CN105885773B - 一种人造板用生物质无醛胶粘剂及其制备方法 - Google Patents
一种人造板用生物质无醛胶粘剂及其制备方法 Download PDFInfo
- Publication number
- CN105885773B CN105885773B CN201610498317.1A CN201610498317A CN105885773B CN 105885773 B CN105885773 B CN 105885773B CN 201610498317 A CN201610498317 A CN 201610498317A CN 105885773 B CN105885773 B CN 105885773B
- Authority
- CN
- China
- Prior art keywords
- wood
- free cement
- based plate
- aldehyde
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例 | 胶合强度/MPa | 浸渍剥离强度/mm | 游离甲醛 |
实施例1 | 1.8 | 0 | 未检出 |
实施例2 | 1.9 | 0 | 未检出 |
实施例3 | 2.0 | 0 | 未检出 |
实施例4 | 1.58 | 0 | 未检出 |
实施例5 | 1.66 | 0 | 未检出 |
实施例6 | 3.0 | 0 | 未检出 |
对比例1 | 0.36 | 249 | 未检出 |
对比例2 | 0.51 | 276 | 未检出 |
Claims (4)