CN106277866A - The manufacture method of durability cement brick - Google Patents

The manufacture method of durability cement brick Download PDF

Info

Publication number
CN106277866A
CN106277866A CN201610734337.4A CN201610734337A CN106277866A CN 106277866 A CN106277866 A CN 106277866A CN 201610734337 A CN201610734337 A CN 201610734337A CN 106277866 A CN106277866 A CN 106277866A
Authority
CN
China
Prior art keywords
weight portions
cement brick
manufacture method
durability
calx
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610734337.4A
Other languages
Chinese (zh)
Inventor
刘兴汉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beihai Jinjiang Cement Products Co Ltd
Original Assignee
Beihai Jinjiang Cement Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beihai Jinjiang Cement Products Co Ltd filed Critical Beihai Jinjiang Cement Products Co Ltd
Priority to CN201610734337.4A priority Critical patent/CN106277866A/en
Publication of CN106277866A publication Critical patent/CN106277866A/en
Pending legal-status Critical Current

Abstract

The present invention discloses the manufacture method of a kind of durability cement brick, and institute at high temperature and pressure, adds the liquid activating agent of 15 weight portions, makes novel high-strength construction material with the flyash of 95 weight portions, the Calx of 15 weight portions, the sand of 1 weight portion.The present invention uses above cement brick, reduces flyash exhaust emission, has the highest stability, durability and resistance to chemical attack, and intensity is high.

Description

The manufacture method of durability cement brick
Technical field
The invention belongs to technical field of buildings, particularly to the manufacture method of a kind of durability cement brick.
Background technology
Now, along with fast development, the input energetically of capital construction of national economy, at present, flyash can mix with cement Closing and use, but the blended cement early strength produced is low and addition content is typically small, otherwise product strength is unable to reach country's mark Accurate requirement.Therefore the utilization rate of flyash is the lowest.
Summary of the invention
It is an object of the invention to provide the manufacture method of a kind of durability cement brick, solve the utilization rate of flyash Problem.
For solving above technical problem, the present invention provides following technical scheme: the manufacture method of a kind of durability cement brick, At high temperature and pressure, 15 weight portions are added with the flyash of 95 weight portions, the Calx of 15 weight portions, the sand of 1 weight portion Liquid activating agent, makes novel high-strength construction material.
Preferably, the raw material of addition also includes the iron filings of 5 weight portions and the aluminum bits of 6 weight portions.
Preferably, described liquid activating agent is quick lime, Calx, KOH, NaOH and strong base-weak acid salt.
The present invention uses above cement brick, reduces flyash exhaust emission, has the highest stability, and durability is with anti- Chemical corrosion, intensity is high.
Detailed description of the invention
The present invention will be further described in conjunction with the embodiments.
The manufacture method of a kind of durability cement brick, at high temperature and pressure, with the flyash of 95 weight portions, 15 weight portions Calx, the sand of 1 weight portion add the liquid activating agent of 15 weight portions, make novel high-strength construction material..
Preferably, the raw material of addition also includes the iron filings of 5 weight portions and the aluminum bits of 6 weight portions.
Preferably, described liquid activating agent is quick lime, Calx, KOH, NaOH and strong base-weak acid salt.
The present invention uses above cement brick, reduces flyash exhaust emission, has the highest stability, durability and anti-chemistry Aggressivity, intensity is high.
Detailed description of the invention of the present invention is not intended that the restriction to the application scope, every at present inventive concept Within spirit and principle, any amendment, equivalent and improvement etc. that one of skill in the art can make should be included in Within protection scope of the present invention.

Claims (3)

1. the manufacture method of a durability cement brick, it is characterised in that at high temperature and pressure, with the fine coal of 95 weight portions Ash, the Calx of 15 weight portions, the sand of 1 weight portion add the liquid activating agent of 15 weight portions, make novel high-strength construction material.
The manufacture method of durability cement brick the most according to claim 1, it is characterised in that the raw material of addition also includes 5 The iron filings of weight portion and the aluminum bits of 6 weight portions.
The manufacture method of durability cement brick the most according to claim 1, it is characterised in that described liquid activating agent is made a living Calx, Calx, KOH, NaOH and strong base-weak acid salt.
CN201610734337.4A 2016-08-28 2016-08-28 The manufacture method of durability cement brick Pending CN106277866A (en)