CN106217669A - 一种提高粘合剂分散的混炼工艺 - Google Patents

一种提高粘合剂分散的混炼工艺 Download PDF

Info

Publication number
CN106217669A
CN106217669A CN201610590599.8A CN201610590599A CN106217669A CN 106217669 A CN106217669 A CN 106217669A CN 201610590599 A CN201610590599 A CN 201610590599A CN 106217669 A CN106217669 A CN 106217669A
Authority
CN
China
Prior art keywords
binding agent
refining
rolling
rotating speed
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610590599.8A
Other languages
English (en)
Other versions
CN106217669B (zh
Inventor
高雪梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SP Reifenwerke GmbH
Original Assignee
SP Reifenwerke GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SP Reifenwerke GmbH filed Critical SP Reifenwerke GmbH
Priority to CN201610590599.8A priority Critical patent/CN106217669B/zh
Publication of CN106217669A publication Critical patent/CN106217669A/zh
Application granted granted Critical
Publication of CN106217669B publication Critical patent/CN106217669B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种提高粘合剂分散的混炼工艺，将RA65粘合剂、N375炭黑、TR551橡胶混合后轧炼成二段胶TR552，所述各组分的比例是以TR552橡胶100份为标准，RA65粘合剂5份，N375炭黑5份；所述轧炼的条件为在转速34‑36转/分的轧炼机内以0.31‑0.41MPa的压力轧炼50‑60s；在轧炼过程中，至35‑45s时以17‑19转/分的转速将物料空提10‑20s，然后以34‑36转/分的转速继续对物料轧炼，最后在140‑150℃的条件下进行空提排出二段胶TR552。本发明的优点在于：本发明通过将RA65粘合剂及N375炭黑加入TR551橡胶中混炼，并通过将轧炼机的转速提高0.75倍，使得RA65粘合剂能进一步分散至物料中，进而能制备出分散性较好的TR557成品胶。

Description

一种提高粘合剂分散的混炼工艺
技术领域
本发明涉及一种轮胎用粘布胶的制备工艺，特别涉及一种能够提高轮胎用粘布胶中粘合剂分散性的混炼工艺。
背景技术
TR557成品胶是常用的轮胎粘布胶，其中中含有原材料RA65粘合剂，进而可提高TR557成品胶的粘合性能。
现有的TR557成品胶制备工艺是将RA65粘合剂在终炼胶中加入，但终炼胶转速低，使得RA65粘合剂与重炼胶混炼不均匀，进而使粘合剂分散不好；同时用TR557成品胶压延，会出现压延粘辊现象。
发明内容
本发明要解决的技术问题是提供一种提高粘合剂分散的混炼工艺，通过将RA65粘合剂及N375炭黑加入TR551橡胶中混炼，并通过提高转速，使粘合剂能进一步分散，减缓TR557成品胶压延粘辊现象。
为解决上述技术问题，本发明的技术方案为：一种提高粘合剂分散的混炼工艺，其创新点在于：将RA65粘合剂、N375炭黑、TR551橡胶混合后轧炼成二段胶TR552，所述各组分的比例是以TR551橡胶100份为标准，RA65粘合剂5份，N375炭黑5份；所述轧炼的条件为在转速34-36转/分的轧炼机内以0.31-0.41MPa的压力轧炼50-60s；在轧炼过程中，至35-45s时以17-19转/分的转速将物料空提10-20s，然后以34-36转/分的转速继续对物料轧炼，最后在140-150℃的条件下进行空提排出二段胶TR552。
本发明的优点在于：本发明提高粘合剂分散的混炼工艺，通过将RA65粘合剂及N375炭黑加入TR552橡胶中混炼，并通过将轧炼机的转速提高0.75倍，使得RA65粘合剂能进一步分散至物料中，进而能制备出分散性较好的TR552二段胶，从而保证TR557成品胶分散均匀；TR557成品胶分散的均匀性可以减缓压延粘辊现象，提高压延速度，并提高加工性能。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明，但并不因此将本发明限制在所述的实施例范围之中。
实施例1
本实施例提高粘合剂分散的混炼工艺，将RA65粘合剂、N375炭黑、TR551橡胶混合后在转速34转/分的轧炼机内以0.41MPa的压力轧炼50s；在轧炼过程中，至35s时以19转/分的转速将物料空提15s，然后以36转/分的转速继续对物料轧炼，最后在150℃的条件下进行空提排出二段胶，排出的二段胶再经加入药粉轧炼，制得TR557成品胶。
实施例2
本实施例提高粘合剂分散的混炼工艺，将RA65粘合剂、N375炭黑、TR551橡胶混合后在转速36转/分的轧炼机内以0.31MPa的压力轧炼60s；在轧炼过程中，至45s时以17转/分的转速将物料空提20s，然后以34转/分的转速继续对物料轧炼，最后在140℃的条件下进行空提排出二段胶，排出的二段胶再经加入药粉轧炼，制得TR557成品胶。
实施例3
本实施例提高粘合剂分散的混炼工艺，将RA65粘合剂、N375炭黑、TR551橡胶混合后在转速35转/分的轧炼机内以0.36MPa的压力轧炼55s；在轧炼过程中，至40s时以18转/分的转速将物料空提15s，然后以35转/分的转速继续对物料轧炼，最后在145℃的条件下进行空提排出二段胶，排出的二段胶再经加入药粉轧炼，制得TR557成品胶。
为了测试TR557成品胶的性能，将实施例1-3提高粘合剂分散的混炼工艺与传统工艺制备得的TR557成品胶进行钢丝压延和小压延试验，试验结果如下：
由上表可以看出，TR557成品胶调整工艺后，小压延按照原先压延工艺生产包边胶，提高了压延速度，钢丝压延生产时无粘辊现象，线速度提高一倍。
以上显示和描述了本发明的基本原理和主要特征以及本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (1)

1.一种提高粘合剂分散的混炼工艺，其特征在于：将RA65粘合剂、N375炭黑、TR551橡胶混合后轧炼成二段胶TR552，所述各组分的比例是以TR551橡胶100份为标准，RA65粘合剂5份，N375炭黑5份；所述轧炼的条件为在转速34-36转/分的轧炼机内以0.31-0.41MPa的压力轧炼50-60s；在轧炼过程中，至35-45s时以17-19转/分的转速将物料空提10-20s，然后以34-36转/分的转速继续对物料轧炼，最后在140-150℃的条件下进行空提排出二段胶TR552。
CN201610590599.8A 2016-07-26 2016-07-26 一种提高粘合剂分散的混炼工艺 Active CN106217669B (zh)