CN106281026A - A kind of fire-retardant uvioresistant ointment waterproof coating material and preparation method thereof - Google Patents
A kind of fire-retardant uvioresistant ointment waterproof coating material and preparation method thereof Download PDFInfo
- Publication number
- CN106281026A CN106281026A CN201610741916.1A CN201610741916A CN106281026A CN 106281026 A CN106281026 A CN 106281026A CN 201610741916 A CN201610741916 A CN 201610741916A CN 106281026 A CN106281026 A CN 106281026A
- Authority
- CN
- China
- Prior art keywords
- fire
- colophonium
- retardant
- parts
- ointment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-retardant uvioresistant ointment waterproof coating material and preparation method thereof, described preparation method includes following step: step 1: open blender, raising blender temperature is 130 150 DEG C, take 10# Colophonium, 70# Colophonium, mineral oil, styrene butadiene styrene block copolymer, butadiene-styrene rubber, PP GRANULES the most respectively, after stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;Step 2: reduction temperature, to 160 170 DEG C, adds fire retardant, antimony oxide, 2 hydroxyl 4 methoxy benzophenones, superfine talcum powder, stirs 1h;Step 3: by the mixture of step 2 circular grinding 1 3h in colloid mill, discharging after being cooled to 150 DEG C.The coating of preparation has good fire prevention, uvioresistant and waterproof intensity.
Description
Technical field
The invention belongs to paint field, relate to a kind of fire-retardant uvioresistant ointment waterproof coating material and preparation method thereof.
Background technology
Water-repellent paint, according to the liquid type of coating, can be divided into solvent-borne type, emulsion type, response type three kinds water-repellent paint.
Initial waterproof material is tar asphalt and oil green grass or young crops asphalt paper, originates from Europe, the twenties in 20th century incoming China.Along with
The progress of science and technology, modern waterproof material develops rapidly, it is seen that 20 century 70s, various high polymer waterproof materials are come out one after another.
China's waterproof material gradually forms coiled material, coating, the big series of encapsulant three.
Synthesis high polymer waterproof material is with synthetic rubber or contract resin as main film forming substance, adds other auxiliary materials
The waterproof coating material expected and be configured to.The brand of synthetic molecules waterproof material is varied, as polyurethane, acrylic acid and they
Mixture etc..Although the application of coating is more and more extensive, in addition to excellent water resistance, the also uvioresistant to coating
Higher requirement is it is also proposed with fire-retardant intensity.
Summary of the invention
Solve the technical problem that: conventional its waterproof strength of water-repellent paint is poor, be easily generated the phenomenon leaked, and easily
Combustion, causes job site potential safety hazard;Loss of properties on aging, embrittlement under long-time action of ultraviolet radiation, cause waterproof failure, this
Bright purpose is to provide a kind of water-repellent paint and preparation method thereof, improves the water resistance of coating, uvioresistant performance and anti-flammability
Energy.
Technical scheme: in order to solve the problems referred to above, the invention discloses a kind of fire-retardant uvioresistant ointment waterproof coating material, institute
The coating stated includes the composition of following weight parts:
10# Colophonium: 3-10 part, 70# Colophonium: 40-50 part, mineral oil: 12-20 part, s-B-S are embedding
Section copolymer: 3-10 part, butadiene-styrene rubber: 1-4 part, PP GRANULES: 5-15 part, fire retardant: 3-8 part, antimony oxide: 3-8
Part, ESCALOL 567: 2-8 part, superfine talcum powder: 10-15 part.
Preferably, described coating includes the composition of following weight parts:
10# Colophonium: 3-10 part, 70# Colophonium: 40-50 part, mineral oil: 12-20 part, s-B-S are embedding
Section copolymer: 3-10 part, butadiene-styrene rubber: 1-4 part, PP GRANULES: 5-15 part, fire retardant: 3-8 part, antimony oxide: 3-8
Part, ESCALOL 567: 2-8 part, superfine talcum powder: 10-15 part, lactoprene: 2-5 part, the poly-fourth of terminal hydroxy group
Diene: 3-6 part.
Preferably, described fire retardant is ethyl phosphonic acid diethylester, APP, isopropylated triphenyl phosphates, season penta
One or more in tetrol phosphate ester.
A kind of preparation method of fire-retardant uvioresistant ointment waterproof coating material, the step including following:
Step 1: open blender, raise blender temperature be 130-150 DEG C, take the most respectively 10# Colophonium 3-10 part,
70# Colophonium 40-50 part, mineral oil 12-20 part, styrene butadiene styrene block copolymer (SBS) 3-10 part, butadiene-styrene rubber 1-4
Part, PP GRANULES 5-15 part, after stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 160-170 DEG C, adds fire retardant 3-8 part, antimony oxide 3-8 part, 2-hydroxyl-4-first
Epoxide benzophenone 2-8 part, superfine talcum powder 10-15 part, stir 1h;
Step 3: by the mixture of step 2 circular grinding 1-3h in colloid mill, discharging after being cooled to 150 DEG C.
Preferably, raising blender temperature in described step 1 is 140 DEG C.
Preferably, circular grinding 2h in described step 3.
Beneficial effect: the coating of the present invention has bigger different from the preparation technology of conventional coating and compositing formula,
The water-repellent paint that the preparation method of the present invention prepares has possessed preferable water resistance, fire resistance and uvioresistant performance.
Its water resistance is significantly better than the coating of routine, and also has higher adhesion strength.
Detailed description of the invention
Embodiment 1
Step 1: open blender, raising blender temperature is 150 DEG C, takes 10# Colophonium 3 parts, 70# Colophonium the most respectively
50 parts, 12 parts of mineral oil, styrene butadiene styrene block copolymer (SBS) 3 parts, 4 parts of butadiene-styrene rubber, PP GRANULES 5 parts,
After stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds fire retardant 8 parts, antimony oxide 3 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 8 parts, superfine talcum powder 10 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 3h in colloid mill, discharging after being cooled to 150 DEG C.
Embodiment 2
Step 1: open blender, raising blender temperature is 130 DEG C, takes 10# Colophonium 10 parts, 70# drip the most respectively
Green grass or young crops 40 parts, 20 parts of mineral oil, styrene butadiene styrene block copolymer (SBS) 10 parts, 1 part of butadiene-styrene rubber, PP GRANULES 15
Part, after stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 160 DEG C, adds fire retardant 3 parts, antimony oxide 8 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 2 parts, superfine talcum powder 15 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 1h in colloid mill, discharging after being cooled to 150 DEG C.
Embodiment 3
Step 1: open blender, raising blender temperature is 140 DEG C, takes 10# Colophonium 6 parts, 70# Colophonium the most respectively
46 parts, 16 parts of mineral oil, styrene butadiene styrene block copolymer (SBS) 6 parts, 2 parts of butadiene-styrene rubber, PP GRANULES 10 parts,
After stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds fire retardant 5 parts, antimony oxide 5 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 5 parts, superfine talcum powder 13 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 2h in colloid mill, discharging after being cooled to 150 DEG C.
Embodiment 4
Step 1: open blender, raising blender temperature is 140 DEG C, takes 10# Colophonium 6 parts, 70# Colophonium the most respectively
46 parts, 16 parts of mineral oil, styrene butadiene styrene block copolymer (SBS) 6 parts, 2 parts of butadiene-styrene rubber, PP GRANULES 10 parts,
After stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds fire retardant 5 parts, antimony oxide 5 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 5 parts, superfine talcum powder 13 parts, lactoprene 5 parts, end hydroxy butadiene 3 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 2h in colloid mill, discharging after being cooled to 150 DEG C.
Embodiment 5
Step 1: open blender, raising blender temperature is 140 DEG C, takes 10# Colophonium 6 parts, 70# Colophonium the most respectively
46 parts, 16 parts of mineral oil, styrene butadiene styrene block copolymer (SBS) 6 parts, 2 parts of butadiene-styrene rubber, PP GRANULES 10 parts,
After stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds fire retardant 5 parts, antimony oxide 5 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 5 parts, superfine talcum powder 13 parts, lactoprene 2 parts, end hydroxy butadiene 6 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 2h in colloid mill, discharging after being cooled to 150 DEG C.
Comparative example 1
Step 1: open blender, raising blender temperature is 150 DEG C, takes 10# Colophonium 3 parts, 70# Colophonium the most respectively
50 parts, 12 parts of mineral oil, PP GRANULES 5 parts, stirring 30min after, rise high-temperature be 190 DEG C insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds fire retardant 8 parts, antimony oxide 3 parts, 2-hydroxyl-4-methoxyl group hexichol
Ketone 8 parts, superfine talcum powder 10 parts, stir 1h;
Step 3: by the mixture of step 2 circular grinding 3h in colloid mill, discharging after being cooled to 150 DEG C.
Comparative example 2
Step 1: open blender, raising blender temperature is 150 DEG C, takes 10# Colophonium 3 parts, 70# Colophonium the most respectively
50 parts, 12 parts of mineral oil, PP GRANULES 5 parts, stirring 30min after, rise high-temperature be 190 DEG C insulation 3h;
Step 2: reduction temperature, to 170 DEG C, adds superfine talcum powder 10 parts, stirs 1h;
Step 3: by the mixture of step 2 circular grinding 3h in colloid mill, discharging after being cooled to 150 DEG C.
Determine embodiment 1 to 5, the water resistance of coating of comparative example 1 and 2, adhesion strength, fire resistance, ageing-resistant
The performance test results is as follows:
Water resistance | Adhesion strength (MPa) | |
Embodiment 1 | 0.3MPa, 60min are without infiltration | 3.1 |
Embodiment 2 | 0.3MPa, 60min are without infiltration | 3.2 |
Embodiment 3 | 0.3MPa, 90min are without infiltration | 3.6 |
Embodiment 4 | 0.3MPa, 120min are without infiltration | 4.5 |
Embodiment 5 | 0.3MPa, 120min are without infiltration | 4.8 |
Comparative example 1 | 0.3MPa, 30min are without infiltration | 2.7 |
Comparative example 2 | 0.3MPa, 30min permeate | 2.0 |
Claims (6)
1. a fire-retardant uvioresistant ointment waterproof coating material, it is characterised in that described coating includes the composition of following weight parts:
10# Colophonium: 3-10 part, 70# Colophonium: 40-50 part, mineral oil: 12-20 part, s-B-S block are altogether
Polymers: 3-10 part, butadiene-styrene rubber: 1-4 part, PP GRANULES: 5-15 part, fire retardant: 3-8 part, antimony oxide: 3-8 part, 2-
Hydroxyl-4-methoxy benzophenone: 2-8 part, superfine talcum powder: 10-15 part.
One the most according to claim 1 fire-retardant uvioresistant ointment waterproof coating material, it is characterised in that described coating bag
Include the composition of following weight parts:
10# Colophonium: 3-10 part, 70# Colophonium: 40-50 part, mineral oil: 12-20 part, s-B-S block are altogether
Polymers: 3-10 part, butadiene-styrene rubber: 1-4 part, PP GRANULES: 5-15 part, fire retardant: 3-8 part, antimony oxide: 3-8 part, 2-
Hydroxyl-4-methoxy benzophenone: 2-8 part, superfine talcum powder: 10-15 part, lactoprene: 2-5 part, end hydroxy butadiene:
3-6 part.
3. according to the fire-retardant uvioresistant ointment waterproof coating material of the one described in claims 1 or 2, it is characterised in that described
Fire retardant is the one in ethyl phosphonic acid diethylester, APP, isopropylated triphenyl phosphates, pentaerythritol phosphate or several
Kind.
4. the preparation method of a fire-retardant uvioresistant ointment waterproof coating material, it is characterised in that under described preparation method includes
The step stated:
Step 1: open blender, raises blender temperature and is 130-150 DEG C, take 10# Colophonium 3-10 part, 70# the most respectively
Colophonium 40-50 part, mineral oil 12-20 part, styrene butadiene styrene block copolymer (SBS) 3-10 part, butadiene-styrene rubber 1-4 part,
PP GRANULES 5-15 part, after stirring 30min, rising high-temperature is 190 DEG C of insulation 3h;
Step 2: reduction temperature, to 160-170 DEG C, adds fire retardant 3-8 part, antimony oxide 3-8 part, 2-hydroxyl-4-methoxyl group
Benzophenone 2-8 part, superfine talcum powder 10-15 part, stir 1h;
Step 3: by the mixture of step 2 circular grinding 1-3h in colloid mill, discharging after being cooled to 150 DEG C.
The preparation method of a kind of fire-retardant uvioresistant ointment waterproof coating material the most according to claim 4, it is characterised in that institute
Raising blender temperature in the step 1 stated is 140 DEG C.
The preparation method of a kind of fire-retardant uvioresistant ointment waterproof coating material the most according to claim 4, it is characterised in that institute
Circular grinding 2h in the step 3 stated.