CN106400086A - 一种水溶性封闭剂配方 - Google Patents

一种水溶性封闭剂配方 Download PDF

Info

Publication number
CN106400086A
CN106400086A CN201610897653.3A CN201610897653A CN106400086A CN 106400086 A CN106400086 A CN 106400086A CN 201610897653 A CN201610897653 A CN 201610897653A CN 106400086 A CN106400086 A CN 106400086A
Authority
CN
China
Prior art keywords
parts
water
agent
soluble
weight portion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610897653.3A
Other languages
English (en)
Inventor
时乾中
王子俊
肖翔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Taitong Refrigeration Technology Co Ltd
Original Assignee
Hefei Taitong Refrigeration Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Taitong Refrigeration Technology Co Ltd filed Critical Hefei Taitong Refrigeration Technology Co Ltd
Priority to CN201610897653.3A priority Critical patent/CN106400086A/zh
Publication of CN106400086A publication Critical patent/CN106400086A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水10‑20份，分散剂20‑30份，成膜助剂5‑10份，乙二醇15‑30份，钛白粉20‑40份、抑泡剂1‑3份、增稠剂1‑4份、消泡剂1‑3份、水性聚氨酯分散体12‑17份、二氧化硅7‑9份。发明的目的是提供一种具有环保且抗腐蚀性好的水溶性封闭剂配方，封闭有后流色轻，色差变化小。

Description

一种水溶性封闭剂配方
技术领域
本发明属铝合金阳极氧化膜后处理技术领域，具体为一种水溶性封闭剂配方。
背景技术
铝及其合金材料是有色金属中使用量最大，应用面最广的金属材料，因其具有一系列优良的物理、化学、力学和加工性能，可以满足从餐厨用具到尖端科技，从建筑装潢到交通运输和航空航天等各行各业对于铝合金材料提出的千差万别、 各不相同的使用要求。但铝的某些应用性能如硬度、耐磨性和耐腐蚀性还不大理想，表面处理技术正好弥补了这些弱点。铝及其合金的阳极氧化处理是改善其应用性能的最佳表面处理技术，铝阳极氧化膜的封闭就是采用物理或化学的方法将纳米孔洞阻塞，从而降低膜的隙率及其吸附性能，改善膜的硬度和抗腐蚀性。沸水或高温蒸汽封孔、铬酸盐封孔和镍盐钴盐封孔是当前较为成熟的封闭技术，但是由于污染问题目前应用已经很少。铬酸盐封闭也是应用较早的一项阳极氧化封闭技术，其原理与水合封闭不尽相同，却与铝合金化学转化成膜的机理有相似之处，铬酸盐与氧化铝的化学反应产物阻塞纳米孔的同时，还在膜表面生成薄薄的一层致密铬化膜，但铬酸盐具有高毒性，所以该技术的应用也已很少。
发明内容
本发明的目的是克服现有技术的不足，提供一种无毒环保的水溶性封闭剂配方。
为了实现上述目的本发明采用如下技术方案：
一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水10-20份，分散剂20-30份，成膜助剂5-10份， 乙二醇15-30份， 钛白粉20-40份、抑泡剂1-3份、增稠剂1-4份、消泡剂1-3份、水性聚氨酯分散体12-17份、二氧化硅7-9份。
所述的抑泡剂由改性聚硅氧烷、改性醇酸树脂、聚酯树脂中的一种或多种。
所述的消泡剂由硅油和高级醇按照重量份1:1混合。
与已有技术相比，本发明的有益效果如下：
本发明的一种水溶性封闭剂配方，不含金属镍、镁、钙、锂盐及氟离子的环境友好型水溶性封闭剂，能广泛适用于本色阳极氧化膜、电解着色阳极氧化膜、硬质氧化膜以及染色阳极氧化膜的封孔处理，从而解决当前铝合金阳极氧化膜含金属盐封闭体系存在的环境污染、封孔膜层品级和封孔剂成本等诸多问题。
具体实施方式
下面结合实施例对本发明作进一步的描述，但本发明不仅限于这些实例，在为脱离本发明宗旨的前提下，所为任何改进均落在本发明的保护范围之内。
实施例1：
一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水10份，分散剂20份，成膜助剂5份， 乙二醇15份， 钛白粉20份、聚硅氧烷1份、增稠剂1份、硅油1份、高级醇1份、水性聚氨酯分散体12份、二氧化硅7份。
实施例2：
一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水20份，分散剂30份，成膜助剂10份， 乙二醇30份， 钛白粉40份、水性聚氨酯分散体3份、增稠剂4份、硅油和高级醇各3份、水性聚氨酯分散体17份、二氧化硅9份。
实施例3：
一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水15份，分散剂25份，成膜助剂7份， 乙二醇20份， 钛白粉30份、聚酯树脂2份、增稠剂3份、硅油和高级醇各2份、水性聚氨酯分散体15份、二氧化硅8份。

Claims (3)

1.一种水溶性封闭剂配方，由以下重量份的原料组成：去离子水10-20份，分散剂20-30份，成膜助剂5-10份， 乙二醇15-30份， 钛白粉20-40份、抑泡剂1-3份、增稠剂1-4份、消泡剂1-3份、水性聚氨酯分散体12-17份、二氧化硅7-9份。
2.根据权利要求1所述的一种水溶性封闭剂配方，其特征在于：所述的抑泡剂由改性聚硅氧烷、改性醇酸树脂、聚酯树脂中的一种或多种。
3.根据权利要求1所述的一种水溶性封闭剂配方，其特征在于：所述的消泡剂由硅油和高级醇按照重量份1:1混合。
CN201610897653.3A 2016-10-16 2016-10-16 一种水溶性封闭剂配方 Pending CN106400086A (zh)