CN106492766A - 一种甲醛快速吸附材料的制备方法 - Google Patents

一种甲醛快速吸附材料的制备方法 Download PDF

Info

Publication number
CN106492766A
CN106492766A CN201611250677.6A CN201611250677A CN106492766A CN 106492766 A CN106492766 A CN 106492766A CN 201611250677 A CN201611250677 A CN 201611250677A CN 106492766 A CN106492766 A CN 106492766A
Authority
CN
China
Prior art keywords
parts
maifanitum
meerschaum
glycine
ethanol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611250677.6A
Other languages
English (en)
Inventor
顾黎明
张宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Mdt Infotech Ltd
Original Assignee
Suzhou Mdt Infotech Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Mdt Infotech Ltd filed Critical Suzhou Mdt Infotech Ltd
Priority to CN201611250677.6A priority Critical patent/CN106492766A/zh
Publication of CN106492766A publication Critical patent/CN106492766A/zh
Pending legal-status Critical Current

Abstract

本发明涉及吸附材料领域，尤其涉及一种甲醛快速吸附材料的制备方法，包括步骤：1）称取活性炭、碳酸钙、乙醇、麦饭石、海泡石、甘氨酸、珍珠岩、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素、正磷酸铁、氯化镁和滑石粉；2）将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁进行升温搅拌，制得搅拌均匀的混合物；3）将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉恒温干燥后与步骤2）的混合物合并；4）继续进行真空干燥，过夜即可。本发明方法制得的产品甲醛去除率高达98‑99.8%；吸附速度快，吸附范围广，取本品放在甲醛含量400‑500μg/m3密闭空间内40‑48h后，甲醛浓度为1‑8μg/m3；制备方法简单，成本低廉，操作性强。

Description

一种甲醛快速吸附材料的制备方法
技术领域
本发明涉及吸附材料领域，尤其涉及一种甲醛快速吸附材料的制备方法。
背景技术
甲醛净化吸附剂是指主要用于家居生活之中用来吸附甲醛的吸附材料，一般具有如下特点：1）比表面极大，吸附能力强；2）对气体有较高的吸附性能，能迅速吸附；3）环保，无污染，制造成本低。
甲醛净化吸附剂可有效吸附因家居装修而释放出来的甲醛、苯、二甲苯等有害物质，主要成分是活性硅，属非晶态物质，取材于天然的石英砂，经过特殊加工工艺处理提炼而成，使其具备了大比表面积以及丰富的与室内有害气体分子大小相匹配的孔隙结构，同时还具有调节空气湿度、去味防霉、除臭杀菌等功效，彻底清除室内环境污染。加之近年来不断地创新开发，各种活性硅已被广泛用于药物提纯、DNA分离、食品干燥、高精电子、高级化妆品、污水净化、啤酒提纯、高级涂料以及树脂生产或保存等方面。
室内甲醛、苯等有害气体作为家居生活中不可避免的隐性杀手，时刻威胁人们的身体健康。而这些有害气体的释放是一个缓慢的过程，即使再好的空气净洁产品，也不可能一次性、彻底净化空气。
如何设计一种甲醛去除率高、使用寿命长和吸附速度快的甲醛吸附材料以满足市场需求，是非常必要的。
发明内容
所要解决的技术问题：
本发明针对现有甲醛吸附剂去除率较低、使用寿命短和吸附速度慢的技术问题而提供一种甲醛快速吸附材料的制备方法。
技术方案：
一种甲醛快速吸附材料的制备方法，其包括如下制备步骤：
第一步：称取活性炭、碳酸钙、乙醇、麦饭石、海泡石、甘氨酸、珍珠岩、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素、正磷酸铁、氯化镁和滑石粉；
第二步：将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至60-80℃，搅拌30-70min，搅拌速度为800-1200转/分钟，制得搅拌均匀的混合物；
第三步：将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在80-120℃下恒温干燥，然后再与第二步搅拌均匀的混合物合并，继续混合搅拌2-6h，搅拌速度为800-1200转/分钟；
第四步：将第三步混合后的产物放入真空干燥箱中，在25-45℃下干燥过夜即可。
作为本发明的一种优选技术方案：所述甲醛吸附材料各原料，按重量份数计：活性炭100份，碳酸钙15-25份，乙醇30-50份，麦饭石10-20份，海泡石25-35份，甘氨酸20-30份，珍珠岩5-15份，硝酸钠2-4份，碳酸氢铵7-9份，二氧化钛3-5份，甲基纤维素4-6份，正磷酸铁14-16份，氯化镁10-20份，滑石粉13-17份。
作为本发明的一种优选技术方案：所述甲醛吸附材料各原料，按重量份数计：活性炭100份，碳酸钙15份，乙醇30份，麦饭石10份，海泡石25份，甘氨酸20份，珍珠岩5份，硝酸钠2份，碳酸氢铵7份，二氧化钛3份，甲基纤维素4份，正磷酸铁14份，氯化镁10份，滑石粉13份。
作为本发明的一种优选技术方案：所述甲醛吸附材料各原料，按重量份数计：活性炭100份，碳酸钙25份，乙醇50份，麦饭石20份，海泡石35份，甘氨酸30份，珍珠岩15份，硝酸钠4份，碳酸氢铵9份，二氧化钛5份，甲基纤维素6份，正磷酸铁16份，氯化镁20份，滑石粉17份。
作为本发明的一种优选技术方案：所述甲醛吸附材料各原料，按重量份数计：活性炭100份，碳酸钙20份，乙醇40份，麦饭石15份，海泡石30份，甘氨酸25份，珍珠岩10份，硝酸钠3份，碳酸氢铵8份，二氧化钛4份，甲基纤维素5份，正磷酸铁15份，氯化镁15份，滑石粉15份。
有益效果：
采用本发明所述方法制得的甲醛吸附材料和现有技术相比，具有以下技术效果：1、产品甲醛去除率高达98-99.8%；2、耐磨性强，使用寿命长，可以重复使用，绿色环保；3、吸附速度快，吸附范围广，取本品放在甲醛含量400-500μg/m3密闭空间内40-48h后，甲醛浓度为1-8μg/m3；4、制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料； 5、本发明产品化学性质稳定，能够长期有效稳定地吸附缓慢释放的有害气体。
具体实施方式
下面结合实施例对本发明做进一步描述。
实施例1
按重量份数配比称取活性炭100份，碳酸钙10份，乙醇20份，麦饭石5份，海泡石20份，甘氨酸15份，珍珠岩1份，硝酸钠1份，碳酸氢铵6份，二氧化钛2份，甲基纤维素3份，正磷酸铁13份，氯化镁5份，滑石粉12份。
将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至60℃，搅拌30min，搅拌速度为800转/分钟。
将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在80℃下恒温干燥，然后再与上一步搅拌均匀的产物合并，混合2h，再将混合后的产物放入真空干燥箱中，在25℃下干燥过夜即可。
产品甲醛去除率高达98%；耐磨性强，使用寿命长，可以重复使用，绿色环保；吸附速度快，吸附范围广，取本品放在甲醛含量500μg/m3密闭空间内48h后，甲醛浓度为8μg/m3；制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料。
实施例2
按重量份数配比称取活性炭100份，碳酸钙30份，乙醇60份，麦饭石25份，海泡石40份，甘氨酸35份，珍珠岩20份，硝酸钠5份，碳酸氢铵10份，二氧化钛6份，甲基纤维素7份，正磷酸铁17份，氯化镁25份，滑石粉18份。
将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至80℃，搅拌70min，搅拌速度为1200转/分钟。
将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在120℃下恒温干燥，然后再与上一步搅拌均匀的产物合并，混合6h，再将混合后的产物放入真空干燥箱中，在45℃下干燥过夜即可。
产品甲醛去除率高达98.5%；耐磨性强，使用寿命长，可以重复使用，绿色环保；吸附速度快，吸附范围广，取本品放在甲醛含量500μg/m3密闭空间内40h后，甲醛浓度为6μg/m3；制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料。
实施例3
按重量份数配比称取活性炭100份，碳酸钙15份，乙醇30份，麦饭石10份，海泡石25份，甘氨酸20份，珍珠岩5份，硝酸钠2份，碳酸氢铵7份，二氧化钛3份，甲基纤维素4份，正磷酸铁14份，氯化镁10份，滑石粉13份。
将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至60℃，搅拌30min，搅拌速度为800转/分钟。
将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在80℃下恒温干燥，然后再与上一步搅拌均匀的产物合并，混合2h，再将混合后的产物放入真空干燥箱中，在25℃下干燥过夜即可。
产品甲醛去除率高达99%；耐磨性强，使用寿命长，可以重复使用，绿色环保；吸附速度快，吸附范围广，取本品放在甲醛含量450μg/m3密闭空间内44h后，甲醛浓度为5μg/m3；制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料。
实施例4
按重量份数配比称取活性炭100份，碳酸钙25份，乙醇50份，麦饭石20份，海泡石35份，甘氨酸30份，珍珠岩15份，硝酸钠4份，碳酸氢铵9份，二氧化钛5份，甲基纤维素6份，正磷酸铁16份，氯化镁20份，滑石粉17份。
将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至80℃，搅拌70min，搅拌速度为1200转/分钟。
将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在120℃下恒温干燥，然后再与上一步搅拌均匀的产物合并，混合6h，再将混合后的产物放入真空干燥箱中，在45℃下干燥过夜即可。
产品甲醛去除率高达99.5%；耐磨性强，使用寿命长，可以重复使用，绿色环保；吸附速度快，吸附范围广，取本品放在甲醛含量400μg/m3密闭空间内48h后，甲醛浓度为2μg/m3；制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料。
实施例5
按重量份数配比称取活性炭100份，碳酸钙20份，乙醇40份，麦饭石15份，海泡石30份，甘氨酸25份，珍珠岩10份，硝酸钠3份，碳酸氢铵8份，二氧化钛4份，甲基纤维素5份，正磷酸铁15份，氯化镁15份，滑石粉15份。
将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至70℃，搅拌50min，搅拌速度为1000转/分钟。
将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在100℃下恒温干燥，然后再与上一步搅拌均匀的产物合并，混合4h，再将混合后的产物放入真空干燥箱中，在35℃下干燥过夜即可。
产品甲醛去除率高达99.8%；耐磨性强，使用寿命长，可以重复使用，绿色环保；吸附速度快，吸附范围广，取本品放在甲醛含量500μg/m3密闭空间内40h后，甲醛浓度为1μg/m3；制备方法简单，成本低廉，操作性强，可以广泛生产并不断代替现有材料。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在和本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。

Claims (6)

1.一种甲醛快速吸附材料的制备方法，其特征在于：包括如下制备步骤：
第一步：称取活性炭、碳酸钙、乙醇、麦饭石、海泡石、甘氨酸、珍珠岩、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素、正磷酸铁、氯化镁和滑石粉；
第二步：将乙醇、甘氨酸、硝酸钠、碳酸氢铵、二氧化钛、甲基纤维素和正磷酸铁投入设有搅拌器和温度计的反应釜中，升温至60-80℃，搅拌30-70min，搅拌速度为800-1200转/分钟，制得搅拌均匀的混合物；
第三步：将活性炭、碳酸钙、麦饭石、海泡石、氯化镁和滑石粉在80-120℃下恒温干燥，然后再与第二步搅拌均匀的混合物合并，继续混合搅拌2-6h，搅拌速度为800-1200转/分钟；
第四步：将第三步混合后的产物放入真空干燥箱中，在25-45℃下干燥过夜即可。
2.根据权利要求1所述的一种甲醛快速吸附材料的制备方法，其特征在于：所述各原料按质量份数计，活性炭100份，碳酸钙10-30份，乙醇20-60份，麦饭石5-25份，海泡石20-40份，甘氨酸15-35份，珍珠岩1-20份，硝酸钠1-5份，碳酸氢铵6-10份，二氧化钛2-6份，甲基纤维素3-7份，正磷酸铁13-17份，氯化镁5-25份，滑石粉12-18份。
3.根据权利要求1所述的一种甲醛快速吸附材料的制备方法，其特征在于：所述各原料按质量份数计，活性炭100份，碳酸钙15-25份，乙醇30-50份，麦饭石10-20份，海泡石25-35份，甘氨酸20-30份，珍珠岩5-15份，硝酸钠2-4份，碳酸氢铵7-9份，二氧化钛3-5份，甲基纤维素4-6份，正磷酸铁14-16份，氯化镁10-20份，滑石粉13-17份。
4.根据权利要求1所述的一种甲醛快速吸附材料的制备方法，其特征在于：所述各原料按质量份数计，活性炭100份，碳酸钙15份，乙醇30份，麦饭石10份，海泡石25份，甘氨酸20份，珍珠岩5份，硝酸钠2份，碳酸氢铵7份，二氧化钛3份，甲基纤维素4份，正磷酸铁14份，氯化镁10份，滑石粉13份。
5.根据权利要求1所述的一种甲醛快速吸附材料的制备方法，其特征在于：所述各原料按质量份数计，活性炭100份，碳酸钙25份，乙醇50份，麦饭石20份，海泡石35份，甘氨酸30份，珍珠岩15份，硝酸钠4份，碳酸氢铵9份，二氧化钛5份，甲基纤维素6份，正磷酸铁16份，氯化镁20份，滑石粉17份。
6.根据权利要求1所述的一种甲醛快速吸附材料的制备方法，其特征在于：所述各原料按质量份数计，活性炭100份，碳酸钙20份，乙醇40份，麦饭石15份，海泡石30份，甘氨酸25份，珍珠岩10份，硝酸钠3份，碳酸氢铵8份，二氧化钛4份，甲基纤维素5份，正磷酸铁15份，氯化镁15份，滑石粉15份。
CN201611250677.6A 2016-12-30 2016-12-30 一种甲醛快速吸附材料的制备方法 Pending CN106492766A (zh)