CN106189758B - 防雾组合物、防雾板及防雾涂层 - Google Patents
防雾组合物、防雾板及防雾涂层 Download PDFInfo
- Publication number
- CN106189758B CN106189758B CN201510909500.1A CN201510909500A CN106189758B CN 106189758 B CN106189758 B CN 106189758B CN 201510909500 A CN201510909500 A CN 201510909500A CN 106189758 B CN106189758 B CN 106189758B
- Authority
- CN
- China
- Prior art keywords
- particle
- antifog
- extinction
- weight percentage
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种防雾组合物，其包含：以重量百分比计为90～99.999％的树酯；及以重量百分比计为0.001～10％的吸光发热粒子，其中，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡、氧化锑锡或六硼化镧。该吸光发热粒子能够有效将光能转换为热能，故可以将具有防雾功能的该防雾组合物直接制备成形各式防雾物品，达到维持防雾持久性的功效。
Description
技术领域
本发明是关于一种组合物，特别是一种防雾组合物，本发明另包含该防雾组合物所制成的防雾板，以及由该防雾组合物所制成的防雾涂层。
背景技术
空气中的水气会自然地凝结于表面温度大幅低于空气的物品上，以在物体表面形成小型水珠，这样的自然现象常对于生活造成许多不便，例如：早晨窗户玻璃附着水雾，及至太阳照射而蒸发干燥后，于玻璃上形成恼人水渍；不仅于此，对居住在气温低寒地区的人民来说，水雾凝结的问题更可能产生意外事故，例如：经常凝结于车窗玻璃雾水是行车安全的一大隐忧，因此，如何有效防止雾水凝结于物品上，便成了相当重要的课题。
一般而言，目前常利用一除雾剂或一电热器以除雾，其中，使用者在欲除雾的物品表面涂布一防雾剂以形成一防雾膜，该防雾剂包含界面活性剂及有机溶剂，当形成该防雾膜后，可以减少水气在物体表面的表面张力，让水气不易在物品表面凝结形成液滴，借此达到防雾的效果。另外，使用者亦可以利用该电热器接触物品表面，以提高物品表面的温度，减少空气中的水气遇冷凝结于物体的情况发生。
然而，该防雾剂的持久性不高，往往于物品表面涂布该防雾剂一段时间后，即因物品与外物产生摩擦、割刮，或遭到大雨冲刷洗涤而使该防雾膜脱落，进而失去对物品的防雾效果，因此当使用该防雾剂以防止雾气在物品表面形成时，必须要经常反复喷涂才能维持效用，然而，由于该喷雾剂含有高挥发性的有机物溶剂，多次喷涂甚至会对人体健康产生负面影响。另外，以该电热器提高物品温度，必须不断提供电力以维持物品于一预定温度，以防止水气遇冷凝结，如此一来，为了防雾而投入大量的能源成本，明显于目前的环保潮流相悖。
有鉴于此，有必要提供一种防雾组合物、防雾板及防雾涂层，以解决过去为了防止雾水形成于物品上而使用该防雾剂及该电热器所产生的问题。
发明内容
本发明提供一种防雾组合物，该防雾组合物可以将光能转换为热能。
本发明提供一种防雾板，该防雾板由前述的防雾组合物所形成者。
本发明提供一种防雾涂层，该防雾涂层由前述的防雾组合物所形成。
本发明提供一种防雾组合物，其包含：以重量百分比计为90～99.999％的树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10％之吸光发热粒子，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡、氧化锑锡或六硼化镧。
本发明的防雾组合物，其中，该含钨氧化物纳米粒子选自由一氧化钨纳米粒子，及一钨青铜复合物纳米粒子所组成的群组。
本发明的防雾组合物，其中，该氧化钨纳米粒子的化学式为WOx，其中，2.2≦x≦3。
本发明的防雾组合物，其中，该钨青铜复合物纳米粒子的化学式为AyWOz，其中，A为主族元素，0.01≦y≦1，2.2≦z≦3。
本发明的防雾组合物，其中，该氧化钨纳米粒子的化学式为WO2.72。
本发明的防雾组合物，其中，A为锂(Li)、钠(Na)、钾(K)、铷(Rb)、铯(Cs)、镁(Mg)、钙(Ca)、锶(Sr)、钡(Ba)、铝(Al)、镓(Ga)、碳(C)、硅(Si)、锡(Sn)、锑(Sb)、氟(F)、氯(Cl)、溴(Br)或碘(I)。
本发明的防雾组合物，其中，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
本发明的防雾组合物，其中，该含钨氧化物纳米粒子的粒径大小为1nm～500nm。
本发明提供一种防雾板，其包含：以重量百分比计为90～99.999％的树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子分散于该树酯中，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡、氧化锑锡或六硼化镧。
本发明的防雾板，其中，该防雾板的厚度为10μm～10mm，且该防雾板包含以重量百分比计0.005～10％的该吸光发热粒子。
本发明的防雾板，其中，该含钨氧化物纳米粒子选自由一氧化钨纳米粒子，及一钨青铜复合物纳米粒子所组成的群组。
本发明的防雾板，其中，该氧化钨纳米粒子的化学式为WOx，其中，2.2≦x≦3。
本发明的防雾板，其中，该钨青铜复合物纳米粒子的化学式为AyWOz，其中，A为主族元素，0.01≦y≦1，2.2≦z≦3。
本发明的防雾板，其中，该氧化钨纳米粒子的化学式为WO2.72。
本发明的防雾板，其中，A为锂(Li)、钠(Na)、钾(K)、铷(Rb)、铯(Cs)、镁(Mg)、钙(Ca)、锶(Sr)、钡(Ba)、铝(Al)、镓(Ga)、碳(C)、硅(Si)、锡(Sn)、锑(Sb)、氟(F)、氯(Cl)、溴(Br)或碘(I)。
本发明的防雾板，其中，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
本发明的防雾板，其中，该含钨氧化物纳米粒子的粒径大小为1nm～500nm。
本发明提供另一种防雾组合物，其包含：以重量百分比计为90～99.999％的粘着剂，该粘着剂为一单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一官能基；及以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡、氧化锑锡或六硼化镧。
本发明的防雾组合物，其中，该粘着剂为一油性压克力胶粘剂、一水性压克力胶粘剂、一聚胺酯胶粘剂或一有机液态硅胶。
本发明的防雾组合物，其中，该油性压克力胶粘剂为一热塑性压克力胶粘剂、一热固性压克力胶粘剂或一聚醇型压克力胶粘剂。
本发明的防雾组合物，其中，该水性压克力胶粘剂为一丙烯酸胶粘剂、一苯丙烯酸胶粘剂或一醋酸丙烯酸胶粘剂。
本发明的防雾组合物，其中，该有机液态硅胶为一有机硅胶粘剂、一甲基有机硅酮胶粘剂、一有机硅醇酸胶粘剂或一有机硅丙烯酸胶粘剂。
本发明的防雾组合物，其中，该含钨氧化物纳米粒子选自由一氧化钨纳米粒子，及一钨青铜复合物纳米粒子所组成的群组。
本发明的防雾组合物，其中，该氧化钨纳米粒子的化学式为WO2.72。
本发明之防雾组合物，其中，该钨青铜复合物纳米粒子的化学式为AyWOz，其中，A为锂(Li)、钠(Na)、钾(K)、铷(Rb)、铯(Cs)、镁(Mg)、钙(Ca)、锶(Sr)、钡(Ba)、铝(Al)、镓(Ga)、碳(C)、硅(Si)、锡(Sn)、锑(Sb)、氟(F)、氯(Cl)、溴(Br)或碘(I)，且0.01≦y≦1，2.2≦z≦3。
本发明的防雾组合物，其中，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
本发明的防雾组合物，其中，该吸光发热粒子的粒径为1nm～500nm。
本发明提供一种防雾涂层，包含：以重量百分比计为90～99.999％的粘着剂，该粘着剂为一单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一官能基；及以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡、氧化锑锡或六硼化镧，其中，该吸光发热粒子分散于该粘着剂中，并经由热固化或紫外光固化以共同形成一防雾涂层。
本发明的防雾涂层，其中，该防雾涂层的厚度为100nm～10mm。
本发明的防雾涂层，其中，该粘着剂为一油性压克力胶粘剂、一水性压克力胶粘剂、一聚胺酯胶粘剂或一有机液态硅胶。
本发明的防雾涂层，其中，该油性压克力胶粘剂为一热塑性压克力胶粘剂、一热固性压克力胶粘剂或一聚醇型压克力胶粘剂。
本发明的防雾涂层，其中，该水性压克力胶粘剂为一丙烯酸胶粘剂、一苯丙烯酸胶粘剂或一醋酸丙烯酸胶粘剂。
本发明的防雾涂层，其中，该有机液态硅胶为一有机硅胶粘剂、一甲基有机硅酮胶粘剂、一有机硅醇酸胶粘剂或一有机硅丙烯酸胶粘剂。
本发明的防雾涂层，其中，该含钨氧化物纳米粒子选自由一氧化钨纳米粒子，及一钨青铜复合物纳米粒子所组成的群组。
本发明的防雾涂层，其中，该氧化钨纳米粒子的化学式为WO2.72。
本发明的防雾涂层，其中，该钨青铜复合物纳米粒子的化学式为AyWOz，其中，A为锂(Li)、钠(Na)、钾(K)、铷(Rb)、铯(Cs)、镁(Mg)、钙(Ca)、锶(Sr)、钡(Ba)、铝(Al)、镓(Ga)、碳(C)、硅(Si)、锡(Sn)、锑(Sb)、氟(F)、氯(Cl)、溴(Br)或碘(I)，且0.01≦y≦1，2.2≦z≦3。
本发明的防雾涂层，其中，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
本发明的防雾组合物包含以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子能够有效地吸收光能，并进一步转换成热能。此外，依据该防雾组合物所包含的树酯或粘着剂的特性，使用者另可以将该防雾组合物进一步成形为该防雾板(亦可以于该基板之防雾面上形成该防雾涂层)，如此即可以借助该吸光发热粒子的作用，使该防雾板(或防雾涂层)的温度上升，使水气无法凝结于该防雾板(或防雾涂层)上，进而达到防雾的效果。
并且，借助将该防雾组合物直接制备成形各式防雾物品，因此，不须在欲防雾的物品上喷涂易于脱落的防雾剂，进而达到维持防雾持久性的功效。
此外，前述的防雾板或形成有该防雾涂层的基板更可以直接作为例如窗户、屋檐等建筑装潢材料之用，或将现有的建筑装潢材料进行防雾涂层之加工，当阳光照射于由该防雾板制成的窗户(或经过防雾涂层加工之窗户)时，窗户因将光能转换为热能使得温度上升，以避免雾气凝结于其上，相较于使用电热器去除窗户表面的雾气，采用本发明的防雾板及形成有该防雾涂层的基板作为建筑装潢材料，可以达到节省防雾所需耗费能量的功效。
附图说明
图1：为本发明防雾板的立体外观图。
图2：为本发明防雾板的剖视放大图。
图3：为聚碳酸酯板第E0组经防雾试验后的照片图。
图4：为本发明防雾板第E1组经防雾试验后的照片图。
具体实施方式
为让本发明的上述及其他目的、特征及优点能更明显易懂，下文特举本发明的较佳实施例，并配合所附图式，作详细说明如下：
本发明防雾组合物包含以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子可以将光能转换为热能，使该防雾组合物具有防雾的效果。
更详言之，该吸光发热粒子为含钨氧化物纳米粒子、氧化铟锡(Indium TinOxide，简称ITO)、氧化锑锡(Antimony Tin Oxide，简称ATO)或六硼化镧(LaB6)，或由上述化合物所组成的群组。其中，该吸光发热粒子的粒径大小为1nm～500nm，且该含钨氧化物纳米粒子可以为氧化钨纳米粒子、钨青铜复合物纳米粒子或上述两者的组合。
详言之，该氧化钨纳米粒子之化学式为WOx，其中，2.2≦x≦3；该钨青铜复合物纳米粒子的化学式为AyWOz，其中，A为元素周期表中的主族元素，0.01≦y≦1，2.2≦z≦3，较佳地，A为锂(Li)、钠(Na)、钾(K)、铷(Rb)、铯(Cs)、镁(Mg)、钙(Ca)、锶(Sr)、钡(Ba)、铝(Al)、镓(Ga)、碳(C)、硅(Si)、锡(Sn)、锑(Sb)、氟(F)、氯(Cl)、溴(Br)或碘(I)，该钨青铜复合物纳米粒子可以为Cs0.33WO3、K0.33WO3、K0.55WO3、Na0.5WO3或Ba0.33WO3纳米粒子。于第一实施例中，该氧化钨纳米粒子为WO2.72纳米粒子，该钨青铜复合物纳米粒子则为Cs0.33WO3纳米粒子。
于本发明第一实施例的防雾组合物可以另包含以重量百分比计为90～99.999％的树酯，该树酯可以为聚碳酸脂(Polycarbonate，简称PC)、聚甲基丙烯酸甲酯(Polymethylmethacrylate，简称PMMA)、玻璃纤维强化塑胶(Fiber Reinforced Plastic，简称FRP)或聚丙烯(Polypropylene，简称PP)；如此，即可以依据所含的树酯种类及其分子量不同，可形成透明、半透明或不透明的防雾板，不同透光度的防雾板各具有不同用途，其中，呈现透明的该防雾板可以作为窗户或其他透视材使用。
请参照图1～2所示，此为本发明防雾板的示意图，该防雾板包含一树酯板1及数个吸光发热粒子2，该数个吸光发热粒子2分散该树酯板1中，该防雾板包含以重量百分比计为90～99.999％的树酯，及以重量百分比计为0.001～10％的吸光发热粒子2，该防雾板具有一厚度d，较佳地，该厚度d为10μm～10mm，且该防雾板可以具有以重量百分比计为0.005～10％的该吸光发热粒子2，其中，该防雾板的该厚度d及该吸光发热粒子2的比例可以互相配合，以达到较佳的除雾效果，举例而言，当该厚度d为10μm时，该防雾板较佳含有100000ppm(即以重量百分比计为10％)的吸光发热粒子；当该厚度d为1mm时，该防雾板较佳含有1000ppm(即以重量百分比计为0.1％)的吸光发热粒子；当该厚度d为2mm时，该防雾板较佳含有500ppm(即以重量百分比计为0.05％)的吸光发热粒子；当该厚度d为10mm时，该防雾板较佳含有50ppm(即以重量百分比计为0.005％)的吸光发热粒子。
该防雾板可以由压出成形法或模具成形法等方法成形，视该树酯的种类、该吸光发热粒子与树酯的混合均匀度及该防雾板的用途进行调整，在此系不多做限制。举例而言：当该树酯为热可塑性树酯(如：聚碳酸酯、聚丙烯或聚甲基丙烯酸甲酯)时，先将该吸光发热粒子2与该树酯于单螺杆压出机或双螺杆压缩机的进料处依预定比例同时进料，并压出各种厚度的该防雾板；当该树酯板的材质为热固性树酯(如：玻璃纤维强化塑胶)时，将特定比例的该吸光发热粒子添加于不饱和聚酯中，并与苯乙烯的单体混合均匀，再加热灌入模具中，以形成特定该厚度d的防雾板。另外，当树酯分别为PC、PMMA、FRP及PP时，成形该防雾板的加工温度较佳分别为250～290℃、180～220℃、80～120℃及190～230℃。
此外，于本发明第二实施例的防雾组合物中，除了包含如前述的以重量百分比计为0.001～10％的该吸光发热粒子之外，另可以包含以重量百分比计为90～99.999％的粘着剂；详而言之，该粘着剂为一单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一官能基。
该粘着剂可以选择为一油性压克力胶粘剂、一水性压克力胶粘剂、一聚胺酯胶粘剂或一有机液态硅胶；举例而言，该油性压克力胶粘剂可以为一热塑性压克力胶粘剂(长兴材料工业股份有限公司，ETERAC 7106-X-58)、一热固性压克力胶粘剂(长兴材料工业股份有限公司，ETERAC 7232-BR-58)或一聚醇型压克力胶粘剂(长兴材料工业股份有限公司，ETERAC 7305-3-XC-50)(有关该油性压克力胶粘剂的特性系可以如http://www.eternal-group.com/Product/Detail？id＝92&lang＝tw所示)；该水性压克力胶粘剂可以为一丙烯酸胶粘剂(长兴材料工业股份有限公司，ETERSOL 1137)、一苯丙烯酸胶粘剂(长兴材料工业股份有限公司，ETERSOL 6515T)或一醋酸丙烯酸胶粘剂(长兴材料工业股份有限公司，ETERSOL 3503)；该聚胺酯胶粘剂可以为例如南宝树脂NP-35或长兴材料工业股份有限公司ETERAC 7786(有关该聚胺酯胶粘剂的特性可以如http://www.nanpao.com.cn/chi/product1.asp？d2＝8及http://www.eternal-group.com/Product/Detail？id＝88&lang＝tw所示)；该有机液态硅胶可以为一有机硅胶粘剂(台湾信越硅利光股份有限公司，KR-282)、一甲基有机硅酮胶粘剂(台湾信越硅利光股份有限公司，KR-500)、一有机硅醇酸胶粘剂(台湾信越硅利光股份有限公司，KR-5206)或一有机硅丙烯酸胶粘剂(台湾信越硅利光股份有限公司，KR-9706)(有关该有机液态硅胶的特性系可以如http://www.shinetsu.com.tw/html/pdt2.asp？area＝65&cat＝212&sn＝85所示)。
又，本发明第二实施例的防雾组合物可以进一步制成一防雾涂层，例如可以利用湿式涂布法涂布于一基板的防雾面，续经由固化即可以于该防雾面形成该防雾涂层。举例而言，该基板的材质选自玻璃、聚碳酸酯或聚丙烯酸甲酯，并且可以依据该基板的材质、或该第二实施例的防雾组合物的组成，选择以刮涂法、淋涂法、滚涂法或喷涂法涂布于该基板的防雾面，另可以选择以热固化法或紫外光固化法以形成该防雾涂层，且该防雾涂层的厚度较佳可以为100nm～10mm，以达到优异的防雾功效。
形成有该防雾涂层之基板可以更进一步制成一防雾门窗或是任何可能因为雾气而影响透光性的结构(例如，车灯的灯罩、眼镜的镜片等)，或者，使用者亦可以依据需求，以市售的门窗作为该基板，于其防雾面上形成该防雾涂层，亦可以获得该防雾门窗。值得注意的是，形成有该防雾涂层的基板的防雾面较佳可以为该基板用以接触低温空气，且较为容易起雾的表面；以冷藏食品展示柜之门为例，该防雾涂层较佳可以形成于该门的内侧表面；以建筑物的窗户为例，该防雾涂层较佳可以形成于窗户的外侧表面以对应气温变化；此外，使用者亦可以选择于该基板的各表面均形成该防雾涂层，于此不加以限制。
本发明的防雾组合物包含以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子能够有效地吸收光能，并进一步转换成热能。此外，依据该防雾组合物所包含的树酯或粘着剂的特性，使用者另可以将该防雾组合物进一步成形为该防雾板(亦可以于该基板的防雾面上形成该防雾涂层)，如此即可以借助该吸光发热粒子的作用，使该防雾板(或防雾涂层)的温度上升，使水气无法凝结于该防雾板(或防雾涂层)上，进而达到防雾的效果。
并且，借助将该防雾组合物直接制备成形各式防雾物品，因此，不须在欲防雾的物品上喷涂易于脱落的防雾剂，进而达到维持防雾持久性的功效。
此外，前述的防雾板或形成有该防雾涂层的基板更可以直接作为例如窗户、屋檐等建筑装潢材料之用，或将现有的建筑装潢材料进行防雾涂层之加工，当阳光照射于由该防雾板制成的窗户(或经过防雾涂层加工之窗户)时，窗户因将光能转换为热能使得温度上升，以避免雾气凝结于其上，相较于使用电热器去除窗户表面的雾气，采用本发明的防雾板及形成有该防雾涂层的基板作为建筑装潢材料，可以达到节省防雾所需耗费能量的功效。
为了证实本发明的防雾组合物所制成的该防雾板确实具有防雾的效用，兹进行下列试验：
温度及防雾能力试验
本试验分别变换不同的实验参数，测验各组与对照组的温度及防雾能力。温度试验方法为将各组放置于室温环境中，以距离15公分的500W的卤素灯照射15秒(第A0、A1组)或30秒(第B0～F0及B1～F1组)，并以红外线温度量测器量测各组照射后的温度数值，防雾能力试验方法为将经卤素灯照射的各组覆盖于盛装80℃热水的杯子开口上方，以肉眼观察水雾附着情况，组别及实验变数的对应关系以及试验结果详如下表1所示，且图3及图4则分别呈现第E0组及第E1组经防雾试验后的情况。其中，第A0～D0及A1～D1组为实心板结构，第E0及E1组为空心板结构。其中F0为厚度3mm的单板清玻璃，F1为涂布0.015mm厚度的含有吸光发热材料浓度以重量百分比计为10％的单板玻璃。
表1：组别及实验变数的对应关系以及试验结果
由本试验的结果可明显看出，照射卤素灯一固定时间后，添加有20～100000ppm的吸光发热粒子的防雾板(第A1、B1、C1、D1、E1及F1组)，相对于由树酯所制成的板状对照组(第A0、B0、C0、D0、E0及F0组)，其温度显著提高。可见相对于对照组，本发明的防雾板能够将照射卤素灯所获得的光能，有效地转换成热能，使该防雾板的温度大幅上升，借此防止空气中的水气遇冷凝结于其上。并且，由图3及图4可知，相较于经照射后的对照组(第E0组)覆盖于热水上方时，表面附着有明显的雾状水珠，经照射的本发明的防雾板(第E1组)表面并未观察到有水珠产生，由此可证本发明防雾板确实可以有效防止雾水形成于该防雾板表面。
综上所述，本发明的防雾组合物包含以重量百分比计为0.001～10％的吸光发热粒子，该吸光发热粒子能够有效地吸收光能，并进一步转换成热能。此外，依据该防雾组合物所包含的树酯或粘着剂的特性，使用者另可以将该防雾组合物进一步成形为该防雾板(亦可以于该基板的防雾面上形成该防雾涂层)，如此即可以借助该吸光发热粒子的作用，使该防雾板(或防雾涂层)的温度上升，使水气无法凝结于该防雾板(或防雾涂层)上，进而达到防雾的效果。
并且，借助将该防雾组合物直接制备成形各式防雾物品，因此，不须在欲防雾的物品上喷涂易于脱落的防雾剂，进而达到维持防雾持久性的功效。
此外，前述的防雾板或形成有该防雾涂层的基板更可以直接作为例如窗户、屋檐等建筑装潢材料之用，或将现有的建筑装潢材料进行防雾涂层的加工，当阳光照射于由该防雾板制成的窗户(或经过防雾涂层加工的窗户)时，窗户因将光能转换为热能使得温度上升，以避免雾气凝结于其上，相较于使用电热器去除窗户表面的雾气，采用本发明的防雾板及形成有该防雾涂层的基板作为建筑装潢材料，可以达到节省防雾所需耗费能量的功效。
以上仅为本发明的较佳实施例，不得以此限定本发明实施的保护范围，因此凡参考本发明的说明书内容所作的简单等效变化与修饰，仍属本发明的保护范围。
Claims (21)
1.一种防雾组合物，其特征在于包含：以重量百分比计为90～99.999%的一个树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子为钨青铜复合物纳米粒子，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
2.一种防雾组合物，其特征在于包含：以重量百分比计为90～99.999%的一个树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子为氧化钨纳米粒子，该氧化钨纳米粒子之化学式为WO2.72。
3.如权利要求1或2所述的防雾组合物，其特征在于，其中，该吸光发热粒子的粒径为1nm～500 nm。
4.一种防雾板，其特征在于包含：以重量百分比计为90～99.999%的一个树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子分散于该树酯中，该吸光发热粒子为钨青铜复合物纳米粒子，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
5.一种防雾板，其特征在于包含：以重量百分比计为90～99.999%的一个树酯，该树酯为聚碳酸脂、聚甲基丙烯酸甲酯、玻璃纤维强化塑胶或聚丙烯；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子分散于该树酯中，该吸光发热粒子为氧化钨纳米粒子，该氧化钨纳米粒子的化学式为WO2.72。
6.如权利要求4或5所述的防雾板，其特征在于，其中，该防雾板的厚度为10 μm～10mm，且该防雾板包含以重量百分比计0.005～10%的该吸光发热粒子。
7.如权利要求4或5所述的防雾板，其特征在于，其中，该吸光发热粒子的粒径为1 nm～500 nm。
8.一种防雾组合物，其特征在于包含：以重量百分比计为90~99.999%的一个粘着剂，该粘着剂为一个单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一个官能基；及以重量百分比计为0.001~10%的一个吸光发热粒子，该吸光发热粒子为钨青铜复合物纳米粒子，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3。
9.一种防雾组合物，其特征在于包含：以重量百分比计为90～99.999%的一个粘着剂，该粘着剂为一个单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一个官能基；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子为氧化钨纳米粒子，该氧化钨纳米粒子的化学式为WO2.72。
10.如权利要求8或9所述的防雾组合物，其特征在于，其中，该粘着剂为一个油性压克力胶粘剂、一个水性压克力胶粘剂、一个聚氨 酯胶粘剂或一个有机液态硅胶。
11.如权利要求10所述的防雾组合物，其特征在于，其中，该油性压克力胶粘剂为一个热塑性压克力胶粘剂、一个热固性压克力胶粘剂或一个聚醇型压克力胶粘剂。
12.如权利要求10所述的防雾组合物，其特征在于，其中，该水性压克力胶粘剂为一个丙烯酸胶粘剂、一个苯丙烯酸胶粘剂或一个醋酸丙烯酸胶粘剂。
13.如权利要求10所述的防雾组合物，其特征在于，其中，该有机液态硅胶为一个有机硅胶粘剂、一个甲基有机硅酮胶粘剂、一个有机硅醇酸胶粘剂或一个有机硅丙烯酸胶粘剂。
14.如权利要求8或9所述的防雾组合物，其特征在于，其中，该吸光发热粒子的粒径为1nm～500 nm。
15.一种防雾涂层，其特征在于包含：以重量百分比计为90~99.999%的一个粘着剂，该粘着剂为一个单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一个官能基；及以重量百分比计为0.001~10%的一个吸光发热粒子，该吸光发热粒子为钨青铜复合物纳米粒子，该钨青铜复合物纳米粒子的化学式为Cs0.33WO3；其中，该吸光发热粒子分散于该粘着剂中，并经由热固化或紫外光固化以共同形成一个防雾涂层。
16.一种防雾涂层，其特征在于包含：以重量百分比计为90～99.999%的一个粘着剂，该粘着剂为一个单体或包含该单体的寡聚物，该单体具有选自由硅氧基、丙烯酸基、氨基甲酸酯基所组成的群组的一个官能基；及以重量百分比计为0.001～10%的一个吸光发热粒子，该吸光发热粒子为氧化钨纳米粒子，该氧化钨纳米粒子的化学式为WO2.72；其中，该吸光发热粒子分散于该粘着剂中，并经由热固化或紫外光固化以共同形成一个防雾涂层。
17.如权利要求15或16所述的防雾涂层，其特征在于，其中，该防雾涂层的厚度为100nm～10 mm。
18.如权利要求15或16所述的防雾涂层，其特征在于，其中，该粘着剂为一个油性压克力胶粘剂、一个水性压克力胶粘剂、一个聚氨 酯胶粘剂或一个有机液态硅胶。
19.如权利要求18所述的防雾涂层，其特征在于，其中，该油性压克力胶粘剂为一个热塑性压克力胶粘剂、一个热固性压克力胶粘剂或一个聚醇型压克力胶粘剂。
20.如权利要求18所述的防雾涂层，其特征在于，其中，该水性压克力胶粘剂为一个丙烯酸胶粘剂、一个苯丙烯酸胶粘剂或一个醋酸丙烯酸胶粘剂。
21.如权利要求18所述的防雾涂层，其特征在于，其中，该有机液态硅胶为一个有机硅胶粘剂、一个甲基有机硅酮胶粘剂、一个有机硅醇酸胶粘剂或一个有机硅丙烯酸胶粘剂。