CN106366918A - Anti-ultraviolet high-flame-retardant yacht leather - Google Patents
Anti-ultraviolet high-flame-retardant yacht leather Download PDFInfo
- Publication number
- CN106366918A CN106366918A CN201610746317.9A CN201610746317A CN106366918A CN 106366918 A CN106366918 A CN 106366918A CN 201610746317 A CN201610746317 A CN 201610746317A CN 106366918 A CN106366918 A CN 106366918A
- Authority
- CN
- China
- Prior art keywords
- parts
- ester
- leather
- black
- yacht
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides anti-ultraviolet high-flame-retardant yacht leather comprising a leather basic layer and a finishing agent coated on the leather basic layer. The leather basic layer is non-woven cloth obtained after sizing. The finishing agent is prepared from acid nigrosine crystals, pupa casein, dioctyl isophthalate, nipagin, borax, ammonia water, water, carbon black, benzoic acid high-carbon alcohol ester, dimethyl aminophenol octyl benzoate, 4-tert-butyl-4'-methoxy-dibenzoylmethane, cetanol and tris(2,3-dibromopropyl)phosphate. The leather can be applied to a yacht, and has effective anti-ultraviolet capacity and excellent ultraviolet shielding performance, and accordingly a greased leather sample can be endowed with a good ultraviolet shielding function. Meanwhile, the leather has a good flame-retardant effect, cannot be combusted easily after making contact with open fire, and effectively improves use safety of the yacht.
Description
Technical field
The invention belongs to field of leather, specifically a kind of uvioresistant high fire-retardance yacht leather.
Background technology
At present, existing yacht is under sunlight irradiation, and the security requirement of yacht is higher.The leather pair adopting in yacht
Poor in the resistance of ultraviolet, need other materials to be made up, most leathers belong to inflammable thing, require in yacht uses
Higher.
Content of the invention
The present invention provides a kind of uvioresistant high fire-retardance yacht leather, in order to solve defect of the prior art.
The present invention is achieved by the following technical programs:
A kind of uvioresistant high fire-retardance yacht leather, including leather substrate and the finishing agent being coated in leather substrate, its feature
It is: described leather substrate is through covering the non-woven fabrics that slurry is processed;Finishing agent is made up of the raw material of following weight parts: acid particle
Black 20-30 part, pupa casein 80-100 part, dioctyl isophthalate 10-15 part, Nipagin ester 10-15 part, Borax 3-6 part,
Ammonia 5-8 part, water 80-150 part, white carbon black 12-30 part, benzoic acid high-carbon alcohol ester 3-5 part, octyl dimethyl p-aminobenzoic acid 4-
6 parts, the 4- tert-butyl group -4'- methoxybenzoyl methane 5-10 part, hexadecanol 5-10 part, tricresyl phosphate (2,3- dibromopropyl) ester 3-
10 parts.
Described finishing agent is made up of the raw material of following weight parts: 20 parts of acid particle black, 90 parts of pupa casein, isophthalic two
15 parts of formic acid dioctyl ester, 10 parts of Nipagin ester, 4.5 parts of Borax, 8 parts of ammonia, 80 parts of water, 21 parts of white carbon black, benzoic acid high-carbon alcohol ester 5
Part, 4 parts of octyl dimethyl p-aminobenzoic acid, 7.5 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 10 parts of hexadecanol, phosphorus
Acid three (2,3- dibromopropyl) 3 parts of ester.
Described finishing agent is made up of the raw material of following weight parts: 25 parts of acid particle black, 100 parts of pupa casein, isophthalic
10 parts of diformazan dioctyl phthalate, 12 parts of Nipagin ester, 6 parts of Borax, 5 parts of ammonia, 100 parts of water, 30 parts of white carbon black, benzoic acid high-carbon alcohol ester
3 parts, 5 parts of octyl dimethyl p-aminobenzoic acid, 10 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 5 parts of hexadecanol, phosphoric acid
Three (2,3- dibromopropyl) 6 parts of ester.
Described finishing agent is made up of the raw material of following weight parts: 30 parts of acid particle black, 80 parts of pupa casein, isophthalic two
13 parts of formic acid dioctyl ester, 15 parts of Nipagin ester, 3 parts of Borax, 6 parts of ammonia, 150 parts of water, 12 parts of white carbon black, benzoic acid high-carbon alcohol ester 4
Part, 6 parts of octyl dimethyl p-aminobenzoic acid, 5 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 7.5 parts of hexadecanol, phosphoric acid
Three (2,3- dibromopropyl) 10 parts of ester.
Described finishing agent, is made up of the method for following step: 1. becomes moisture according to 45%, 45% and 10% point of weight ratio
Become three parts, standby;2. by pupa casein weight, the clear water than 45% is tuned into paste, is warming up to 60 DEG C, insulated and stirred and add ammonia and
Borax, insulated and stirred 1-2h, adding the clear water that weight is than 45%, Nipagin ester, the 4- tert-butyl group -4'- methoxybenzoyl first
Alkane, hexadecanol, tricresyl phosphate (2,3- dibromopropyl) ester, insulated and stirred 15min, cold go to room temperature, use 150 mesh screen, obtain
Protein milk;3. by dioctyl isophthalate, white carbon black, benzoic acid high-carbon alcohol ester, octyl dimethyl p-aminobenzoic acid mixing all
Even, ground uniformly with three-roll grinder, prepare black wash material;4. the clear water fusing acid particle black than 10% with weight, plus
The hot black wash material that to 45 DEG C, 3. addition step is prepared and the protein milk that 2. step is prepared, stop heating after stirring, are cooled to
Room temperature, obtains final product.
The invention has the advantage that the present invention can apply in yacht, the present invention has effectively anti-ultraviolet ability,
There is excellent shielding ultraviolet rays performance, thus the good shielding ultraviolet rays function of leather sample after stuffing can be given;Meanwhile, the present invention
There is good flame retardant effect, nonflammable after touching naked light, effectively improve the safety of yacht use.
Specific embodiment
Purpose, technical scheme and advantage for making the embodiment of the present invention are clearer, below will be in the embodiment of the present invention
Technical scheme be clearly and completely described it is clear that described embodiment a part of embodiment that is the present invention, rather than
Whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creative work premise
Lower obtained every other embodiment, broadly falls into the scope of protection of the invention.
A kind of uvioresistant high fire-retardance yacht leather, including leather substrate and the finishing agent being coated in leather substrate, its
It is characterised by: described leather substrate is through covering the non-woven fabrics that slurry is processed;Finishing agent is made up of the raw material of following weight parts: acid
Particle black 20-30 part, pupa casein 80-100 part, dioctyl isophthalate 10-15 part, Nipagin ester 10-15 part, Borax 3-
6 parts, ammonia 5-8 part, water 80-150 part, white carbon black 12-30 part, benzoic acid high-carbon alcohol ester 3-5 part, dimethyl-p-aminobenzoate pungent
Ester 4-6 part, the 4- tert-butyl group -4'- methoxybenzoyl methane 5-10 part, hexadecanol 5-10 part, tricresyl phosphate (2,3- dibromopropyl)
Ester 3-10 part.
Described finishing agent is made up of the raw material of the weight portion of following embodiments:
Embodiment one:
20 parts of acid particle black, 90 parts of pupa casein, 15 parts of dioctyl isophthalate, 10 parts of Nipagin ester, 4.5 parts of Borax,
8 parts of ammonia, 80 parts of water, 21 parts of white carbon black, 5 parts of benzoic acid high-carbon alcohol ester, 4 parts of octyl dimethyl p-aminobenzoic acid, the 4- tert-butyl group-
7.5 parts of 4'- methoxybenzoyl methane, 10 parts of hexadecanol, tricresyl phosphate (2,3- dibromopropyl) 3 parts of ester.
Embodiment two:
25 parts of acid particle black, 100 parts of pupa casein, 10 parts of dioctyl isophthalate, 12 parts of Nipagin ester, 6 parts of Borax, ammonia
5 parts of water, 100 parts of water, 30 parts of white carbon black, 3 parts of benzoic acid high-carbon alcohol ester, 5 parts of octyl dimethyl p-aminobenzoic acid, the 4- tert-butyl group-
10 parts of 4'- methoxybenzoyl methane, 5 parts of hexadecanol, tricresyl phosphate (2,3- dibromopropyl) 6 parts of ester.
Embodiment three:
Finishing agent is made up of the raw material of following weight parts: 30 parts of acid particle black, 80 parts of pupa casein, dioctyl isophthalate
13 parts, 15 parts of Nipagin ester, 3 parts of Borax, 6 parts of ammonia, 150 parts of water, 12 parts of white carbon black, 4 parts of benzoic acid high-carbon alcohol ester, dimethyl pair
6 parts of amino benzoic Acid monooctyl ester, 5 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 7.5 parts of hexadecanol, tricresyl phosphate (2,3- dibromo
Propyl group) 10 parts of ester.
Described finishing agent, is made up of the method for following step: 1. becomes moisture according to 45%, 45% and 10% point of weight ratio
Become three parts, standby;2. by pupa casein weight, the clear water than 45% is tuned into paste, is warming up to 60 DEG C, insulated and stirred and add ammonia and
Borax, insulated and stirred 1-2h, adding the clear water that weight is than 45%, Nipagin ester, the 4- tert-butyl group -4'- methoxybenzoyl first
Alkane, hexadecanol, tricresyl phosphate (2,3- dibromopropyl) ester, insulated and stirred 15min, cold go to room temperature, use 150 mesh screen, obtain
Protein milk;3. by dioctyl isophthalate, white carbon black, benzoic acid high-carbon alcohol ester, octyl dimethyl p-aminobenzoic acid mixing all
Even, ground uniformly with three-roll grinder, prepare black wash material;4. the clear water fusing acid particle black than 10% with weight, plus
The hot black wash material that to 45 DEG C, 3. addition step is prepared and the protein milk that 2. step is prepared, stop heating after stirring, are cooled to
Room temperature, that is,.
A kind of preparation method of uvioresistant high fire-retardance yacht leather, comprises the steps: 1. to enter the base fabric of non-woven fabrics
Row polishing wharf's pavement quality, the base fabric after process carries out impregnation process 10-15min, removes base fabric using roll compacting roller after dipping
In moisture;2. the base fabric after 1. processing step carries out covering slurry, and the serosity covering slurry is scraped smooth painting using roller knife
Overlay on base
On cloth, starching amount is 200-500g/;3. the base fabric after coating is put into drying and setting machine to be dried, drying temperature
It is set as 130 DEG C -150 DEG C, drying time is set as 5-10min;Uniformly spontaneously dry 3 after the finishing agent of coating 300g/ again
My god, obtain final product.
Finally it is noted that above example, only in order to technical scheme to be described, is not intended to limit;Although
With reference to the foregoing embodiments the present invention is described in detail, it will be understood by those within the art that: it still may be used
To modify to the technical scheme described in foregoing embodiments, or equivalent is carried out to wherein some technical characteristics;
And these modification or replace, do not make appropriate technical solution essence depart from various embodiments of the present invention technical scheme spirit and
Scope.
Claims (5)
1. a kind of uvioresistant high fire-retardance yacht leather it is characterised in that: include leather substrate and being coated in leather substrate
Finishing agent it is characterised in that: described leather substrate be through covering slurry process non-woven fabrics;Finishing agent is by the raw material of following weight parts
Make: acid particle black 20-30 part, pupa casein 80-100 part, dioctyl isophthalate 10-15 part, Nipagin ester 10-15
Part, Borax 3-6 part, ammonia 5-8 part, water 80-150 part, white carbon black 12-30 part, benzoic acid high-carbon alcohol ester 3-5 part, dimethyl are to ammonia
Yl benzoic acid monooctyl ester 4-6 part, the 4- tert-butyl group -4'- methoxybenzoyl methane 5-10 part, hexadecanol 5-10 part, tricresyl phosphate (2,3-
Dibromopropyl) ester 3-10 part.
2. a kind of uvioresistant high fire-retardance yacht leather according to claim 1 it is characterised in that: described finishing agent by
The raw material of following weight parts is made: 20 parts of acid particle black, 90 parts of pupa casein, 15 parts of dioctyl isophthalate, nipalgin
10 parts of ester, 4.5 parts of Borax, 8 parts of ammonia, 80 parts of water, 21 parts of white carbon black, 5 parts of benzoic acid high-carbon alcohol ester, dimethyl-p-aminobenzoate
4 parts of monooctyl ester, 7.5 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 10 parts of hexadecanol, tricresyl phosphate (2,3- dibromopropyl) ester 3
Part.
3. a kind of uvioresistant high fire-retardance yacht leather according to claim 1 it is characterised in that: described finishing agent by
The raw material of following weight parts is made: 25 parts of acid particle black, 100 parts of pupa casein, 10 parts of dioctyl isophthalate, nipalgin
12 parts of ester, 6 parts of Borax, 5 parts of ammonia, 100 parts of water, 30 parts of white carbon black, 3 parts of benzoic acid high-carbon alcohol ester, dimethyl-p-aminobenzoate
5 parts of monooctyl ester, 10 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 5 parts of hexadecanol, tricresyl phosphate (2,3- dibromopropyl) 6 parts of ester.
4. a kind of uvioresistant high fire-retardance yacht leather according to claim 1 it is characterised in that: described finishing agent by
The raw material of following weight parts is made: 30 parts of acid particle black, 80 parts of pupa casein, 13 parts of dioctyl isophthalate, nipalgin
15 parts of ester, 3 parts of Borax, 6 parts of ammonia, 150 parts of water, 12 parts of white carbon black, 4 parts of benzoic acid high-carbon alcohol ester, dimethyl-p-aminobenzoate
6 parts of monooctyl ester, 5 parts of the 4- tert-butyl group -4'- methoxybenzoyl methane, 7.5 parts of hexadecanol, tricresyl phosphate (2,3- dibromopropyl) ester 10
Part.
5. a kind of uvioresistant high fire-retardance yacht leather according to claim 1 it is characterised in that: described finishing agent,
It is made up of the method for following step: 1. moisture is become to be divided into three parts according to weight than 45%, 45% and 10%, standby;2. by pupa cheese
The clear water than 45% for the element weight is tuned into paste, is warming up to 60 DEG C, and insulated and stirred simultaneously adds ammonia and Borax, insulated and stirred 1-2h,
Add the clear water than 45% for the weight, Nipagin ester, the 4- tert-butyl group -4'- methoxybenzoyl methane, hexadecanol, tricresyl phosphate (2,3-
Dibromopropyl) ester, insulated and stirred 15min, cold go to room temperature, use 150 mesh screen, obtain protein milk;3. by M-phthalic acid
Dioctyl ester, white carbon black, benzoic acid high-carbon alcohol ester, octyl dimethyl p-aminobenzoic acid mix homogeneously, are ground all with three-roll grinder
Even, prepare black wash material;4. the clear water fusing acid particle black than 10% with weight, is heated to 45 DEG C, adds step 3.
The black wash material of preparation and the protein milk 2. prepared of step, stop heating after stirring, are cooled to room temperature, obtain final product.