CN103224641A - Coating process of latex gloves - Google Patents
Coating process of latex gloves Download PDFInfo
- Publication number
- CN103224641A CN103224641A CN2013101185208A CN201310118520A CN103224641A CN 103224641 A CN103224641 A CN 103224641A CN 2013101185208 A CN2013101185208 A CN 2013101185208A CN 201310118520 A CN201310118520 A CN 201310118520A CN 103224641 A CN103224641 A CN 103224641A
- Authority
- CN
- China
- Prior art keywords
- emgloves
- coating process
- latex gloves
- minutes
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a coating process of latex gloves, which relates to the technical field of latex gloves production, and is characterized in comprising (1) based on the weight, thoroughly mixing 70-95 parts of acrylic acid ester with 5-30 parts of polyurethane; (2) heating the liquid mixture up to the temperature of between 20 and 30 DEG C; (3) placing the latex gloves into the mixed solution obtained by step (2) to be continuously soaked for 2 to 5 minutes; (4) moving the latex gloves into the coagulant solution to be continuously soaked for 2 to 5 minutes; (5) taking out, turning over and drying the resultant latex gloves obtained by step (4). The present invention has simple technological operation, few components and steps, and coating process is easy to control with good coating effect.
Description
Technical field:
The present invention relates to the production technical field of emgloves, specifically is the coating process of emgloves.
Background technology:
Emgloves is a kind of in the gloves, its different and general gloves, and it is processed by latex.Can be used as industries such as family, industry, medical treatment, beauty treatment and use, is indispensable hand protection articles for use.Adopt natural emulsion, be equipped with the emgloves that other meticulous auxiliary agent processes, product is handled through special surface, dresses comfortablely, all has a wide range of applications in industrial and agricultural production, medical treatment, daily life.The surfaces externally and internally of emgloves can scribble the coated membrane of one deck waterproof, and traditional steeping fluid that is used for coating has plenty of peptizer is mixed with main raw material of coating mould etc., Jin Zi weak effect like this, and component is more, and technology is more loaded down with trivial details.
Summary of the invention:
It is a kind of simple to operate that technical problem to be solved by this invention is to provide, and step is less, the coating process of the emgloves that coating result is good.
Technical problem to be solved by this invention adopts following technical scheme to realize:
The coating process of emgloves is characterized in that:
(1) be that 70～95 acrylate and weight part are that 5～30 urethane fully mixes with weight part;
(2), make its temperature reach 20～30 ℃ with mixed liquid heat;
(3) emgloves is put in the mixed solution in the step (2), continued to soak 2～5 minutes;
(4) emgloves is taken out, put lasting the immersion 2～5 minutes in the coagulant solution into;
(5) will carry out emgloves after the step (4) takes out flange and dries.
Described coagulant solution is one or more in gelatin, calcium chloride solution and the ca nitrate soln.
The concentration of described calcium chloride solution and ca nitrate soln is 1～3%.
The invention has the beneficial effects as follows: technological operation of the present invention is simple, and component is few, and step is few, control easily, and coating result is good.
Embodiment:
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
The coating process of emgloves follows these steps to carry out:
(1) be that 85 acrylate and weight part are that 15 urethane fully mixes with weight part;
(2), make its temperature reach 25 ℃ with mixed liquid heat;
(3) emgloves is put in the mixed solution in the step (2), continued to soak 3 minutes;
(4) emgloves is taken out, put lasting the immersion 3 minutes in the coagulant solution into;
(5) will carry out emgloves after the step (4) takes out flange and dries.
Coagulant solution is that the mixing in calcium chloride solution and the ca nitrate soln is easy.
The concentration of calcium chloride and nitrocalcite mixing solutions is 2%.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in the foregoing description and the specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. the coating process of emgloves is characterized in that:
(1) be that 70～95 acrylate and weight part are that 5～30 urethane fully mixes with weight part;
(2), make its temperature reach 20～30 ℃ with mixed liquid heat;
(3) emgloves is put in the mixed solution in the step (2), continued to soak 2～5 minutes;
(4) emgloves is taken out, put lasting the immersion 2～5 minutes in the coagulant solution into;
(5) will carry out emgloves after the step (4) takes out flange and dries.
2. the coating process of emgloves according to claim 1, it is characterized in that: described coagulant solution is one or more in gelatin, calcium chloride solution and the ca nitrate soln.
3. the coating process of emgloves according to claim 2, it is characterized in that: the concentration of described calcium chloride solution and ca nitrate soln is 1～3%.