CN106379010A - 一种扇面用抗菌面料 - Google Patents

一种扇面用抗菌面料 Download PDF

Info

Publication number
CN106379010A
CN106379010A CN201610782752.7A CN201610782752A CN106379010A CN 106379010 A CN106379010 A CN 106379010A CN 201610782752 A CN201610782752 A CN 201610782752A CN 106379010 A CN106379010 A CN 106379010A
Authority
CN
China
Prior art keywords
fan
base cloth
covering
cloth layer
silk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610782752.7A
Other languages
English (en)
Inventor
盛春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Lingyun Craft Fan Factory
Original Assignee
Suzhou Lingyun Craft Fan Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Lingyun Craft Fan Factory filed Critical Suzhou Lingyun Craft Fan Factory
Priority to CN201610782752.7A priority Critical patent/CN106379010A/zh
Publication of CN106379010A publication Critical patent/CN106379010A/zh
Pending legal-status Critical Current

Abstract

本发明涉扇子制作技术领域，具体涉及一种扇面用抗菌面料；包括基布层和面料层；所述基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；所述面料层是以丝绸为原料，经助剂加工后表面涂覆银离子制得，所述丝绸为22‑40姆米；所述基布层和面料层之间用粘合剂粘接；本发明提供的扇面用抗菌面料原料资源丰富，易于制取，制得的扇面抗菌性能好。

Description

一种扇面用抗菌面料
技术领域
本发明涉扇子制作技术领域，具体涉及一种扇面用抗菌面料。
背景技术
中国汉族扇文化有着深厚的文化底蕴，是汉民族文化的一个集成部分，它与竹文化、佛教文化有着密切关系。历来中国有“制扇王国”之称。扇子史传上最初称为“五明扇”，据传是虞舜所制。晋代崔豹的《古今注·舆服》记:“五明扇，舜所作也。既受尧禅，广开视听，求人以自辅，故作五明扇焉。秦，汉公卿，士大夫，皆得用之”。
在南方的盛夏季节，空气中蚊虫、蜉蝣易携带病菌，且人体新陈代谢旺盛，汗液溶液染湿扇面。扇子是引风用品，作为夏令必备之物，使用频率高，但不易清洁。使用时，扇面上常易沾染细菌，尤其致使病原微生物贴附在扇面上，造成扇面上菌落较多，使用时挥扇引风入喉，对人体健康造成潜在威胁。因此，扇面上急需一种与扇子加工工艺相适应的抗菌面料，以提高扇面的抗菌性能，和使用时的安全健康性能。
发明内容
针对现有技术的不足，本发明提供了一种抗菌性能优异的扇面用抗菌面料。
为实现以上目的，本发明通过以下技术方案予以实现：
一种扇面用抗菌面料，包括基布层和面料层；
所述基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；
所述面料层是以丝绸为原料，经助剂加工后表面涂覆银离子制得，所述丝绸为22-40姆米；
所述基布层和面料层之间用粘合剂粘接。
进一步的，所述中药提取物选自五加皮、木香、檀香、桂花、佛手丝川、玫瑰、薰衣草提取物中的任意两种或两种以上组合物。
进一步的，所述基布层中的功能助剂为OP-10、TWEEN-80、脂肪醇聚氧乙烯醚、聚氧乙烯月桂基醚、甜菜碱型表面活性剂。
进一步的，所述粘胶纤维的制备方法为：由来树、苦树、金银忍冬提取出浆粕，用烧碱、二硫化碳处理，得到纤维素黄原酸钠，再溶解在稀氢氧化钠溶液中，成为粘稠的纺丝原液，将溶液加热至65-80℃，加入中药提取物和功能助剂，保温1-2小时，在凝固浴中经湿法纺丝，纤维素黄原酸钠分解析出纤维素，再经水洗、脱硫、漂白、干燥后，用淘米水清洗一遍，按扇骨形状剪制成型，即得基布层；
进一步的，所述面料层的助剂为抗菌防霉整理剂、抗光老化整理剂、有机硅柔软剂。
进一步的，所述粘合剂的制备方法为：取面粉和糯米煮熟，加入占熟料2-5wt％的水拌匀，调成浆糊，即得。
本发明的有益效果为：
(1)来树、苦树、金银忍冬的抗菌性能突出，菌谱较广，且植物资源丰富，原料易得，本发明采用来树、苦树、金银忍冬作为扇面的基布层材料，经处理后，面料有一定硬度，且细菌抑制率达82.4-93.2％，抗菌性能优越，适用于扇面制作工艺；基布层还用具有芳香气味的中药提取物进行处理，使得面料在制成扇面后，在引风时，会带来扑面而来的清淡草本芳香气味，有助于提高扇面的应用价值。
(2)面料层采用纹理细腻柔滑的丝绸做表层，能赋予扇面柔和的光泽感和良好的视觉、触觉感受，经助剂处理后，具有更好的使用性能；本发明在丝绸表层涂覆银离子，能起到很好的抑菌作用。
(3)本发明采用的粘合剂为常用物料制得，使用安全，环保性能好，适用于制扇工艺。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种扇面用抗菌面料，包括基布层和面料层；
基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；其中，中药提取物选自五加皮、檀香、玫瑰提取物混合物；功能助剂为OP-10、TWEEN-80、脂肪醇聚氧乙烯醚、聚氧乙烯月桂基醚、甜菜碱型表面活性剂；
基布层的制备方法为：由来树、苦树、金银忍冬提取出浆粕，用烧碱、二硫化碳处理，得到纤维素黄原酸钠，再溶解在稀氢氧化钠溶液中，成为粘稠的纺丝原液，将溶液加热至65-80℃，加入8wt％中药提取物和4wt％功能助剂，保温1-2小时，在凝固浴中经湿法纺丝，纤维素黄原酸钠分解析出纤维素，再经水洗、脱硫、漂白、干燥后，用淘米水清洗一遍，按扇骨形状剪制成型；
面料层是以22-40姆米的丝绸为原料，经助剂加工后表面涂覆银离子制得；其中，助剂为抗菌防霉整理剂、抗光老化整理剂、有机硅柔软剂；
基布层和面料层之间用粘合剂粘接；其中，粘合剂的制备方法为：取面粉和糯米煮熟，加入占熟料2-5wt％的水拌匀，调成浆糊，即得。
实施例2：
一种扇面用抗菌面料，包括基布层和面料层；
基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；其中，中药提取物选自木香、桂花、佛手丝川提取物组合物；功能助剂为OP-10、TWEEN-80、脂肪醇聚氧乙烯醚、聚氧乙烯月桂基醚、甜菜碱型表面活性剂；
基布层的制备方法为：由来树、苦树、金银忍冬提取出浆粕，用烧碱、二硫化碳处理，得到纤维素黄原酸钠，再溶解在稀氢氧化钠溶液中，成为粘稠的纺丝原液，将溶液加热至65-80℃，加入10wt％中药提取物和2wt％功能助剂，保温1-2小时，在凝固浴中经湿法纺丝，纤维素黄原酸钠分解析出纤维素，再经水洗、脱硫、漂白、干燥后，用淘米水清洗一遍，按扇骨形状剪制成型；
面料层是以22-40姆米的丝绸为原料，经助剂加工后表面涂覆银离子制得；其中，助剂为抗菌防霉整理剂、抗光老化整理剂、有机硅柔软剂；
基布层和面料层之间用粘合剂粘接；其中，粘合剂的制备方法为：取面粉和糯米煮熟，加入占熟料2-5wt％的水拌匀，调成浆糊，即得。
实施例3：
一种扇面用抗菌面料，包括基布层和面料层；
基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；其中，中药提取物选自木香、佛手丝川、薰衣草提取物组合物；功能助剂为OP-10、TWEEN-80、脂肪醇聚氧乙烯醚、聚氧乙烯月桂基醚、甜菜碱型表面活性剂；
基布层的制备方法为：由来树、苦树、金银忍冬提取出浆粕，用烧碱、二硫化碳处理，得到纤维素黄原酸钠，再溶解在稀氢氧化钠溶液中，成为粘稠的纺丝原液，将溶液加热至65-80℃，加入16wt％中药提取物和1wt％功能助剂，保温1-2小时，在凝固浴中经湿法纺丝，纤维素黄原酸钠分解析出纤维素，再经水洗、脱硫、漂白、干燥后，用淘米水清洗一遍，按扇骨形状剪制成型；
面料层是以22-40姆米的丝绸为原料，经助剂加工后表面涂覆银离子制得；其中，助剂为抗菌防霉整理剂、抗光老化整理剂、有机硅柔软剂；
基布层和面料层之间用粘合剂粘接；其中，粘合剂的制备方法为：取面粉和糯米煮熟，加入占熟料2-5wt％的水拌匀，调成浆糊，即得。
以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。

Claims (6)

1.一种扇面用抗菌面料，包括基布层和面料层；其特征在于，
所述基布层是以来树、苦树、金银忍冬、中药提取物和功能助剂为原料制成的粘胶纤维；
所述面料层是以丝绸为原料，经助剂加工后表面涂覆银离子制得，所述丝绸为22-40姆米；
所述基布层和面料层之间用粘合剂粘接。
2.如权利要求1所述的扇面用抗菌面料，其特征在于，所述中药提取物选自五加皮、木香、檀香、桂花、佛手丝川、玫瑰、薰衣草提取物中的任意两种或两种以上组合物。
3.如权利要求1所述的扇面用抗菌面料，其特征在于，所述基布层中的功能助剂为OP-10、TWEEN-80、脂肪醇聚氧乙烯醚、聚氧乙烯月桂基醚、甜菜碱型表面活性剂。
4.如权利要求1所述的扇面用抗菌面料，其特征在于，所述粘胶纤维的制备方法为：由来树、苦树、金银忍冬提取出浆粕，用烧碱、二硫化碳处理，得到纤维素黄原酸钠，再溶解在稀氢氧化钠溶液中，成为粘稠的纺丝原液，将溶液加热至65-80℃，加入中药提取物和功能助剂，保温1-2小时，在凝固浴中经湿法纺丝，纤维素黄原酸钠分解析出纤维素，再经水洗、脱硫、漂白、干燥后，用淘米水清洗一遍，按扇骨形状剪制成型，即得基布层。
5.如权利要求1所述的扇面用抗菌面料，其特征在于，所述面料层的助剂为抗菌防霉整理剂、抗光老化整理剂、有机硅柔软剂。
6.如权利要求1所述的扇面用抗菌面料，其特征在于，所述粘合剂的制备方法为：取面粉和糯米煮熟，加入占熟料2-5wt％的水拌匀，调成浆糊，即得。
CN201610782752.7A 2016-08-31 2016-08-31 一种扇面用抗菌面料 Pending CN106379010A (zh)