CN106243905A - A kind of high-temperature-resistant insulating paint and preparation method thereof - Google Patents
A kind of high-temperature-resistant insulating paint and preparation method thereof Download PDFInfo
- Publication number
- CN106243905A CN106243905A CN201610719736.3A CN201610719736A CN106243905A CN 106243905 A CN106243905 A CN 106243905A CN 201610719736 A CN201610719736 A CN 201610719736A CN 106243905 A CN106243905 A CN 106243905A
- Authority
- CN
- China
- Prior art keywords
- temperature
- resistant insulating
- insulating paint
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of high-temperature-resistant insulating paint and preparation method thereof.Preparation method is as follows: (1) grinds after mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas-phase silica mixing, and being ground to particle diameter is 20 40um;(2) by polysiloxane resin, acrylic resin, sodium polyacrylate, dimethylbenzene, Oleum Terebinthinae, butyl acetate, it is mixed and heated to 60 80 DEG C, stirs 120 180 minutes;(3) granulate mixture that step (1) obtains is joined in the mixed resin solution of step (2), stir 60 80 minutes, ultrasonic shear 20 40 minutes;(4) LaMgAl is added11O19, phenolic resin, glass fibre, ceramic fine bead, stir 50 80 minutes.The high-temperature-resistant insulating paint of the present invention has good resistance to elevated temperatures, remains to keep good insulating properties after high temperature.
Description
Technical field
The present invention relates to new coating field, be specifically related to a kind of high-temperature-resistant insulating paint and preparation method thereof.
Background technology
In recent years, along with improving constantly of scientific and technological level, the development of insulant the most increasingly receives publicity.At present, absolutely
The kind of edge material is a lot, such as insulating bag closure material, insulating paper, ambroin, coatings etc., wherein coatings due to
Preparation method is simple, and construction technology is convenient, and therefore coatings is more and more used on every profession and trade insulator arrangement.Its
In, one of coatings focus becoming current research that thermostability is good.High-temperature resistant coating is also known as heat-resisting paint, is usually
Referring to more than 200 DEG C, paint film invariant color, do not fall off, remain to keep the coating of suitable physical and mechanical properties, it is right to make to be protected
As the special functional coating that can normally play a role in hot environment.High-temperature resistant coating typically by heat-resistant polymer, fill out
Material, solvent and auxiliary agent composition.Compared with other high temperature oxidation corrosion resistance means, high-temperature resistant coating is easy to use, to protection object
Normal performance does not produce impact.At present, existing the most multiple adapting to the coatings in hot environment, these coating are in hot environment
Under remain to keep good dielectric properties, there is good insulating properties, but although some coating can meet hot environment again
The requirement of middle insulating properties, but because of the formula of coating itself and technological problems, under the high temperature conditions, especially more than 300 DEG C
Use environment in, the defects such as tack is not enough, easy to fall off.
Summary of the invention
Solve the technical problem that: it is an object of the invention to provide a kind of high-temperature-resistant insulating paint, have the most still
There are good insulating properties.
Technical scheme: a kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane tree
Fat 15-40 part, mica powder 5-15 part, Pulvis Talci 5-15 part, acrylic resin 0.1-1 part, sodium polyacrylate 0.1-0.5 part, two
Toluene 5-15 part, Oleum Terebinthinae 1-10 part, butyl acetate 1-5 part, LaMgAl11O193-8 part, SiC10-20 part, daiamid epoxy are solid
Agent 0.5-1.5 part, phenolic resin 20-40 part, glimmering brilliant Fluorspar Powder 5-15 part, ceramic fine bead 3-10 part, gas-phase silica 3-10
Part, glass fibre 2-8 part.
It is further preferred that described a kind of high-temperature-resistant insulating paint, following component it is prepared from by weight: poly-have
Organic siloxane resin 25-35 part, mica powder 6-12 part, Pulvis Talci 6-11 part, acrylic resin 0.3-0.8 part, sodium polyacrylate
0.2-0.4 part, dimethylbenzene 8-15 part, Oleum Terebinthinae 3-7 part, butyl acetate 2-4 part, LaMgAl11O195-7 part, SiC12-18 part,
Daiamid epoxy curing agent 0.8-1.2 part, phenolic resin 25-38 part, glimmering brilliant Fluorspar Powder 7-13 part, ceramic fine bead 4-8 part, gas phase
White carbon 4-8 part, glass fibre 4-6 part.
The preparation method of above-mentioned high-temperature-resistant insulating paint comprises the following steps:
(1) grinding after mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas-phase silica mixing, being ground to particle diameter is 20-
40um;(2) by polysiloxane resin, acrylic resin, sodium polyacrylate, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing
Post-heating is 60-80 DEG C to temperature, stirs 120-180 minute;
(3) granulate mixture that step (1) obtains is joined in the mixed resin solution of step (2), stirs 60-80 minute,
Ultrasonic shear 20-40 minute;
(4) LaMgAl is added11O19, phenolic resin, glass fibre, ceramic fine bead, stir 50-80 minute.
Further, the preparation method of described a kind of high-temperature-resistant insulating paint, in described step (1), particle diameter is 20-
30um。
Further, the preparation method of described a kind of high-temperature-resistant insulating paint, in described step (2), temperature is 65-
75 DEG C, mixing time is 140-160 minute.
Further, the preparation method of described a kind of high-temperature-resistant insulating paint, stirring 65-75 in described step (3)
Minute, ultrasonic shear 25-35 minute.
Further, the preparation method of described a kind of high-temperature-resistant insulating paint, in described step (4), mixing time is
60-70 minute.
Beneficial effect: the high-temperature-resistant insulating paint of the present invention has good resistance to elevated temperatures, at 600 DEG C, paint film is just
Often;At room temperature, optimal specific insulation is more than or equal to 1.9 × 1017Ω cm, breakdown strength is more than or equal to 196KV/m,
Lower return to the optimal specific insulation of room temperature more than or equal to 7.2 × 10 through 50h17Ω cm, breakdown strength is more than or equal to 226KV/
mm.Coating prepared by the present invention is simple and easy to get, and cost is relatively low, is suitable for promoting.
Detailed description of the invention
Embodiment 1
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 15 parts, mica powder
15 parts, Pulvis Talci 5 parts, acrylic resin 0.1 part, sodium polyacrylate 0.1 part, dimethylbenzene 5 parts, Oleum Terebinthinae 10 parts, butyl acetate 1
Part, LaMgAl11O198 parts, SiC10 part, daiamid epoxy curing agent 0.5 part, 40 parts of phenolic resin, glimmering brilliant Fluorspar Powder 5 parts, pottery
Porcelain microballon 10 parts, gas-phase silica 10 parts, glass fibre 2 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas phase
Grinding after white carbon mixing, being ground to particle diameter is 20um;(2) by polysiloxane resin, acrylic resin, polyacrylic acid
Sodium, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 60 DEG C, stirs 180 minutes;(3) step (1) is obtained
Granulate mixture join in the mixed resin solution of step (2), stir 60 minutes, ultrasonic shear 40 minutes;(4) add
LaMgAl11O19, phenolic resin, glass fibre, ceramic fine bead, stir 50 minutes.
Embodiment 2
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 40 parts, mica powder
5 parts, Pulvis Talci 15 parts, acrylic resin 1 part, sodium polyacrylate 0.5 part, dimethylbenzene 15 parts, Oleum Terebinthinae 1 part, butyl acetate 5
Part, LaMgAl11O193 parts, SiC20 part, daiamid epoxy curing agent 1.5 parts, 20 parts of phenolic resin, glimmering brilliant Fluorspar Powder 15 parts, pottery
Porcelain microballon 3 parts, gas-phase silica 3 parts, glass fibre 8 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas phase
Grinding after white carbon mixing, being ground to particle diameter is 40um;(2) by polysiloxane resin, acrylic resin, polyacrylic acid
Sodium, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 80 DEG C, stirs 120 minutes;(3) step (1) is obtained
Granulate mixture join in the mixed resin solution of step (2), stir 80 minutes, ultrasonic shear 20 minutes;(4) add
LaMgAl11O19, phenolic resin, glass fibre, ceramic fine bead, stir 80 minutes.
Embodiment 3
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 35 parts, mica powder
6 parts, Pulvis Talci 11 parts, acrylic resin 0.8 part, sodium polyacrylate 0.4 part, dimethylbenzene 15 parts, Oleum Terebinthinae 3 parts, butyl acetate 2
Part, LaMgAl11O197 parts, SiC12 part, daiamid epoxy curing agent 1.2 parts, 25 parts of phenolic resin, glimmering brilliant Fluorspar Powder 7 parts, pottery
Porcelain microballon 4 parts, gas-phase silica 8 parts, glass fibre 6 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas phase
Grinding after white carbon mixing, being ground to particle diameter is 20um;(2) by polysiloxane resin, acrylic resin, polyacrylic acid
Sodium, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 65 DEG C, stirs 160 minutes;(3) step (1) is obtained
Granulate mixture join in the mixed resin solution of step (2), stir 65 minutes, ultrasonic shear 25 minutes;(4) add
LaMgAl11O19, phenolic resin, glass fibre, ceramic fine bead, stir 70 minutes.
Embodiment 4
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 25 parts, mica powder
12 parts, Pulvis Talci 6 parts, acrylic resin 0.3 part, sodium polyacrylate 0.2 part, dimethylbenzene 8 parts, Oleum Terebinthinae 7 parts, butyl acetate 4
Part, LaMgAl11O195 parts, SiC18 part, daiamid epoxy curing agent 0.8 part, 38 parts of phenolic resin, glimmering brilliant Fluorspar Powder 13 parts, pottery
Porcelain microballon 8 parts, gas-phase silica 4 parts, glass fibre 4 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas phase
Grinding after white carbon mixing, being ground to particle diameter is 30um;(2) by polysiloxane resin, acrylic resin, polyacrylic acid
Sodium, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 75 DEG C, stirs 140 minutes;(3) step (1) is obtained
Granulate mixture join in the mixed resin solution of step (2), stir 75 minutes, ultrasonic shear 35 minutes;(4) add
LaMgAl11O19, phenolic resin, glass fibre, ceramic fine bead, stir 60 minutes.
Embodiment 5
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 35 parts, mica powder
8 parts, Pulvis Talci 10 parts, acrylic resin 0.5 part, sodium polyacrylate 0.3 part, dimethylbenzene 11 parts, Oleum Terebinthinae 5 parts, butyl acetate 3
Part, LaMgAl11O196 parts, SiC15 part, daiamid epoxy curing agent 1 part, 35 parts of phenolic resin, glimmering brilliant Fluorspar Powder 10 parts, pottery
Microballon 6 parts, gas-phase silica 6 parts, glass fibre 5 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas phase
Grinding after white carbon mixing, being ground to particle diameter is 20um;(2) by polysiloxane resin, acrylic resin, polyacrylic acid
Sodium, dimethylbenzene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 70 DEG C, stirs 150 minutes;(3) step (1) is obtained
Granulate mixture join in the mixed resin solution of step (2), stir 70 minutes, ultrasonic shear 30 minutes;(4) add
LaMgAl11O19, phenolic resin, glass fibre, ceramic fine bead, stir 65 minutes.
Comparative example 1
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 15 parts, mica powder
15 parts, Pulvis Talci 5 parts, acrylic resin 0.1 part, sodium polyacrylate 0.1 part, dimethylbenzene 5 parts, Oleum Terebinthinae 10 parts, butyl acetate 1
Part, daiamid epoxy curing agent 0.5 part, 40 parts of phenolic resin, glimmering brilliant Fluorspar Powder 5 parts, ceramic fine bead 10 parts, gas-phase silica 10
Part, glass fibre 2 parts.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) is by mica powder, Pulvis Talci, glimmering brilliant Fluorspar Powder, gas phase Linesless charcoal
Grinding after black mixing, being ground to particle diameter is 20um;(2) by polysiloxane resin, acrylic resin, sodium polyacrylate, two
Toluene, Oleum Terebinthinae, butyl acetate, mixing post-heating to temperature is 60 DEG C, stirs 180 minutes;(3) step (1) is obtained
Grain mixture joins in the mixed resin solution of step (2), stirs 60 minutes, ultrasonic shear 40 minutes;(4) phenolic aldehyde is added
Resin, glass fibre, ceramic fine bead, stir 50 minutes.
Comparative example 2
A kind of high-temperature-resistant insulating paint, is prepared from by weight by following component: polysiloxane resin 40 parts, mica powder
5 parts, Pulvis Talci 15 parts, acrylic resin 1 part, sodium polyacrylate 0.5 part, dimethylbenzene 15 parts, Oleum Terebinthinae 1 part, butyl acetate 5
Part, LaMgAl11O193 parts, SiC20 part, daiamid epoxy curing agent 1.5 parts, 20 parts of phenolic resin.
The preparation method of above-mentioned high-temperature-resistant insulating paint is: (1) grinds after mica powder, Pulvis Talci, SiC mixing, grinds
It is 40um to particle diameter;(2) by polysiloxane resin, acrylic resin, sodium polyacrylate, dimethylbenzene, Oleum Terebinthinae, acetic acid fourth
Ester, mixing post-heating to temperature is 80 DEG C, stirs 120 minutes;(3) granulate mixture that step (1) obtains is joined step
(2), in mixed resin solution, stir 80 minutes, ultrasonic shear 20 minutes;(4) LaMgAl is added11O19, phenolic resin, stir
Mix 80 minutes.
With reference to GB1981-81, the high-temperature-resistant insulating paint of preparation in the embodiment of the present invention is carried out performance test, Ge Xiangxing
Can result see table, it may be seen that this high-temperature-resistant insulating paint has good resistance to elevated temperatures, at 600 DEG C, paint film
Normally;At room temperature, optimal specific insulation is more than or equal to 1.9 × 1017Ω cm, breakdown strength is more than or equal to 196KV/m,
The optimal specific insulation of room temperature is returned to more than or equal to 7.2 × 10 through 50h lower17Ω cm, breakdown strength is more than or equal to
226KV/mm。
The property indices of table 1 high-temperature-resistant insulating paint
Claims (7)
1. a high-temperature-resistant insulating paint, it is characterised in that be prepared from by weight by following component: polysiloxane tree
Fat 15-40 part, mica powder 5-15 part, Pulvis Talci 5-15 part, acrylic resin 0.1-1 part, sodium polyacrylate 0.1-0.5 part, two
Toluene 5-15 part, Oleum Terebinthinae 1-10 part, butyl acetate 1-5 part, LaMgAl11O193-8 part, SiC10-20 part, daiamid epoxy are solid
Agent 0.5-1.5 part, phenolic resin 20-40 part, glimmering brilliant Fluorspar Powder 5-15 part, ceramic fine bead 3-10 part, gas-phase silica 3-10
Part, glass fibre 2-8 part.
A kind of high-temperature-resistant insulating paint the most according to claim 1, it is characterised in that prepared by weight by following component
Form: polysiloxane resin 25-35 part, mica powder 6-12 part, Pulvis Talci 6-11 part, acrylic resin 0.3-0.8 part, poly-
Sodium acrylate 0.2-0.4 part, dimethylbenzene 8-15 part, Oleum Terebinthinae 3-7 part, butyl acetate 2-4 part, LaMgAl11O195-7 part,
SiC12-18 part, daiamid epoxy curing agent 0.8-1.2 part, phenolic resin 25-38 part, glimmering brilliant Fluorspar Powder 7-13 part, pottery are micro-
Pearl 4-8 part, gas-phase silica 4-8 part, glass fibre 4-6 part.
3. the preparation method of a high-temperature-resistant insulating paint, it is characterised in that comprise the following steps:
(1) grinding after mica powder, Pulvis Talci, SiC, glimmering brilliant Fluorspar Powder, gas-phase silica mixing, being ground to particle diameter is 20-
40um;
(2) by polysiloxane resin, acrylic resin, sodium polyacrylate, dimethylbenzene, Oleum Terebinthinae, butyl acetate, after mixing
It is heated to temperature and is 60-80 DEG C, stir 120-180 minute;
(3) granulate mixture that step (1) obtains is joined in the mixed resin solution of step (2), stirs 60-80 minute,
Ultrasonic shear 20-40 minute;
(4) LaMgAl is added11O19, phenolic resin, glass fibre, ceramic fine bead, stir 50-80 minute.
The preparation method of a kind of high-temperature-resistant insulating paint the most according to claim 3, it is characterised in that: described step (1)
Middle particle diameter is 20-30um.
The preparation method of a kind of high-temperature-resistant insulating paint the most according to claim 3, it is characterised in that: described step (2)
Middle temperature is 65-75 DEG C, and mixing time is 140-160 minute.
The preparation method of a kind of high-temperature-resistant insulating paint the most according to claim 3, it is characterised in that: described step (3)
Middle stirring 65-75 minute, ultrasonic shear 25-35 minute.
The preparation method of a kind of high-temperature-resistant insulating paint the most according to claim 3, it is characterised in that: described step (4)
Middle mixing time is 60-70 minute.