CN106474819A - A kind of gas filtration cotton containing graphene oxide and preparation method thereof - Google Patents
A kind of gas filtration cotton containing graphene oxide and preparation method thereof Download PDFInfo
- Publication number
- CN106474819A CN106474819A CN201610924946.6A CN201610924946A CN106474819A CN 106474819 A CN106474819 A CN 106474819A CN 201610924946 A CN201610924946 A CN 201610924946A CN 106474819 A CN106474819 A CN 106474819A
- Authority
- CN
- China
- Prior art keywords
- graphene oxide
- filter cotton
- cotton
- preparation
- gas filtration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of gas filtration cotton containing graphene oxide of the present invention, is made up of filter cotton, contains graphene oxide in filter cotton.Additionally provide the preparation method of above-mentioned gas filter cotton, including one prepare graphene oxide solution the step of, graphite oxide is prepared using chemical oxidization method, after washing to neutrality, ultrasound peel off, obtain graphene oxide dispersion;The step of one immersion filtration cotton, filter cotton impregnated in the graphene oxide dispersion of gained, dispersion liquid did not at least have filter cotton;The step of one freezing, the filter cotton of gained is placed in the freezing chamber of freeze drier so as to be solidified as solid;The step of one drying, the filter cotton of gained is vacuumized, and is kept low temperature so that solvent is distilled, is obtained the gas filtration cotton containing graphene oxide.The filter cotton of the present invention with the toxic gas in oxidation air, purify air, and can increase specific surface area, improve absorption property, can adsorb the tiny particles contents such as the PM2.5 of in the air.
Description
Technical field
The invention belongs to materialogy field, is related to a kind of filter cotton, a kind of specifically gas containing graphene oxide
Body filter cotton and preparation method thereof.
Background technology
Although nowadays the trend of air pollution is suppressed under the improvement energetically of country, the air of China part
Still the health to human body constitutes a certain degree of threat, and especially the case of PUD D is more and more.The scope of activities of people
Mainly family and workplace, it is contemplated that maintain excellent air quality, need to carry out certain air circulation, and to circulation
Air carries out filtration, purification, and this is accomplished by using filter cotton.The mainly pure filter cotton that now applies on the market, in order to dust-proof or
Activated carbon filter cotton filtration fraction pernicious gas.
Activated carbon filter cotton is carrier using the aluminium honeycomb of through-hole structure, plastic honeycomb, paper honeycomb, it is adaptable to air filtration
System fine filtering and high efficiency particulate air filter are filtered.Its suitable carrier scope is narrower, and it cannot be guaranteed that can be uniformly dispersed in load
In body, it is difficult and carrier collaborative filtering gas, and its activated carbon dosage is more, it is also contemplated that the combination degree with carrier, these
The use of activated carbon filter cotton is all limited.It is thus desirable to exploitation one kind more efficient evenly can be disperseed in the carrier, carrier
The scope of application is wider, and quality is lighter, it is possible to act synergistically with carrier, resource-effective filter cotton packing material.
Presently disclosed patent mainly has:
A kind of activated carbon filter cotton of the Yu Xiaodong invention of Fengqiao Purifying Equipment Factory, xin District, Suzhou, the patent No. 201410036615,
The patent is uniformly distributed in activated carbon granule inside filter cotton, and the top surface of filter cotton and bottom surface are all bonded with protection film layer.
In activated carbon filter cotton obtained in the method, the degree that is evenly distributed of activated carbon is relatively low, and is combined defective tightness with filter cotton.
The novel absorbent charcoal fiber filter cotton of Yang Jianjun of Jiangsu Kejing Carbon Fiber Co., Ltd. et al. invention, the patent No.
201320102790, the patent filter cotton includes upper and lower terylene layers, arranges 1-2 layer between upper and lower terylene layers
Activated carbon fiber layers.The method preparation technology needs interlayer to arrange activated carbon fiber layers, it is impossible to effectively cooperateed with layers
Filter.
A kind of efficient air filter wool of the Lv Zesheng invention of Hangzhou DEESTAR Fiber Technology Co., Ltd., the patent No.
201020290772.Filter cotton in the patent includes upright cotton layer, and its bottom surface is compounded with layer of meltblown fibers, described upright cotton
Layer is that the compound layer of meltblown fibers in bottom surface is ultra-fine fiber construction through cuing open the upright cotton of layer process, in order to catch dust granules
Filtration, the filter cotton need to add new operation in filter cotton preparation technology, increased preparation complexity, and not
Can effective filtering poisonous gas.
A kind of New type filtering cotton of the Wang Zheng invention of Dongguan Lianying Cotton Products Co., Ltd, the patent No.
200820178490.The New type filtering cotton includes acupuncture cotton and fibrefill, acupuncture cotton and fibrefill multilayer cross lamination, its
Fibrefill is terylene, and the method effectively can not be filtered to pernicious gas.
In sum, current filter cotton all exist can not effectively filtering noxious gas, or filler skewness,
Can not be with the problem of carrier cooperation-removal pollutant.Therefore little in the urgent need to seeking a kind of bulk density, specific surface area is big, absorption
Efficiency high, can be widely used for processing containing the organic gas for being unfavorable for health and working environment and containing dust and micro
The filter cotton of all kinds of gases of heavy metal, or Adsorption Concentration can be carried out to waste gas, purify after the filter cotton that directly can discharge.
This preparation technology is namely based on these theories and researches and develops making.
Content of the invention
For above-mentioned technical problem of the prior art, the invention provides a kind of gas filtration containing graphene oxide
Cotton and preparation method thereof, described this gas filtration cotton containing graphene oxide and preparation method thereof prior art to be solved
In the filtering noxious gas of filter cotton effect on driving birds is not good technical problem.
The invention provides a kind of gas filtration cotton containing graphene oxide, is made up of filter cotton, described filter cotton
In contain graphene oxide.
Present invention also offers a kind of preparation method of above-mentioned gas filtration cotton containing graphene oxide, including as follows
Step:
The step of (1) preparation graphene oxide solution, graphite oxide is prepared using chemical oxidization method, after washing to neutrality,
Ultrasound is peeled off, and obtains graphene oxide dispersion;
The step of (2) immersion filtration cottons, filter cotton impregnated in step(1)In the graphene oxide dispersion of gained, point
Dispersion liquid there at least was not filter cotton;
The step of (3) freezings, by step(2)The filter cotton of gained is placed in the freezing chamber of freeze drier so as to solidified
For solid;
The step of (4) dryings, by step(3)The filter cotton of gained is vacuumized, and is kept low temperature so that solvent is distilled, is contained
There is the gas filtration cotton of graphene oxide.
Further, in the step of described preparation graphene oxide solution, by natural flake graphite be added to sulphur
Acid and phosphoric acid volume ratio are 9:In the nitration mixture of 1 composition, mix in autoclave, the matter of natural flake graphite and nitration mixture
Amount volume ratio is 0.1-1g:50ml, is slowly added to potassium permanganate, potassium permanganate and natural scale stone under conditions of less than 20 DEG C
The mass ratio of ink is 1-5g:0.1-1g, sealed reactor, after being warming up to 50-80 DEG C of 3 ~ 9h of reaction, room temperature is cooled to, by product
4 ~ 6 times of volume is taken out and is diluted to from reactor, is subsequently adding hydrogen peroxide, described hydrogen peroxide and natural flake graphite
Mass volume ratio is 10ml:0.1-1g;Obtain jonquilleous graphite oxide solution;Then it is more than 5% watery hydrochloric acid pickling with mass fraction
After washing, then deionized water centrifuge washing, it is 5 ~ 7 to supernatant pH, ultrasonic disperse graphite oxide, ultrasonic power 100-200W,
Obtain graphene oxide dispersion.
Further, the pressure in described autoclave is 10MPa≤p < 100.0MPa.
Further, the mass percent concentration of described sulfuric acid is 70 ~ 98%;The percent mass of described phosphosulfate
Specific concentration is 80 ~ 98%.
Further, the step(2)In, the concentration of graphene oxide dispersion is 0.01-2mg/ml, solvent for use for go from
Sub- water or salting liquid.
Further, described filter cotton is marketed synthetic fibers filter cotton, non-woven fabrics filter cotton, glass fibre
Filter cotton, activated carbon filter cotton, or self-control filter cotton.
Further, cryogenic temperature is less than 0 DEG C.
Further, vacuum is vacuumized less than 100Pa, keeping temperature is less than room temperature.
The present invention is prepared after graphite oxide using chemical method, is washed to neutrality, and ultrasound obtains certain density oxygen after peeling off
Graphite alkene dispersion liquid, filter cotton is impregnated in suspension, freeze-drying, you can is obtained cotton-shaped graphene oxide and is uniformly filled
Graphene oxide filter cotton inside filter cotton.As graphene oxide contains abundant oxygen-containing functional group, by above-mentioned side
The filter cotton that method is obtained with the toxic gas in oxidation air, purify air, and can increase specific surface area, improve filter cotton
Filter effect and absorption property, the tiny particles contents such as the PM2.5 of in the air can be adsorbed, can be widely applied to air cleaning,
In the industries such as mouth mask making.
The present invention is compared with prior art, and its technological progress is significant.The filter cotton filler bulk density of the present invention
Little, specific surface area is big, adsorption efficiency is high, and filling is uniform and is tightly combined with carrier, can be widely used for processing containing being unfavorable for people
Body health and organic gas and all kinds of gases containing dust and micro heavy of working environment.The filter cotton can be to useless
Gas carry out Adsorption Concentration, purify after directly can discharge.
Description of the drawings
Fig. 1 is the structural representation of the graphene oxide filter cotton of the present invention.
Fig. 2 is the SEM figure of the cotton-shaped graphene oxide of the present invention.
Specific embodiment
With reference to embodiment to the detailed description of the invention, so that those skilled in the art more fully understand the present invention, but
The invention is not limited in following case study on implementation.
SEM used by the present invention (ESEM) adopts Philips XL30 type electron microscope.
Embodiment 1
(1) graphene oxide is prepared:0.5g natural flake graphite and the 50ml concentrated sulfuric acid/SPA volume ratio are 9:1 composition
Nitration mixture is mixed in autoclave, is slowly added to 4g potassium permanganate, sealed reactor, liter under conditions of less than 20 DEG C
Temperature is cooled to room temperature, product is taken out from reactor and is diluted to 200ml, be subsequently adding 10ml dioxygen to 80 DEG C of reaction 3h
Water obtains jonquilleous graphite oxide solution;Then with mass fraction more than after 5% watery hydrochloric acid acid elution 5 times, deionized water is centrifuged
Washing, is 5 ~ 7 to supernatant pH, ultrasonic disperse graphite oxide 2h, ultrasonic power 200W.Obtain graphene oxide dispersion;
(2) immersion filtration cotton:Activated carbon filter cotton impregnated in concentration for, in 0.01mg/ml dispersion liquid, dispersion liquid did not had synthesis fine
Dimensional filter cotton;
(3) freeze:Step(2)After gained dipping, filter cotton is placed in the freezing chamber of freeze drier, and -50 DEG C are solidified as which
Solid.
(4) dry:Vacuumize, vacuum is less than 10Pa, and 0 DEG C is kept below, low temperature makes solvent distil, obtain aoxidizing stone
Black alkene filter cotton.
Embodiment 2
(1) graphene oxide is prepared:Take embodiment 1 and obtain graphene oxide dispersion;
(2) immersion filtration cotton:Non-woven fabrics filter cotton impregnated in concentration for, in 0.1mg/ml dispersion liquid, dispersion liquid did not had synthesis fine
Dimensional filter cotton.
(3) freeze:Step(2)After gained dipping, filter cotton is placed in the freezing chamber of freeze drier, and -50 DEG C coagulate which
Admittedly it is solid.
(4) dry:Vacuumize, vacuum is less than 10Pa, so that solvent is distilled under room temperature, obtain graphene oxide filter cotton.
Embodiment 3
(1) graphene oxide is prepared:Take embodiment 1 and obtain graphene oxide dispersion;
(2) immersion filtration cotton:Glass fiber filter cotton impregnated in concentration for, in 1mg/ml dispersion liquid, dispersion liquid did not had synthesis fine
Dimensional filter cotton.
(3) freeze:Step(2)After gained dipping, filter cotton is placed in the freezing chamber of freeze drier, and -20 DEG C coagulate which
Admittedly it is solid;
(4) dry:Vacuumize, vacuum is less than 10Pa, so that solvent is distilled under room temperature, obtain graphene oxide filter cotton.
Embodiment 4
(1) graphene oxide is prepared:Take embodiment 1 and obtain graphene oxide dispersion;
(2) immersion filtration cotton:Synthetic fibers filter cotton impregnated in concentration for, in 2mg/ml dispersion liquid, dispersion liquid did not had synthesis fine
Dimensional filter cotton.
(3) freeze:Step(2)After gained dipping, filter cotton is placed in the freezing chamber of freeze drier, and -20 DEG C coagulate which
Admittedly it is solid;
(4) dry:Vacuumize, keep low temperature so that solvent is distilled, obtain graphene oxide filter cotton.
Embodiments of the invention are the foregoing is only, the scope of the claims of the present invention is not thereby limited, every using this
Equivalent structure or equivalent flow conversion that bright specification is made, or other related technical fields are directly or indirectly used in, all
It is included within the scope of the present invention in the same manner.
Claims (8)
1. a kind of gas filtration cotton containing graphene oxide, it is characterised in that:It is made up of filter cotton, contains in described filter cotton
There is graphene oxide.
2. the preparation method of a kind of gas filtration cotton containing graphene oxide described in claim 1, it is characterised in that include
Following steps:
The step of (1) preparation graphene oxide solution, graphite oxide is prepared using chemical oxidization method, after washing to neutrality,
Ultrasound is peeled off, and obtains graphene oxide dispersion;
The step of (2) immersion filtration cottons, filter cotton impregnated in step(1)In the graphene oxide dispersion of gained, point
Dispersion liquid there at least was not filter cotton;
The step of (3) freezings, by step(2)The filter cotton of gained is placed in the freezing chamber of freeze drier so as to solidified
For solid;
The step of (4) dryings, by step(3)The filter cotton of gained is vacuumized, and is kept low temperature so that solvent is distilled, is contained
There is the gas filtration cotton of graphene oxide.
3. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 2, it is characterised in that:?
In the step of described preparation graphene oxide solution, by natural flake graphite with to be added to sulfuric acid and phosphoric acid volume ratio be 9:1
In the nitration mixture of composition, mix in autoclave, the mass volume ratio of natural flake graphite and nitration mixture is 0.1-1g:
50ml, is slowly added to potassium permanganate under conditions of less than 20 DEG C, and the mass ratio of potassium permanganate and natural flake graphite is 1-5g:
0.1-1g, sealed reactor, after being warming up to 50-80 DEG C of 3 ~ 9h of reaction, room temperature is cooled to, product is taken out from reactor and is diluted
To 4 ~ 6 times of volume, hydrogen peroxide is subsequently adding, the mass volume ratio of described hydrogen peroxide and natural flake graphite is 10ml:
0.1-1g;Obtain jonquilleous graphite oxide solution;Then it is more than after 5% watery hydrochloric acid acid elution with mass fraction, then deionized water
Centrifuge washing, is 5 ~ 7 to supernatant pH, ultrasonic disperse graphite oxide, and ultrasonic power 100-200W obtains graphene oxide dispersion
Liquid.
4. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 3, it is characterised in that:Institute
The mass percent concentration of the sulfuric acid that states is 70 ~ 98%;The mass percent concentration of described phosphosulfate is 80 ~ 98%.
5. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 2, it is characterised in that:Institute
State step(2)In, the concentration of graphene oxide dispersion is 0.01-2mg/ml, and solvent for use is deionized water or salting liquid.
6. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 2, it is characterised in that:Institute
The filter cotton that states be marketed synthetic fibers filter cotton, non-woven fabrics filter cotton, glass fiber filter cotton, activated carbon filter
Cotton, or self-control filter cotton.
7. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 2, it is characterised in that:Cold
Freeze temperature and be less than 0 DEG C.
8. a kind of preparation method of the gas filtration cotton containing graphene oxide as claimed in claim 2, it is characterised in that:Take out
Vacuum vacuum is less than 100Pa, and keeping temperature is less than room temperature.