CN102312264B - 铝及铝合金的装饰性氧化法 - Google Patents

铝及铝合金的装饰性氧化法 Download PDF

Info

Publication number
CN102312264B
CN102312264B CN 201110240298 CN201110240298A CN102312264B CN 102312264 B CN102312264 B CN 102312264B CN 201110240298 CN201110240298 CN 201110240298 CN 201110240298 A CN201110240298 A CN 201110240298A CN 102312264 B CN102312264 B CN 102312264B
Authority
CN
China
Prior art keywords
cleaning
oxidation
aluminum
current density
hard anodizing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN 201110240298
Other languages
English (en)
Other versions
CN102312264A (zh
Inventor
谢利荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wujiang Fine Workmanship and Aluminum Word Manufactory
Original Assignee
Wujiang Fine Workmanship and Aluminum Word Manufactory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wujiang Fine Workmanship and Aluminum Word Manufactory filed Critical Wujiang Fine Workmanship and Aluminum Word Manufactory
Priority to CN 201110240298 priority Critical patent/CN102312264B/zh
Publication of CN102312264A publication Critical patent/CN102312264A/zh
Application granted granted Critical
Publication of CN102312264B publication Critical patent/CN102312264B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其特征在于：硬质阳极氧化步骤的氧化液是：草酸20-50g/L、乙二醇 30-50g/L、硼酸1-10 g/L、硫酸铵0.1-1g/L、磺酸铵0.1-1g/L；硬质阳极氧化步骤工艺参数是：温度10-25℃、电压起始0-50V，最终大于100V、阳极电流密度2.5-3.0A/dm2，时间50-70min，阴极材料是铅板，阳极移动25-30次/min。本发明获得的膜层呈黄色，细腻、致密，硬度达到HV450-700，厚度达到40-50微米，可以连续生产。

Description

铝及铝合金的装饰性氧化法
技术领域
    本发明涉及一种铝及铝合金的装饰性氧化法，具体地讲是涉及铝及铝合金的阳极氧化法。属于铝合金的表面处理工艺。
背景技术
铝及铝合金的装饰性氧化法种类很多，一般可以分为化学氧化法和电化学氧化法即阳极氧化法两大类，其中后者应用更为广泛，因为阳极氧化法所获得的氧化膜比一切化学氧化法所获得的氧化膜性能更优良。一般而言阳极氧化法所获得的氧化膜光洁、光亮、透明度较高，再经过染色，可以得到各种色彩鲜艳夺目的表面。
发明内容
本发明所要解决的技术问题是提供一种铝及铝合金的装饰性氧化法，能获得细腻、致密、高硬度的膜层。
为解决上述技术问题，本发明是这样实现的 
一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其特征在于：硬质阳极氧化步骤的氧化液是：草酸20-50g/L、乙二醇   30-50 g/L、硼酸1-10  g/L、硫酸铵 0.1-1g/L、磺酸铵0.1-1g/L；硬质阳极氧化步骤工艺参数是：温度 10-25℃、电压起始0-50V，最终大于100V、阳极电流密度2.5-3.0A/dm2，时间50-70min，阴极材料是铅板，阳极移动 25-30次/min。
草酸浓度太低，则氧化膜薄，浓度太高，则膜层疏松，能被溶解掉。
电解液的温度对膜层的硬度和耐磨性影响很大，通常，温度下降硬度和耐磨性能增强。
阳极电流密度和成膜速度有关，提高电流密度则成膜速度加快，氧化时间缩短，但超过极限电流密度时，氧化时发热加大，则膜层硬度降低。
本发明有以下积极的效果：本发明获得的膜层呈黄色，细腻、致密，硬度达到HV450-700，厚度达到40-50微米，可以连续生产。
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
以下实施例的试件为表面积为0.25dm2 的工业纯铝板。
实施例1
一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层。
硬质阳极氧化步骤的氧化液是：草酸20g/L、乙二醇 30 g/L、硼酸1 g/L、硫酸铵 0.1g/L、磺酸铵0.1g/L；
硬质阳极氧化步骤工艺参数是：温度 10℃、电压起始0-50V，最终大于100V、阳极电流密度2.5A/dm2，30s内将电流密度升至预定初始电流后，让电流和电压随着氧化过程的进行自动变化，时间70min，阴极材料是铅板，阳极移动 30次/min。电解液用循环水冷却。
获得的膜层呈黄色，细腻、致密，硬度达到HV470，厚度达到40微米，可以连续生产。
实施例2
一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层。
硬质阳极氧化步骤的氧化液是：草酸30g/L、乙二醇 40 g/L、硼酸3 g/L、硫酸铵 0.5g/L、磺酸铵0.4g/L；
硬质阳极氧化步骤工艺参数是：温度 15℃、电压起始20V，最终大于100V、阳极电流密度3.0A/dm2，30s内将电流密度升至预定初始电流后，让电流和电压随着氧化过程的进行自动变化，时间60min，阴极材料是铅板，阳极移动 26次/min。电解液用循环水冷却。
获得的膜层呈黄色，细腻、致密，硬度达到HV540，厚度达到42微米，可以连续生产。
实施例3
一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层。
硬质阳极氧化步骤的氧化液是：草酸50g/L、乙二醇 50 g/L、硼酸10 g/L、硫酸铵 1g/L、磺酸铵1g/L；
硬质阳极氧化步骤工艺参数是：温度 25℃、电压起始50V，最终大于100V、阳极电流密度3.0A/dm2，30s内将电流密度升至预定初始电流后，让电流和电压随着氧化过程的进行自动变化，时间50min，阴极材料是铅板，阳极移动 28次/min。电解液用循环水冷却。
获得的膜层呈黄色，细腻、致密，硬度达到HV680，厚度达到45微米，可以连续生产。
上述具体实施方式不以任何形式限制本发明的技术方案，凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。

Claims (1)

1.一种铝及铝合金的装饰性氧化法，铝制件经化学除油、清洗、中和、清洗、硬质阳极氧化、清洗、封闭后得到膜层，其特征在于：硬质阳极氧化步骤的氧化液是：草酸20-50g/L、乙二醇   30-50 g/L、硼酸1-10  g/L、硫酸铵 0.1-1g/L、磺酸铵0.1-1g/L；硬质阳极氧化步骤工艺参数是：温度 10-25℃、电压起始0-50V，最终大于100V、阳极电流密度2.5-3.0A/dm2，30s内将电流密度升至预定初始电流后，让电流和电压随着氧化过程的进行自动变化,时间50-70min，阴极材料是铅板，阳极移动 25-30次/min。
CN 201110240298 2011-08-22 2011-08-22 铝及铝合金的装饰性氧化法 Active CN102312264B (zh)