CN103396076B - A kind of thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture - Google Patents
A kind of thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture Download PDFInfo
- Publication number
- CN103396076B CN103396076B CN201310314145.4A CN201310314145A CN103396076B CN 103396076 B CN103396076 B CN 103396076B CN 201310314145 A CN201310314145 A CN 201310314145A CN 103396076 B CN103396076 B CN 103396076B
- Authority
- CN
- China
- Prior art keywords
- mineral particle
- complex mineral
- oxidized starch
- thermal insulation
- insulation mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture; it is to be made by the raw material of following weight parts: complex mineral particle 30-50; cement 100-150; desulfurated plaster 70-80; dry powder 4-6, redispersable latex powder 30-40, hydroxypropyl methyl cellulose ether 7-9, pottery sand 10-20; expanded and vitrified small ball 70-90, aluminium chloride 1-2, oxidized starch 12-15, tea seed cake powder 0.04-0.05, gluconic acid sodium salt 0.1-0.2, sodium sulfite 0.1-0.2.
Description
Technical field
The present invention relates to thermal insulation mortar field, is exactly a kind of complex mineral particle manufacture of utilizingThe thermal insulation mortar that contains oxidized starch.
Background technology
Thermal insulation mortar is taking various light materials as aggregate, taking cement as gelating material, admixes some modificationsAdditive, is uniformly mixed and a kind of premixing dry powder and mortar of making through manufacturing enterprise. Be mainly used inBuilding exterior wall heat preserving, has the advantage such as easy construction, good endurance.
Summary of the invention
The object of the present invention is to provide a kind of oxidized starch that contains that utilizes complex mineral particle manufactureThermal insulation mortar
Above-mentioned purpose realizes by following scheme:
A thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture, is characterized in that: it is to be made by the raw material of following weight parts: complex mineral particle 30-50, cement 100-150, desulfurated plaster 70-80, dry powder 4-6, redispersable latex powder 30-40, hydroxypropyl methyl fibreTie up plain ether 7-9, pottery sand 10-20, expanded and vitrified small ball 70-90, aluminium chloride 1-2, oxidized starch12-15, tea seed cake powder 0.04-0.05, gluconic acid sodium salt 0.1-0.2, sodium sulfite 0.1-0.2, suitable quantity of water.
Described a kind of thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture, its spyLevy and be:
Preparation method is:
(1) 10-20 part carbide slag, 10-20 part gypsum, 1-2 part cement, 20-30 part phosphorus ore slag are mixedAfter even, at 700-800 DEG C, calcine after 3-4 hour, take out, cooling, then be ground to particleFootpath is 0.075mm-0.090mm, takes out, and adds the alcohol ether glucoside that is equivalent to material gross weight 1-2%, the sodium Diacetate of 2-4%, the epoxidized soybean oil of 1-2%, and suitable quantity of water, 100-200 rev/minAfter lower stirring mixes for 10-20 minute, granulation, balling-up particle diameter, at 0.5-1.5mm, obtains grandidieriteComposition granule is for subsequent use;
(2) take by weight all raw materials, after stirring under 50-100 rev/min and mixing for 10-20 minute,Obtain.
Beneficial effect of the present invention is: the complex mineral particle that the present invention makes, in contain carbide slag, phosphorusSlagThis class waste material, turns waste into wealth, and can increase intensity and the heat insulating ability of mortar for the preparation of thermal insulation mortarEnergy.
Oxidized starch reduces starch gelatinization temperature, and heat paste viscosity diminishes and heat endurance increase, productColor is pure white, stick with paste transparent, good film-forming property, freeze-thaw resistance is good, is the thickening of low viscosity high concentrationAgent.
Detailed description of the invention
Utilize a thermal insulation mortar that contains oxidized starch for complex mineral particle manufacture, it is by followingThe raw material of weight portion (kg) makes: complex mineral particle 30, and cement 150, desulfurated plaster 80,Dry powder 6, redispersable latex powder 35, hydroxypropyl methyl cellulose ether 8, pottery sand 20, expandGlass bead 90, aluminium chloride 1, oxidized starch 15, tea seed cake powder 0.05, gluconic acid sodium salt 0.2, sodium sulfite 0.2, suitable quantity of water.
Described a kind of thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture, preparationMethod is:
(1) after 20 parts of carbide slags, 20 parts of gypsum, 2 parts of cement, 30 parts of phosphorus ore slags are mixed, in 80At 0 DEG C, calcine after 4 hours, take out, cooling, then to be ground to grain diameter be 0.075mm-0.080mm, takes out, and adds and is equivalent to the alcohol ether glucoside of material gross weight 2%, 4% sodium Diacetate, 1The epoxidized soybean oil of %, and suitable quantity of water, after stirring under 200 revs/min and mixing for 20 minutes, granulation,Balling-up particle diameter, at 1.5mm, obtains complex mineral particle for subsequent use;
(2) take by weight all raw materials, after stirring under 100 revs/min and mixing for 20 minutes, to obtain final product.
Products obtained therefrom test result is as follows:
Claims (1)
1. one kind is utilized the thermal insulation mortar that contains oxidized starch of complex mineral particle manufacture, it is characterized in that: it is to be made by the raw material of following weight parts: complex mineral particle 30-50, cement 100-150, desulfurated plaster 70-80, dry powder 4-6, redispersable latex powder 30-40, hydroxypropyl methyl cellulose ether 7-9, pottery sand 10-20, expanded and vitrified small ball 70-90, aluminium chloride 1-2, oxidized starch 12-15, tea seed cake powder 0.04-0.05, gluconic acid sodium salt 0.1-0.2, sodium sulfite 0.1-0.2, suitable quantity of water;
The preparation method of the described thermal insulation mortar that contains oxidized starch that utilizes complex mineral particle manufacture is:
(1) after 10-20 part carbide slag, 10-20 part gypsum, 1-2 part cement, 20-30 part phosphorus ore slag are mixed, at 700-800 DEG C, calcine after 3-4 hour, take out, cooling, being ground to grain diameter is 0.075mm-0.090mm again, take out, add and be equivalent to the alcohol ether glucoside of material gross weight 1-2%, the sodium Diacetate of 2-4%, the epoxidized soybean oil of 1-2%, and suitable quantity of water, after stirring under 100-200 rev/min and mixing for 10-20 minute, granulation, balling-up particle diameter, at 0.5-1.5mm, obtains complex mineral particle for subsequent use;
(2) take by weight all raw materials, after stirring under 50-100 rev/min and mixing for 10-20 minute, to obtain final product.