CN106087254A - A kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth and preparation method thereof - Google Patents
A kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth and preparation method thereof Download PDFInfo
- Publication number
- CN106087254A CN106087254A CN201610476241.2A CN201610476241A CN106087254A CN 106087254 A CN106087254 A CN 106087254A CN 201610476241 A CN201610476241 A CN 201610476241A CN 106087254 A CN106087254 A CN 106087254A
- Authority
- CN
- China
- Prior art keywords
- fibre web
- middle level
- acarien
- magnet
- web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth, include top layer fibre web, middle level fibre web, nexine fibre web the most successively, wherein, middle level fibre web is that Nidus Vespae through vertical lapping is cotton again after carding, and top layer fibre web, nexine fibre web are the fibre web that spun-bonded non-woven is composited with melt-blowing nonwoven.The lower surface of middle level fibre web is embedded with equally distributed slim Magnet.Prepare through fibre web, spray antibacterial anti-acarien microcapsule, inlay slim Magnet, compound, the drying of fibre web, cooling, rolling step prepare finished product.The present invention not only warmth retention property is good, good springiness, can bear the bigger pulling force of horizontal direction, and possesses antibiosis anti-acarien, magnetic therapy functions, it is easy to popularization and application.
Description
Technical field
The present invention relates to a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth and preparation method thereof, belong to non-woven cloth collar
Territory, particularly relates to a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth and preparation method thereof, it is particularly applicable to strengthen fill and uses
The warmth retention property of non-weaving cloth with elastic, the bigger pulling force of horizontal direction can be born, and there is antibiosis anti-acarien magnetic therapy functions.
Background technology
Filling non-weaving cloth, as a common kind in nonwoven fabric, is widely used in thermal insulation field.Human body
Carry out heat exchange by clothing, bed pad, sleeping bag etc. with environment, thus arrive the Thermal comfort of human body.The bar that thermal comfort is most basic
Part is the energy exchange between heat and the heat of the human body that scatters and disappears to environment that the thermal balance maintaining human body, i.e. human body self produce
Reach relative equilibrium.Heat insulating material formed effect makes sinking path be strengthened or weaken exactly, so that energy exchange reaches phase
To balance, human body is made to produce snugness sense.Classify according to heat insulating material formed used fiber source, can be warming material
Material be divided into natural heat insulating material formed, synthesize heat insulating material formed and mixed type is heat insulating material formed.
Natural heat insulating material formed mainly silk warmth-keeping material, Pilus Caprae seu Ovis be heat insulating material formed, cotton heat insulating material formed and down thermal material.
Silkworm silk and Pilus Caprae seu Ovis warmth retention property are preferable, but the easy breed bacteria of fiber, it being weak to damage by worms, and silkworm silk is expensive, wool fiber has
Abnormal flavour, Pilus Caprae seu Ovis is heat insulating material formed because of Pilus Caprae seu Ovis shrinkage greatly simultaneously, yielding.Cotton the most traditional heat insulating material formed product, has good suction
Moist, moisture retention, thermostability and wholesomeness, but loft is the highest, heavier-weight.Down thermal material has soft guarantor
The feature that warm, moisture absorption dissipates, but resistance to damage by worms and resistance to poor performance of going mouldy, make packing material higher to fabric requirement, otherwise bore floss
Phenomenon is the most serious.Along with the development of chemical fibre industry, synthesis with chemical fibre as raw material is heat insulating material formed is succeeded in developing in succession, thus
Broken traditional with the natural heat insulating material formed general layout being used as warming resisting cold textile implant, synthesize heat insulating material formed mainly by
The chemical fibre that terylene, polypropylene and acrylon are main is heat insulating material formed, have light weight, warming, good permeability, Radix Saposhnikoviae, mildew-resistant, mothproof,
The features such as acid and alkali-resistance, its product have quick-drying washable, use instead conveniently, produce environmental protection, use the advantages such as health.Such as gum sprayed cotton, pin
The far infrareds such as thorn cotton, space wadding, hot melting wool, melt-blown far infrared hot melting wool cotton, ultra-fine, down-like cotton, wherein hot blast method produces
Non-weaving cloth there is the advantages such as environmentally-friendly sanitary, loft height, air content height, comfortable ventilating, account in heat insulating material formed market
There is the bigger market share.Mixed type is heat insulating material formed refers to the different fiber such as various natural fiber, synthetic fibers and functional fiber
Between compound and heat insulating material formed and other fabrics between compound, its object is to adjust the structure of heat insulating material formed finished product, inhale
Take the feature of various types of materials, meet consumer's demand to heat insulating material formed each side.
Along with the raising of people's living standard, the heat insulating material formed performance requirement in the field such as clothing, bedding is got over by people
Come the highest, not only warmth retention property, compression resilience, comfortable ventilating, environmentally-friendly sanitary are required height, and require heat insulating material formed tool
There is some particular characteristic such as antibiosis anti-acarien, magnetic therapy functions, to reach multi-functional purpose.Develop multi-functional filling non woven cloth tool
Significant.
Summary of the invention
It is an object of the invention to overcome and can not meet high heat-retention, high resiliency present in prior art simultaneously, can bear
The defect of horizontal direction pulling force and problem, it is provided that one can meet high heat-retention, high resiliency simultaneously, can bear horizontal direction pulling force
Antibiosis anti-acarien magnetic therapy functions filling non woven cloth and preparation method thereof.
To achieve these goals, the technical scheme is that a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth,
It is characterized in that: be made up of top layer fibre web, middle level fibre web, nexine fibre web, middle level fibre web internal spray has antibacterial anti-acarien microcapsule,
The lower surface of middle level fibre web is provided with several slim Magnet, and slim Magnet is embedded in the lower surface of middle level fibre web, described top layer
Fibre web, nexine fibre web are the fibre web that spun-bonded non-woven is composited with melt-blowing nonwoven, the one side of melt-blowing nonwoven with
Middle level fibre web is superimposed together.
Described middle level fibre web is that carding is cotton through the Nidus Vespae of vertical lapping, and in the fibre web of middle level, low melting point is washed
The percentage by weight of synthetic fibre chopped fiber is 20% ~ 30%, the percentage by weight of the hollow pet staple fiber of three-dimensional crimp is 70% ~
80%, low-melting point polyester staple fiber is skin-core structure type polyester staple fiber, and fusing point is less than or equal to 110 °.
The lower surface of described middle level fibre web is embedded with multiple slim Magnet, and this slim Magnet is equal at the lower surface of middle level fibre web
Even layout, its arrangement is: the width along middle level fibre web is Magnet row, the polar orientation one of slim Magnet in Magnet row
Cause；Length direction along middle level fibre web is rows of magnets, and in rows of magnets, the polar orientation of adjacent slim Magnet (5) is contrary.
A kind of preparation method of above-mentioned antibiosis anti-acarien magnetic therapy functions filling non woven cloth, it is characterised in that: described method
Comprise the steps:
(1) prepared by fibre web: takes Spunbonded Nonwovens to be combined with melt-blowing nonwoven and makes top layer fibre web and nexine fibre web；Adopt
Make the middle level fibre web of Nidus Vespae cotton like through vertical lapping technique with carding.
(2) antibacterial anti-acarien microcapsule is sprayed: antibacterial anti-acarien microcapsule be sprayed onto in the fibre web of middle level under a certain pressure
Portion.
(3) slim Magnet is inlayed: multiple slim Magnet are evenly arranged in the lower surface of middle level fibre web, slim magnet array
Becoming clathrate, the width along middle level fibre web is Magnet row, and in Magnet row, the polar orientation of slim Magnet is consistent；Fine along middle level
The length direction of net is rows of magnets, and in rows of magnets, the polar orientation of adjacent slim Magnet is contrary.
(4) fibre web is compound: top layer fibre web, middle level fibre web, nexine fibre web are compound to one, and top layer fibre web has melt-blown non-
The one side of woven cloths overlaps with the upper surface of middle level fibre web, and nexine fibre web has the one side of melt-blowing nonwoven to arrange with middle level fibre web
The lower surface overlapping of slim Magnet, obtains composite web；
(5) drying: composite web is carried out drying；
(6) cooling: the composite web after drying is cooled down；
(7) winding: winding, prepares antibiosis anti-acarien magnetic therapy functions filling non woven cloth.
Owing to using above technical scheme, the multi-functional filling non woven cloth of the present invention, have the following characteristics that
One, middle level of the present invention fibre web uses carded web cotton through the Nidus Vespae of vertical lapping, the three-dimensional crimp in Nidus Vespae cotton
The warmth retention property of hollow pet staple fiber is good, and low-melting fiber plays cementation, prepares with prior art cross lapping mode
Flocculus material is compared, and can be greatly improved warmth retention property and the elasticity of product.
Two, the present invention uses multiple structure, top layer fibre web and nexine fibre web to be clipped in the middle by middle level fibre web, vertical lapping shape
Although the middle level fibre web elasticity in vertical direction become is the best, but it is susceptible to showing of web layer separation in the horizontal direction
As.Top layer fibre web and nexine fibre web are the fibre web that spun-bonded non-woven is composited with melt-blowing nonwoven, spun-bonded non-woven
Strength high so that the antibiosis anti-acarien magnetic therapy functions filling non woven cloth of preparation can bear the pulling force of horizontal direction, it is to avoid
Middle level fibre web in use occurs web layer to separate, and improves product quality and service life.Nexine fibre web is the thinnest, no
Affect the magnetic therapy effect of slim Magnet.
Three, top layer fibre web and nexine fibre web are the fibre web that spun-bonded non-woven is composited with melt-blowing nonwoven, melt-blown
Fiber gap in non-weaving cloth is little, can reach 2 ~ 8um, the ratio individual 0.1-0.5mm much smaller size of acarid, and acarid can not
By top layer fibre web or nexine fibre web, outside acarid does not enters the inside of packing material, and the inside acarid of packing material goes out
Do not go, because of obtain not nutrient and dead, play the effect of anti-mite.
Four, the evenly distributed lower surface being embedded in middle level fibre web of slim Magnet, slim magnet array becomes clathrate.Can be in order to
Put on the meridians of human body, acupuncture point and diseased region by artificial field and treat some disease, reduce human body and lack magnetic initiation for a long time respectively
Planting the probability of disease, product has health care and the function of magnetic therapy.As implant, can be widely used for bedding, garment industry.
Five, when the internal spray of middle level fibre web has the implant that antibacterial anti-acarien microcapsule, product make clothing, bedding etc.,
During use, friction and Extrusion can make antibacterial anti-acarien microcapsule wall material Slow fractures, gradually release microcapsule inner core repeatedly
The effective ingredient of material, the internal core of microcapsule progressively can also be discharged by microcapsule wall material surface micropore, has antibiosis anti-acarien
Effect persistency is good.
Six, the present invention is on the equipment of the Nidus Vespae cotton processing of existing vertical lapping, increases fibre web set composite the most permissible
Producing, equipment investment is few, and beneficially industrialization promotion uses.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
Fig. 2 is the upward view of the middle level fibre web in Fig. 1.
Fig. 3 is the structural representation of top layer fibre web in Fig. 1.
Fig. 4 is the structural representation of nexine fibre web in Fig. 1.
Fig. 5 is the structural representation of skin-core structure type polyester staple fiber in the present invention.
In figure: top layer fibre web 1, middle level fibre web 2, nexine fibre web 3, antibacterial anti-acarien microcapsule 4, slim Magnet 5, Magnet arrange
51, rows of magnets 52.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the present invention is described in further detail.
See Fig. 1 to Fig. 5, a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth, by top layer fibre web 1, middle level fibre web 2,
Nexine fibre web 3 is constituted, and the internal spray of middle level fibre web 2 has antibacterial anti-acarien microcapsule 4, if the lower surface of middle level fibre web 2 is provided with
Dry slim Magnet 5, slim Magnet 5 is embedded in the lower surface of middle level fibre web 2, and described top layer fibre web 1, nexine fibre web 3 are spunbond
The fibre web that non-weaving cloth and melt-blowing nonwoven are composited, the one side of melt-blowing nonwoven is superimposed together with middle level fibre web 2.
Described middle level fibre web 2 is that carding is cotton through the Nidus Vespae of vertical lapping, in middle level fibre web 2, and low melting point
The percentage by weight of polyester staple fiber is 20% ~ 30%, the percentage by weight of the hollow pet staple fiber of three-dimensional crimp is 70% ~
80%, low-melting point polyester staple fiber is skin-core structure type polyester staple fiber, and fusing point is less than or equal to 110 °.
The lower surface of described middle level fibre web 2 is embedded with multiple slim Magnet 5, and this slim Magnet 5 is in the following table of middle level fibre web 2
Face is evenly arranged, and its arrangement is: the width along middle level fibre web 2 is Magnet row 51, slim Magnet 5 in Magnet row 51
Polar orientation is consistent；Length direction along middle level fibre web 2 is rows of magnets 52, the polarity side of adjacent slim Magnet 5 in rows of magnets 52
To on the contrary.
The preparation method of a kind of above-mentioned antibiosis anti-acarien magnetic therapy functions filling non woven cloth, described method includes walking as follows
Rapid:
(1) prepared by fibre web: takes Spunbonded Nonwovens to be combined with melt-blowing nonwoven and makes top layer fibre web 1 and nexine fibre web 3；
Carding is used to make the middle level fibre web 2 of Nidus Vespae cotton like through vertical lapping technique.In order to improve the matter of production efficiency and fibre web
Amount, Spunbonded Nonwovens and melt-blowing nonwoven Combined Mining online compound mode, on the production line of many die heads, one
Die head prepares spun-bonded non-woven, and another die head prepares melt-blowing nonwoven, and melt-blowing nonwoven is directly superimposed upon spunbond non-
In woven cloths.Top layer fibre web 1 and nexine fibre web 3 use Spunbonded Nonwovens and melt-blowing nonwoven to be combined and make, spun-bond process
The strength of non-weaving cloth is higher, is possible to prevent middle level fibre web 2 to separate because being susceptible to web layer during by horizontal direction pulling force, carries
The quality of high product, on the other hand between the fiber in melt-blowing nonwoven and fiber, void ratio is the least, can reach 2 ~
8um, the ratio individual 0.1-0.5mm much smaller size of acarid, acarid can not pass through top layer fibre web 1 or nexine fibre web 3, outside
Acarid does not enters the inside of packing material, and the inside acarid of packing material goes out not go, because of obtain not nutrient and dead, play anti-demodicid mite
The effect of worm.
(2) antibacterial anti-acarien microcapsule is sprayed: spray the micro-glue of antibiosis anti-acarien prepared under a certain pressure to middle level fibre web 2
Capsule 4, makes antibacterial anti-acarien microcapsule 4 can be evenly distributed in the inside of middle level fibre web 2 as far as possible, it is simple to obtain good resisting after drying
Bacterium performance.
(3) slim Magnet is inlayed: multiple slim Magnet 5 are evenly arranged in the lower surface of middle level fibre web 2, slim Magnet 5
Being arranged in clathrate, the width along middle level fibre web 2 is Magnet row 51, the polar orientation one of slim Magnet 5 in Magnet row 51
Cause；Length direction along middle level fibre web 2 is rows of magnets 52, and in rows of magnets 52, the polar orientation of adjacent slim Magnet 5 is contrary.This sets
The advantage of meter is can be formed much to close magnet ring, improves magnetic therapy effect.The lower surface of middle level fibre web 2 and the distance of human body are
Closely, the nearlyest effect of magnetic influence of distance is the biggest, and the effect of magnetic therapy is best.The various shapes of slim Magnet, circle, ellipse, triangle,
Polygon etc. can, its thickness is usually 1mm-3mm, main considers it is that clothing, bedding etc. can not be the thickest, and packing material is also
Can not be the thickest.Nexine fibre web 3 ratio is relatively thin, does not interferes with magnetic therapy effect.
(4) fibre web is compound: top layer fibre web 1, middle level fibre web 2, nexine fibre web 3 are compound to one, and top layer fibre web 1 has molten
The one side of blowing nonwoven overlaps with the upper surface of middle level fibre web 2, and nexine fibre web 3 has one side and the middle level fibre of melt-blowing nonwoven
Net 2 arranges the lower surface overlapping of slim Magnet 5, obtains composite web.
(5) drying: composite web is carried out drying；By containing low-melting point polyester staple fiber in middle level fibre web 2, low melting point is washed
Synthetic fibre chopped fiber melt-flow also condenses upon in fiber intersection points, and middle level fibre web 2 is consolidated.In top layer fibre web 1, nexine fibre web 3
Melt-blowing nonwoven in fiber be ultra-fine chopped fiber, the most carefully, 2 ~ 8um can be reached, attach ability strong, it is possible to be close to
Middle level fibre web 2；On the other hand uneven the most small owing to vertical lapping is easily formed in middle level fibre web 2 surface, melt-blown non-
Woven cloths is easily attached onto with middle level fibre web 2, adds middle level fibre web 2 surface and also has the existence of low melting point meldable fibre,
Meldable fibre melts, and melt-blowing nonwoven is more closely attached to the surface of middle level fibre web 2.Top layer fibre web 1, nexine fibre web 3 energy
Enough combine with middle level fibre web 2, without departing from.
(6) cooling: the composite web after drying is cooled down；Cooling can be in the way of being to blow a cold wind over, after drying
Composite web carries out cooling process, makes the low-melting fiber solidification melted, and composite web shape and size after drying are consolidated
Fixed.
(7) winding: winding, prepares antibiosis anti-acarien magnetic therapy functions filling non woven cloth.
Embodiment:
Seeing Fig. 1 to Fig. 5, a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth, by top layer fibre web 1, middle level fibre web 2, nexine
Fibre web 3 is constituted, and the internal spray antibacterial anti-acarien microcapsule 4 of middle level fibre web 2, it is thin that the lower surface of middle level fibre web 2 is provided with several
Type Magnet 5, slim Magnet 5 is embedded in the lower surface of middle level fibre web 2, and described top layer fibre web 1, nexine fibre web 3 are spunbonded nonwoven
The fibre web that cloth and melt-blowing nonwoven are composited, the one side of melt-blowing nonwoven is superimposed together with middle level fibre web 2.
The preparation method of a kind of above-mentioned antibiosis anti-acarien magnetic therapy functions filling non woven cloth, described method includes walking as follows
Rapid:
(1) prepared by fibre web: takes Spunbonded Nonwovens to be combined with melt-blowing nonwoven and makes top layer fibre web 1 and nexine fibre web 3；
Carding is used to make the middle level fibre web 2 of Nidus Vespae cotton like through vertical lapping technique.The constituent of middle level fibre web 2 and weight portion
Ratio is: the percentage by weight of the hollow pet staple fiber of three-dimensional crimp is 70% ~ 80%, the weight of low-melting point polyester staple fiber
Percentage ratio is 20% ~ 30%.The parameter of the hollow pet staple fiber of three-dimensional crimp can be fineness be 3D, a length of 51mm.Low melting point
Polyester staple fiber is skin-core structure type polyester staple fiber, and fusing point is less than or equal to 110 °, and the parameter of low-melting point polyester staple fiber can
It is 2D for fineness, a length of 51mm.Top layer fibre web 1 and nexine fibre web 3 use Spunbonded Nonwovens and melt-blowing nonwoven to exist
Prepared by the mode that line is combined, the web density of top layer fibre web 1 and nexine fibre web 3 is 10g/m2~20g/m2。
(2) spray antibacterial anti-acarien microcapsule: under a certain pressure to middle level fibre web 2 upper surface spray prepare antibacterial
Anti-demodicid mite microcapsule 4, in order to make antibacterial anti-acarien microcapsule 4 can be evenly distributed in the inside of middle level fibre web 2 as far as possible, can be in middle level
Lower surface one side of fibre web 2 arranges air intake device.
(3) slim Magnet is inlayed: multiple slim Magnet 5 are evenly arranged in the lower surface of middle level fibre web 2, slim Magnet 5
Being arranged in clathrate, the width along middle level fibre web 2 is Magnet row 51, the polar orientation one of slim Magnet 5 in Magnet row 51
Cause；Length direction along middle level fibre web 2 is rows of magnets 52, and in rows of magnets 52, the polar orientation of adjacent slim Magnet 5 is contrary.Slim
The thickness of Magnet 5 is 1mm-3mm.
(4) fibre web is compound: top layer fibre web 1, middle level fibre web 2, nexine fibre web 3 are compound to one, and top layer fibre web 1 has molten
The one side of blowing nonwoven overlaps with the upper surface of middle level fibre web 2, and nexine fibre web 3 has one side and the middle level fibre of melt-blowing nonwoven
Net 2 arranges the lower surface overlapping of slim Magnet 5, obtains composite web.
(5) drying: composite web is carried out drying.
(6) cooling: the composite web after drying is cooled down；Cooling can be in the way of being to blow a cold wind over.
(7) winding: winding, prepares antibiosis anti-acarien magnetic therapy functions filling non woven cloth.
Claims (4)
1. an antibiosis anti-acarien magnetic therapy functions filling non woven cloth, it is characterised in that: by top layer fibre web (1), middle level fibre web (2),
Nexine fibre web (3) is constituted, and the internal spray of middle level fibre web (2) has antibacterial anti-acarien microcapsule (4), the lower surface of middle level fibre web (2)
Being provided with several slim Magnet (5), slim Magnet (5) is embedded in the lower surface of middle level fibre web (2), described top layer fibre web (1),
Nexine fibre web (3) is the fibre web that spun-bonded non-woven is composited with melt-blowing nonwoven, the one side of melt-blowing nonwoven with in
Layer fibre web (2) is superimposed together.
2. a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth as claimed in claim 1, it is characterised in that: described middle level
Fibre web (2) is that carding is cotton through the Nidus Vespae of vertical lapping, in middle level fibre web (2), and the weight of low-melting point polyester staple fiber
Amount percentage ratio is 20%～30%, and the percentage by weight of the hollow pet staple fiber of three-dimensional crimp is 70%～80%, low melting point
Polyester staple fiber is skin-core structure type polyester staple fiber, and fusing point is less than or equal to 110 °.
3. a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth as claimed in claim 1 or 2, it is characterised in that: in described
The lower surface of layer fibre web (2) is embedded with multiple slim Magnet (5), and this slim Magnet (5) is uniform at the lower surface of middle level fibre web (2)
Arranging, its arrangement is: the width along middle level fibre web (2) is that Magnet arranges (51), slim Magnet (5) in Magnet row (51)
Polar orientation consistent；Length direction along middle level fibre web (2) is rows of magnets (52), adjacent slim Magnet in rows of magnets (52)
(5) polar orientation is contrary.
4. the preparation method of a kind of antibiosis anti-acarien magnetic therapy functions filling non woven cloth as according to any one of claim 1-3,
It is characterized in that: the method comprises the steps:
(1) prepared by fibre web: takes Spunbonded Nonwovens to be combined with melt-blowing nonwoven and makes top layer fibre web (1) and nexine fibre web
(3)；Carding is used to make the middle level fibre web (2) of Nidus Vespae cotton like through vertical lapping technique；
(2) antibacterial anti-acarien microcapsule is sprayed: under a certain pressure antibacterial anti-acarien microcapsule (4) is sprayed onto middle level fibre web (2)
Internal；
(3) slim Magnet is inlayed: multiple slim Magnet (5) are evenly arranged in the lower surface of middle level fibre web (2), slim Magnet
(5) being arranged in clathrate, the width along middle level fibre web (2) is that Magnet arranges (51), slim Magnet (5) in Magnet row (51)
Polar orientation is consistent；Length direction along middle level fibre web (2) is rows of magnets (52), adjacent slim Magnet (5) in rows of magnets (52)
Polar orientation contrary；
(4) fibre web is compound: top layer fibre web (1), middle level fibre web (2), nexine fibre web (3) are compound to one, top layer fibre web (1)
Having the one side of melt-blowing nonwoven to overlap with the upper surface of middle level fibre web (2), nexine fibre web (3) has the one side of melt-blowing nonwoven
Lower surface overlapping with middle level fibre web (2) arranges slim Magnet (5), obtains composite web；
(5) drying: composite web is carried out drying；
(6) cooling: the composite web after drying is cooled down；
(7) winding: winding, prepares antibiosis anti-acarien magnetic therapy functions filling non woven cloth.