CN106046978A - Water-resistant anticorrosive paint for outdoor fitness equipment - Google Patents
Water-resistant anticorrosive paint for outdoor fitness equipment Download PDFInfo
- Publication number
- CN106046978A CN106046978A CN201610473232.8A CN201610473232A CN106046978A CN 106046978 A CN106046978 A CN 106046978A CN 201610473232 A CN201610473232 A CN 201610473232A CN 106046978 A CN106046978 A CN 106046978A
- Authority
- CN
- China
- Prior art keywords
- water
- fitness equipment
- powder
- outdoor fitness
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-resistant anticorrosive paint for outdoor fitness equipment. The water-resistant anticorrosive paint for outdoor fitness equipment is prepared from a siloxane-modified acrylic resin, a carboxyl acrylic resin, a carboxylic nitrile latex, modified talcum powder, pigments, squalane, palm wax, cotton shell powder, ethyl maltol, sodium petroleum sulfonate, dialkyl dialkoxysilane, nano zinc oxide and aluminum oxide. Compared with the prior art, the water-resistant anticorrosive paint for outdoor fitness equipment has the following advantages: by using the two resins as the main raw materials, the paint has higher water resistance and weather resistance after treatment; under the combined actions of the carboxylic nitrile latex, squalane and palm wax, the binding properties among the raw materials can be enhanced, so that the paint can be closely combined with the metal; the added modified talcum powder is beneficial to forming a compact firm coating after use; and the paint has the advantages of smooth surface, favorable water resistance, favorable corrosion resistance, and low volatility under high-temperature conditions, and is economical and environment-friendly.
Description
Technical field
The invention belongs to the correlative technology field of body-building apparatus, be specifically related to a kind of waterproof anti-for outdoor fitness equipment
Rotten coating.
Background technology
Along with the raising of people's living standard, people increasingly pursue the build of health, and outdoor strong raw equipment is extensively applied
In park, square, the public place such as residential quarter, be suitable for men and women, old and young and take exercise, increasing resident joins various open air
In body-building, but being arranged at outdoor for a long time due to body-building apparatus, long-term acceptance is exposed to the sun and rain, and gradually causes coating aging,
The coating water-proof rotproofness of body-building apparatus face coat is poor at present, the most aging, and the time one for a long time, is easy for coming off, affects body-building
The normal use of equipment.
Summary of the invention
It is an object of the invention to for existing problem, it is provided that a kind of water-tight corrosion-proof for outdoor fitness equipment is coated with
Material.
The present invention is achieved by the following technical solutions: a kind of water proof anti-corrosive paint for outdoor fitness equipment, by
The raw material of following weight portion is made: Silicone modified acryl's resin 22-28 part, carboxyl acrylic resin 16-20 part, carboxyl fourth
Nitrile latex 20-25 part, modified talc powder 3-6 part, pigment 2-6 part, squalane 1-2 part, palm wax 3-6 part, Exocarpium Gossypii powder 4-6
Part, ethylmaltol 2-4 part, petroleum sodium sulfonate 1-2 part, dialkyl dialkoxy silicane 2-4 part, nano zine oxide 3-6 part, oxygen
Change aluminum 1-2 part；
Wherein, the preparation method of modified talc powder is: roasting 4-5 hour under the hot conditions of 500 DEG C, then with 8-12%'s
Sodium hydroxide solution soaks 2-3 hour, then with deionized water rinsing to neutral, add the oxygen being equivalent to its weight portion 1-3%
Change magnesium powder, the diethylene glycol ether of 2-4% and the OPE of 2-4%, stir 4-8 minute with high speed 2500-2800 rev/min,
Ovendry power is broken into superfines and get final product.
As further improvement of these options, the preparation method of described Exocarpium Gossypii powder is: by Exocarpium Gossypii 50-60 DEG C
Warm water soaking 6-8 hour, after taking-up, dry under conditions of 40-50 DEG C to water content less than 8%, be subsequently adding and be equivalent to it
The nano silicon of weight portion 2-4% and the 2-Butoxyethyl acetate of 4-6%, mix homogeneously, cross the vapours of 450-500 DEG C
Process, after drying, be ground into micropowders.
As further improvement of these options, the particle diameter of described nano zine oxide is 60-75nm, described aluminium oxide
Particle diameter is 25-40 μm.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, its preparation method comprises the following steps:
(1) Silicone modified acryl's resin, carboxyl acrylic resin, Exocarpium Gossypii powder, nano zine oxide and aluminium oxide are added
Be equivalent to, in the water of its weight portion 2 times, be stirred until homogeneous dispersion, process under conditions of supersonic frequency 24KHz, power 150W
30-40 minute, obtain mixed material；
(2) add in said mixture material I after modified talc powder, petroleum sodium sulfonate and dialkyl dialkoxy silicane at microwave
Process 8-15 minute under frequency 2200MHz, power 800W, obtain mixed material II；
(3) in said mixture material II, carboxylic acrylonitrile butadiene rubber latex, squalane, palm wax and ethylmaltol are added at 80-90 DEG C
Under conditions of mix and blend 15-20 minute, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
The film forming thickness of coating prepared by the present invention is 120-150 μm.
The present invention has the advantage that with two kinds of resins as primary raw material in the present invention compared to existing technology, after treatment
There is stronger resistance to water and weatherability；Carboxylic acrylonitrile butadiene rubber latex acts on jointly with squalane, palm wax, can improve gluing between raw material
Knot property, makes coating be combined with metal in close；The interpolation of modified talc powder, contributes to making coating form fine and close hard painting after using
Layer, smooth surface, water-fast rotproofness is preferable, and under hot conditions, low volatilization, economic and environment-friendly.
Detailed description of the invention
Embodiment 1
A kind of water proof anti-corrosive paint for outdoor fitness equipment, is made up of the raw material of following weight portion: silicone-modified propylene
Acid resin 26 parts, carboxyl acrylic resin 18 parts, carboxylic acrylonitrile butadiene rubber latex 24 parts, modified talc powder 5 parts, pigment 2 parts, squalane 2
Part, palm wax 3 parts, 5 parts of Exocarpium Gossypii powder, ethylmaltol 2 parts, petroleum sodium sulfonate 2 parts, dialkyl dialkoxy silicane 3 parts, receive
Rice zinc oxide 6 parts, aluminium oxide 2 parts；
Wherein, the preparation method of modified talc powder is: roasting 4-5 hour under the hot conditions of 500 DEG C, then with 8-12%'s
Sodium hydroxide solution soaks 2-3 hour, then with deionized water rinsing to neutral, add the oxygen being equivalent to its weight portion 1-3%
Change magnesium powder, the diethylene glycol ether of 2-4% and the OPE of 2-4%, stir 4-8 minute with high speed 2500-2800 rev/min,
Ovendry power is broken into superfines and get final product.
Wherein, the preparation method of described Exocarpium Gossypii powder is: by warm water soaking 6-8 hour of Exocarpium Gossypii 50-60 DEG C, takes out
After, dry under conditions of 40-50 DEG C to water content less than 8%, be subsequently adding the nanometer titanium dioxide being equivalent to its weight portion 2-4%
Silicon and the 2-Butoxyethyl acetate of 4-6%, mix homogeneously, cross the vapours process of 450-500 DEG C, after drying, be ground into ultra micro
Fine powder.
Wherein, the particle diameter of described nano zine oxide is 60-75nm, and the particle diameter of described aluminium oxide is 25-40 μm.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, its preparation method comprises the following steps:
(1) Silicone modified acryl's resin, carboxyl acrylic resin, Exocarpium Gossypii powder, nano zine oxide and aluminium oxide are added
Be equivalent to, in the water of its weight portion 2 times, be stirred until homogeneous dispersion, process under conditions of supersonic frequency 24KHz, power 150W
30-40 minute, obtain mixed material；
(2) add in said mixture material I after modified talc powder, petroleum sodium sulfonate and dialkyl dialkoxy silicane at microwave
Process 8-15 minute under frequency 2200MHz, power 800W, obtain mixed material II；
(3) in said mixture material II, carboxylic acrylonitrile butadiene rubber latex, squalane, palm wax and ethylmaltol are added at 80-90 DEG C
Under conditions of mix and blend 15-20 minute, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
In the present embodiment, the film forming thickness of the coating of preparation is 140 μm, uses Byk pendulum hardness tester, measures hardness
It is 56.72%；Temperature be 80 DEG C, humidity be to store 2-3 days under conditions of 70%, outward appearance is without significant change.
Embodiment 2
A kind of water proof anti-corrosive paint for outdoor fitness equipment, is made up of the raw material of following weight portion: silicone-modified propylene
Acid resin 28 parts, carboxyl acrylic resin 20 parts, carboxylic acrylonitrile butadiene rubber latex 25 parts, modified talc powder 4 parts, pigment 3 parts, squalane 2
Part, palm wax 3 parts, 4 parts of Exocarpium Gossypii powder, ethylmaltol 2 parts, petroleum sodium sulfonate 1 part, dialkyl dialkoxy silicane 4 parts, receive
Rice zinc oxide 3 parts, aluminium oxide 1 part；
Wherein, the preparation method of modified talc powder is: roasting 4-5 hour under the hot conditions of 500 DEG C, then with 8-12%'s
Sodium hydroxide solution soaks 2-3 hour, then with deionized water rinsing to neutral, add the oxygen being equivalent to its weight portion 1-3%
Change magnesium powder, the diethylene glycol ether of 2-4% and the OPE of 2-4%, stir 4-8 minute with high speed 2500-2800 rev/min,
Ovendry power is broken into superfines and get final product.
In the present embodiment, the film forming thickness of the coating of preparation is 120 μm, uses Byk pendulum hardness tester, measures hardness
It is 56.48%；Temperature be 80 DEG C, humidity be to store 2-3 days under conditions of 70%, outward appearance is without significant change.
Embodiment 3
A kind of water proof anti-corrosive paint for outdoor fitness equipment, is made up of the raw material of following weight portion: silicone-modified propylene
Acid resin 22 parts, carboxyl acrylic resin 20 parts, carboxylic acrylonitrile butadiene rubber latex 24 parts, modified talc powder 5 parts, pigment 5 parts, squalane 1
Part, palm wax 5 parts, 5 parts of Exocarpium Gossypii powder, ethylmaltol 3 parts, petroleum sodium sulfonate 2 parts, dialkyl dialkoxy silicane 2 parts, receive
Rice zinc oxide 4 parts, aluminium oxide 2 parts；
Wherein, the preparation method of modified talc powder is: roasting 4-5 hour under the hot conditions of 500 DEG C, then with 8-12%'s
Sodium hydroxide solution soaks 2-3 hour, then with deionized water rinsing to neutral, add the oxygen being equivalent to its weight portion 1-3%
Change magnesium powder, the diethylene glycol ether of 2-4% and the OPE of 2-4%, stir 4-8 minute with high speed 2500-2800 rev/min,
Ovendry power is broken into superfines and get final product.
In the present embodiment, the film forming thickness of the coating of preparation is 150 μm, uses Byk pendulum hardness tester, measures hardness
It is 57.15%；Temperature be 80 DEG C, humidity be to store 2-3 days under conditions of 70%, outward appearance is without significant change.
Claims (5)
1. the water proof anti-corrosive paint for outdoor fitness equipment, it is characterised in that be made up of the raw material of following weight portion: silicon
Siloxane modified acrylic resin 22-28 part, carboxyl acrylic resin 16-20 part, carboxylic acrylonitrile butadiene rubber latex 20-25 part, modified talc
Powder 3-6 part, pigment 2-6 part, squalane 1-2 part, palm wax 3-6 part, Exocarpium Gossypii powder 4-6 part, ethylmaltol 2-4 part, oil
Sodium sulfonate 1-2 part, dialkyl dialkoxy silicane 2-4 part, nano zine oxide 3-6 part, aluminium oxide 1-2 part；
Wherein, the preparation method of modified talc powder is: roasting 4-5 hour under the hot conditions of 500 DEG C, then with 8-12%'s
Sodium hydroxide solution soaks 2-3 hour, then with deionized water rinsing to neutral, add the oxygen being equivalent to its weight portion 1-3%
Change magnesium powder, the diethylene glycol ether of 2-4% and the OPE of 2-4%, stir 4-8 minute with high speed 2500-2800 rev/min,
Ovendry power is broken into superfines and get final product.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, it is characterised in that described Exocarpium Gossypii
The preparation method of powder is: by warm water soaking 6-8 hour of Exocarpium Gossypii 50-60 DEG C, after taking-up, dries under conditions of 40-50 DEG C
Do to water content less than 8%, be subsequently adding the butyl glycol ether vinegar of nano silicon and the 4-6% being equivalent to its weight portion 2-4%
Acid esters, mix homogeneously, cross the vapours process of 450-500 DEG C, after drying, be ground into micropowders.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, it is characterised in that described nano oxygen
The particle diameter changing zinc is 60-75nm, and the particle diameter of described aluminium oxide is 25-40 μm.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, it is characterised in that its preparation method
Comprise the following steps:
(1) Silicone modified acryl's resin, carboxyl acrylic resin, Exocarpium Gossypii powder, nano zine oxide and aluminium oxide are added
Be equivalent to, in the water of its weight portion 2 times, be stirred until homogeneous dispersion, process under conditions of supersonic frequency 24KHz, power 150W
30-40 minute, obtain mixed material；
(2) add in said mixture material I after modified talc powder, petroleum sodium sulfonate and dialkyl dialkoxy silicane at microwave
Process 8-15 minute under frequency 2200MHz, power 800W, obtain mixed material II；
(3) in said mixture material II, carboxylic acrylonitrile butadiene rubber latex, squalane, palm wax and ethylmaltol are added at 80-90 DEG C
Under conditions of mix and blend 15-20 minute, add pigment after being cooled to room temperature, after stirring 5-10 minute, obtain mixed material III；
(4) said mixture material III is put into ACM flour mill carries out classification pulverizing, cross 180 mesh sieves, get product.
A kind of water proof anti-corrosive paint for outdoor fitness equipment, it is characterised in that described coating
Film forming thickness is 120-150 μm.