CN104312239A - Anti-corrosion and flame-retardant coating for ships, and preparation method thereof - Google Patents
Anti-corrosion and flame-retardant coating for ships, and preparation method thereof Download PDFInfo
- Publication number
- CN104312239A CN104312239A CN201410624314.9A CN201410624314A CN104312239A CN 104312239 A CN104312239 A CN 104312239A CN 201410624314 A CN201410624314 A CN 201410624314A CN 104312239 A CN104312239 A CN 104312239A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- corrosion
- ships
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-corrosion and flame-retardant coating for ships, and a preparation method thereof. The anti-corrosion and flame-retardant coating for ships includes the following components in parts by mass: 5 to 12 parts of iso-octyl acrylate, 4 to 10 parts of epoxy resin, 3 to 5 parts of talcum powders, 1 to 3 parts of sodium lauryl sulfate, 1 to 2 parts of modified inorganic silicate, 1 to 3 parts of dimethyl sulfoxide, and 6 to 10 parts of deionized water. The coating provided by the invention is not only anti-corrosion and flame-retardant, but also highly waterproof; on the basis of complying with relevant national standards for flame-retardant and waterproof performances of coatings for the field of ships, the coating achieves remarkable anti-corrosion effect.
Description
Technical field
The present invention relates to marine finish field, relate in particular to a kind of water-proof acrylic acid paint and preparation method thereof.
Background technology
Acrylic resin coating is widely used in industrial antisepsis, boats and ships and freight container, metal protection, construction wall and leather finish; but can sex change be there is in the sun in its long-term exposure; and its anticorrosion and inflammable feature is conflicting, becomes always and keep people in check and use it as the reason of anti-flaming dope seemingly.And the coating water-proof performance with its anticorrosion and fire-retardant feature all can decline greatly.
Summary of the invention
Goal of the invention: the object of this invention is to provide a kind of water-proof acrylic acid paint and preparation method thereof.
Technical scheme: in order to realize foregoing invention object, a kind of water-proof acrylic acid paint of the present invention comprises each component of following mass fraction:
Isooctyl acrylate monomer 5 ~ 12 parts;
Epoxy resin 4 ~ 10 parts;
Talcum powder 3 ~ 5 parts;
Sodium lauryl sulphate 1 ~ 3 part;
Modified inorganic silicate 1 ~ 2 part;
Dimethyl sulfoxide (DMSO) 1 ~ 3 part;
Deionized water 6 ~ 10 parts.
Preferably, described water-proof acrylic acid paint comprises each component of following mass fraction: Isooctyl acrylate monomer 8 parts;
Epoxy resin 7 parts;
Talcum powder 4 parts;
Sodium lauryl sulphate 2 parts;
Modified inorganic silicate 1 part
Dimethyl sulfoxide (DMSO) 2 parts;
Deionized water 8 parts.
A kind of preparation method of water-proof acrylic acid paint, by Isooctyl acrylate monomer, the reaction of epoxy resin mix and blend 2 ~ 4 hours under 80 ~ 95 DEG C of environment, adding deionized water, dimethyl sulfoxide (DMSO), talcum powder, sodium lauryl sulphate, modified inorganic silicate is under the condition of 7.2 at pH, stirs 30 ~ 50min and cool to less than 50 DEG C acquisitions under shear agitation speed 600 ~ 1000rpm.
Beneficial effect: coating of the present invention is not only anticorrosion, fire-retardant, also has a function of height waterproof.Meet the relevant criterion of China to ship domain coating flame retardant properties and water resistance, on its basis, there is significant preservative effect.
Embodiment
Below in conjunction with embodiment, technical solution of the present invention is further described.
A kind of boats and ships antiseptic fire-retardation coating, comprises each component of following mass fraction: Isooctyl acrylate monomer 5 ~ 12 parts; Epoxy resin 4 ~ 10 parts; Talcum powder 3 ~ 5 parts; Sodium lauryl sulphate 1 ~ 3 part; Modified inorganic silicate 1 ~ 2 part; Dimethyl sulfoxide (DMSO) 1 ~ 3 part; Deionized water 6 ~ 10 parts.
Preferably, above-mentioned anti-flaming dope is by epoxy resin 7 parts; Talcum powder 4 parts; Sodium lauryl sulphate 2 parts; Modified inorganic silicate 1 part of dimethyl sulfoxide (DMSO) 2 parts; Deionized water 8 parts composition.
Preparation method: by Isooctyl acrylate monomer, the reaction of epoxy resin mix and blend 2 ~ 4 hours under 80 ~ 95 DEG C of environment, adding deionized water, dimethyl sulfoxide (DMSO), talcum powder, sodium lauryl sulphate, modified inorganic silicate is under the condition of 7.2 at pH, stirs 30 ~ 50min and cool to less than 50 DEG C acquisitions under shear agitation speed 600 ~ 1000rpm.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. a water-proof acrylic acid paint, is characterized in that, comprises each component of following mass fraction:
Isooctyl acrylate monomer 5 ~ 12 parts;
Epoxy resin 4 ~ 10 parts;
Talcum powder 3 ~ 5 parts;
Sodium lauryl sulphate 1 ~ 3 part;
Modified inorganic silicate 1 ~ 2 part;
Dimethyl sulfoxide (DMSO) 1 ~ 3 part;
Deionized water 6 ~ 10 parts.
2. a kind of water-proof acrylic acid paint according to claim 1, is characterized in that, comprises each component of following mass fraction:
Isooctyl acrylate monomer 8 parts;
Epoxy resin 7 parts;
Talcum powder 4 parts;
Sodium lauryl sulphate 2 parts;
Modified inorganic silicate 1 part;
Dimethyl sulfoxide (DMSO) 2 parts;
Deionized water 8 parts.
3. the preparation method of a kind of water-proof acrylic acid paint as claimed in claim 1 or 2, it is characterized in that: by Isooctyl acrylate monomer, the reaction of epoxy resin mix and blend 2 ~ 4 hours under 80 ~ 95 DEG C of environment, adding deionized water, dimethyl sulfoxide (DMSO), talcum powder, sodium lauryl sulphate, modified inorganic silicate is under the condition of 7.2 at pH, stirs 30 ~ 50min and cool to less than 50 DEG C acquisitions under shear agitation speed 600 ~ 1000rpm.