CN104194549A - Water-base paint used for indoor woodware - Google Patents
Water-base paint used for indoor woodware Download PDFInfo
- Publication number
- CN104194549A CN104194549A CN201410406711.9A CN201410406711A CN104194549A CN 104194549 A CN104194549 A CN 104194549A CN 201410406711 A CN201410406711 A CN 201410406711A CN 104194549 A CN104194549 A CN 104194549A
- Authority
- CN
- China
- Prior art keywords
- water
- indoor
- borne coatings
- base paint
- woodware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a water-base paint used for indoor woodware. The paint is prepared from the following components in percentage by weight: 20-30% of silicone acrylic emulsion, 5-20% of color pigments, 5-10% of a modifier, 10-30% of composite filler and 40-50% of water, wherein the color pigments comprise 2-8% of low-arsenic ferric oxide, 5-11% of iron oxide red and 1-2% of methylbenzene; the composite filter comprises 1-5% of silica sol, 5-15% of calcium carbonate and 1-5% of a scratch-resistant wax auxiliary. The water-base paint has the advantages that the low-arsenic ferric oxide, iron oxide red and methylbenzene used as pigments are good in red formation and color homogeneity; the silicone acrylic emulsion can be used for effectively solving the antiseptic problem of the water-base paint to a certain extent; the modifier further improves the curing speed; the indoor woodware is coated with a good effect, and the service life of the woodware is prolonged. The water-base paint is suitable for being popularized.
Description
Technical field
The present invention relates to a kind of water-borne coatings, the water-borne coatings that especially indoor woodenware uses.
Background technology
Every coating that uses water as solvent or make dispersion medium, all can be described as water-borne coatings.Water-borne coatings comprises 3 kinds of water soluble paints, water-reducible coatings, water-dispersible paint (latex coating).Water soluble paint is taking water soluble resin as film forming matter, taking polyvinyl alcohol and various modifier thereof as representative, in addition also has water-soluble Synolac, water-soluble epoxy resin and inorganic polymer water-base resin etc.
At present, the water-borne coatings using at indoor woodenware is more, and the speed no matter normally used water-borne coatings still solidifies at film-forming properties does not all reach perfect condition, and current applied organosilicon crylic acid latex also exists certain hidden danger on antiseptic property simultaneously.
Summary of the invention
The technical problem to be solved in the present invention is to provide the water-borne coatings that a kind of indoor woodenware uses, and can effectively solve water-borne coatings film forming curing speed and antiseptic property is provided.
The present invention is achieved through the following technical solutions.
The water-borne coatings that a kind of indoor woodenware uses, according to mass percent, its composition comprises organosilicon crylic acid latex 20%-30%, color filler 5%-20%, properties-correcting agent 5%-10%, compounded mix 10%-30%, water 40%-50%, wherein color filler comprises low arsenic ferric oxide 2%-8%, red iron oxide 5%-11%, toluene 1%-2%, and compounded mix comprises silicon sol 1%-5%, calcium carbonate 5%-15%, scratch resistance wax assistant 1%-5%.
Further, above-mentioned properties-correcting agent comprises film forming auxiliary 1%-2%, acid esters emulsion 3%-5%, wooden fat slurry 1%-4%.
Further, above-mentioned acid esters emulsion is polyacrylate dispersion.
Further, above-mentioned film forming auxiliary is glycol phenyl ether.
Further, above-mentioned organosilicon crylic acid latex comprises butyl acrylate 10%-15%, Soxylat A 25-7 1%-5%, salt of wormwood 1%-5%, deionized water 5%-10%.
Beneficial effect of the present invention:
Low arsenic ferric oxide, red iron oxide, toluene are better as Pigment red quality, look even property, adopt butyl acrylate, Soxylat A 25-7, salt of wormwood, deionized water, can solve effectively to a certain extent the Anticorrosion of water-borne coatings; By using glycol phenyl ether to strengthen film-formation result as film forming auxiliary, and coordinate other compositions of properties-correcting agent that curing speed is also improved; The effect of indoor woodenware painting use is better, has extended work-ing life, is suitable for promoting.
Embodiment
According to embodiment, the present invention is described in further detail below.
Case study on implementation 1:
The water-borne coatings that a kind of indoor woodenware uses, according to mass percent, its composition comprises organosilicon crylic acid latex 20%, color filler 15%, properties-correcting agent 10%, compounded mix 15%, water 40%, wherein color filler comprises low arsenic ferric oxide 5%, red iron oxide 9%, toluene 1%, and compounded mix comprises silicon sol 2%, calcium carbonate 11%, scratch resistance wax assistant 2%.
Wherein, properties-correcting agent comprises film forming auxiliary 1%, acid esters emulsion 5%, wooden fat slurry 4%, and above-mentioned acid esters emulsion is polyacrylate dispersion, and above-mentioned film forming auxiliary is glycol phenyl ether.
Organosilicon crylic acid latex comprises butyl acrylate 10%, Soxylat A 25-7 1%, salt of wormwood 3%, deionized water 6%.
Case study on implementation 2:
The water-borne coatings that a kind of indoor woodenware uses, according to mass percent, its composition comprises organosilicon crylic acid latex 30%, color filler 10%, properties-correcting agent 5%, compounded mix 15%, water 50%, wherein color filler comprises low arsenic ferric oxide 2%, red iron oxide 6%, toluene 2%, and compounded mix comprises silicon sol 3%, calcium carbonate 10%, scratch resistance wax assistant 2%.
Wherein, above-mentioned properties-correcting agent comprises film forming auxiliary 1%, acid esters emulsion 3%, wooden fat slurry 1%, and above-mentioned acid esters emulsion is polyacrylate dispersion, and above-mentioned film forming auxiliary is glycol phenyl ether.
Organosilicon crylic acid latex comprises butyl acrylate 15%, Soxylat A 25-7 5%, salt of wormwood 5%, deionized water 5%.
Above-described embodiment is only explanation technical conceive of the present invention and feature, and its object is to allow the personage who is familiar with this art can understand content of the present invention and be implemented, and can not limit the scope of the invention with this.All equivalences that spirit is done according to the present invention change or modify, and all should be encompassed in protection scope of the present invention.
Claims (5)
1. the water-borne coatings that indoor woodenware uses, it is characterized in that, according to mass percent, its composition comprises organosilicon crylic acid latex 20%-30%, color filler 5%-20%, properties-correcting agent 5%-10%, compounded mix 10%-30%, water 40%-50%, wherein color filler comprises low arsenic ferric oxide 2%-8%, red iron oxide 5%-11%, toluene 1%-2%, and compounded mix comprises silicon sol 1%-5%, calcium carbonate 5%-15%, scratch resistance wax assistant 1%-5%.
2. the water-borne coatings that indoor woodenware according to claim 1 uses, is characterized in that, described properties-correcting agent comprises film forming auxiliary 1%-2%, acid esters emulsion 3%-5%, wooden fat slurry 1%-4%.
3. the water-borne coatings that indoor woodenware according to claim 2 uses, is characterized in that, described acid esters emulsion is polyacrylate dispersion.
4. the water-borne coatings that indoor woodenware according to claim 2 uses, is characterized in that, described film forming auxiliary is glycol phenyl ether.
5. the water-borne coatings that indoor woodenware according to claim 1 uses, is characterized in that, described organosilicon crylic acid latex comprises butyl acrylate 10%-15%, Soxylat A 25-7 1%-5%, salt of wormwood 1%-5%, deionized water 5%-10%.