CN106183321B - 纸质载带用盖带 - Google Patents
纸质载带用盖带 Download PDFInfo
- Publication number
- CN106183321B CN106183321B CN201610585945.3A CN201610585945A CN106183321B CN 106183321 B CN106183321 B CN 106183321B CN 201610585945 A CN201610585945 A CN 201610585945A CN 106183321 B CN106183321 B CN 106183321B
- Authority
- CN
- China
- Prior art keywords
- functional layer
- layer
- cover strip
- carrying belt
- paper carrying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种纸质载带用盖带，包括：基材层；位于所述基材层之上的中间层；依次设置在中间层之上的第一功能层和第二功能层，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；所述第一功能层的主成分为乙烯丙烯共聚物以及聚苯乙烯和聚丁二烯加氢得到的乙烯‑丁烯为中间弹性嵌段的线性三嵌共聚物；所述第二功能层包括纳米级氧化锡及锑混合物、蜡、SEBS、丙烯酸酯。本发明通过选择合适的第一功能层和第二功能层，剥离时第二功能层残留在载带上，解决了拉起纸纤维问题且不影响元器件的取用；并一定程度上提高了盖带软化点，在高温高湿下不会出现融胶现象。
Description
技术领域
本发明属于电子元器件的包装领域，涉及一种纸质载带用盖带。
背景技术
电子元器件的运输与使用，一般需要用到包装承载体，承载体一般有纸质载带或塑料载带，载带设有电子元器件形状的口袋，以收纳电子元器件。收纳完成后，在载带上表面均需覆盖一层盖带，以防止载带收纳的电子元器件逃逸出来，也保护电子元器件不受外界灰尘及静电等的干扰；盖带既需要可以与收纳载带表面密封，又要在使用电子元器件时可以与收纳载带表面相互剥离。如申请号为201510335854X公开的一种电子元器件收纳载带的封装带，包括基材层、稳定层、连接层、中间层以及通用粘合层，可以与收纳载带的表面热封，又可以控制一定的剥离力，在需要时剥离开封装带，暴露出电子元器件；封装带的使用性能也稳定，卷曲时不会出现开裂、爆带的情况。其主要是针对收纳大型电子元器件的塑料载带，而对于纸质载带，粘合层树脂受挤压易渗入纸纤维内。取用元器件时，需将盖带剥离纸质载带，剥离力同时也会拉起载带纸纤维（因之前封合时树脂渗入纸纤维中），引起毛屑现象，而一般毛屑尺寸大于元器件，因此会挡住载带收纳元器件的口袋，影响贴片机的取用。而上述专利中的通用粘合层对纸质载带并不适用，连接力和剥离力都不理想。
发明内容
本发明的目的是针对纸质载带，提供一种盖带，采用内聚剥离，剥离时第一功能层与第二功能层分离，第二功能层残留在载带上，解决了拉起纸纤维问题且不影响元器件的取用。
为了达到上述目的，本发明采用如下的技术方案：
用于封装纸质载带的盖带，包括：
用于形成盖带主体并提供支撑强度的基材层；
位于所述基材层之上并用于增强盖带韧性的中间层；
涂覆在所述中间层之上的第一功能层；
覆盖在所述第一功能层之上的第二功能层，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；
所述第一功能层的主成分为乙烯丙烯共聚物以及聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物；
所述第二功能层包括纳米级氧化锡及锑混合物、蜡、SEBS、丙烯酸酯。
上述技术方案，通过设定特定组分的第一功能层和第二功能层，第二功能层与纸质载带之间具有稳定的连接力，且连接力大于第一功能层与第二功能层之间的连接力，剥离时第二功能层残留在载带上，解决了拉起纸纤维问题且不影响元器件的取用；
纸质载带不同于塑料载带，所以第二功能层需要特定的组分配方，本方案中的配方与纸质纤维之间的结合力好，并且具热封粘合功能，能够实现盖带低温快速封合，添加的蜡会迁移至表面，防止盖带表面粘结。第一功能层与第二功能层配合，其两者之间具有一定的连接力，并且要保证两者之间的连接力小于第二功能层与纸质载带之间的连接力。
而且第一、二功能层在一定程度上提高了盖带软化点，在高温高湿下不会出现融胶现象。
作为优选，所述第一功能层的主成分包括：乙烯丙烯共聚物20质量%-60质量%、聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物40质量%-80质量%。
作为优选，所述第二功能层各成分添加的重量份如下：纳米级氧化锡与锑的混合物0.5-1.5份、蜡0.1-0.5份；SEBS 50-75份、丙烯酸酯10-25份。
作为优选，纳米级氧化锡与锑的混合比为80-95:5。
作为优选，所述蜡为聚酯蜡，防粘结效果更好。
作为优选，所述中间层为乙烯丙烯酸甲酯共聚物层，能够增加盖带整体韧性，即使之具有良好的抗拉伸度、不易断。
作为优选，所述中间层的厚度为8μm-16μm。
作为优选，所述第二功能层的厚度为1μm-2μm。
通过实施上述技术方案，本发明具有如下的有益效果：本发明通过选择合适的第一功能层和第二功能层，第二功能层与纸质载带之间具有稳定的连接力，且连接力大于第一功能层与第二功能层之间的连接力，剥离时第二功能层残留在载带上，解决了拉起纸纤维问题且不影响元器件的取用；并一定程度上提高了盖带软化点，在高温高湿下不会出现融胶现象。
具体实施方式
下面结合具体实施例，对本发明作进一步详细说明。
实施例1：
一种纸质载带用盖带，包括：
用于形成盖带主体并提供支撑强度的基材层；
位于所述基材层之上并用于增强盖带韧性的中间层，为乙烯丙烯酸甲酯共聚物层，厚度为8μm；
涂覆在所述中间层之上的第一功能层；
覆盖在所述第一功能层之上的第二功能层，厚度为2μm，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；
所述第一功能层的主成分包括：乙烯丙烯共聚物20质量%、聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物80质量%；
所述第二功能层包括如下质量百分比组分：纳米级氧化锡与锑的混合物1份、聚酯蜡0.25份；SEBS 65份、丙烯酸酯15份；其中，纳米级氧化锡与锑的混合比为80:5。
实施例2：
一种纸质载带用盖带，包括：
用于形成盖带主体并提供支撑强度的基材层；
位于所述基材层之上并用于增强盖带韧性的中间层，为乙烯丙烯酸甲酯共聚物层，厚度为10μm；
涂覆在所述中间层之上的第一功能层；
覆盖在所述第一功能层之上的第二功能层，厚度为1.5μm，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；
所述第一功能层的主成分包括：乙烯丙烯共聚物50质量%、聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物50质量%；
所述第二功能层包括如下质量百分比组分：纳米级氧化锡与锑的混合物0.5份、聚酯蜡0.5份；SEBS 50份、丙烯酸酯25份；其中，纳米级氧化锡与锑的混合比为95:5。
实施例3：
一种纸质载带用盖带，包括：
用于形成盖带主体并提供支撑强度的基材层；
位于所述基材层之上并用于增强盖带韧性的中间层，为乙烯丙烯酸甲酯共聚物层，厚度为16μm；
涂覆在所述中间层之上的第一功能层；
覆盖在所述第一功能层之上的第二功能层，厚度为1μm，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；
所述第一功能层的主成分包括：乙烯丙烯共聚物60质量%、聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物40质量%；
所述第二功能层包括如下重量份的组分：纳米级氧化锡与锑的混合物1.5份、聚酯蜡0.1份；SEBS 75份、丙烯酸酯10份；其中，纳米级氧化锡与锑的混合比为90:5。
Claims (6)
1.纸质载带用盖带，其特征在于，包括：
用于形成盖带主体并提供支撑强度的基材层；
位于所述基材层之上并用于增强盖带韧性的中间层；
涂覆在所述中间层之上的第一功能层；
覆盖在所述第一功能层之上的第二功能层，且所述第一功能层与第二功能层之间的连接力小于第二功能层与纸质载带之间的连接力；
所述第一功能层的主成分为乙烯丙烯共聚物以及聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物；
所述第二功能层包括纳米级氧化锡及锑混合物、蜡、SEBS、丙烯酸酯；
所述第一功能层的主成分包括：乙烯丙烯共聚物20质量%-60质量%、聚苯乙烯和聚丁二烯加氢得到的乙烯-丁烯为中间弹性嵌段的线性三嵌共聚物40质量%-80质量%；
所述第二功能层各成分添加的重量份如下：纳米级氧化锡与锑的混合物0.5-1.5份、蜡0.1-0.5份；SEBS 50-75份、丙烯酸酯10-25份。
2.根据权利要求1所述纸质载带用盖带，其特征在于，纳米级氧化锡与锑的混合比为80-95:5。
3.根据权利要求1所述纸质载带用盖带，其特征在于，所述蜡为聚酯蜡。
4.根据权利要求1所述纸质载带用盖带，其特征在于，所述中间层为乙烯丙烯酸甲酯共聚物层。
5.根据权利要求4所述纸质载带用盖带，其特征在于，所述中间层的厚度为8μm-16μm。
6.根据权利要求1所述纸质载带用盖带，其特征在于，所述第二功能层的厚度为1μm-2μm。