CN106084752B - 一种墙体现场发泡胶及隔音隔热墙体 - Google Patents

一种墙体现场发泡胶及隔音隔热墙体 Download PDF

Info

Publication number
CN106084752B
CN106084752B CN201610617449.1A CN201610617449A CN106084752B CN 106084752 B CN106084752 B CN 106084752B CN 201610617449 A CN201610617449 A CN 201610617449A CN 106084752 B CN106084752 B CN 106084752B
Authority
CN
China
Prior art keywords
parts
component
wall
insulating
foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610617449.1A
Other languages
English (en)
Other versions
CN106084752A (zh
Inventor
杨京学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangxi Hesheng Antai New Materials Co ltd
Original Assignee
Aegis Fire Prevention Science And Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Aegis Fire Prevention Science And Technology Ltd filed Critical Aegis Fire Prevention Science And Technology Ltd
Priority to CN201610617449.1A priority Critical patent/CN106084752B/zh
Publication of CN106084752A publication Critical patent/CN106084752A/zh
Application granted granted Critical
Publication of CN106084752B publication Critical patent/CN106084752B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提出一种墙体现场发泡胶，是由A组分和B组分组成，A组分包括质量份的以下成分：主料为50份的三聚氰胺甲醛树脂和40‑60份的聚醚多元醇，及30‑40份交联剂，4‑8份稳定剂，0‑2份催化剂，20‑40份发泡剂，0‑2份溶剂，10‑20份阻燃剂；B组分为200‑300质量份的异氰酸酯。因本发明提出的墙体现场发泡胶，具有不燃的特点，主要原料为三聚氰胺甲醛树脂，不含任何有毒物质和气体，而且环保。

Description

一种墙体现场发泡胶及隔音隔热墙体
技术领域
本发明属于有机化合物的组合物领域，具体涉及一种含有聚硅氧烷的有机组合物及其应用。
背景技术
保温隔热墙体是由粘结层、基材、锚固件、密封材料等组成，同时具有保温和隔音的功效，已有的隔音隔热墙体构成包括：轻钢龙骨纸面石膏板墙，轻钢龙骨纤维水泥板墙或双层3mm厚钢板，中间填充80mm岩棉。
现有的无机的石膏、岩棉、珍珠岩等保温材料相比，虽然隔热性能好，但隔音性能相对不足，而且填充的隔热隔音材料和基材的结合部位由于材质的不同，膨胀系数不同，遇到冷热环境极易分离脱落，产品的寿命不长。
目前市场用的墙体现场发泡材料主要是以聚酯类为原料，其含有毒气体，易燃，如发生火灾，会给生命和财产造成不可估算的损失。
发明内容
针对现有技术的不足，本发明的目的是提供一种墙体现场发泡胶。
本发明的另一目的是提出由所述墙体现场发泡胶制备的墙体。
实现本发明上述目的的技术方案为：
一种墙体现场发泡胶，是由A组分和B组分组成，其中，
A组分包括质量份的以下成分：主料为50份的三聚氰胺甲醛树脂和40-60份的聚醚多元醇，及30-40份交联剂，4-8份稳定剂，0-2份催化剂，20-40份发泡剂，0-2份溶剂，10-20份阻燃剂；
B组分为200-300质量份的异氰酸酯。
优选地，
所述A组分包括质量份的以下成分：主料为50份的三聚氰胺甲醛树脂和40-60份的聚醚多元醇，及35-40份交联剂，4-8份稳定剂，0.2-1份催化剂，20-40份发泡剂，1-2份溶剂，10-18份阻燃剂；
B组分为200-240质量份的二苯基甲烷二异氰酸酯。
异氰酸酯主要包括甲苯二异氰酸酯(简称TDI)；二苯基甲烷二异氰酸酯(简称MDI)两种。对于墙体材料来说，优选用具有较高强度的MDI。
本发明所述的质量份为本领域技术人员常用的质量单位，例如可以是克，千克，吨，或为了操作方便自定的质量单位。在同一个配方中，“份”表示的单位质量相同。
其中，所述交联剂为聚碳酸酯二醇、聚己内酯多元醇、芳香族聚酯(聚对苯二甲酸丙二醇酯PTT)、己二酸系聚酯(例如环保增塑剂己二酸二辛脂DOA，聚己二酸-1，2-丙二醇酯增塑剂)中的一种或多种。
其中，所述稳定剂为聚氨酯硬泡硅油。聚氨酯硬泡硅油用于增加泡孔细密度和均匀度。聚氨酯硬泡硅油市购可得，例如中山市东峻化工公司产的H-3603、H-3908、H-3609、H-3615、H-3618硅油。
其中，所述催化剂二月桂酸二丁基锡(DBTDL-T12，简称t12)
所述发泡剂为HCFC-141b、正戊烷、一氯二氟、二氧化碳、一氯甲烷中的一种或多种；
所述溶剂为三乙醇胺。
其中，所述阻燃剂选自氯化石蜡70#、聚磷酸三聚氰胺、硼酸锌、五氧化二锑、三氧化钼、磷酸三(1,3-二氯丙基)酯(TDCPP)、三聚氰胺中的一种或多种。
优选地，所述阻燃剂为氯化石蜡70#和磷酸三(1,3-二氯丙基)酯(TDCPP)质量比为1-3：15的混合物。
由本发明所述墙体现场发泡胶制成的隔音隔热墙体。
一种隔音隔热墙体，其是用所述的A组分和B组分混合，喷涂到基材上制成；所述基材为混凝土、木材、塑料板材，金属板材、墙砖中的一种或多种。
本发明的有益效果在于：
因本发明提出的墙体现场发泡胶，具有不燃的特点，主要原料为三聚氰胺，不含任何有毒物质和气体，而且环保。
本发明提出的墙体现场发泡不燃胶添加了闭孔发泡助剂，使墙体隔音、隔热。可根据用户要求在现场施工中增设金属防护网，使墙体增强抗震能力和防破坏能力，现场施工节省了搬运劳动力，使生命财产得到保障。
本发明提出的墙体现场发泡不燃胶，可广泛应用于建筑装饰、装修、老建筑改造领域。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例中，如无特别说明，所使用的手段和设备均为本领域常规的手段和设备。
实施例1：
原料配方如下：
在施工现场，将A组分和B组分混合，喷涂到砖墙墙体(砖墙墙体厚20cm,涂层厚3cm)上。所得墙体的计权隔声量为42dB。
实施例2：
原料配方如下：
在施工现场，将A组分和B组分混合，喷涂到砖墙墙体(砖墙墙体厚20cm,涂层厚3cm)上。所得墙体的计权隔声量为50dB。
实施例3：
原料配方如下：
在施工现场，将A组分和B组分混合，喷涂到砖墙墙体(砖墙墙体厚20cm,涂层厚3cm)上。所得墙体的计权隔声量为48dB。
实验例：防火测试不然级别
将实施例1、实施例2、实施例3发泡胶喷涂在边长为400mm的方形不锈钢网上，厚度均为3cm，每个实施例制二个样品。依据国家标准“GB/T20285-2006材料产烟毒性危险分级进行测试，测试结果为：产烟毒性t0级。
产烟毒性试验装置，依据国家标准“GB/T20285-2006材料产烟毒性危险分级进行测试，测试结果为：产烟毒性t0级。
表1：板材阻燃性能测试结果
燃烧时间s 烟密度
实施例1样品 16 62
实施例2样品 10 53
实施例3样品 19 71
通过以上测试可知，本发明提出的墙体材料完全符合现行中华人民共和国GB8624-2006《建筑材料及制品燃烧性能分级》的A级标准及中华人民共和国GB5022--95《建筑内部装修设计防火规范》的A级要求。
虽然，上文中已经本发明作了详尽的描述，但在本发明基础上，可以对之作一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。

Claims (1)

1.一种墙体现场发泡胶，是由A组分和B组分组成，其特征在于，
所述A组分由质量份的以下成分组成：主料为50份的三聚氰胺甲醛树脂和50份的聚醚多元醇，及40份聚对苯二甲酸丙二醇酯，5份稳定剂H-3908硅油，0.5份催化剂二月桂酸二丁基锡，30份发泡剂HCFC-141b，1份三乙醇胺，16份阻燃剂；
其中所述阻燃剂为氯化石蜡70#和磷酸三(1,3-二氯丙基)酯质量比为1：15的混合物；
B组分为220质量份的二苯基甲烷二异氰酸酯。
CN201610617449.1A 2016-07-29 2016-07-29 一种墙体现场发泡胶及隔音隔热墙体 Active CN106084752B (zh)