CN106007515B - 一种烧结砖粉预拌干混砂浆 - Google Patents
一种烧结砖粉预拌干混砂浆 Download PDFInfo
- Publication number
- CN106007515B CN106007515B CN201610343403.5A CN201610343403A CN106007515B CN 106007515 B CN106007515 B CN 106007515B CN 201610343403 A CN201610343403 A CN 201610343403A CN 106007515 B CN106007515 B CN 106007515B
- Authority
- CN
- China
- Prior art keywords
- brick powder
- fired brick
- cement
- mixed mortar
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:70~90份,水泥:10~30份,抗裂纤维:0.2~1份,不含抗离析外加剂。本发明的烧结砖粉预拌干混砂浆,仅以建筑垃圾烧结砖粉、水泥、抗裂纤维为原料,不仅操作简单,而且有效的实现了把建筑垃圾变废为宝,解决了建筑垃圾处理的难题,进而解决了建筑垃圾对污染环境的问题。本发明的烧结砖粉预拌干混砂浆,以烧结砖粉代替了传统的沙子,不会产生离析问题,故不含有减水剂、保水增稠剂等化学制品的外加剂,这不仅减少了财力、物力的消耗,而且解决了化学制品外加剂对环境污染的问题。
Description
技术领域
本发明属于建筑垃圾回收技术领域,涉及一种烧结砖粉预拌干混砂浆。
背景技术
预拌干混砂浆是指经干燥筛分处理的骨料(如石英砂)、无机胶凝材料(如水泥)和添加剂(如聚合物)等按一定比例进行物理混合而成的一种颗粒状或粉状,以袋装或散装的形式运至工地,加水拌和后即可直接使用的物料。预拌干混砂浆为散体粉状和颗粒状材料的混合物,多以沙子、水泥、矿物掺合料为主,在粉状和颗粒状材料混合后,由于其各自的属性如密度不同,在储存、运输、使用过程中都可能发生粉体和颗粒物的二次分离,这种现象就是干混砂浆的“离析”现象。如果“离析”现象不能得到有效控制,将严重影响干混砂浆的成品质量和建筑施工质量。
为了解决预拌干混砂浆在储存、运输、使用过程因运动、颠簸产生的离析问题,厂家在制造干混砂浆的过程中,会添加抗离析外加剂,如保水增稠剂、减水剂等来提高砂浆的质量。毫无疑问,这些化学制品的抗离析外加剂不仅消耗了财力、物力,而且在砂浆的制作过程中还会随水渗入地下、造成环境污染,砂浆应用到建筑物上后由于这些化学制品中某些成分的挥发,还会威胁着居住者的健康。
发明内容
本发明的目的:为了解决预拌干混砂浆在储存、运输、使用过程因运动、颠簸产生的离析问题,本发明提供了一种制备方法简单、以烧结砖粉、水泥、抗裂纤维为原料的预拌干混砂浆。
本发明的技术方案:一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:70~90份,水泥:10~30份,抗裂纤维:0.2~1份,不含抗离析外加剂。
所述的烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:70份,水泥:10份,抗裂纤维:0.2份,不含抗离析外加剂。
所述的烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:80份,水泥:20份,抗裂纤维:0.5份,不含抗离析外加剂。
所述的烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:85份,水泥:25份,抗裂纤维:0.8份,不含抗离析外加剂。
所述的烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:90份,水泥:30份,抗裂纤维:1份,不含抗离析外加剂。
所述的烧结砖粉的粒径≤3.75mm,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3。
所述的抗裂纤维为聚丙烯纤维、耐碱玻璃纤维中的至少一种,长度为1~10mm。
本发明所述的烧结砖是以粘土、页岩、煤矸石或粉煤灰为原料,经成型和高温焙烧而制得的用于砌筑承重和非承重墙体的砖的统称。
本发明的有益效果:
1、本发明的烧结砖粉预拌干混砂浆,仅以建筑垃圾烧结砖粉、水泥、抗裂纤维为原料,不仅操作简单,而且有效的实现了把建筑垃圾变废为宝,解决了建筑垃圾处理的难题,进而解决了建筑垃圾对污染环境的问题。
2、本发明的烧结砖粉预拌干混砂浆,以烧结砖粉代替了传统的沙子,具有很好的抗离析作用,具体原因如下:(1)因烧结砖粉的密度与水泥相近,且烧结砖粉表面存在微孔,相比表面光滑的天然砂材料,水泥在砖粉上的附着力较大,因此在运输的过程,水泥和烧结砖粉之间不容易产生物理离析,解决了现有技术中沙子与水泥运输过程中的物理离析问题,确保了砂浆的质量。(2)因烧结砖粉的密度与水泥相近,使用时搅拌更为均匀,且由于砖粉表面微孔的存在,水泥水化产物可以深入到砖粉内部,砂浆凝结硬化以后,水泥水化产物可以和砖粉深度连接,不容易出现化学离析。
3、本发明的烧结砖粉预拌干混砂浆,以烧结砖粉代替了传统的沙子,不会产生离析问题,故不含有减水剂、保水增稠剂等化学制品的外加剂,这不仅减少了财力、物力的消耗,而且解决了化学制品外加剂对环境污染的问题。
具体实施方式
为了更好的理解本发明,下面结合具体实施例进一步说明。
实施例1
一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:70份,水泥:10份,抗裂纤维:0.2份,不含抗离析外加剂;其中,烧结砖粉的粒径≤3.75mm,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3;抗裂纤维为聚丙烯纤维,长度为1~10mm。
按照以上原料重量份的组分加入,搅拌均匀,即得到本发明的烧结砖粉预拌干混砂浆。
实施例2
一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成,烧结砖粉:80份,水泥:20份,抗裂纤维:0.5份,不含抗离析外加剂;其中,烧结砖粉的粒径≤3.75mm,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3;抗裂纤维为聚丙烯纤维,长度为1~10mm。
按照以上原料重量份的组分加入,搅拌均匀,即得到本发明的烧结砖粉预拌干混砂浆。
实施例3
一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成,烧结砖粉:85份,水泥:25份,抗裂纤维:0.8份,不含抗离析外加剂;其中,烧结砖粉的粒径≤3.75mm,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3;抗裂纤维为聚丙烯纤维,长度为1~10mm。
按照以上原料重量份的组分加入,搅拌均匀,即得到本发明的烧结砖粉预拌干混砂浆。
实施例4
一种烧结砖粉预拌干混砂浆,由以下重量份的组分组成:烧结砖粉:90份,水泥:30份,抗裂纤维:1份,不含抗离析外加剂;其中,烧结砖粉的粒径≤3.75mm之间,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3;抗裂纤维为耐碱玻璃纤维,长度为1~10mm。
按照以上原料重量份的组分加入,搅拌均匀,即得到本发明的烧结砖粉预拌干混砂浆。
Claims (2)
1.一种烧结砖粉预拌干混砂浆,其特征在于,由以下重量份的组分组成:烧结砖粉:90份,水泥:30份,抗裂纤维:1份,不含抗离析外加剂;所述的烧结砖粉的粒径≤3.75mm,烧结砖粉的密度与水泥相近,为3.0~3.15g/cm3。
2.根据权利要求1所述的烧结砖粉预拌干混砂浆,其特征在于,所述的抗裂纤维为聚丙烯纤维、耐碱玻璃纤维中的至少一种,长度为1~10mm。