CN106362733A - High-temperature resistant manganite catalyst and preparation method thereof - Google Patents
High-temperature resistant manganite catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN106362733A CN106362733A CN201610844375.5A CN201610844375A CN106362733A CN 106362733 A CN106362733 A CN 106362733A CN 201610844375 A CN201610844375 A CN 201610844375A CN 106362733 A CN106362733 A CN 106362733A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- manganese
- source
- preparation
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature resistant manganite catalyst for catalytic purification of nitric oxides and a preparation method thereof. The preparation method comprises the steps that firstly, a composite oxide Mn0.5W0.1TiOx is obtained through a homogeneous precipitation method, and an oxide catalyst (MnOx)0.5-(WO3)0.1-TiO2 is obtained after calcination is performed. Non-toxic and harmless raw materials are adopted, the manganite catalyst prepared through the simple and easy method has the non-toxicity, excellent low-temperature activity and high temperature resistance, and on the aspect of stationary source De-NOx, the manganite catalyst can be adopted as the catalyst replacing a vanadium-based catalyst; the manganite catalyst has the quite excellent NOx adsorption capacity, NO independent oxidizing capacity and high-temperature NH3 independent oxidizing capacity; the manganite catalyst is applicable to a nitric oxide catalyst purification device with a stationary source represented by coal-fired power plant flue gas and a mobile source represented by diesel vehicle exhaust gas.
Description
Technical field
The present invention relates to catalyst and preparation method thereof, particularly a kind of manganio oxidation for catalytic cleaning nitrogen oxide
Thing catalyst and preparation method thereof.
Background technology
Nitrogen oxides (nox, refer mainly to no and no2) it is one of major pollutants in air, gray haze, photochemical can be led to
Learn the great environmental problem such as smog and acid rain, health can also be produced and directly endanger.Therefore, control noxDischarge gesture
Must go, very urgent.
noxSource can be divided into natural source and artificial source, in artificial source noxIn discharge, with coal-fired plant flue gas as representative
Stationary source and the moving source with exhaust gas from diesel vehicle as representative be China's topmost discharged nitrous oxides source.At present according to nitrogen oxygen
Compound (nox) generation mechanism difference, control nitrogen oxides technology to be broadly divided into following three kinds: to start the burning controlling from Combustion Source
Front control；By transforming the structure of burner, control burning condition, reduce in the combustion process that thermal NO generates and control
System；Control after the burning nitrogen oxides of generation in flue gas being converted and being processed.The denitration skill of domestic and international main flow at present
Art is the selective catalytic reduction (scr) in controlling after burning, and SCR technology is according to the difference of reducing agent, main
Nh to be divided into3- scr technology and hc-scr technology, because hc-scr low-temperature reactivity difference and water resistant resistance to SO_2 difference the shortcomings of,
Limit the development of hc-scr, therefore, current research worker is mainly carried out with nh3Nh for reducing agent3The research of-scr technology.
The R and D of catalyst are whole nh3The core of-scr system and key.Using the preparation of traditional infusion process
v2o5-wo3/tio2Catalyst is in nearly 40 years of stationary source denitration field industrial applications, and is introduced into exhaust gas from diesel vehicle nox
The field of catalytic purification.But vanadio nh3- scr catalyst yet suffers from bio-toxicity, poor high temperature stability, operation temperature
The shortcomings of window is narrower, therefore, is highly desirable to traditional v2o5-wo3/tio2Catalyst improves.Numerous for nh3-
In the metal oxide catalyst systems of scr reaction, mn base oxide catalyst is due to having excellent low temperature nh3- scr activity
Widely paid close attention to cheap price.Therefore, noxious substance v is replaced preparation have excellent catalysis activity,
High temperature heat-resistant stability, wide temperature window, high n2Generate selective mnox-wo3-tio2Catalyst has to commercial Application
Very important meaning.
Content of the invention
It is an object of the invention to, for existing v2o5-wo3/tio2The deficiency that catalyst exists, the present invention provides first
One kind replaces v with mn, and dispersed for tri- kinds of species of mn, w, ti formation had excellent catalysis activity, high-temperature stability
And n2Generate selective metal oxide catalyst and preparation method thereof.
In order to achieve the above object, present invention employs following technical scheme:
A kind of resistant to elevated temperatures manganese-base oxide catalyst for catalytic cleaning nitrogen oxide, catalyst is metal-oxide
Catalyst (mnox)0.5-(wo3)0.1-tio2, described mnoxFor mn2+、mn3+And mn4+Mixed oxide, 1 < x < 2.
The preparation method of the manganese-base oxide catalyst of the present invention is sluggish precipitation, and it comprises the following specific steps that:
Step 1, adds manganese source, tungsten source and titanium source to generate mixed solution, stirs under normal temperature condition；
Step 2, adds slow release precipitator in the mixed solution in step 1；
Step 3, is heated to 70～95 DEG C, and under this temperature conditions, continues stirring precipitation 3～24h；
Step 4, the precipitate generating is separated and washed in step 3；
Step 5, the precipitate after washing is carried out drying, roasting, obtains (mnox)0.5-(wo3)0.1-tio2Catalyst.
In step 1, one or more of the preferred manganese nitrate of manganese source, manganese chloride or manganese sulfate.Tungsten source is preferably ammonium tungstate
One or more of with ammonium paratungstate.Titanium source is preferably one or more of titanium sulfate, titanium tetrachloride or butyl titanate.
Wherein, the mol ratio of manganese source, tungsten source and titanium source is 5:1:10.
In step 2, one or more of the preferred ammonium carbonate of slow release precipitator, ammonium hydrogen carbonate or carbamide.Slow release precipitator
Molal quantity is 8～20 times of the total mole number of manganese source, tungsten source and titanium source.
In step 3, preferably 80～90 DEG C of heating-up temperature.The stirring sedimentation time is preferably 6～12h.
In step 5, drying temperature is 90～110 DEG C.Roasting is carried out in air atmosphere, and sintering temperature is 400～800
DEG C, preferably 500 DEG C；Described roasting time is 1～24h, preferably 4～6h.
Compared with prior art, the present invention has the advantage that
(1) the manganese-base oxide catalyst of present invention preparation has avirulence, excellent low temperature active and resistance to elevated temperatures,
In terms of stationary source denitrating flue gas, can be used as the alternative catalysts of catalytic component based on vanadium；
(2) the manganese-base oxide catalyst of present invention preparation has very excellent noxAbsorbability.
(3) the manganese-base oxide catalyst of present invention preparation has the independent oxidability of very excellent no；
(4) the manganese-base oxide catalyst of present invention preparation has very excellent high temperature nh3Individually oxidability, can prevent
During only using, nh occurs3Leakage；
(5) preparation process of manganese-base oxide catalyst of the present invention makes tri- kinds of species of mn, w, ti dispersed, so that its
Possesses above-mentioned excellent catalytic performance.
Specific embodiment
For the present invention is better described, readily appreciate technical scheme, the present invention's is typical but non-limiting
Embodiment is as follows:
Embodiment 1
It is 5:1:10 according to mn, w, ti mol ratio, titanium sulfate is dissolved in deionized water, is subsequently adding ammonium tungstate and nitric acid
Manganese, and add manganese source, tungsten source and titanium source 20 times of total mole number carbamide as precipitant, be then heated to 90 DEG C and continuously stir
Mix 12h, then filtered and wash, by gained solid content put in baking oven in 100 DEG C dry 12h, after through Muffle furnace in
500 DEG C of in the air roasting 5h are obtained (mnox)0.5-(wo3)0.1-tio2Powder catalyst, referred to as catalyst a.
Comparative example 2
It is 5:1 according to mn:w mol ratio, ammonium tungstate is dissolved in oxalic acid, is continuously stirring to ammonium tungstate and is completely dissolved, then to
In this solution add manganese nitrate, and add manganese source and tungsten source 20 times of total mole number carbamide as precipitant, be then heated to
90 DEG C and continuous stirring 12h, are then filtered and are washed, and gained solid content is put in baking oven and dries 12h in 100 DEG C,
Powder catalyst, referred to as catalyst b are obtained by Muffle furnace in 500 DEG C of in the air roasting 5h.
Comparative example 3
It is 1:10 according to w:ti mol ratio, ammonium tungstate is dissolved in titanium sulfate solution, is continuously stirring to ammonium tungstate complete
Dissolving, then add 20 times of precipitant carbamide of the total mole number of tungsten source and titanium source in this solution, it is then heated to 90 DEG C and connect
Continuous stirring 12h, is then filtered and is washed, gained solid content is put in baking oven and dries 12h in 100 DEG C, after through Muffle
Stove is obtained powder catalyst, referred to as catalyst c in 500 DEG C of in the air roasting 5h.
Comparative example 4
It is 1:2 according to mn:ti mol ratio, prepares manganese nitrate and titanium sulfate mixed solution, be subsequently adding manganese source and titanium source
The carbamide that 20 times of total mole number, is then heated to 90 DEG C and continuous stirring 12h, is then filtered and wash, by gained solid
Thing put in baking oven in 100 DEG C dry 12h, after through Muffle furnace in 500 DEG C of in the air roasting 5h be obtained powder catalyst, claim
For catalyst d.
Comparative example 5
Conventional impregnation is adopted to be prepared for tio2For carrier, load 1wt%v2o5And 10wt%wo3V2o5-wo3/tio2
Catalyst.By c2h2o·2h2o、nh4vo3, and h4n10o41w12·xh2O is dissolved in 100ml deionized water, then in mixed solution
Add tio2Dust carrier, stirring more than 1h is mixed with abundant, then by mixed solution rotary evaporation until moisture fully volatilizees,
Dry overnight in the baking oven putting into 100 DEG C, then through the Muffle furnace roasting 5h under the conditions of 500 DEG C, produce powder catalyst, referred to as
Catalyst e.
Application examples 1
Sample a, b, c, d, e of being obtained are carried out tabletting, grind, sieve, takes 40～60 mesh granules in fixed bed reactors
On carry out nh3SCR nox(nh3- scr) reactivity investigation.
The usage amount of catalyst is 0.24ml, the consisting of of reaction mixture gas: [no]=[nh3]=500ppm, [o2]=
5%, n2Make Balance Air, total gas flow rate is 200ml/min, air speed is 50,000h-1, 100～300 DEG C of reaction temperature.No and
nh3And by-product n2o、no2All measured using nicolet antaris igs infrared gas analyser.noxConversion ratio and n2Generate
Selectivity is respectively as shown in Table 1 and Table 2.
The no of the different sample of table 1xConversion ratio
As shown in Table 1, under the same reaction conditions, catalyst d is in 100～150 DEG C of temperature section noxTransformation efficiency highest,
Show that it has excellent low temperature active；The no of catalyst cxTransformation efficiency is relatively low, shows that mn element has very to catalyst activity
Important contribution；Catalyst a is in the no of 150～300 DEG C of temperature sectionsxTransformation efficiency, all more than 80%, shows that it has excellent
Nh3The active and wider temperature window of-scr.The catalyst a of the method preparation being provided using the present invention is in (250 DEG C of low-temperature zone
No below)xTransformation efficiency, apparently higher than the catalyst e using traditional infusion process preparation, shows that mn replaces v and can play very well
Catalytic effect.
Application examples 2
Sample a, c, d, e of being obtained are carried out tabletting, grind, sieve, takes 40～60 mesh granules on fixed bed reactors
Investigate the no of catalystxAbsorbability.
The usage amount of catalyst is 0.3g, the consisting of of reaction mixture gas: [no]=500ppm, [o2]=5%, n2Put down
Weighing apparatus gas, total gas flow rate is 200ml/min.No and by-product n2o、no2All using nicolet antaris igs infrared-gas
Analysis-e/or determining.nox、n2o、no2Adsorbance is as shown in table 2.
The different sample of table 2 is in 50 DEG C of nox、no、no2Adsorbance
As shown in Table 2, under the same reaction conditions, the manganese-base oxide catalyst of the method preparation being provided using the present invention
A, d have excellent noxAbsorbability, primary attachment for no.The no of the catalyst d of method preparation being provided using the present inventionx
Absorbability is far above the catalyst e using traditional infusion process preparation, shows that mn replaces v and is conducive to improving the no of catalystxInhale
Attached ability.
Application examples 3
Sample a, c, d, e of being obtained are carried out tabletting, grind, sieve, takes 40～60 mesh granules on fixed bed reactors
Investigate the independent oxidability of catalyst.
The consisting of of reaction mixture gas: [no]=500ppm or [nh3]=500ppm, [o2]=5%, n2Make Balance Air, gas
Body total flow is 200ml/min, 100～300 DEG C of reaction temperature.The usage amount of catalyst is 0.24ml, corresponding reaction velocity
For 50,000h-1.No and nh3And by-product n2o、no2All measured using nicolet antaris igs infrared gas analyser.
The no that no individually aoxidizes2Growing amount and nh3The individually nh of oxidation3Conversion ratio is as shown in Table 3 and Table 4.
The no of the different sample independent no oxidation of table 32Growing amount
As shown in Table 3, under the same reaction conditions, the no of the catalyst a of method preparation being provided using the present invention2Generate
Amount is very high, is above the catalyst e using traditional infusion process preparation, illustrates that catalyst a has excellent in whole temperature range
Different no oxidability, mn replaces v and is conducive to improving the no oxidability of catalyst.
The different independent nh of sample of table 43The nh of oxidation3Conversion ratio
As shown in Table 4, under same reaction conditions, the nh of the catalyst a of method preparation being provided using the present invention3Conversion ratio
It is far above the catalyst e using traditional infusion process preparation in whole temperature range, show that mn replaces v and is conducive to improving catalyst
Nh3Oxidability.
When actually used, catalyst is placed in exhaust pipe way, sprays into reducing agent in the upstream of catalyst and tail gas mixes
Close, reducing agent adopt ammonia or carbamide (can get ammonia after hydrolysis), reducing agent consumption be nitrogen oxide in tail gas 0.8～
1.2 times, can be by no in very wide temperature window under excess oxygenxIt is reduced to n2And h2O, is provided simultaneously with very high n2Generate
Selectivity and water repelling property.
Tail gas is stationary source gas containing nitrogen oxide, such as coal-fired plant flue gas, or moving source gas containing nitrogen oxide,
Such as exhaust gas from diesel vehicle.
Applicant states, the present invention illustrates detailed composition and the method for the present invention by above-described embodiment, but the present invention
It is not limited to above-mentioned detailed composing method, that is, do not mean that the present invention has to rely on above-mentioned detailed composition and method could be real
Apply.Person of ordinary skill in the field is it will be clearly understood that any improvement in the present invention, equivalent to each raw material of product of the present invention
The interpolation of replacement and auxiliary element, selection of concrete mode etc., within the scope of all falling within protection scope of the present invention and disclosure.
Claims (7)
1. a kind of high temperature resistant manganese-base oxide catalyst is it is characterised in that described catalyst is manganio metal-oxide
(mnox)0.5-(wo3)0.1-tio2Catalyst, described mnoxFor mn2+、mn3+And mn4+Mixed oxide, 1 < x < 2.
2. a kind of preparation method of high temperature resistant manganese-base oxide catalyst, comprises the following specific steps that:
Step 1, adds manganese source, tungsten source and titanium source to generate mixed solution, stirs under normal temperature condition；
Step 2, adds slow release precipitator in the mixed solution in step 1；
Step 3, is heated to 70～95 DEG C, and under this temperature conditions, continues stirring precipitation 3～24h；
Step 4, the precipitate generating is separated and washed in step 3；
Step 5, the precipitate after washing is carried out drying, roasting, obtains (mnox)0.5-(wo3)0.1-tio2Catalyst.
3. the preparation method of high temperature resistant manganese-base oxide catalyst according to claim 2 is it is characterised in that in step 1,
Described manganese source is one or more of manganese nitrate, manganese chloride and manganese sulfate；Described tungsten source is ammonium tungstate, in ammonium paratungstate
One or more；Described titanium source is one or more of titanium sulfate, titanium tetrachloride and butyl titanate；Described manganese
The mol ratio in source, tungsten source and titanium source is 5:1:10.
4. the preparation method of high temperature resistant manganese-base oxide catalyst according to claim 2 is it is characterised in that in step 2,
Described slow release precipitator is one or more of ammonium carbonate, ammonium hydrogen carbonate and carbamide；Described slow release precipitator molal quantity
For the total mole number of manganese source, tungsten source and titanium source 8～20 times.
5. the preparation method of high temperature resistant manganese-base oxide catalyst according to claim 2 is it is characterised in that in step 3,
Described heating-up temperature is 80～90 DEG C；The described stirring sedimentation time is 6～12h.
6. the preparation method of high temperature resistant manganese-base oxide catalyst according to claim 2 is it is characterised in that in step 5,
Described drying temperature is 90～110 DEG C.
7. the preparation method of high temperature resistant manganese-base oxide catalyst according to claim 2 is it is characterised in that in step 5,
Described roasting is carried out in air atmosphere；Sintering temperature is 400～800 DEG C, and roasting time is 1～24h.