CN106381054A - Vacuum circuit breaker surface special-purpose heatproof paint - Google Patents
Vacuum circuit breaker surface special-purpose heatproof paint Download PDFInfo
- Publication number
- CN106381054A CN106381054A CN201610766957.6A CN201610766957A CN106381054A CN 106381054 A CN106381054 A CN 106381054A CN 201610766957 A CN201610766957 A CN 201610766957A CN 106381054 A CN106381054 A CN 106381054A
- Authority
- CN
- China
- Prior art keywords
- parts
- circuit breaker
- vacuum circuit
- paint
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to vacuum circuit breaker surface special-purpose heatproof paint. The vacuum circuit breaker surface special-purpose heatproof paint comprises, by weight, 140-170 parts of methyl phenyl silicone resin, 30-50 parts of a polymer resin emulsion, 12-19 parts of glycol, 4-9 parts of pearl powder, 1-5 parts of a dispersant, 2-9 parts of polydimethylsiloxane, 3-7 parts of polydimethylphenylsiloxane, 2-6 parts of an anti-settling agent, 3-8 parts of powdered steatile, 1-5 parts of heavy calcium powder, 2-6 parts of organic bentonite, 0.7-2.1 parts of a dispersant and 19-25 parts of water. The heatproof paint utilizes less materials, has a low preparation cost, has good heat resistance, realizes normal work of a vacuum circuit breaker in various high temperature complex environments, and has stable work performances and good quality.
Description
Technical field
The present invention relates to coating, the special heat-resisting paint in specifically a kind of vacuum circuit breaker surface.
Background technology
Coating is that one kind is coated body surface and formed film under certain condition and play protection, decorate and specific
One class I liquid I of effect or fixing material, with expanding economy, coating obtains in industrial or agricultural, national defence, scientific research and people's lives
To being increasingly widely applied.With the continuous development of electric utility, such as vacuum contactor, low-vacuum load-tripping device, vacuum circuit breaker
Coating has also been used on the electrical equipment surfaces such as device, high-voltage switch gear, air insulated phase-change switch, and what these electric parts had works in
Under various complexity hot environments, because coating does not have good heat resistance, electric parts internal stability is led to increase, impact is just
Often use.
Content of the invention
For above-mentioned technical problem, the present invention provides a kind of vacuum circuit breaker surface special heat-resisting paint, prepares material
Point few, preparation cost is low, heat resistance good so that vacuum circuit breaker under various high temperature complex environments can with normal work,
Stable work in work, quality is good.
The technical problem to be solved employs the following technical solutions to realize：
A kind of special heat-resisting paint in vacuum circuit breaker surface, this heat-resisting paint is grouped into by the group of following weight portion：Methyl
Phenyl polysiloxane 140-170 part, macromolecule resin emulsion 30-50 part, ethylene glycol 12-19 part, pearl essence 4-9 part, dispersant 1-5
Part, dimethyl silicone polymer 2-9 part, polydimethyl phenyl siloxane 3-7 part, anti-settling agent 2-6 part, talcum powder 3-8 part, dicalcium powder
1-5 part, organobentonite 2-6 part, dispersant 0.7-2.1 part and water 19-25 part.
A kind of special heat-resisting paint in vacuum circuit breaker surface, this heat-resisting paint is grouped into by the group of following optimum weight part：
155 parts of methyl phenyl silicone resin, 40 parts of macromolecule resin emulsion, 16 parts of ethylene glycol, 6 parts of pearl essence, 3 parts of dispersant, poly- diformazan
5 parts of radical siloxane, 5 parts of polydimethyl phenyl siloxane, 4 parts of anti-settling agent, 6 parts of talcum powder, 3 parts of dicalcium powder, organobentonite 4
Part, 1.4 parts of dispersant and 22 parts of water.
As a preferred technical solution of the present invention, described water type is distilled water.
The invention has the beneficial effects as follows：Compared to existing technology, material composition prepared by the heat-resisting paint that the present invention prepares
Few, preparation cost is low, and heat resistance is good so that vacuum circuit breaker can be with normal work under various high temperature complex environments, work
Make stable performance, quality is good.
Specific embodiment
In order that the technological means of present invention realization and creation characteristic are easy to understand, below the present invention is explained further
State.
Embodiment one：
A kind of special heat-resisting paint in vacuum circuit breaker surface, this heat-resisting paint is grouped into by the group of following weight portion：Methyl
140 parts of phenyl polysiloxane, 30 parts of macromolecule resin emulsion, 12 parts of ethylene glycol, 4 parts of pearl essence, 1 part of dispersant, poly dimethyl silicon
2 parts of oxygen alkane, 3 parts of polydimethyl phenyl siloxane, 2 parts of anti-settling agent, 3 parts of talcum powder, 1 part of dicalcium powder, organobentonite 2 part, point
0.7 part of powder and 19 parts of water.
Described water type is distilled water.
Embodiment two：
A kind of special heat-resisting paint in vacuum circuit breaker surface, this heat-resisting paint is grouped into by the group of following weight portion：Methyl
155 parts of phenyl polysiloxane, 40 parts of macromolecule resin emulsion, 16 parts of ethylene glycol, 6 parts of pearl essence, 3 parts of dispersant, poly dimethyl silicon
5 parts of oxygen alkane, 5 parts of polydimethyl phenyl siloxane, 4 parts of anti-settling agent, 6 parts of talcum powder, 3 parts of dicalcium powder, organobentonite 4 part, point
1.4 parts of powder and 22 parts of water.
Described water type is distilled water.
Embodiment three：
A kind of special heat-resisting paint in vacuum circuit breaker surface, this heat-resisting paint is grouped into by the group of following weight portion：Methyl
170 parts of phenyl polysiloxane, 50 parts of macromolecule resin emulsion, 19 parts of ethylene glycol, 9 parts of pearl essence, 5 parts of dispersant, poly dimethyl silicon
9 parts of oxygen alkane, 7 parts of polydimethyl phenyl siloxane, 6 parts of anti-settling agent, 8 parts of talcum powder, 5 parts of dicalcium powder, organobentonite 6 part, point
2.1 parts of powder and 25 parts of water.
Described water type is distilled water.
By implementing one, implementing two and implementing the heat-resisting paint for preparing of three each compositions, compared to existing technology in general
Logical coating, it is few to prepare material composition, and preparation cost is low, and heat resistance is good so that vacuum circuit breaker is in the complicated ring of various high temperature
Can be with normal work under border, stable work in work, quality is good.
General principle, principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
The simply present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and specification for the personnel
Principle, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these change and
Improvement both falls within scope of the claimed invention.Claimed scope is by appending claims and its equivalent
Thing defines.
Claims (3)
1. a kind of special heat-resisting paint in vacuum circuit breaker surface it is characterised in that：This heat-resisting paint is by the component of following weight portion
Composition：Methyl phenyl silicone resin 140-170 part, macromolecule resin emulsion 30-50 part, ethylene glycol 12-19 part, pearl essence 4-9 part,
Dispersant 1-5 part, dimethyl silicone polymer 2-9 part, polydimethyl phenyl siloxane 3-7 part, anti-settling agent 2-6 part, talcum powder 3-8
Part, dicalcium powder 1-5 part, organobentonite 2-6 part, dispersant 0.7-2.1 part and water 19-25 part.
2. a kind of special heat-resisting paint in vacuum circuit breaker surface according to claim 1 it is characterised in that：This heat-resisting paint
It is grouped into by the group of following optimum weight part：155 parts of methyl phenyl silicone resin, 40 parts of macromolecule resin emulsion, 16 parts of ethylene glycol,
6 parts of pearl essence, 3 parts of dispersant, 5 parts of dimethyl silicone polymer, 5 parts of polydimethyl phenyl siloxane, 4 parts of anti-settling agent, talcum powder 6
Part, 3 parts of dicalcium powder, 4 parts of organobentonite, 1.4 parts of dispersant and 22 parts of water.
3. a kind of special heat-resisting paint in vacuum circuit breaker surface according to claim 1 and 2 it is characterised in that：Described
Water type is distilled water.