CN106007618A - Light and thin asbestos board - Google Patents
Light and thin asbestos board Download PDFInfo
- Publication number
- CN106007618A CN106007618A CN201610335743.3A CN201610335743A CN106007618A CN 106007618 A CN106007618 A CN 106007618A CN 201610335743 A CN201610335743 A CN 201610335743A CN 106007618 A CN106007618 A CN 106007618A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- light
- asbestos board
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light and thin asbestos board. The light and thin asbestos board is prepared from, by weight, 50-60 parts of waste wood, 15-20 parts of sunflower straws, 5-7 parts of gypsophila, 10-12 parts of straw fibers, 3-5 parts of glass waste residues, 2-4 parts of calcium silicate slag, 10-12 parts of modified clay, 11-13 parts of modified gypsum powder, 1-2 parts of an antifoaming agent, 10-12 parts of silica sol, 4-6 parts of graphite powder, 2-4 parts of a suspending agent, 8-10 parts of nitric acid, 5-8 parts of bamboo charcoal powder, 1-2 parts of nano zinc powder, 7-9 parts of adhesives and 60-70 parts of water. By adoption of the sunflower straws, the straw fibers, the bamboo charcoal powder, the graphite powder and the like, the light and thin asbestos board has advantages of excellent bonding properties, good fireproof performance, light weight, thinness, high vibration resistance, convenience in construction and the like. In addition, decoration cost is greatly reduced, and the light and thin asbestos board is long in service cycle.
Description
Technical field
The present invention relates to sheet material field, specifically a kind of light and thin type asbestos board.
Background technology
Asbestos board is the most most widely used class Novel ceiling ornament materials, it is a kind of novel house decorative material, being applicable to basic, normal, high shelves decoration, have lightweight, fire prevention, protection against the tide, easily processing, install the features such as simple, price is cheap compared with other finial material.Current asbestos board structural strength is inadequate, and the asbestos board thickness that structural strength is good is bigger than normal.
Summary of the invention
It is an object of the invention to provide a kind of light and thin type asbestos board, there is the feature such as fire prevention, light weight, thickness is thin, shock resistance good, easy construction, decoration cost is also greatly reduced, use the cycle long.
Technical scheme is as follows:
A kind of light and thin type asbestos board, is made up of the following component of following weight portion meter: culled wood 50-60 part, sunflower straw 15-20 part, flower stone 5-7 part, rice-straw fibre 10-12 part, glass waste residue 3-5 part, calcium silicate slag 2-4 part, modified clay 10-12 part, modified landplaster 11-13 part, defoamer 1-2 part, Ludox 10-12 part, graphite powder 4-6 part, suspending agent 2-4 part, nitric acid 8-10 part, bamboo charcoal powder 5-8 part, nano zinc powder 1-2 part, bonding agent 7-9 part, water 60-70 part；Its preparation method comprises the steps:
(1) culled wood, sunflower straw, flake asbestos, bamboo charcoal powder are first crushed to fineness and reach 150-180 mesh, put in agitating device, it is sequentially added into nano zinc powder, suspending agent, the water of water gross weight 30-40%, input ageing storehouse ageing after stirring, raw material after ageing is carried out secondary mixing, mixing speed is 600-700rpm, and mixing time is 12-15min, and moisture control is at 10-13%；
(2) glass waste residue, flower stone, calcium silicate slag, modified clay are added in the high temperature kiln of 450-500 DEG C and heat calcination 40-50min, take out after cooling and grind, 1-1.5h is ground after being added thereto to graphite powder, rice-straw fibre, modified landplaster high-speed stirred again, it is subsequently adding the mixing of remaining water, stirring to mixed material is completely dissolved, obtain mixed solution, standby；
(3) product obtained in step (1), (2) is mixed with surplus stock stirring in addition blender, stirring 3-5min, the slip mixed is poured in mould, after solidification 10-15min, start hydraulic liftout apparatus from forming machine bottom by building block from mold ejection, cutting, be placed on drying cart, it is dried in being moved to continuous way hot air drying kiln by track again,.
Light and thin type asbestos board, is made up of the following component of following weight portion meter: culled wood 55 parts, sunflower straw 18 parts, 6 parts of stone of flower, rice-straw fibre 11 parts, 4 parts of glass waste residue, modified clay 11 parts, modified landplaster 12 parts, defoamer 1.5 parts, Ludox 11 parts, graphite powder 5 parts, suspending agent 3 parts, 9 parts of nitric acid, bamboo charcoal powder 7 parts, nano zinc powder 1.5 parts, bonding agent 8 parts, 65 parts of water.
Beneficial effects of the present invention is as follows:
The present invention uses the raw materials such as sunflower straw, bamboo charcoal powder, graphite powder, obtained sheet material has enough intensity, fire resistance also improves simultaneously, the addition of rice-straw fibre, considerably increase again tensile strength and wearability, excellent bonding performance, there is the feature such as fire prevention, light weight, thickness is thin, shock resistance good, easy construction, decoration cost is also greatly reduced, uses the cycle long.
Detailed description of the invention
A kind of light and thin type asbestos board, is made up of the following component of following weight portion meter: culled wood 55 parts, sunflower straw 18 parts, 6 parts of stone of flower, rice-straw fibre 11 parts, 4 parts of glass waste residue, modified clay 11 parts, modified landplaster 12 parts, defoamer 1.5 parts, Ludox 11 parts, graphite powder 5 parts, suspending agent 3 parts, 9 parts of nitric acid, bamboo charcoal powder 7 parts, nano zinc powder 1.5 parts, bonding agent 8 parts, 65 parts of water；Its preparation method comprises the steps:
(1) culled wood, sunflower straw, flake asbestos, bamboo charcoal powder are first crushed to fineness and reach 160 mesh, put in agitating device, it is sequentially added into nano zinc powder, suspending agent, the water of water gross weight 35%, input ageing storehouse ageing after stirring, raw material after ageing is carried out secondary mixing, mixing speed is 650rpm, and mixing time is 13min, and moisture control is 12%；
(2) glass waste residue, flower stone, calcium silicate slag, modified clay are added in the high temperature kiln of 480 DEG C and heat calcination 45min, take out after cooling and grind, 1.2h is ground after being added thereto to graphite powder, rice-straw fibre, modified landplaster high-speed stirred again, it is subsequently adding the mixing of remaining water, stirring to mixed material is completely dissolved, obtain mixed solution, standby；
(3) product obtained in step (1), (2) is mixed with surplus stock stirring in addition blender, stirring 3-5min, the slip mixed is poured in mould, after solidification 13min, start hydraulic liftout apparatus from forming machine bottom by building block from mold ejection, cutting, be placed on drying cart, it is dried in being moved to continuous way hot air drying kiln by track again,.
Claims (2)
1. a light and thin type asbestos board, it is characterized in that, be made up of the following component of following weight portion meter: culled wood 50-60 part, sunflower straw 15-20 part, flower stone 5-7 part, rice-straw fibre 10-12 part, glass waste residue 3-5 part, calcium silicate slag 2-4 part, modified clay 10-12 part, modified landplaster 11-13 part, defoamer 1-2 part, Ludox 10-12 part, graphite powder 4-6 part, suspending agent 2-4 part, nitric acid 8-10 part, bamboo charcoal powder 5-8 part, nano zinc powder 1-2 part, bonding agent 7-9 part, water 60-70 part；Its preparation method comprises the steps:
(1) culled wood, sunflower straw, flake asbestos, bamboo charcoal powder are first crushed to fineness and reach 150-180 mesh, put in agitating device, it is sequentially added into nano zinc powder, suspending agent, the water of water gross weight 30-40%, input ageing storehouse ageing after stirring, raw material after ageing is carried out secondary mixing, mixing speed is 600-700rpm, and mixing time is 12-15min, and moisture control is at 10-13%；
(2) glass waste residue, flower stone, calcium silicate slag, modified clay are added in the high temperature kiln of 450-500 DEG C and heat calcination 40-50min, take out after cooling and grind, 1-1.5h is ground after being added thereto to graphite powder, rice-straw fibre, modified landplaster high-speed stirred again, it is subsequently adding the mixing of remaining water, stirring to mixed material is completely dissolved, obtain mixed solution, standby；
(3) product obtained in step (1), (2) is mixed with surplus stock stirring in addition blender, stirring 3-5min, the slip mixed is poured in mould, after solidification 10-15min, start hydraulic liftout apparatus from forming machine bottom by building block from mold ejection, cutting, be placed on drying cart, it is dried in being moved to continuous way hot air drying kiln by track again,.
Light and thin type asbestos board the most according to claim 1, it is characterized in that, be made up of the following component of following weight portion meter: culled wood 55 parts, sunflower straw 18 parts, 6 parts of stone of flower, rice-straw fibre 11 parts, 4 parts of glass waste residue, modified clay 11 parts, modified landplaster 12 parts, defoamer 1.5 parts, Ludox 11 parts, graphite powder 5 parts, suspending agent 3 parts, 9 parts of nitric acid, bamboo charcoal powder 7 parts, nano zinc powder 1.5 parts, bonding agent 8 parts, 65 parts of water.