，该工艺可最大限度保持纤维的长径比，制备的导电塑料各项性能优异，但国内尚没有突破。
发明内容
本发明的目的在于提出一种复合型导电塑料的制备方法，。
为达此目的，本发明采用以下技术方案：
一种复合型导电塑料的制备方法，包括：所述导电塑料由30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维组成，其制备工艺工艺包括：将30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维在开炼机上熔融共混，熔融温度为320～350℃，混合均匀后，挤出，冷却制粒。
本发明打破了国外对我国的技术垄断，成功制备了不锈钢纤维/聚碳酸酯/丙烯晴-丁二烯-苯乙烯(SSF/PC/ABS)复合型导电塑料，其体积电阻率最低可达到10-2Ω·cm，拉伸强度最高可达247MPa，弯曲强度可到299MPa，屏蔽效能可达到70～90dB，能够满足航空航天和军用要求。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
实施例1
一种复合型导电塑料的制备方法，包括：所述导电塑料由30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维组成，其制备工艺工艺包括：将30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维在开炼机上熔融共混，熔融温度为320～350℃，混合均匀后，挤出，冷却制粒
实施例1成功制备了不锈钢纤维/聚碳酸酯/丙烯晴-丁二烯-苯乙烯(SSF/PC/ABS)复合型导电塑料，其体积电阻率最低可达到10-2Ω·cm，拉伸强度最高可达247MPa，弯曲强度可到299MPa，屏蔽效能可达到70～90dB，能够满足航空航天和军用要求。

Claims (1)

1.一种复合型导电塑料的制备方法，包括：所述导电塑料由30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维组成，其制备工艺工艺包括：将30～60％丙烯腈-丁二烯-苯乙烯，20～35％聚碳酸酯和20～35％不锈钢纤维在开炼机上熔融共混，熔融温度为320～350℃，混合均匀后，挤出，冷却制粒。
CN201610990319.2A 2016-11-10 2016-11-10 一种复合型导电塑料的制备方法 Pending CN106496918A (zh)