CN106218182A - A kind of preparation method of moldproof polyethylene light-type conveyer belt - Google Patents
A kind of preparation method of moldproof polyethylene light-type conveyer belt Download PDFInfo
- Publication number
- CN106218182A CN106218182A CN201510728266.2A CN201510728266A CN106218182A CN 106218182 A CN106218182 A CN 106218182A CN 201510728266 A CN201510728266 A CN 201510728266A CN 106218182 A CN106218182 A CN 106218182A
- Authority
- CN
- China
- Prior art keywords
- mildew
- conveyer belt
- preparation
- type conveyer
- polyethylene light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to handling and conveying band technical field, be specifically related to the preparation method of a kind of moldproof polyethylene light-type conveyer belt, antifungus agent and water are configured to the mildew-retarding liquid that concentration is 50-100g/L;Be impregnated in by fabric in mildew-retarding liquid, pickup is 150-200g/m2, heat-shaping, form mildew-proof fabric;PE is combined by the method using calendering with mildew-proof fabric, forms conveyer belt composite bed;In recombination process, rolling temperature is 130-150 DEG C, and composite pressure is 10-15Pa;The PE surface of conveyer belt composite bed is carried out sided corona treatment;Antifungus agent is added in water polyurethane surface treating agent formation mildew-resistant surface treatment liquid, then mildew-resistant surface treatment liquid is coated in the PE surface of the conveyer belt composite bed after sided corona treatment, dries.Shown moldproof polyethylene light-type conveyer belt can kill mycete, and suppresses mycete to regenerate, harmless, and has the highest chemical stability and heat stability.
Description
Technical field
The invention belongs to handling and conveying band technical field, be specifically related to the preparation method of a kind of moldproof polyethylene light-type conveyer belt.
Background technology
Flourish along with logistic industry, logistics streamline equipment develops the most therewith, and this development proposes requirements at the higher level to the conveyer belt as streamline visual plant.PE light-type conveyer belt is typically with polyester textile as framework material, mainly for delivery of quality article light, middle.PE light-type conveyer belt is lightweight with it, life-span length, easy for installation, be not likely to produce the advantages such as friction, be widely used in the industries such as food processing, Nicotiana tabacum L..But at the processing environment that food or Nicotiana tabacum L. etc. are damp and hot, on conveyer belt, easy mould growth, pollutes product.Such as, the tobacco product hot and humid environment in the course of processing, it is easy to make PE light-type conveyer belt surface contamination mycete and can breed rapidly and extend, bringing harm to the health of tobacco product quality and people.
Therefore, meeting in the performance basis such as PE light-type conveyer belt physics and machinery, giving PE light-type conveyer belt mildew-resistant, drive mould function, there is very important practical value, the health level improving the people is had positive and important meaning.
Summary of the invention
It is an object of the invention to provide the preparation method of a moldproof polyethylene light-type conveyer belt, the fungistatic effect of mildew-resistant conveyer belt prepared by the method is notable, lasting, and nontoxic, complies fully with U.S. FDA food hygienic standard and EU REACH Legislation.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of preparation method of moldproof polyethylene light-type conveyer belt, its step includes:
(1), antifungus agent and water are configured to the mildew-retarding liquid that concentration is 50-100g/L;
(2), by fabric impregnated in the mildew-retarding liquid in step (1), pickup is 150-200g/m2, heat-shaping, form mildew-proof fabric;Preferably, described fabric is PET polyester textile.
(3), use the method for calendering to be combined with mildew-proof fabric by PE, form conveyer belt composite bed;In recombination process, rolling temperature is 130-150 DEG C, and composite pressure is 10-15Pa, and the cloth surface temperature of mildew-proof fabric is maintained at 120-150 DEG C;
(4), the PE surface of the conveyer belt composite bed in step (3) is carried out sided corona treatment;
(5), by antifungus agent it is added in water polyurethane surface treating agent formation mildew-resistant surface treatment liquid, then mildew-resistant surface treatment liquid is coated in step (4) the PE surface of the conveyer belt composite bed after sided corona treatment, dries.
In described step (2), it is 0.5-1 minute that fabric impregnated in the dip time of mildew-retarding liquid;The condition of described heat-shaping is Far-infrared Heating, and heating-up temperature is 80-90 DEG C.Fabric be impregnated in mildew-retarding liquid so that be filled with mildew-retarding liquid between the surface of fabric and the gap of fabric, add the anti-mold effect of final products.
In described step (3), the thickness of the PE layer in described conveyer belt composite bed is 0.05-0.1cm, and the thickness of mildew-proof fabric is 0.05cm.Suitably textile matte structure and thickness, determines conveyer belt and has and the most flexible the most also have higher intensity, can meet the needs of various use environment.
In described step (4), during sided corona treatment, the corona time is 0.5-1 minute, corona discharge power 1-3KW;Preferably, during sided corona treatment, the corona time is 0.5 minute, corona discharge power 1.95KW.PE surface is processed, the attachment of follow-up mildew-resistant surface treatment liquid, preferred corona condition, determine the existing a number of active group in PE surface, it is easy to follow-up mildew-resistant process, the structure of PE will not be caused excessive injury again, affect its serviceability.
In described step (5), the antifungus agent content in mildew-resistant surface treatment liquid is 0.5-2%;Mildew-resistant surface treatment liquid coated weight is 20-40g/m2.Preferably, the antifungus agent content in mildew-resistant surface treatment liquid is 1%;Mildew-resistant surface treatment liquid coated weight is 30g/m2.Coating by mildew-resistant surface treatment liquid so that antifungus agent can concentrate on PE surface, and suitably coated weight, determine itself and the PE compatibility, thus have impact on mildew-resistant endurance.Coated weight is too much, easily causes unnecessary waste, adds production cost, and coated weight is very few, does not reaches anti-mold effect.
Preferably, described antifungus agent is N-(2-2 chlorovinyl) salicylamide.
The invention has the beneficial effects as follows:
1, the moldproof polyethylene light-type conveyer belt prepared by the present invention can kill mycete, and suppresses mycete to regenerate, harmless, and has the highest chemical stability and heat stability.
2, the antifungus agent on the moldproof polyethylene light-type conveyer belt surface in the present invention is good with the PE compatibility, processing characteristics and other mechanical property on conveyer belt are without impact, antifungus agent concentrates on PE surface, there is the most potent anti-mold effect, and the fabric of conveyer belt also impregnated in mildew-retarding liquid, significantly increased anti-mold effect.
3, the present invention provides moldproof polyethylene light-type conveyer belt to comply fully with U.S. FDA food hygienic standard and EU REACH Legislation, is a kind of long-lived conveying products, can be used for the conveying in the field such as food, medicine.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
(1) configuration of mildew-retarding liquid: N-(2-2 chlorovinyl) salicylamide and water are configured to the mildew-retarding liquid of N-(2-2 chlorovinyl) salicylamide concentration 60g/L;
(2), by PET polyester textile impregnated in the mildew-retarding liquid in step (1), dip time is 0.5-1 minute, and pickup is 150g/m2, is dried through Far-infrared Heating baking oven and shapes, baking temperature 80 DEG C, forms mildew-proof fabric;
(3), use the method for calendering to be combined with mildew-proof fabric by PE, form conveyer belt composite bed;In recombination process, rolling temperature is 130 DEG C, and composite pressure is 10Pa, and the cloth surface temperature of mildew-proof fabric remains at 120-150 DEG C;
(4), the PE surface of the conveyer belt composite bed in step (3) being carried out sided corona treatment, the corona time is 0.5 minute, corona discharge power 1.95KW;
(5), the configuration of mildew-resistant surface treatment liquid: antifungus agent is added in water polyurethane surface treating agent formation mildew-resistant surface treatment liquid, and the concentration of the antifungus agent in this treatment fluid is 1%;
(6), by mildew-resistant surface treatment liquid being coated in step (4) the PE surface of the conveyer belt composite bed after sided corona treatment, mildew-resistant surface treatment liquid coated weight is 30g/m2, dry for 85-90 DEG C.
The moldproof polyethylene light-type conveyer belt prepared in the present embodiment is carried out fungicidal properties test, and concrete test result is as shown in table 1.
Embodiment 2
(1) configuration of mildew-retarding liquid: N-(2-2 chlorovinyl) salicylamide and water are configured to the mildew-retarding liquid of N-(2-2 chlorovinyl) salicylamide concentration 100g/L;
(2), by PET polyester textile impregnated in the mildew-retarding liquid in step (1), dip time is 0.5 minute, and pickup is 200g/m2, is dried through Far-infrared Heating baking oven and shapes, baking temperature 90 DEG C, forms mildew-proof fabric;
(3), use the method for calendering to be combined with mildew-proof fabric by PE, form conveyer belt composite bed;In recombination process, rolling temperature is 150 DEG C, and composite pressure is 15Pa, and the cloth surface temperature of mildew-proof fabric remains at 120-150 DEG C;
(4), the PE surface of the conveyer belt composite bed in step (3) being carried out sided corona treatment, the corona time is 0.5 minute, corona discharge power 1.95KW;
(5), the configuration of mildew-resistant surface treatment liquid: with embodiment 1;
(6), by mildew-resistant surface treatment liquid being coated in step (4) the PE surface of the conveyer belt composite bed after sided corona treatment, mildew-resistant surface treatment liquid coated weight is 25g/m2, dry for 85-90 DEG C.
The moldproof polyethylene light-type conveyer belt prepared in the present embodiment is carried out fungicidal properties test, and concrete test result is as shown in table 1.
Comparative example 1:
PE with PET polyester textile is combined by the method using calendering, and in recombination process, rolling temperature is 150 DEG C, and composite pressure is 15Pa, forms polyethylene light conveyer belt.Concrete test result is as shown in table 1.
Fungus-proof test: the conveyer belt prepared in above-described embodiment and comparative example carries out fungicidal properties test, and result is as shown in table 1 below;
As shown in Table 1, moldproof polyethylene light-type conveyer belt prepared by the present invention, having preferable anti-mold effect, mildew-resistant grade is 0 grade.Additionally, this moldproof polyethylene light-type conveyer belt safety non-toxic, meet hygienic requirements, the pollution to environment is not caused while harmless, comply fully with U.S. FDA food hygienic standard and EU REACH Legislation, and there is extraordinary anti-mold effect, can be used for the transport of the product such as food, Nicotiana tabacum L..
The above is presently preferred embodiments of the present invention, but the present invention should not be limited to this embodiment disclosure of that.So every without departing from the equivalence completed under spirit disclosed in this invention or amendment, both fall within the scope of protection of the invention.
Claims (8)
1. a preparation method for moldproof polyethylene light-type conveyer belt, its step includes:
(1), antifungus agent and water are configured to the mildew-retarding liquid that concentration is 50-100g/L;
(2), by fabric impregnated in the mildew-retarding liquid in step (1), pickup is 150-200g/m2, heat-shaping, form mildew-proof fabric;
(3), use the method for calendering to be combined with mildew-proof fabric by PE, form conveyer belt composite bed;In recombination process, rolling temperature is 130-150 DEG C, and composite pressure is 10-15Pa, and the cloth surface temperature of mildew-proof fabric is maintained at 120-150 DEG C;
(4), the PE surface of the conveyer belt composite bed in step (3) is carried out sided corona treatment;
(5), by antifungus agent it is added in water polyurethane surface treating agent formation mildew-resistant surface treatment liquid, then mildew-resistant surface treatment liquid is coated in step (4) the PE surface of the conveyer belt composite bed after sided corona treatment, dries.
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 1, it is characterised in that: in described step (2), it is 1-2 minute that fabric impregnated in the dip time of mildew-retarding liquid;The condition of described heat-shaping is Far-infrared Heating, and heating-up temperature is 80-90 DEG C.
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 1, it is characterised in that: in described step (3), the thickness of the PE layer in described conveyer belt composite bed is 0.05-0.1cm, and the thickness of mildew-proof fabric is 0.05cm.
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 1, it is characterised in that: in described step (4), during sided corona treatment, the corona time is 0.5-1 minute, corona discharge power 1-3KW.
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 4, it is characterised in that: during sided corona treatment, the corona time is 0.5 minute, corona discharge power 1.95KW.
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 1, it is characterised in that: in described step (5), the antifungus agent content in mildew-resistant surface treatment liquid is 0.5-2%;Mildew-resistant surface treatment liquid coated weight is 20-40g/m2。
The preparation method of moldproof polyethylene light-type conveyer belt the most according to claim 6, it is characterised in that: in described step (5), the antifungus agent content in mildew-resistant surface treatment liquid is 1%;Mildew-resistant surface treatment liquid coated weight is 30g/m2。
8. according to the preparation method of the moldproof polyethylene light-type conveyer belt described in claim 1,6 or 7, it is characterised in that: described antifungus agent is N-(2-2 chlorovinyl) salicylamide.