CN105802296A - Coating for indoor woodware - Google Patents
Coating for indoor woodware Download PDFInfo
- Publication number
- CN105802296A CN105802296A CN201610181270.6A CN201610181270A CN105802296A CN 105802296 A CN105802296 A CN 105802296A CN 201610181270 A CN201610181270 A CN 201610181270A CN 105802296 A CN105802296 A CN 105802296A
- Authority
- CN
- China
- Prior art keywords
- parts
- ether
- kaolin
- glycerol
- tert
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A coating for indoor woodware is prepared from, by weight, 29-35 parts of tripropylene glycol diacrylate, 21-26 parts of tert-butyl methacrylate, 8-15 parts of ethoxylation trihydroxymethyl triacrylate, 10-15 parts of polyamide resin polyhydric alcohol, 8-14 parts of epoxy resin, 4-7 parts of hexamethylene diisocyanate, 7-11 parts of ethyl acetate, 10-13 parts of polyoxyethylene ether, 3-6 parts of dipropylene glycol methyl ether, 1-4 parts of octadecyltrichlorosilane, 8-11 parts of hydroxypropyl methyl cellulose, 5-8 parts of hydroxyethyl methacrylate, 6-10 parts of kaolin, 5-7 parts of white mica, 3-5 parts of glass powder, 1.5-2.5 parts of light calcium carbonate, 2-3 parts of silicon dioxide, 1-2 parts of diol phenyl ether, 2-4 parts of triphenyl phosphite, 2-3 parts of glycerol and 30-45 parts of deionized water.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of indoor wood coating.
Background technology
Woodwork coating refers to that timber-work includes coating used on the goods of solid wood and wood-based plate, including furniture, door and window, floor
Coating selected by Deng, in general woodwork coating is based on coatings for furniture.Woodwork coating give timber and wood-base materials color,
The aesthetic features that gloss etc. are required, can also make woodenware resist because of humidity, bacteria breed, biodegradation, chemical damage etc. simultaneously and make
The destruction become.
China is currently the maximum Furniture manufacturing in the whole world and big export country, the most all can consume substantial amounts of coatings for furniture and (often be referred to as " wood
Device paint ").Along with the development of China's economic, the raising of living standards of the people and improvement, the indoor environment cause of China has had considerable
Development, people to living environment pollute consciousness improving constantly, but aggregate level still allows of no optimist, room air pollution
Remain one of primary killers of pollution health.It is introduced, the primary pollution source of China's indoor environment is from building, dress at present
Decorations and furniture, formaldehyde, benzene, ammonia pollute to exceed standard and have had a strong impact on the healthy of people.And currently used woodenware
Paint, the most all contains toxic gas, the equal severe overweight of these harmful gass, and brushing, on building, wooden object top layer, is given
The healthy of people brings bigger infringement.Another when our living space virus and antibacterial be always have, ubiquitous
, the extent of injury of human body is perplexed always and threatens everybody physical and mental health by the existence of virus and bacteria.
In May, 2015, country put into effect the tightest environmental law in history " wood furniture manufacturing industry atmosphere pollutants emission standards ",
Wherein for the control requirement of wood furniture manufacturing industry Air Pollutant Emission, and entered the first rank of standard regulation July 1
Section.New standard specifies that in wood furniture, the prescribed limits of contained benzene particulate matter the highest permission concentration of emission to be greatly reduced.If family
Production line is not transformed by tool enterprise, still uses oil paint, and does not use the water paint that pollutant emission level is lower, then
Its product, hardly consistent with the requirement of new standard, ultimately results in and cannot commercially sell.
At present, on market, coatings for furniture uses modified alkyd resin, polyester resin, polyurethane, toluene and some additives, leads
Cause existing chemical coating and the most all contain the noxious substances such as benzene, the health of life-time service meeting harmful to human, the performance of natural paint
Unstable again.Along with the development of society, the demand of coating is constantly risen by people, but coating exists various shortcoming,
Such as the embrittlement that easily turns to be yellow, paint film richness are poor, and time length may be sent out and come off.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of indoor wood coating.
The above-mentioned purpose of the present invention is realized by following technical proposals:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 29-35 part;Methyl
Tert-butyl acrylate 21-26 part;Ethoxylation tri methylol triacrylate 8-15 part;Polyamide polyhydric alcohol 10-15 part;
Epoxy resin 8-14 part;Hexamethylene diisocyanate 4-7 part;Ethyl acetate 7-11 part;Polyoxyethylene ether 10-13 part;Dipropylene glycol
Methyl ether 3-6 part;Octadecyl trichlorosilane alkane 1-4 part;Hydroxypropyl methyl cellulose 8-11 part;Hydroxyethyl methylacrylate 5-8
Part;Kaolin 6-10 part;White mica 5-7 part;Glass dust 3-5 part;Precipitated calcium carbonate 1.5-2.5 part;Silicon dioxide 2-3 part;
Glycol phenyl ether 1-2 part;Triphenyl phosphite 2-4 part;Glycerol 2-3 part;Deionized water 30-45 part.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 29 parts;Tert-butyl Methacrylate
22 parts;Ethoxylation tri methylol triacrylate 14 parts;Polyamide polyhydric alcohol 13 parts;Epoxy resin 10 parts;Oneself
Diisocyanate 4 parts;Ethyl acetate 7 parts;Polyoxyethylene ether 13 parts;Dipropylene glycol methyl ether 3 parts;Octadecyl trichlorosilane alkane
1 part;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methylacrylate 5 parts;Kaolin 6 parts;White mica 5 parts;Glass dust 5
Part;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 2 parts;Glycerol 2 parts;
Deionized water 35 parts.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 32 parts;Tert-butyl Methacrylate
21 parts;Ethoxylation tri methylol triacrylate 15 parts;Polyamide polyhydric alcohol 15 parts;Epoxy resin 8 parts;Oneself is two years old
Isocyanates 7 parts;Ethyl acetate 11 parts;Polyoxyethylene ether 10 parts;Dipropylene glycol methyl ether 6 parts;Octadecyl trichlorosilane alkane
3 parts;Hydroxypropyl methyl cellulose 11 parts;Hydroxyethyl methylacrylate 8 parts;Kaolin 10 parts;White mica 6 parts;Glass
3 parts of powder;Precipitated calcium carbonate 2 parts;Silicon dioxide 2.5 parts;Glycol phenyl ether 1.5 parts;Triphenyl phosphite 4 parts;Glycerol
2.5 part;Deionized water 30 parts.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 33 parts;Tert-butyl Methacrylate
23 parts;Ethoxylation tri methylol triacrylate 8 parts;Polyamide polyhydric alcohol 14 parts;Epoxy resin 12 parts;Oneself is two years old
Isocyanates 5 parts;Ethyl acetate 10 parts;Polyoxyethylene ether 12 parts;Dipropylene glycol methyl ether 5 parts;Octadecyl trichlorosilane alkane
2 parts;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methylacrylate 6 parts;Kaolin 10 parts;White mica 7 parts;Glass dust
4.5 part;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;Glycol phenyl ether 2 parts;Triphenyl phosphite 3 parts;Glycerol 3
Part;Deionized water 45 parts.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 35 parts;Tert-butyl Methacrylate
25 parts;Ethoxylation tri methylol triacrylate 10 parts;Polyamide polyhydric alcohol 10 parts;Epoxy resin 14 parts;Oneself
Diisocyanate 6 parts;Ethyl acetate 9 parts;Polyoxyethylene ether 11 parts;Dipropylene glycol methyl ether 4 parts;Octadecyl trichlorosilane alkane
4 parts;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methylacrylate 7 parts;Kaolin 8 parts;White mica 7 parts;Glass dust 4
Part;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;Glycol phenyl ether 1.5 parts;Triphenyl phosphite 3.5 parts;Glycerol 3
Part;Deionized water 40 parts.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 32 parts;Tert-butyl Methacrylate
26 parts;Ethoxylation tri methylol triacrylate 12 parts;Polyamide polyhydric alcohol 11 parts;Epoxy resin 12 parts;Oneself
Diisocyanate 6 parts;Ethyl acetate 8 parts;Polyoxyethylene ether 11 parts;Dipropylene glycol methyl ether 4 parts;Octadecyl trichlorosilane alkane
2 parts;Hydroxypropyl methyl cellulose 10 parts;Hydroxyethyl methylacrylate 8 parts;Kaolin 7 parts;White mica 5 parts;Glass dust
3.5 part;Precipitated calcium carbonate 2 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 3.5 parts;Glycerol 2
Part;Deionized water 42 parts.
Further, including the raw material of following parts by weight: tripropylene glycol diacrylate 33 parts;Tert-butyl Methacrylate
23 parts;Ethoxylation tri methylol triacrylate 11 parts;Polyamide polyhydric alcohol 12 parts;Epoxy resin 11 parts;Oneself
Diisocyanate 5 parts;Ethyl acetate 11 parts;Polyoxyethylene ether 12 parts;Dipropylene glycol methyl ether 5 parts;Octadecyl trichlorosilane
2 parts of alkane;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methylacrylate 7 parts;Kaolin 8 parts;White mica 5 parts;Glass
3 parts of powder;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 4 parts;Glycerol 3
Part;Deionized water 30 parts.
Further, described Kaolin fineness is 500~800 mesh.
Further, described white mica fineness is 400~600 mesh.
Compared with prior art, the product adhesive force of the present invention is higher for a kind of indoor wood coating of the present invention, resistance to impact,
The performance such as salt spray resistance, wet-heat resisting is more superior, and construction is simple, low cost, and efficiency is high, is suitable for industrialized production.
Detailed description of the invention
For making the purpose of the embodiment of the present invention, technical scheme and advantage clearer, below in conjunction with the embodiment skill to the present invention
Art scheme is clearly and completely described.Obviously, described embodiment is the part of the present invention rather than whole realities
Execute example.Based on described embodiments of the invention, those of ordinary skill in the art are obtained on the premise of without creative work
The every other embodiment obtained, broadly falls into the scope of protection of the invention.
Embodiment 1:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 29 parts;Metering system
Tert-butyl acrylate 22 parts;Ethoxylation tri methylol triacrylate 14 parts;Polyamide polyhydric alcohol 13 parts;Epoxy resin
10 parts;Hexamethylene diisocyanate 4 parts;Ethyl acetate 7 parts;Polyoxyethylene ether 13 parts;Dipropylene glycol methyl ether 3 parts;Octadecane
Base trichlorosilane 1 part;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methylacrylate 5 parts;Kaolin 6 parts;White mica 5
Part;5 parts of glass dust;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 2 parts;
Glycerol 2 parts;Deionized water 35 parts.
Preferably, described Kaolin fineness is 500~800 mesh.
Preferably, described white mica fineness is 400~600 mesh.
The preparation method of described indoor wood coating comprises the steps:
(1) by tripropylene glycol diacrylate, Tert-butyl Methacrylate, ethoxylation tri methylol triacrylate, polyamides
Polyimide resin polyhydric alcohol, epoxy resin, hexamethylene diisocyanate, ethyl acetate, polyoxyethylene ether, dipropylene glycol methyl ether, octadecane
Base trichlorosilane, hydroxypropyl methyl cellulose, hydroxyethyl methylacrylate, deionized water are added separately in reaction vessel, add
Heat to 65-75 DEG C, 300r/min stir, time 40min, after standby;
(2) according to described parts by weight, Kaolin, white mica, glass dust, precipitated calcium carbonate, silicon dioxide are delivered to ball mill,
Being milled to particle diameter is 10-20nm, then mix and blend, and the speed of 100-120r/min stirs 40-50 minute, is uniformly mixing to obtain mixed
Compound;
(3) mixture that step (2) prepares is added in the mixture that step (1) prepares, ultrasonic high speed dispersion, ultrasound wave
Frequency is 20kHz, rate of dispersion 5500r/min, and jitter time is 35min;
(4) adding glycol phenyl ether, triphenyl phosphite, glycerol, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz,
Rate of dispersion 4800r/min, jitter time is 40min, obtains indoor wood coating.
Embodiment 2:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 32 parts;Metering system
Tert-butyl acrylate 21 parts;Ethoxylation tri methylol triacrylate 15 parts;Polyamide polyhydric alcohol 15 parts;Epoxy resin 8
Part;Hexamethylene diisocyanate 7 parts;Ethyl acetate 11 parts;Polyoxyethylene ether 10 parts;Dipropylene glycol methyl ether 6 parts;Octadecyl
Trichlorosilane 3 parts;Hydroxypropyl methyl cellulose 11 parts;Hydroxyethyl methylacrylate 8 parts;Kaolin 10 parts;White mica 6
Part;3 parts of glass dust;Precipitated calcium carbonate 2 parts;Silicon dioxide 2.5 parts;Glycol phenyl ether 1.5 parts;Triphenyl phosphite 4 parts;
Glycerol 2.5 parts;Deionized water 30 parts.
Preparation method is with embodiment 1.
Embodiment 3:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 33 parts;Metering system
Tert-butyl acrylate 23 parts;Ethoxylation tri methylol triacrylate 8 parts;Polyamide polyhydric alcohol 14 parts;Epoxy resin 12
Part;Hexamethylene diisocyanate 5 parts;Ethyl acetate 10 parts;Polyoxyethylene ether 12 parts;Dipropylene glycol methyl ether 5 parts;Octadecyl
Trichlorosilane 2 parts;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methylacrylate 6 parts;Kaolin 10 parts;White mica 7 parts;
4.5 parts of glass dust;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;Glycol phenyl ether 2 parts;Triphenyl phosphite 3 parts;Third
Triol 3 parts;Deionized water 45 parts.
Preparation method is with embodiment 1.
Embodiment 4:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 35 parts;Metering system
Tert-butyl acrylate 25 parts;Ethoxylation tri methylol triacrylate 10 parts;Polyamide polyhydric alcohol 10 parts;Epoxy resin
14 parts;Hexamethylene diisocyanate 6 parts;Ethyl acetate 9 parts;Polyoxyethylene ether 11 parts;Dipropylene glycol methyl ether 4 parts;Octadecane
Base trichlorosilane 4 parts;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methylacrylate 7 parts;Kaolin 8 parts;White mica 7
Part;4 parts of glass dust;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;Glycol phenyl ether 1.5 parts;Triphenyl phosphite 3.5
Part;Glycerol 3 parts;Deionized water 40 parts.
Preparation method is with embodiment 1.
Embodiment 5:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 32 parts;Metering system
Tert-butyl acrylate 26 parts;Ethoxylation tri methylol triacrylate 12 parts;Polyamide polyhydric alcohol 11 parts;Epoxy resin
12 parts;Hexamethylene diisocyanate 6 parts;Ethyl acetate 8 parts;Polyoxyethylene ether 11 parts;Dipropylene glycol methyl ether 4 parts;Octadecane
Base trichlorosilane 2 parts;Hydroxypropyl methyl cellulose 10 parts;Hydroxyethyl methylacrylate 8 parts;Kaolin 7 parts;White mica 5
Part;3.5 parts of glass dust;Precipitated calcium carbonate 2 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 3.5 parts;
Glycerol 2 parts;Deionized water 42 parts.
Preparation method is with embodiment 1.
Embodiment 6:
A kind of indoor wood coating, including the raw material of following parts by weight: tripropylene glycol diacrylate 33 parts;Metering system
Tert-butyl acrylate 23 parts;Ethoxylation tri methylol triacrylate 11 parts;Polyamide polyhydric alcohol 12 parts;Epoxy resin
11 parts;Hexamethylene diisocyanate 5 parts;Ethyl acetate 11 parts;Polyoxyethylene ether 12 parts;Dipropylene glycol methyl ether 5 parts;Octadecane
Base trichlorosilane 2 parts;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methylacrylate 7 parts;Kaolin 8 parts;White mica 5
Part;3 parts of glass dust;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Glycol phenyl ether 1 part;Triphenyl phosphite 4 parts;
Glycerol 3 parts;Deionized water 30 parts.
Preparation method is with embodiment 1.
Product for embodiment 1-6 carries out performance measurement, and measured data are as shown in table 1.
It will be seen that the product adhesive force of the present invention is higher, the performance such as resistance to impact, salt spray resistance, wet-heat resisting is more superior.
Last it is noted that above example is only in order to illustrate technical scheme, it is not intended to limit;Although reference
The present invention has been described in detail by previous embodiment, it will be understood by those within the art that: it still can be to front
State the technical scheme described in each embodiment to modify, or wherein portion of techniques feature is carried out equivalent;And these are repaiied
Change or replace, not making the essence of appropriate technical solution depart from the scope of various embodiments of the present invention technical scheme.
Claims (9)
1. an indoor wood coating, it is characterised in that include the raw material of following parts by weight: tripropylene glycol diacrylate
29-35 part;Tert-butyl Methacrylate 21-26 part;Ethoxylation tri methylol triacrylate 8-15 part;Polyamide
Polyhydric alcohol 10-15 part;Epoxy resin 8-14 part;Hexamethylene diisocyanate 4-7 part;Ethyl acetate 7-11 part;Polyoxyethylene ether 10-13
Part;Dipropylene glycol methyl ether 3-6 part;Octadecyl trichlorosilane alkane 1-4 part;Hydroxypropyl methyl cellulose 8-11 part;Metering system
Acid hydroxyl ethyl ester 5-8 part;Kaolin 6-10 part;White mica 5-7 part;Glass dust 3-5 part;Precipitated calcium carbonate 1.5-2.5 part;Two
Silicon oxide 2-3 part;Glycol phenyl ether 1-2 part;Triphenyl phosphite 2-4 part;Glycerol 2-3 part;Deionized water 30-45 part.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 29 parts;Tert-butyl Methacrylate 22 parts;Ethoxylation tri methylol triacrylate 14 parts;Poly-
Amide resin polyhydric alcohol 13 parts;Epoxy resin 10 parts;Hexamethylene diisocyanate 4 parts;Ethyl acetate 7 parts;Polyoxyethylene ether 13
Part;Dipropylene glycol methyl ether 3 parts;1 part of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methacrylate second
Ester 5 parts;Kaolin 6 parts;White mica 5 parts;5 parts of glass dust;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Glycol
Phenyl ether 1 part;Triphenyl phosphite 2 parts;Glycerol 2 parts;Deionized water 35 parts.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 32 parts;Tert-butyl Methacrylate 21 parts;Ethoxylation tri methylol triacrylate 15 parts;Poly-
Amide resin polyhydric alcohol 15 parts;Epoxy resin 8 parts;Hexamethylene diisocyanate 7 parts;Ethyl acetate 11 parts;Polyoxyethylene ether 10
Part;Dipropylene glycol methyl ether 6 parts;3 parts of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 11 parts;Hydroxyethyl methacrylate second
Ester 8 parts;Kaolin 10 parts;White mica 6 parts;3 parts of glass dust;Precipitated calcium carbonate 2 parts;Silicon dioxide 2.5 parts;Glycol
Phenyl ether 1.5 parts;Triphenyl phosphite 4 parts;Glycerol 2.5 parts;Deionized water 30 parts.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 33 parts;Tert-butyl Methacrylate 23 parts;Ethoxylation tri methylol triacrylate 8 parts;Poly-
Amide resin polyhydric alcohol 14 parts;Epoxy resin 12 parts;Hexamethylene diisocyanate 5 parts;Ethyl acetate 10 parts;Polyoxyethylene ether
12 parts;Dipropylene glycol methyl ether 5 parts;2 parts of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 8 parts;Hydroxyethyl methacrylate
Ethyl ester 6 parts;Kaolin 10 parts;White mica 7 parts;4.5 parts of glass dust;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;
Glycol phenyl ether 2 parts;Triphenyl phosphite 3 parts;Glycerol 3 parts;Deionized water 45 parts.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 35 parts;Tert-butyl Methacrylate 25 parts;Ethoxylation tri methylol triacrylate 10 parts;Poly-
Amide resin polyhydric alcohol 10 parts;Epoxy resin 14 parts;Hexamethylene diisocyanate 6 parts;Ethyl acetate 9 parts;Polyoxyethylene ether 11
Part;Dipropylene glycol methyl ether 4 parts;4 parts of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methacrylate second
Ester 7 parts;Kaolin 8 parts;White mica 7 parts;4 parts of glass dust;Precipitated calcium carbonate 2.5 parts;Silicon dioxide 3 parts;Glycol
Phenyl ether 1.5 parts;Triphenyl phosphite 3.5 parts;Glycerol 3 parts;Deionized water 40 parts.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 32 parts;Tert-butyl Methacrylate 26 parts;Ethoxylation tri methylol triacrylate 12 parts;Poly-
Amide resin polyhydric alcohol 11 parts;Epoxy resin 12 parts;Hexamethylene diisocyanate 6 parts;Ethyl acetate 8 parts;Polyoxyethylene ether 11
Part;Dipropylene glycol methyl ether 4 parts;2 parts of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 10 parts;Hydroxyethyl methacrylate second
Ester 8 parts;Kaolin 7 parts;White mica 5 parts;3.5 parts of glass dust;Precipitated calcium carbonate 2 parts;Silicon dioxide 2 parts;Glycol
Phenyl ether 1 part;Triphenyl phosphite 3.5 parts;Glycerol 2 parts;Deionized water 42 parts.
Indoor wood coating the most according to claim 1, it is characterised in that include the raw material of following parts by weight: three
Propylene glycol diacrylate 33 parts;Tert-butyl Methacrylate 23 parts;Ethoxylation tri methylol triacrylate 11 parts;Poly-
Amide resin polyhydric alcohol 12 parts;Epoxy resin 11 parts;Hexamethylene diisocyanate 5 parts;Ethyl acetate 11 parts;Polyoxyethylene ether
12 parts;Dipropylene glycol methyl ether 5 parts;2 parts of octadecyl trichlorosilane alkane;Hydroxypropyl methyl cellulose 9 parts;Hydroxyethyl methacrylate
Ethyl ester 7 parts;Kaolin 8 parts;White mica 5 parts;3 parts of glass dust;Precipitated calcium carbonate 1.5 parts;Silicon dioxide 2 parts;Two
Alcohol phenyl ether 1 part;Triphenyl phosphite 4 parts;Glycerol 3 parts;Deionized water 30 parts.
Indoor wood coating the most according to claim 1, it is characterised in that: described Kaolin fineness is 500~800
Mesh.
Indoor wood coating the most according to claim 1, it is characterised in that: described white mica fineness is 400~600
Mesh.